CN104342248B - 松锈、除锈润滑气雾剂 - Google Patents

松锈、除锈润滑气雾剂 Download PDF

Info

Publication number
CN104342248B
CN104342248B CN201410492104.9A CN201410492104A CN104342248B CN 104342248 B CN104342248 B CN 104342248B CN 201410492104 A CN201410492104 A CN 201410492104A CN 104342248 B CN104342248 B CN 104342248B
Authority
CN
China
Prior art keywords
rust
aerosol
pine
rust cleaning
lubrication
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201410492104.9A
Other languages
English (en)
Other versions
CN104342248A (zh
Inventor
闫建新
李长奎
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
DONGYUAN Technology Co Ltd
Original Assignee
DONGYUAN Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by DONGYUAN Technology Co Ltd filed Critical DONGYUAN Technology Co Ltd
Priority to CN201410492104.9A priority Critical patent/CN104342248B/zh
Publication of CN104342248A publication Critical patent/CN104342248A/zh
Application granted granted Critical
Publication of CN104342248B publication Critical patent/CN104342248B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种松锈、除锈润滑气雾剂，属于清洗剂技术领域。解决了现有技术除锈效率低，表面拒水防锈时间短的缺陷。由以下重量份的原料组成：羊毛脂0.3-5份、抗氧化剂BHT 0.5-3份、石油磺酸钡2-12份、丙二醇甲醚2-15份、润滑脂5-35份、表面活性剂3-15份、液体石蜡3-25份、无味煤油70-120份、二甲醚80-130份。制备方法包括：清洗设备；准确称量羊毛脂、抗氧化剂BHT等并依此加入配料釜中，升温、搅拌使之完全溶解；在反应釜中加入无味煤油，开启搅拌后加入上述混合液、丙二醇甲醚和液体石蜡，分散均匀后灌装即可。本发明能够快速松锈、除锈，同时去除表面油污，并且具有润滑和防水防锈功能。

