CN104762049A - 一种阻燃树脂胶黏剂及其制备方法和应用 - Google Patents
一种阻燃树脂胶黏剂及其制备方法和应用 Download PDFInfo
- Publication number
- CN104762049A CN104762049A CN201510209701.0A CN201510209701A CN104762049A CN 104762049 A CN104762049 A CN 104762049A CN 201510209701 A CN201510209701 A CN 201510209701A CN 104762049 A CN104762049 A CN 104762049A
- Authority
- CN
- China
- Prior art keywords
- flame
- accounts
- sizing agent
- gross weight
- retarded resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明属于胶黏剂技术领域,特别涉及一种阻燃树脂胶黏剂及其制备方法和应用。阻燃树脂胶黏剂,它由黏胶剂原料制得,所述胶黏剂原料包括:甲醛、苯酚、DOPO、碱性物质、三聚氰胺和水;其中:甲醛和苯酚的重量之和占总重量的25-40%,所述甲醛/苯酚的摩尔比为1.5-3.5;DOPO占总重量的2-10%;碱性物质,占总重量的5-15%;三聚氰胺,占总重量的2-15%;水,占总重量的15-30%。本发明所述阻燃树脂胶黏剂具有耐高温、游离甲醛少的特点。
Description
技术领域
本发明属于胶黏剂技术领域,特别涉及一种阻燃树脂胶黏剂及其制备方法和应用。
背景技术
随着经济的繁荣,人们生活形态呈现多样化、丰富化,近几年,恶性火灾事故时有发生,不仅造成大量人员伤亡、财产损失,还给社会造成恶劣影响,因此,国家消防局加强了建筑尤其是公共场所的消防要求,规定人员密集场所必须采用阻燃制品。
CN201210266243.0,该发明采用苯酚与甲醛在弱碱性条件下生成热固性酚醛树脂,三聚氰胺对酚醛树脂进行改性,与未经改性的酚醛树脂相比,阻燃性能虽然有一定的提高,但还是不能满足有特殊要求的高温条件下板材的粘合,并有一定量的甲醛产生。
发明内容
为了克服现有技术的不足,本发明提供了一种耐高温、游离甲醛少的阻燃木材粘合剂及其制备方法和应用。
本发明的第一目的是提供一种阻燃树脂胶黏剂,具体技术方案如下:
一种阻燃树脂胶黏剂,其特征在于,它由黏胶剂原料制得,所述胶黏剂原料包括:甲醛、苯酚、DOPO(9,10-二氢-9-氧杂-10-磷杂菲-10-氧化物的简称)、碱性物质、三聚氰胺和水;
其中:甲醛和苯酚的重量之和占总重量的25-40%,所述甲醛/苯酚的摩尔比为1.5-3.5;DOPO占总重量的2-10%;碱性物质,占总重量的5-15%;三聚氰胺,占总重量的2-15%;水,占总重量的15-30%。
作为优选,所述碱性物质为氢氧化钠、氢氧化钾、氢氧化钙、氢氧化钡或氨水。
作为优选,所述胶黏剂原料包括:甲醛和苯酚的重量之和占总重量的25-30%,所述甲醛/苯酚的摩尔比为1.5-2.5;DOPO占总重量的5-10%;氢氧化钠占总重量的5-10%;三聚氰胺占总重量的2-10%;水占总重量的15-20%。
作为优选,所述DOPO为以下物质:
A
或
B
本发明的第二目的是提供一种阻燃树脂胶黏剂的制备方法,其特征在于包括以下步骤:
1)配置质量浓度为15-50%的碱性溶液;
2)将苯酚液化;
3)在反应容器中加入步骤2)所得液化苯酚、DOPO和水,加热至75-100℃,再加入三聚氰胺,保温20-90min,得到混合溶液;
4)向步骤3)所得混合溶液降温至40-60℃,加入步骤1)所得碱性溶液和甲醛,搅拌,保温30-40min;
5)升温至70-100℃,搅拌,保温50-70min,降温至30-40℃出胶。
