CN104388730A - 一种铝合金用高效精炼剂及其制备方法 - Google Patents
一种铝合金用高效精炼剂及其制备方法 Download PDFInfo
- Publication number
- CN104388730A CN104388730A CN201410666499.XA CN201410666499A CN104388730A CN 104388730 A CN104388730 A CN 104388730A CN 201410666499 A CN201410666499 A CN 201410666499A CN 104388730 A CN104388730 A CN 104388730A
- Authority
- CN
- China
- Prior art keywords
- parts
- refining agent
- aluminium alloy
- preparation
- aluminum alloy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明提供一种铝合金用高效精炼剂，所述精炼剂由以下质量份数的各组分组成：NaCl30-35份、KCl25-28份、Na3AlF68-10份、Na2SiF66-8份、Na2CO33-5份、NaF2-5份、Na2SO4 2-5份、<sub/>CaS2-3份。本发明还提供其制备方法。使用本发明精炼剂对铝合金进行熔炼，除气除杂效果更好，可以使铝合金熔体中的氢含量更低，能更有效地降低金属的烧损。本发明的精炼剂的制备方法简单，可操作性强。
Description
技术领域
本发明涉及一种铝合金用高效精炼剂。
背景技术
在生产中，铝合金溶液在凝固过程中，铝合金溶液中的氢原子自发的形成氢气分子，氢气分子和以非金属夹杂物在凝固时候形成气泡，而夹杂是铝合金铸件中产生缺陷的主要原因，铝合金溶液中绝大部分的杂质和气体来自于回炉料，故在铝合金熔炼时，铝合金的精炼处理必不可少。通过精炼提高铝合金的冶金质量显得非常重要，目前所用精炼剂普遍存在着精炼效果不佳的问题。
发明内容
为了解决现有技术中存在的问题，本发明提供了一种铝合金用高效精炼剂；为此，本发明还提供其制备方法。
本发明提供一种铝合金用高效精炼剂，所述精炼剂由以下质量份数的各组分组成：NaCl 30-35份、KCl 25-28份、Na3AlF6 8-10份、Na2SiF6 6-8份、Na2CO3 3-5份、NaF 2-5份、Na2SO42-5份、、CaS 2-3份。
优选地，所述精炼剂由以下质量份数的各组分组成：NaCl 32份、KCl 26份、Na3AlF6 9份、Na2SiF6 7份、Na2CO3 4份、NaF 3份、Na2SO44份、、CaS 2.5份。
本发明还提供上述铝合金用高效精炼剂的制备方法，是将配方量的各组分混合均匀，充分搅拌，放入坩埚中过热熔化除去结晶水，再保温30～60分钟；最后，冷却后加工，即可得到精炼剂。
使用本发明精炼剂对铝合金进行熔炼，除气除杂效果更好，可以使铝合金熔体中的氢含量更低，能更有效地降低金属的烧损。本发明的精炼剂的制备方法简单，可操作性强。
具体实施方式
以下的实施例便于更好地理解本发明，但并不限定本发明。下述实施例中的实验方法，如无特殊说明，均为常规方法。
实施例1
本发明的铝合金用高效精炼剂的配方如下：
NaCl 32kg、KCl 26kg、Na3AlF6 9kg、Na2SiF6 7kg、Na2CO3 4kg、NaF 3kg、Na2SO44kg、、CaS 2.5kg。
本发明的铝合金用高效精炼剂的制备方法如下：
将NaCl 32kg、KCl 26kg、Na3AlF6 9kg、Na2SiF6 7kg、Na2CO3 4kg、NaF 3kg、Na2SO4 4kg、、CaS 2.5kg混合均匀，充分搅拌，放入坩埚中过热熔化除去结晶水，再保温45分钟；最后，冷却后加工，即可得到精炼剂。
实施例2
本发明的铝合金用高效精炼剂的配方如下：
NaCl 35kg、KCl 25kg、Na3AlF6 8kg、Na2SiF6 6kg、Na2CO3 3kg、NaF 2kg、Na2SO45kg、、CaS 2kg。
本发明的铝合金用高效精炼剂的制备方法如下：
将配方量的混合均匀，充分搅拌，放入坩埚中过热熔化除去结晶水，再保温30分钟；最后，冷却后加工，即可得到精炼剂。
实施例3
本发明的铝合金用高效精炼剂的配方如下：
NaCl 30kg、KCl 28kg、Na3AlF6 10kg、Na2SiF6 8kg、Na2CO3 5kg、NaF 5kg、Na2SO42kg、、CaS 3kg。
本发明的铝合金用高效精炼剂的制备方法如下：
将配方量的混合均匀，充分搅拌，放入坩埚中过热熔化除去结晶水，再保温60分钟；最后，冷却后加工，即可得到精炼剂。
使用时，将本发明的精炼剂放入精炼罐中，当铝合金液体温度达到700-740℃时，向所述精炼罐内通入氮气，将本发明的精炼剂送入铝合金液体中。
最后应说明的是：以上所述仅为本发明的优选实施例而已，并不用于限制本发明，尽管参照前述实施例对本发明进行了详细的说明，对于本领域的技术人员来说，其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换。凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (3)
1.一种铝合金用高效精炼剂，其特征在于：所述精炼剂由以下质量份数的各组分组成：NaCl 30-35份、KCl 25-28份、Na3AlF6 8-10份、Na2SiF6 6-8份、Na2CO3 3-5份、NaF 2-5份、Na2SO4 2-5份、、CaS 2-3份。
2.根据权利要求1所述的铝合金用高效精炼剂，其特征在于：所述精炼剂由以下质量份数的各组分组成：NaCl 32份、KCl 26份、Na3AlF6 9份、Na2SiF6 7份、Na2CO3 4份、NaF 3份、Na2SO44份、、CaS 2.5份。
3.权利要求1或2所述的铝合金用高效精炼剂的制备方法，其特征在于：是将配方量的各组分混合均匀，充分搅拌，放入坩埚中过热熔化除去结晶水，再保温30～60分钟；最后，冷却后加工，即可得到精炼剂。