CN104321384B - 可固化组合物 - Google Patents
可固化组合物 Download PDFInfo
- Publication number
- CN104321384B CN104321384B CN201380028076.9A CN201380028076A CN104321384B CN 104321384 B CN104321384 B CN 104321384B CN 201380028076 A CN201380028076 A CN 201380028076A CN 104321384 B CN104321384 B CN 104321384B
- Authority
- CN
- China
- Prior art keywords
- formula
- sio
- curable compositions
- aryl
- polysiloxane
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明提供一种可固化组合物及其用途。所述可固化组合物能够表现优异的可加工性与可操作性。所述可固化组合物在固化后表现出优异的光提取效率、硬度、耐热冲击性、抗湿性、透气性和粘合性。此外,所述可固化组合物能够提供表现长期耐久性和可靠性,并且即使在苛刻条件下,也不产生白化和表面粘性的固化产物。
Description
技术领域
本申请涉及一种可固化组合物及其用途。
背景技术
发光二极管(LED),尤其是发射波长为大约250nm至550nm的蓝光或紫外(UV)LED,为使用诸如GaN、GaAlN、InGaN或InAlGaN的GaN类化合物半导体的高亮度产品。此外,通过将红光LED与绿光LED和蓝光LED结合的方法可以形成高质量的全色彩图像。例如,已知一种通过将蓝光或紫外LED与荧光物质结合而制备白光LED的技术。
此类LED广泛用作液晶显示器(LCD)或普通照明的背光。
广泛使用具有高粘合强度和优异机械耐久性的环氧树脂作为LED封装剂。然而,所述环氧树脂具有较低的蓝光或紫外线区域透光率,以及低耐热耐光性。例如,日本专利申请号H11-274571、2001-196151和2002-226551提出了解决上述问题的技术。然而上述参考文献公开的封装剂不具有足够的耐热性与耐光性。
[在先技术文件]
专利文件1:日本特许公开平11-274571号
专利文件2:日本特许公开第2001-196151号
专利文件3:日本特许公开第2002-226551号
发明内容
技术目的
本申请提供一种可固化组合物及其应用。
技术方案
本申请的一个方面提供包含能够通过氢化硅烷化(例如,脂族不饱和键和氢原子之间的反应)固化的组分的可固化组合物。例如,可固化组合物可以包括含有聚有机硅氧烷的聚合产物(下文称为“聚有机硅氧烷(A)”),所述聚有机硅氧烷具有包含脂族不饱和键的官能团。
本文所用术语“M单元”可以指单官能硅氧烷单元,在本领域中可以由(R3SiO1/2)表示,本文所用术语“D单元”可以指双官能硅氧烷单元,在本领域中可以由(R2SiO2/2)表示,本文所用术语“T单元”可以指三官能硅氧烷单元,在本领域中可以由(RSiO3/2)表示,本文所用术语“Q单元”可以指四官能硅氧烷单元,可以由(SiO4/2)表示。此处,R是与硅原子连接的官能团,并且可以为例如,氢原子、羟基、环氧基、烷氧基或一价烃基。