所述步骤1)和步骤2)无先后顺序。
作为优选,所述步骤1)中碱性溶液的质量浓度为15-25%。
作为优选,所述步骤3)加热温度为75-80℃。
作为优选,所述步骤4)降温至40-50℃。
作为优选,所述步骤5)升温至95℃。
本发明的第三目的是提供一种阻燃树脂胶黏剂在阻燃板材粘合方面的应用,如:高等级阻燃强化板材和阻燃实木板材方面的应用。将本发明所述的阻燃树脂胶黏剂直接涂覆在板材上,在受热过程,会形成一层均匀的炭质泡沫层,起到耐高温、抑烟、隔氧的作用。
本发明所述的种阻燃树脂胶黏剂的原料组份包括苯酚、三聚氰胺、甲醛等,以苯酚、三聚氰胺、甲醛为基体,把9,10-二氢-9-氧杂-10-磷杂菲-10-氧化物(DOPO)与甲醛的加成反应产物(见反应式一)加入基体中参加缩聚反应,从而引入磷杂菲基团(见式反应式二、三)。
反应式一
反应式二
反应式三
1)本发明把含磷杂菲基团的DOPO(如:A、B)引入阻燃树脂胶粘剂,合成了一种反应型阻燃胶粘剂,用三聚氰胺对酚醛树脂进行改性,阻燃性能提高,固化后生成三位网状交联结构体系,结构较为稳定,在反应过程中,甲醛跟磷杂菲发生加成反应,再进一步与固化后生成的三位网状交联结构进行缩聚,所得含磷杂菲的缩聚物结构更稳定,所以所得阻燃胶黏剂非常稳定,同时还降低了游离甲醛的排放,符合绿色环保的要求。
磷杂菲基团具有杂环含磷特性、非共平面性、与分子内或分子间基团的相互作用性、分子极性等特点,将磷杂菲基团引入阻燃胶粘剂中,固化后的阻燃胶粘剂的玻璃化转变温度将会明显提高,燃烧时无熔滴且发烟量更低,其受热降解后的成炭量将会明显提高,将此胶黏剂涂覆在板材上,在受热过程,会形成一层均匀的炭质泡沫层,耐高温的同时,还能起到抑烟、隔氧的作用,即达到良好的阻燃的效果。
另一方面,本发明为合成反应型阻燃胶粘剂,相比添加型阻燃胶粘剂,反应型阻燃胶粘剂的阻燃效果更持久、阻燃效率更高,具有耐溶出、难迁移、不易扩散和优良的熔流速率,同时符合无卤、低毒、低烟、环保的主流发展趋势。
2)本发明所述阻燃胶粘剂可直接用于阻燃板材的粘合,如:高等级阻燃强化板材和阻燃实木板材的生产。将此胶黏剂涂覆在板材上,在受热过程,会形成一层均匀的炭质泡沫层,改变了现有的常规浸渍生产方案,起到简化工艺,降低成本作用,有助于阻燃板材产品的推广应用。
3)本发明提供的阻燃树脂胶黏剂的制备方法,制备工艺简单,条件温和,所制得的产品具有耐高温、游离甲醛少等优点。
具体实施方式
为能清楚说明本方案的技术特点,下面通过具体实施方式对本方案进行阐述。
以下实施例中所述A、B物质对应的结构式在发明内容中已有说明。
实施例1
一种阻燃树脂胶黏剂,它由黏胶剂原料制得,所述胶黏剂原料包括:甲醛和苯酚的重量之和占总重量的25%,所述甲醛/苯酚的摩尔比为1.5;A占总重量的10%;氢氧化钠,占总重量的5%;三聚氰胺,占总重量的15%;水,占总重量的15%。
实施例2
一种阻燃树脂胶黏剂,它由黏胶剂原料制得,所述胶黏剂原料包括:甲醛和苯酚的重量之和占总重量的40%,所述甲醛/苯酚的摩尔比为3.5;B占总重量的5%;氢氧化钙,占总重量的15%;三聚氰胺,占总重量的2%;水,占总重量的30%。
实施例3
一种阻燃树脂胶黏剂,它由黏胶剂原料制得,所述胶黏剂原料包括:甲醛和苯酚的重量之和占总重量的30%,所述甲醛/苯酚的摩尔比为2.5;A占总重量的2%;氨水,占总重量的10%;三聚氰胺,占总重量的10%;水,占总重量的20%。
实施例4(采用实施例1的原料配比)
1)配置质量浓度为15%的氢氧化钠溶液;
2)将苯酚液化;
3)在反应容器中加入步骤2)所得液化苯酚、A和水,加热至100℃,再加入三聚氰胺,保温20min,得到混合溶液;
4)向步骤3)所得混合溶液降温至60℃,加入步骤1)所得氢氧化钠溶液和甲醛,搅拌,保温30min;
5)升温至100℃,搅拌,保温50min,降温至40℃出胶。
所述步骤1)和步骤2)无先后顺序。
实施例5(采用实施例2的原料配比)
