CN101444842B - 一种钢包用碱性引流砂 - Google Patents

一种钢包用碱性引流砂 Download PDF

Info

Publication number
CN101444842B
CN101444842B CN2008102469155A CN200810246915A CN101444842B CN 101444842 B CN101444842 B CN 101444842B CN 2008102469155 A CN2008102469155 A CN 2008102469155A CN 200810246915 A CN200810246915 A CN 200810246915A CN 101444842 B CN101444842 B CN 101444842B
Authority
CN
China
Prior art keywords
flow guiding
steel ladle
alkaline flow
sand used
percent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN2008102469155A
Other languages
English (en)
Other versions
CN101444842A (zh
Inventor
孙中强
陆彩云
芮树森
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Northeastern University Metallurgical Technology Institute Co Ltd
Original Assignee
METALLURGY TECHNOLOGY RESEARCH INSTITUTE Co Ltd NORTHEAST UNIVERSITY
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by METALLURGY TECHNOLOGY RESEARCH INSTITUTE Co Ltd NORTHEAST UNIVERSITY filed Critical METALLURGY TECHNOLOGY RESEARCH INSTITUTE Co Ltd NORTHEAST UNIVERSITY
Priority to CN2008102469155A priority Critical patent/CN101444842B/zh
Publication of CN101444842A publication Critical patent/CN101444842A/zh
Application granted granted Critical
Publication of CN101444842B publication Critical patent/CN101444842B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种钢包用碱性引流砂，属于冶金技术领域，该引流砂的化学组成按重量百分比为：30～50％的钝化石灰、5～15％的方解石、5～10％的刚玉、20～40％的煅烧镁橄榄石砂、1～5％的鳞片状石墨，各成分按比例配制后均匀混合而成。本发明所制备的钢包用碱性引流砂具有耐火度高、抗侵蚀性强、自开率高、价格低廉、不会造成环境污染、不破坏中间包冶金环境、使用方便的特点。