聚有机硅氧烷(A)可以具有例如线性结构或部分交联的结构。术语“线性结构”可以指由M单元和D单元构成的聚有机硅氧烷的结构。此外,术语“部分交联的结构”可以指聚有机硅氧烷的衍生自D单元并且部分引入T单元或Q单元(例如T单元)的足够长的线性结构。在一个实施方案中,具有部分交联结构的聚有机硅氧烷可以指聚有机硅氧烷中包含的D单元与全部D、Q和T单元的比例(D/(D+T+Q)为0.65以上的聚有机硅氧烷。
在一个实施方案中,具有部分交联结构的聚有机硅氧烷(A)可以包含共用一个氧原子并彼此连接的D单元和T单元。所述相连接的单元可以由例如式1表示。
[式1]
在式1中,Ra和Rb各自独立地为烷基、烯基或芳基,Rc为烷基或芳基。
在式1中,Rc和Rb可以同时为例如烷基或芳基。
具有部分交联结构的聚有机硅氧烷(A)可以包含至少一个式1的单元。式1的单元是指,在形成聚有机硅氧烷(A)的硅氧烷单元中,D单元的硅原子和T单元的硅原子经由氧原子直接连接的类型的单元。例如,以下将进行说明,包含式1的单元的聚有机硅氧烷可以通过聚合(例如,开环聚合)包含环状硅氧烷化合物的混合物来制备。当应用该方法时,可以制备包含式1的单元并在其结构中具有最小数量的与烷氧基连接的硅原子和与羟基连接的硅原子的聚有机硅氧烷。
聚有机硅氧烷(A)可以包含至少一个含有脂族不饱和键的官能团,例如,至少一个烯基。例如,聚有机硅氧烷(A)中包含脂族不饱和键(Ak)的官能团与全部硅原子(Si)的摩尔比(Ak/Si)可以为大约0.01至0.3,或0.02至0.25。由于该摩尔比(Ak/Si)控制至0.01以上或0.02以上,因而可以适当地保持反应活性,并且可以防止由固化产物表面渗漏未反应的组分。此外,由于该摩尔比(Ak/Si)控制至0.3以下或0.25以下,因而可以优异地保持固化产物的抗龟裂性。
聚有机硅氧烷(A)可以包含芳基,例如,至少一个与硅原子连接的芳基。例如,聚有机硅氧烷(A)中芳基的摩尔数(Ar)与所有与硅连接的官能团的摩尔数(R)的比例可以为大约30%至60%的百分比(100×Ar/R)。在此范围内,所述组合物固化前可以具有优异的可加工性和可操作性,并且可以在固化后优异地保持抗湿性、透光率、折射率、光提取效率和硬度。具体地,由于所述比例(100×Ar/R)保持在30%以上,因而能够合适地确保固化产物的机械强度和透气性,所述比例(100×Ar/R)保持在60%以下则能够优异地保持固化产物的抗龟裂性和透光率。
聚有机硅氧烷(A)可以包含式2的单元和式3的单元作为D单元。
[式2]
(R1R2SiO2/2)
[式3]
(R3 2SiO2/2)
在式2和式3中,R1和R2各自独立地为环氧基或一价烃基,R3为芳基。在一个实施方案中,R1和R2各自独立地为烷基。
除非另有特别定义,本发明所用术语“一价烃基”可以指衍生自碳和氢组成的有机化合物或其衍生物的一价残基。例如,一价烃基可以包含1至25个碳原子。一价烃基可以为,例如,烷基、烯基、炔基或芳基。
除非另有特别定义,本发明所用术语“烷基”可以指具有1个碳原子至20个碳原子、1个碳原子至16个碳原子、1个碳原子至12个碳原子、1个碳原子至8个碳原子或1个碳原子至4个碳原子的烷基。所述烷基可以具有直链、支链或环状结构,并且可以任选地被至少一个取代基取代。
除非另有特别定义,本发明所用术语“烯基”可以指具有2个碳原子至20个碳原子、2个碳原子至16个碳原子、2个碳原子至12个碳原子、2个碳原子至8个碳原子或2个碳原子至4个碳原子的烯基。所述烯基可以具有直链、支链或环状结构,并且可以任选地被至少一个取代基取代。
