CN104356963A - 一种耐高温螺纹锁固厌氧胶及其制备方法 - Google Patents
一种耐高温螺纹锁固厌氧胶及其制备方法 Download PDFInfo
- Publication number
- CN104356963A CN104356963A CN201410664200.7A CN201410664200A CN104356963A CN 104356963 A CN104356963 A CN 104356963A CN 201410664200 A CN201410664200 A CN 201410664200A CN 104356963 A CN104356963 A CN 104356963A
- Authority
- CN
- China
- Prior art keywords
- temperature resistant
- high temperature
- resistant thread
- thread locking
- anaerobic glue
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种耐高温螺纹锁固厌氧胶及其制备方法,以质量百分数计,包括如下配比的组分:甲基丙烯酸酯单体70~83%,稳定剂1~3%,双马来酰亚胺7~15%,促进剂2~5%,引发剂2~5%,填料2~5%,染料0.1~0.5%。本发明制备的厌氧胶能耐高温230℃,可用于一些对温度有较高要求的螺纹锁固。
Description
技术领域
本发明涉及一种耐高温螺纹锁固厌氧胶,属于胶黏剂技术领域。
背景技术
厌氧胶是指能起粘接、固定和密封作用的一系列厌氧固化特性的组成物,一般由丙烯酸酯类单体、稳定剂、促进剂和引发剂组成,另外还可根据需要加入某些助剂等。在储存时,胶液由于与空气接触不会发生固化,而使用时,胶液隔绝空气后,在金属离子的作用下会自发固化,从而起到粘接、固定或密封的作用。在螺纹连接中,各种螺钉由于受轴向和横向外力的作用非常容易松动,使用机械的方法,如提高紧固扭矩或提高轴向力的方法,虽然一定程度上使其松动是困难的,但是可靠性不高,而在螺纹装配时使用厌氧胶可保证连接的可靠性,用普通螺母就可以取代昂贵的保险螺母。但由于普通的厌氧胶只能用于150℃以下的环境中,限制了在其在较高温度下的使用,而越来越多的行业对耐高温厌氧胶的使用需求不断提高,因此开发一种耐高温的螺纹锁固厌氧胶以满足较高温度的使用要求是很有必要的。
发明内容
针对现有技术中存在的问题,本发明的目的在于提供一种耐高温螺纹锁固厌氧胶。
实现本发明目的的技术解决方案为:一种耐高温螺纹锁固厌氧胶,以质量百分数计,包括如下组分及其配比(%):
甲基丙烯酸酯单体 70~83
稳定剂 1~3
双马来酰亚胺 7~15
促进剂 2~5
引发剂 2~5
填料 2~5
染料 0.1~0.5。
上述甲基丙烯酸酯单体选自聚乙二醇200双甲基丙烯酯、二缩三乙二醇双甲基丙烯酸酯、三缩四乙二醇双甲基丙烯酸酯、乙氧化双酚A双甲基丙烯酸酯、甲基丙烯酸羟乙酯或甲基丙烯酸羟丙酯中的一种或几种的混合物。
上述稳定剂选自对苯二酚、萘醌、对甲氧基苯酚、乙二胺四乙酸二钠或乙二胺四乙酸四钠中的一种或几种的混合物。
上述促进剂选自乙酰苯肼、马来酸、N,N-二甲基对甲苯胺、N,N-二乙基对甲苯胺或邻苯甲酰磺酰亚胺中的一种或几种的混合物。
上述引发剂选自异丙苯过氧化氢或叔丁基过氧化氢中的一种。
上述填料选自气相二氧化硅、聚四氟乙烯粉或聚乙烯粉中的一种。
上述染料选自油化红、油化蓝或油化绿中的一种。
一种耐高温螺纹锁固厌氧胶的制备方法包括如下制备步骤:
步骤1、将70~83%的甲基丙烯酸酯单体和1~3%的稳定剂加入反应釜中,在50℃下搅拌混合60分钟;
步骤2、冷却至常温,然后在搅拌下依次加入7~15%的双马来酰亚胺,2~5%的促进剂,2~5%的引发剂,2~5%的填料,0.1~0.5%的染料搅拌120分钟至全溶即可。
具体实施方式
分别配置如下实施例所述组分及其配比的厌氧剂,并进行测试。各实施例的配比均以质量百分数计。
实施例1
二缩三乙二醇双甲基丙烯酸酯 55
甲基丙烯酸羟丙酯 15
双马来酰亚胺 15
乙二胺四乙酸二钠 1
对甲氧基苯酚 2