1)配置质量浓度为50%的氢氧化钙溶液;
2)将苯酚液化;
3)在反应容器中加入步骤2)所得液化苯酚、B和水,加热至75℃,再加入三聚氰胺,保温90min,得到混合溶液;
4)向步骤3)所得混合溶液降温至40℃,加入步骤1)所得氢氧化钙溶液和甲醛,搅拌,保温40min;
5)升温至70℃,搅拌,保温70min,降温至30℃出胶。
所述步骤1)和步骤2)无先后顺序。
实施例6(采用实施例3的原料配比)
1)配置质量浓度为25%的氨水溶液;
2)将苯酚液化;
3)在反应容器中加入步骤2)所得液化苯酚、A和水,加热至80℃,再加入三聚氰胺,保温50min,得到混合溶液;
4)向步骤3)所得混合溶液降温至50℃,加入步骤1)所得氨水溶液和甲醛,搅拌,保温35min;
5)升温至95℃,搅拌,保温70min,降温至40℃出胶。
所述步骤1)和步骤2)无先后顺序。
对照实施例1-3
与实施例4-6分别对应,不同之处仅仅在于未添加DOPO(A或B)。
以上实施例所得实验数据参考下表:
本发明所述的碱性物质还可以为氢氧化钾、氢氧化钡,从以上实施例及表格数据可以看出,在制备板材阻燃粘合剂过程中,通过添加磷杂菲化合物DOPO(A或B),参与聚合反应,所制得的胶黏剂具有较好的阻燃效果,而且游离甲醛少,所以本发明所述的阻燃树脂胶黏剂不仅耐高温,阻燃性好,而且甲醛释放量少,适应绿色环保的要求。
申请人通过大量的实验证明,以纤维板、刨花板、胶合板等为基材,使用本发明所述的阻燃树脂粘合剂粘合,所制得木质复合地板符合防火阻燃地板国标(GB/T24509-2009)要求,达到B1级别的阻燃标准以及烟毒等级标准。
当然,上述说明并非是对本发明的限制,本发明也并不仅限于上述举例,本技术领域的普通技术人员在本发明的实质范围内所做出的变化、改型、添加或替换,并不构成实质创新,也都属于本发明的保护范围。
Claims (10)
1.一种阻燃树脂胶黏剂,其特征在于,它由黏胶剂原料制得,所述胶黏剂原料包括:甲醛、苯酚、DOPO、碱性物质、三聚氰胺和水;
其中:甲醛和苯酚的重量之和占总重量的25-40%,所述甲醛/苯酚的摩尔比为1.5-3.5;DOPO占总重量的2-10%;碱性物质,占总重量的5-15%;三聚氰胺,占总重量的2-15%;水,占总重量的15-30%。
2.根据权利要求1所述的阻燃树脂胶黏剂,所述碱性物质为氢氧化钠、氢氧化钾、氢氧化钙、氢氧化钡或氨水。
3.根据权利要求1所述的阻燃树脂胶黏剂,其特征在于所述胶黏剂原料包括:甲醛和苯酚的重量之和占总重量的25-30%,所述甲醛/苯酚的摩尔比为1.5-2.5;DOPO占总重量的5-10%;氢氧化钠占总重量的5-10%;三聚氰胺占总重量的2-10%;水占总重量的15-20%。
4.根据权利要求1所述的阻燃树脂胶黏剂,其特征在于所述DOPO为以下物质:
A
或
B。
5.根据权利要求1所述的阻燃树脂胶黏剂的制备方法,其特征在于包括以下步骤:
1)配置质量浓度为15-50%的碱性溶液;
2)将苯酚液化;
3)在反应容器中加入步骤2)所得液化苯酚、DOPO和水,加热至75-100℃,再加入三聚氰胺,保温20-90min,得到混合溶液;
4)向步骤3)所得混合溶液降温至40-60℃,加入步骤1)所得碱性溶液和甲醛,搅拌,保
温30-40min;
5)升温至70-100℃,搅拌,保温50-70min,降温至30-40℃出胶;
所述步骤1)和步骤2)无先后顺序。
6.根据权利要求4所述的阻燃树脂胶黏剂的制备方法,其特征在于,所述步骤1)中的质量浓度为15-25%。
7.根据权利要求4所述的阻燃树脂胶黏剂的制备方法,其特征在于,所述步骤3)加热温度为75-80℃。
8.根据权利要求4所述的阻燃树脂胶黏剂的制备方法,其特征在于,所述步骤4)降温至40-50℃。
9.根据权利要求4所述的阻燃树脂胶黏剂的制备方法,其特征在于,所述步骤5)升温至95℃。
10.根据权利要求1所述的阻燃树脂胶黏剂在阻燃板材的粘合方面的应用。