除非另有特别定义,本发明所用术语“炔基”可以指具有2个碳原子至20个碳原子、2个碳原子至16个碳原子、2个碳原子至12个碳原子、2个碳原子至8个碳原子或2个碳原子至4个碳原子的炔基。所述炔基可以具有直链、支链或环状结构,并且可以任选地被至少一个取代基取代。
除非另有特别定义,本发明所用术语“芳基”可以指衍生自包括苯环或包括至少两个苯环以共有一个或两个碳原子的方式稠合或通过共价键连接的结构的化合物或其衍生物的一价残基。在芳基的范围内,除了常规上称为芳基的官能团之外,还可以包括常规上称为芳烷基或芳基烷基的官能团。例如,芳基可以为具有6个碳原子至25个碳原子、6个碳原子至21个碳原子、6个碳原子至18个碳原子或6个碳原子至12个碳原子的芳基。所述芳基可以为苯基、二氯苯基、氯苯基、苯乙基、苯丙基、苄基、甲苯基、二甲苯基或萘基。
除非另有特别定义,本发明所用术语“环氧基”可以指衍生自具有三个成环原子的环醚或包含所述环醚的化合物的一价残基。所述环氧基可以为环氧丙基、环氧基烷基、环氧丙氧烷基或脂环族环氧基。脂环族环氧基可以包含衍生自包含脂族烃环结构的化合物的一价残基,以及由脂族烃环的两个碳原子形成的环氧基结构。脂环族环氧基可以为具有6至12个碳原子的脂环族环氧基,例如,3,4-环氧基环己基乙基。
可以使用诸如氯或氟的卤素、环氧丙基、环氧烷基、环氧丙氧烷基、诸如脂环族环氧基的环氧基、丙烯酰基、甲基丙烯酰基、异氰酸酯基、硫醇基或一价烃基作为可以任选地取代环氧基或一价烃基的取代基,但本申请并不限于此。
在聚有机硅氧烷(A)中,式2的硅氧烷单元的摩尔数(Dm)与式3的硅氧烷单元的摩尔数(Dp)的比例(Dm/Dp)可以为例如大约0.3至2.0、0.3至1.5或0.5至1.5。在此比例范围内,可固化组合物能够具有优异的透光率和机械强度、无表面粘性、并且通过控制水分和透气性能够确保长期耐久性。
聚有机硅氧烷(A)中式3的硅氧烷单元的摩尔数(Dp)与全部D单元的摩尔数(D)的百分比(100×Dp/D)可以为大约30%以上、30%至65%或30%至60%。在此范围内,可固化组合物可以具有优异的透光性和机械强度,无表面粘性,并且通过控制水分和透气性能够确保长期耐久性。
聚有机硅氧烷(A)中式3的硅氧烷单元的摩尔数(Dp)与全部D单元中包含芳基的D单元的摩尔数(ArD)的百分比(100×Dp/ArD)可以为大约70%以上或80%以上。所述百分比(100×Dp/ArD)的上限无特别限制,并且可以为例如100%。在此范围内,可以提供固化前具有优异的可加工性和可操作性,固化后具有优异的机械强度、透气性、抗湿性、透光率、折射率、光提取效率和硬度的可固化组合物。
在一个实施方案中,聚有机硅氧烷(A)可以具有式4的平均组成式。
[式4]
(R4 3SiO1/2)a(R4 2SiO2/2)b(R4SiO3/2)c(SiO4/2)d
在式4中,R4各自独立地为环氧基或一价烃基,至少一个R4为烯基,并且至少一个R4为芳基。可以包含烯基和芳基,例如,以满足上述摩尔比。
本发明所用“聚有机硅氧烷由某一平均组成式表示”的表达意指所述聚有机硅氧烷为由某一平均组成式表示的单一组分,或至少两种组分的混合物,在所述混合物中组分的平均组成由所述平均组成式表示。
在式4的平均组成式中,a、b、c和d为聚有机硅氧烷(A)中各个硅氧烷单元的摩尔比。例如,a和b可以各自为正数,c和d可以各自为0或正数。例如,当所述摩尔比之和(a+b+c+d)调整为1时,a可以为0.01至0.3,b可以为0.65至0.97,c可以为0至0.30或0.01至0.30,d可以为0至0.2。此处,b/(b+c+d)可以为0.7至1。当聚有机硅氧烷(A)具有部分交联的结构时,b/(b+c+d)可以为0.65至0.97或0.7至0.97。由于如上所述控制硅氧烷单元的比例,可以确保根据应用的适当的物理性质。