Description

松锈、除锈润滑气雾剂
技术领域
本发明涉及一种松锈、除锈润滑气雾剂，属于清洗剂技术领域。
背景技术
金属生锈是一个全球性的问题，每年世界上都有几千万吨的钢铁变成铁锈。日常生活中铁锅几个月不用就锈迹斑斑，自行车经雨淋后也会满身是锈；工业生产中也常因为设备生锈而产生各种故障。随着社会生产工业化的不断发展，冶金、模具、船运、通讯设备、飞机、汽车、摩托车以及家居等行业，均对于除锈润滑产品提出了需求。目前，市售的除锈剂一种为非气雾剂型的桶装润滑防锈剂，除锈效率低，浪费严重，而且对于缝隙小的特殊部位不易达到除锈目的；另一种为以煤油、机械油和液体石蜡为主要成分的松锈润滑气雾剂，虽然除锈效果好，但是被处理物体表面拒水防锈时间短，短时间内容易再次生锈。
发明内容
本发明的目的在于提供一种松锈、除锈润滑气雾剂，使用方便，除锈迅速，同时兼具设备润滑效果，被处理表面拒水防锈时间长。
所述的松锈、除锈润滑气雾剂，由以下重量份的原料组成：
所述的松锈、除锈润滑气雾剂，由以下重量份的原料组成：
所述的表面活性剂由以下质量百分比的原料组成：
司盘-8030-70％
单硬脂酸甘油酯30-70％。
所述的润滑脂为极压锂基润滑脂。
所述的松锈、除锈润滑气雾剂的制备方法，包括以下步骤：
(1)清洗设备；
(2)准确称量羊毛脂、抗氧化剂BHT、石油磺酸钡、润滑脂、表面活性剂并依此加入配料釜中，升温至60-80℃并搅拌使之完全溶解后待用；
(3)在反应釜中加入无味煤油，开启搅拌后依此加入步骤(2)制备的混合液、丙二醇甲醚和液体石蜡，充分搅拌使之分散均匀后用200目滤网过滤后灌装入气雾罐，气雾罐封口后充入二甲醚，检漏合格即得本发明松锈、除锈润滑气雾剂。
与现有技术相比，本发明的有益效果是：
(1)本发明使用方便，除锈效率高，并且通过添加拒水表面活性剂和羊毛脂成分，很大程度上延长了被处理物体表面的拒水防锈时间；
(2)添加特殊润滑脂，使得产品在除锈同时增加润滑性能；
(3)添加丙二醇甲醚等清洁成分，使得松锈、除锈、润滑的同时去除被处理表面的油泥；
(4)使用二甲醚作为抛射剂，在产品性能不变的前提下大大降低了成本；
(5)本发明为气雾剂除锈剂，能够轻松喷入各种狭小缝隙，松绣、除锈效率高；
(6)本发明在25℃条件下，喷出率大于95％，在55℃条件下内压力小于1.0Mpa。
具体实施方式
下面结合具体实施例对本发明做进一步说明。
实施例1
所述的松锈、除锈润滑气雾剂，由以下重量份的原料组成：
所述的表面活性剂由以下质量百分比的原料组成：
司盘-8050％
单硬脂酸甘油酯50％。
所述的松锈、除锈润滑气雾剂的制备方法，包括以下步骤：
(1)清洗设备；
(2)准确称量羊毛脂、抗氧化剂BHT、石油磺酸钡、润滑脂、表面活性剂并依此加入配料釜中，升温至60-80℃并搅拌使之完全溶解后待用；
(3)在反应釜中加入无味煤油，开启搅拌后依此加入步骤(2)制备的混合液、丙二醇甲醚和液体石蜡，充分搅拌使之分散均匀后用200目滤网过滤后灌装入气雾罐，气雾罐封口后充入二甲醚，检漏合格即得本发明松锈润滑气雾剂。
实施例2
所述的松锈、除锈润滑气雾剂，由以下重量份的原料组成：
所述的表面活性剂由以下质量百分比的原料组成：
司盘-8030％
单硬脂酸甘油酯70％。
制备方法同实施例1。
实施例3
所述的松锈、除锈润滑气雾剂，由以下重量份的原料组成：
所述的表面活性剂由以下质量百分比的原料组成：
司盘-8070％
单硬脂酸甘油酯30％。
制备方法同实施例1。
实施例4
所述的松锈、除锈润滑气雾剂，由以下重量份的原料组成：
所述的表面活性剂由以下质量百分比的原料组成：
司盘-8060％
单硬脂酸甘油酯40％。
制备方法同实施例1。
对上述松锈、除锈润滑气雾剂进行如下检测：
内压检测：内压指气雾剂容器内单位面积所承受的压力。测试温度为55℃，以三次测量的最大值为准。
喷出率检测：喷出率指气雾剂可喷出物占内容物总量的质量百分比。测试温度为25℃。
表1对实施例1-4的松锈、除锈润滑气雾剂的检测结果：
实施例1 实施例2 实施例3 实施例4
内压(Mpa) 0.85 0.86 0.84 0.86
喷出率(％) 99.3 98.7 99.2 98.9

Claims (3)

1.一种松锈、除锈润滑气雾剂，其特征在于，由以下重量份的原料组成：
所述的表面活性剂由以下质量百分比的原料组成：
司盘-8030-70％
单硬脂酸甘油酯30-70％；
所述的润滑脂为极压锂基润滑脂。
2.根据权利要求1所述的松锈、除锈润滑气雾剂，其特征在于，由以下重量份的原料组成：
3.一种权利要求1所述的松锈、除锈润滑气雾剂的制备方法，其特征在于，包括以下步骤：
(1)清洗设备；
(2)准确称量羊毛脂、抗氧化剂BHT、石油磺酸钡、润滑脂、表面活性剂并依此加入配料釜中，升温至60-80℃并搅拌使之完全溶解后待用；
(3)在反应釜中加入无味煤油，开启搅拌后依此加入步骤(2)制备的混合液、丙二醇甲醚和液体石蜡，充分搅拌使之分散均匀后用200目滤网过滤后灌装入气雾罐，气雾罐封口后充入二甲醚，检漏合格即得松锈、除锈润滑气雾剂。
CN201410492104.9A 2014-09-24 2014-09-24 松锈、除锈润滑气雾剂 Active CN104342248B (zh)