N,N-二甲基对甲苯胺 2
邻苯甲酰磺酰亚胺 3
异丙苯过氧化氢 4.5
气相二氧化硅 2
油化红 0.5。
实施例2
聚乙二醇200双甲基丙烯酯 55
甲基丙烯酸羟丙酯 15
双马来酰亚胺 15
乙二胺四乙酸二钠 1
对甲氧基苯酚 2
N,N-二甲基对甲苯胺 2
邻苯甲酰磺酰亚胺 3
异丙苯过氧化氢 4.5
气相二氧化硅 2
油化红 0.5。
实施例3
三缩四乙二醇双甲基丙烯酸酯 63
甲基丙烯酸羟乙酯 20
双马来酰亚胺 7
乙二胺四乙酸四钠 0.7
对苯二酚 1
N,N-二乙基对甲苯胺 1
邻苯甲酰磺酰亚胺 2
叔丁基过氧化氢 2
聚四氟乙烯粉 3
油化绿 0.3。
实施例4
乙氧化双酚A双甲基丙烯酸酯 63
甲基丙烯酸羟乙酯 20
双马来酰亚胺 7
乙二胺四乙酸四钠 0.7
对苯二酚 1
N,N-二乙基对甲苯胺 1
邻苯甲酰磺酰亚胺 2
叔丁基过氧化氢 2
聚四氟乙烯粉 3
油化绿 0.3。
实施例5
乙氧化双酚A双甲基丙烯酸酯 55
甲基丙烯酸羟乙酯 20
双马来酰亚胺 11.9
乙二胺四乙酸二钠 0.5
萘醌 0.5
乙酰苯肼 0.5
马来酸 0.5
邻苯甲酰磺酰亚胺 1
异丙苯过氧化氢 5
聚乙烯粉 5
油化蓝 0.1。
比较例6
乙氧化双酚A双甲基丙烯酸酯 55
甲基丙烯酸羟乙酯 26.9
乙二胺四乙酸二钠 0.5
萘醌 0.5
乙酰苯肼 0.5
马来酸 0.5
邻苯甲酰磺酰亚胺 1
异丙苯过氧化氢 5
聚乙烯粉 10
油化蓝 0.1。
参考标准:GB 18747.1-2002 厌氧胶粘剂扭矩强度的测定(螺纹紧固件)
实施例1~5、比较例6所得的螺纹锁固厌氧胶的相关性能测试结果如下表所以:
由上表可以看出,本发明耐高温螺纹锁固厌氧胶与现有技术相比,耐热性能优良。
本发明同时公开了一种耐高温螺纹锁固厌氧胶的制备方法包括如下制备步骤:
步骤1、将70~83%的甲基丙烯酸酯单体和1~3%的稳定剂加入反应釜中,在50℃下搅拌混合60分钟;
步骤2、冷却至常温,然后在搅拌下依次加入7~15%的双马来酰亚胺,2~5%的促进剂,2~5%的引发剂,2~5%的填料,0.1~0.5%的染料搅拌120分钟至全溶即可。
以上所述本发明的实施例方案,都只能认为是对本发明的说明而不能限制本发明,权利要求书指出了本发明的保护范围,任何相当的含义和范围内的任何比例改变,若没有带来其他显著的、意想不到效果,都应认为也包括在本权利要求书的范围内。
Claims (8)
1.一种耐高温螺纹锁固厌氧胶,其特征在于,以质量百分数计,包括如下配比的组分:
甲基丙烯酸酯单体70~83%;
稳定剂 1~3%;
双马来酰亚胺 7~15%;
促进剂 2~5%;
引发剂 2~5%;
填料 2~5%;
染料 0.1~0.5%。
2.根据权利要求1所述的耐高温螺纹锁固厌氧胶,其特征在于:
所述甲基丙烯酸酯单体选自聚乙二醇200双甲基丙烯酯、二缩三乙二醇双甲基丙烯酸酯、三缩四乙二醇双甲基丙烯酸酯、乙氧化双酚A双甲基丙烯酸酯、甲基丙烯酸羟乙酯或甲基丙烯酸羟丙酯中的一种或几种的混合物。
3.根据权利要求1所述的耐高温螺纹锁固厌氧胶,其特征在于:
所述稳定剂选自对苯二酚、萘醌、对甲氧基苯酚、乙二胺四乙酸二钠或乙二胺四乙酸四钠中的一种或几种的混合物。
4.根据权利要求1所述的耐高温螺纹锁固厌氧胶,其特征在于:
所述促进剂选自乙酰苯肼、马来酸、N,N-二甲基对甲苯胺、N,N-二乙基对甲苯胺或邻苯甲酰磺酰亚胺中的一种或几种的混合物。
5.根据权利要求1所述的耐高温螺纹锁固厌氧胶,其特征在于:
所述引发剂选自异丙苯过氧化氢或叔丁基过氧化氢中的一种。
6.根据权利要求1所述的耐高温螺纹锁固厌氧胶,其特征在于:
所述填料选自气相二氧化硅、聚四氟乙烯粉或聚乙烯粉中的一种。
7.根据权利要求1所述的耐高温螺纹锁固厌氧胶,其特征在于:
所述染料选自油化红、油化蓝或油化绿中的一种。
8.一种权利要求1至7之一所述的耐高温螺纹锁固厌氧胶的制备方法,其特征在于,包括如下步骤:
步骤1、将70~83%的甲基丙烯酸酯单体和1~3%的稳定剂加入反应釜中,在50℃下搅拌混合60分钟;
步骤2、冷却至常温,然后在搅拌下依次加入7~15%的双马来酰亚胺,2~5%的促进剂,2~5%的引发剂,2~5%的填料,0.1~0.5%的染料搅拌120分钟至全溶即可。