在另一个实施方案中,聚有机硅氧烷(A)可以具有式5的平均组成式。
[式5]
(R5R6 2SiO1/2)e(R7R8SiO2/2)f(R9 2SiO2/2)g(R10SiO3/2)h
在式5的平均组成式中,R5至R10各自独立地为环氧基或一价烃基。此处,至少一个R5和R7至R9可以为烯基,至少一个R7至R9可以为芳基。R7和R8各自独立地为烷基,R9为芳基。
在一个实施方案中,式5的R5可以为一价烃基,例如烯基,R6可以为具有1至4个碳原子的烷基,R7至R9可以各自独立地为烷基或芳基,R9可以为芳基。
在式5的平均组成式中,e、f、g和h为聚有机硅氧烷(A)中各个硅氧烷单元的摩尔比。例如,e可以为正数,f和g可以各自独立地为0或正数,h可以为0或正数。当所述摩尔比之和(e+f+g+h)调整为1时,e可以为0.01至0.3,f可以为0至0.97或0.65至0.97,g可以为0至0.97或0.65至0.97,h可以为0至0.30或0.01至0.30。此处,(f+g)/(f+g+h)可以为0.7至1。
当聚有机硅氧烷(A)具有部分交联的结构时,(f+g)/(f+g+h)可以为大约0.7至0.97或0.65至0.97。由于如上所述控制硅氧烷单元的比例,可以确保根据应用的适当的物理性质。例如,在式5的平均组成式中,所有f和g均可以不为0。当所有f和g均不为0时,f/g可以在0.3至2.0、0.3至1.5或0.5至1.5的范围内。
包含聚有机硅氧烷(A)的聚合产物可以为,例如环状聚有机硅氧烷的混合物的开环聚合产物。当聚有机硅氧烷(A)具有部分交联结构时,所述混合物还可以包括例如具有笼状或部分笼状结构或包含T单元的聚有机硅氧烷。可以使用例如由式6表示的化合物作为环状聚有机硅氧烷化合物。
[式6]
在式6中,Rd和Re各自独立地为环氧基或一价烃基,o为3至6。
环状聚有机硅氧烷还可以包括式7的化合物和式8的化合物。
[式7]
[式8]
在式7和式8中,Rf和Rg各自为环氧基或烷基,Rh和Ri各自为环氧基或芳基,p为3至6的数,q为3至6的数。在式7和式8中,Rf和Rg各自独立地为烷基,Rh和Ri可以各自独立地为芳基。
在式6至式8中,可以根据聚有机硅氧烷(A)的期望结构确定Rf至Ri的具体种类,或者o、p和q的具体值,以及混合物中各组分的比例。
当聚有机硅氧烷(A)具有部分交联的结构时,所述混合物还可以包括例如,具有式9的平均组成式的化合物,或具有式10的平均组成式的化合物。
[式9]
[RjSiO3/2]
[式10]
[RkRl 2SiO1/2]p[RmSiO3/2]q
在式9和式10中,Rj、Rk和Rm各自独立地为环氧基或一价烃基,Rl为环氧基或具有1至4个碳原子的烷基,p为1至3,q为1至10。
在式9至式10中,可以根据聚有机硅氧烷(A)的期望结构确定Rj至Rm的具体种类,或p和q的具体值,以及混合物中各组分的比例。
当环状聚有机硅氧烷与具有笼状或部分笼状结构或包含T单元的聚有机硅氧烷反应时,可以以适当分子量合成具有期望的部分交联结构的聚有机硅氧烷。此外,根据所述方法,通过使聚有机硅氧烷或包含其的聚合产物中连接至硅原子的官能团(例如烷氧基或羟基)最少化,可以制备具有优异物理性质的期望的产物。