Description

一种钢包用碱性引流砂
技术领域
本发明属于冶金技术领域，特别涉及一种钢包用碱性引流砂。
背景技术
随着洁净钢需求的不断增加和人们对环境保护问题的关注，工业生产对引流砂使用性能的要求不断提高，不仅要求引流砂能使钢包自动开浇，还应减少引流砂带进的成分对中间包冶金过程的不利影响，对环境污染小。优质的引流砂应自然流动性好、热膨胀倾向小，与钢液接触后迅速在钢-砂界面形成致密的烧结层，以防止钢液的渗透和引流砂颗粒的上浮，且烧结后的引流砂强度较低，能被钢液的静压力冲破，达到自然开浇的效果。钢包实现自动引流开浇是稳定全保护连续浇铸操作工艺，保证钢液质量的关键环节。
目前国内外使用的引流砂以硅质、铬质和镁质为主。
硅质引流砂以石英砂为基料，配以长石低熔物作为促进烧结剂，具有较高的自开浇率。但石英砂中的SiO2会降低中间包覆盖剂的碱度和侵蚀碱性包衬，给中间包碱性冶金环境带来不利的影响。有的厂家采用了精制石英砂作为主要原料，但是，加工精制石英砂会造成生产成本提高，同时加工石英砂产生的硅质粉尘会严重影响工人身体健康。
铬质引流砂以铬矿砂为主，其烧结性能好、开浇率高，但铬矿砂价格昂贵，不仅提高了生产成本，更重要的是铬矿砂中原本无害的Cr3+在碱性气氛下被氧化生成Cr6+，对环境造成极大污染。
镁质引流砂以镁橄榄石和镁砂为主要原料，呈弱碱性，有利于中间包碱性环境的形成。但其烧结性能难于控制，需加入铬矿砂控制烧结，且其弱碱性对中间包碱性环境去除夹杂物所发挥的作用有限。
发明内容
本发明针对现有引流砂存在的问题，提供一种耐火度高、抗侵蚀性强、自开率离、价格低廉、不会造成环境污染、不破坏中间包冶金环境、使用方便的碱性引流砂。
本发明所采用的技术方案是：先将30～50％的钝化石灰、5～15％的方解石、5～10％的刚玉、20～40％的煅烧镁橄榄石砂、1～5％的鳞片石墨混合均匀，然后按照每袋10kg分袋包装，以防止物料偏析。
其中，钝化石灰中CaO＞92％，粒径为＜2mm，水分≯0.5％；方解石中CaCO3＞95％，白度大于90％，平均粒径＜1mm，水分≯0.5％；刚玉中Al2O3＞85％，平均粒径＜1mm，水分≯0.5％；煅烧镁橄榄石砂中MgO＞40％，SiO2＞35％，粒径为2～1mm，水分≯0.5％；鳞片状石墨中固定C＞95％，平均粒径＜0.074mm。
由于采用上述技术方案，本发明所制备的钢包用环保型碱性引流砂具有耐火度高、抗侵蚀性强、自开率高、价格低廉、不会造成环境污染、不破坏中间包冶金环境、使用方便的特点。
具体实施方式
实施例1
先将40％的钝化石灰、15％的方解石、10％的刚玉、33％的煅烧镁橄榄石砂、2％份的鳞片石墨混合均匀，然后按照每袋10kg分袋包装，以防止物料偏析。
其中，钝化石灰中CaO＞92％，粒径为＜2mm，水分≯0.5％；方解石中CaCO3＞95％，白度大于90％，平均粒径＜1mm，水分≯0.5％；刚玉中Al2O3＞85％，平均粒径＜1mm，水分≯0.5％；煅烧镁橄榄石砂中MgO＞40％，SiO2＞35％，粒径为2～1mm，水分≯0.5％；鳞片状石墨中固定C＞95％，平均粒径＜0.074mm。
将此配比的引流砂用于某钢厂，自开率达98％以上。
实施例2
先将50％的钝化石灰、10％的方解石、5％的刚玉、30％的煅烧镁橄榄石砂、5％的鳞片石墨混合均匀，然后按照每袋10kg分袋包装，以防止物料偏析。
其中，钝化石灰中CaO＞92％，粒径为＜2mm，水分≯0.5％；方解石中CaCO3＞95％，白度大于90％，平均粒径＜1mm，水分≯0.5％；刚玉中Al2O3＞85％，平均粒径＜1mm，水分≯0.5％；煅烧镁橄榄石砂中MgO＞40％，SiO2＞35％，粒径为2～1mm，水分≯0.5％；鳞片状石墨中固定C＞95％，平均粒径＜0.074mm。
将此配比的引流砂用于某钢厂，自开率达97％以上。

Claims (6)

1.一种钢包用碱性引流砂，其特征在于该引流砂的化学组成按重量百分比为：30～50％的钝化石灰、5～15％的方解石、5～10％的刚玉、20～40％的煅烧镁橄榄石砂、1～5％的鳞片状石墨，各成分按比例配制后均匀混合而成。
2.根据权利要求1所述的钢包用碱性引流砂，其特征在于所述的钝化石灰中CaO＞92％，粒径为＜2mm，水分≯0.5％。
3.根据权利要求1所述的钢包用碱性引流砂，其特征在于所述的方解石含CaCO3＞95％，白度大于90％，平均粒径＜1mm，水分≯0.5％。
4.根据权利要求1所述的钢包用碱性引流砂，其特征在于所述的刚玉含Al2O3＞85％，平均粒径＜1mm，水分≯0.5％。
5.根据权利要求1所述的钢包用碱性引流砂，其特征在于所述的煅烧镁橄榄石砂中MgO＞40％，SiO2＞35％，粒径为2～1mm，水分≯0.5％。
6.根据权利要求1所述的钢包用碱性引流砂，其特征在于所述的鳞片状石墨中固定C＞98％，平均粒径＜0.074mm。
CN2008102469155A 2008-12-30 2008-12-30 一种钢包用碱性引流砂 Expired - Fee Related CN101444842B (zh)