在一个实施方案中,所述混合物还可以包括由式11表示的化合物。
[式11]
(RnRo 2Si)2O
在式11中,Rn和Ro各自为环氧基或一价烃基。
在式11中,一价烃基的具体种类或在混合物中的共混比可以根据期望的聚有机硅氧烷(A)确定。
混合物中各组分的反应可以在适当催化剂存在下进行。因此,所述混合物还可以包含催化剂。
作为可以包含于混合物中的催化剂,可以使用例如碱性催化剂。合适的碱性催化剂可以为但并不限于诸如KOH、NaOH或CsOH的金属氢氧化物;包括碱金属化合物和硅氧烷的硅烷醇金属化物;或诸如四甲基氢氧化铵、四乙基氢氧化铵或四丙基氢氧化铵的季铵化合物。
催化剂在混合物中的比例可以考虑期望的反应活性而适当选择,例如,相对于混合物中100重量份的反应产物的总重量,可以为0.01重量份至30重量份,或0.03重量份至5重量份。在本说明书中,除非另有特别定义,单位“重量份”指组分之间的重量比。
在一个实施方案中,上述反应可以在无溶剂(不使用溶剂)或在适当溶剂存在的条件下进行。作为溶剂,可以使用其中混合物中的反应产物(即二硅氧烷或聚硅氧烷)可以与催化剂适当混合,并且不干扰反应活性的任何种类的溶剂。所述溶剂可以为但不限于脂族烃类溶剂,例如正戊烷、异戊烷、正己烷、异己烷、2,2,4-三甲基戊烷、环己烷或甲基环己烷;芳族溶剂,例如苯、甲苯、二甲苯、三甲苯、乙苯或甲乙苯;酮类溶剂,例如甲乙酮、甲基异丁基酮、二乙基酮、甲基正丙基酮、甲基正丁基酮、环己酮、甲基环己酮或乙酰丙酮;醚类溶剂,例如四氢呋喃、2-甲基四氢呋喃、乙醚、正丙醚、异丙醚、二甘醇二甲醚、二氧杂环己烯(dioxine)、二甲基二氧杂环己烯(dimethyldioxine)、乙二醇单甲醚、乙二醇二甲醚、乙二醇二乙醚、丙二醇单甲醚或丙二醇二甲醚;酯类溶剂,例如碳酸二乙酯、乙酸甲酯、乙酸乙酯、乳酸乙酯、乙二醇单甲醚乙酸酯(ethyleneglycol monomethylether acetate)、丙二醇单甲醚乙酸酯(propyleneglycol monomethylether acetate)或乙二醇二乙酸酯;或者酰胺类溶剂,例如N-甲基吡咯烷酮、甲酰胺、N-甲基甲酰胺、N-乙基甲酰胺、N,N-二甲基乙酰胺或N,N-二乙基乙酰胺。
反应可以通过向反应产物中添加催化剂而进行。此处,反应温度可以控制在例如0至150℃或30至130℃的范围内。此外,反应时间可以控制在例如1小时至3天的范围内。
在通过1H NMR获得的光谱中,聚有机硅氧烷(A)或包含其的聚合产物中,来自连接至硅原子的烷氧基的峰的面积与来自含有连接至硅的脂族不饱和键的官能团(例如,诸如乙烯基的烯基)的峰的面积之比可以为0.01以下、0.005以下或0。在上述范围内,可以表现出适当的粘度,并且可以优异地保持其他物理性质。
聚有机硅氧烷(A)或包含其的聚合产物可以具有0.02以下或0.01以下或0的酸值(通过KOH滴定获得)。在上述范围内,可以表现出适当的粘度,并且可以优异地保持其他物理性质。
聚有机硅氧烷(A)或包含其的聚合产物在25℃下粘度可以为500以上、1000cP以上、2000cP以上或5000cP以上。在上述范围内,能够适当保持可加工性和硬度。粘度的上限无特别限制,粘度可以为例如500000cP以下、400000cP以下、300000cP以下、200000cP以下、100000cP以下、80000cP以下、70000cP以下或65000cP以下。
聚有机硅氧烷(A)或包含其的聚合产物的重均分子量可以为500至50000或1500至30000。术语“重均分子量”可以指通过凝胶渗透色谱(GPC)测量的相对于标准聚苯乙烯的转换值。除非另有特别定义,本发明所用术语“分子量”可以指重均分子量。在此分子量范围内,可以适当地保持模制性能、硬度和强度。
可固化组合物还可以包含可交联聚有机硅氧烷(下文称为“聚有机硅氧烷(B)”)。术语“可交联聚有机硅氧烷”可以指基本上包含T单元或Q单元作为硅氧烷单元,并具有小于0.65的D单元与D、T和Q单元的比例(D/(D+T+Q))的聚有机硅氧烷。
可交联的聚有机硅氧烷可以具有式12的平均组成式。
[式12]
(R11 3SiO1/2)a(R11 2SiO2/2)b(R11SiO3/2)c(SiO4/2)d
在式12中,R11各自独立地为环氧基或一价烃基,至少一个R11为烯基,至少一个R11为芳基,a为正数,b为0或正数,c为正数,d为0或正数,b/(b+c+d)为小于0.65、0.5以下或0.3以下,c/(c+d)为0.8以上、0.85以上或0.9以上。
在式12中,至少一个或两个R11可以为烯基。在一个实施方案中,烯基存在的量使得烯基(Ak)与聚有机硅氧烷(B)中包含的全部硅原子(Si)的摩尔比(Ak/Si)大约为0.05至0.4或0.05至0.35。由于该摩尔比(Ak/Si)控制为0.05以上,因而可以优异地保持反应活性,并且可以防止由固化产物表面渗漏未反应的组分。此外,当摩尔比(Ak/Si)控制为0.4以下或0.35以下时,能够优异地保持固化产物的硬度、抗龟裂性和耐热冲击性。
在式12中,至少一个R11可以为芳基。因此,能够有效控制固化产物的折射率和硬度。芳基存在的量使得芳基(Ar)与聚有机硅氧烷(B)中包含的全部硅原子(Si)的摩尔比(Ar/Si)大约为0.5至1.5或0.5至1.2。由于所述摩尔比(Ar/Si)控制为0.5以上,因而能够使固化产物的折射率和硬度最大化。此外,由于摩尔比(Ar/Si)控制为1.5以下或1.2以下,能够适当地保持所述组合物的粘度和耐热冲击性。
在式12的平均组成式中,a、b、c和d是各个硅氧烷单元的摩尔比。例如,当其总和(a+b+c+d)调整为1时,a为0.05至0.5,b为0至0.3,c为0.6至0.95,d为0至0.2。为最大化固化产物的强度、抗龟裂性和耐热冲击性,(a+b)/(a+b+c+d)可以控制为0.2至0.7,b/(b+c+d)可以控制为小于0.65、0.5以下或0.3以下,c/(c+d)可以控制为0.8以上、0.85以上或0.9以上。此处,b/(b+c+d)的下限无特别限制,例如可以为大于0。此外,此处,c/(c+d)的上限无特别限制,例如可以为1.0。
聚有机硅氧烷(B)在25℃下粘度可以为5000cP以上或1000000cP以上,因此能够适当保持固化前的可加工性和固化后的硬度。
聚有机硅氧烷(B)的分子量可以为例如800至20000或800至10000。由于分子量控制为800以上,因而能够优异地保持固化前的模制性能和固化后的强度,由于分子量控制为20000以下或10000以下,因而粘度可以保持在适当的水平。
聚有机硅氧烷(B)的制备方法可以为,例如本领域中已知的常规制备聚硅氧烷的方法,或者可以为与制备聚有机硅氧烷(A)类似的方法。
例如,可以以使聚有机硅氧烷(A)与聚有机硅氧烷(A)和聚有机硅氧烷(B)的混合物的重量比(A/(A+B))为大约10至50的量包含聚有机硅氧烷(B)。在上述范围内,能够优异地保持固化产物的强度和耐热冲击性,还能够防止表面粘性。
可固化组合物还可以包含硅化合物,所述硅化合物包含连接至硅原子的氢原子(下文称为“硅化合物(C)”)。硅化合物(C)可以具有至少一个或两个氢原子。
硅化合物(C)可以用作交联剂,通过与聚有机硅氧烷的含有脂族不饱和键的官能团反应,使组合物发生交联。例如,交联和固化可以通过使硅化合物(C)的氢原子和聚有机硅氧烷(A)和/或(B)的烯基发生加成反应来进行。
可以使用多种在分子中包含连接至硅原子的氢原子(Si-H)的硅化合物中的任意一种作为硅化合物(C)。硅化合物(C)可以为例如直链、支链、环状的或可交联的有机聚硅氧烷。硅化合物(C)可以为具有2个硅原子至1,000个硅原子,优选3个硅原子至300个硅原子的化合物。
硅化合物(C)可以为例如式13的化合物,或具有式14的平均组成式的化合物。
[式13]
R12 3SiO(R12 2SiO)nSiR12 3
[式14]
(R13 3SiO1/2)a(R13 2SiO2/2)b(R13SiO3/2)c(SiO2)d
在式13和式14中,R12各自独立地为氢或一价烃基,至少两个R12为氢原子,至少一个R12为芳基,n为1至100。此外,R13各自独立地为氢或一价烃基,至少两个R13为氢原子,至少一个R13为芳基,a为正数,b为0或正数,c为正数,d为0或正数。例如,当其总和(a+b+c+d)调整为1时,a为0.1至0.8,b为0至0.5,c为0.1至0.8,d为0至0.2。
式13的化合物是具有至少两个连接至硅原子的氢原子的线性硅氧烷化合物。在式13中,n可以为1至100、1至50、1至25、1至10或1至5。
由式14的平均组成式表示的化合物可以为具有交联结构或部分交联结构的聚硅氧烷。
在一个实施方案中,连接至硅原子的氢原子(H)与硅化合物(C)中包含的全部硅原子(Si)的摩尔比(H/Si)可以为0.2至0.8或0.3至0.75。由于该摩尔比控制为0.2以上或0.3以上,因而能够优异地保持组合物的可固化性,由于该摩尔比控制为0.8以下或0.75以下,因而可以优异地保持抗龟裂性和耐热冲击性。
硅化合物(C)可以包含至少一个芳基,因此,至少一个式13中的R12或至少一个式14中的R13可以为芳基。因此,能够有效控制固化产物的折射率和硬度。芳基存在的量使得芳基(Ar)与聚有机硅氧烷(C)中包含的全部硅原子(Si)的摩尔比(Ar/Si)为大约0.5至1.5或0.5至1.3。由于该摩尔比(Ar/Si)控制为0.5以上,因而固化产物的折射率和硬度能够最大化,由于该摩尔比(Ar/Si)控制为1.5以下或1.3以下,因而能够适当保持组合物的粘度和抗龟裂性。
化合物(C)在25℃下的粘度可以为0.1cP至100000cP、0.1cP至10000cP、0.1cP至1000cP或0.1cP至300cP。在上述粘度范围内,能够优异地保持组合物的可加工性和固化产物的硬度。
此外,化合物(C)的分子量可以为例如小于2,000、小于1,000或小于800。当分子量为1,000以上时,固化产物的强度可能降低。化合物(C)的分子量的下限可以为但并不特别限定于例如250。在化合物(C)中,所述分子量可以为化合物的重均分子量或常规分子量。
制备化合物(C)的方法无特别限制,可以使用本领域中已知的常规的制备聚有机硅氧烷的方法,或与制备聚有机硅氧烷(A)类似的方法。
可以选择化合物(C)的含量,使得在化合物(C)包含的连接至硅原子的氢原子(H)与可固化组合物包含的全部含有脂族不饱和键的官能团的摩尔比(H/Ak)为大约0.5至2.0或0.7至1.5,所述含有脂族不饱和键的官能团为例如聚有机硅氧烷(A)和/或(B)中包含的全部含有脂族不饱和键(例如烯基)的官能团(Ak)。在上述摩尔比(H/Ak)范围内,能够提供一种组合物,所述组合物固化前表现优异的可加工性和可操作性,固化后表现优异的抗龟裂性、硬度、耐热冲击性和粘合性,并且即使在苛刻的条件下也不导致白化或表面粘性。
可固化组合物还可以包括有机聚硅氧烷,所述有机聚硅氧烷包含具有脂族不饱和键的官能团,例如烯基和环氧基(下文称为“聚有机硅氧烷(D)”)。
聚有机硅氧烷(D)可以用作例如增粘剂以增强粘合强度。
在一个实施方案中,聚有机硅氧烷(D)可以由式15的平均组成式表示。
[式15]
(R14 3SiO1/2)a(R14 2SiO2/2)b(R14SiO3/2)c(SiO4/2)d
在式15中,R14各自独立地为环氧基或一价烃基,至少一个R14为烯基,至少一个R14为环氧基,a、b、c和d各自独立地为0或正数,(c+d)/(a+b+c+d)可以为0.2至0.7,c/(c+d)可以为0.8以上。例如,当所述摩尔比的总和(a+b+c+d)调整为1时,a可以为0至0.7,b可以为0至0.5,c可以为0至0.8,d可以为0至0.2。
在式15中,至少一个R14可以为烯基。在一个实施方案中,烯基存在的量使得烯基(Ak)与聚有机硅氧烷(D)中包含的全部硅原子(Si)的摩尔比(Ak/Si)为0.05至0.35或0.05至0.3。在此摩尔比(Ak/Si)内,能够提供一种固化产物,所述固化产物表现出优异的与另一种化合物的反应活性,并具有优异的粘合强度和优异的物理性质,例如耐冲击性。
在式15中,至少一个R14可以为环氧基。因此,可以适当保持固化产物的强度和耐刮擦性,并且可以实现优异的粘合性。环氧基存在的量使得环氧基(Ep)与聚有机硅氧烷(D)中包含的全部硅原子(Si)的摩尔比(Ep/Si)可以为0.1以上或0.2以上。在此摩尔比(Ep/Si)内,可以适当地保持固化产物的交联结构,还可以优异地保持耐热性和粘合性。所述摩尔比(Ep/Si)的上限无特别限制,可以为例如1.0。
在式15的平均组成式中,a、b、c和d为各个硅氧烷单元的摩尔比,当其总和调整为1时,a可以为0至0.7,b可以为0至0.5,c可以为0至0.8,d可以为0至0.2。此处,c和d可以不同时为0。为最大化固化产物的强度、抗龟裂性和耐热冲击性,(a+b)/(a+b+c+d)可以控制为0.3至0.7,c/(c+d)可以控制为0.8以上。此处,c/(c+d)的上限无特别限制,可以为例如1.0。
聚有机硅氧烷(D)在25℃下的粘度可以为100cP以上或100,000cP以上,因此能够适当地保持固化前的可加工性和固化后的硬度。
聚有机硅氧烷(D)的分子量可以为例如1,000以上或1,500以上。由于分子量控制为1,000以上或1,500以上,因而能够提供固化前具有优异的可加工性与可操作性,固化后具有优异的抗龟裂性、耐热冲击性以及对基板的粘合性的固化产物。分子量的上限无特别限制,可以为例如20,000。
制备聚有机硅氧烷(D)的方法无特别限制,并且可以使用例如本领域中已知的常规制备聚有机硅氧烷的方法,或者与制备聚有机硅氧烷(A)类似的方法。
相对于100重量份的可固化组合物中另一种化合物(例如聚有机硅氧烷(A)、聚有机硅氧烷(B)和/或硅化合物(C))的总重量,可以以例如0.2重量份至10重量份或0.5重量份至5重量份的量包含聚有机硅氧烷(D)。在上述范围内,可以优异地保持粘合性和透明性。
可固化组合物可以包括纤维型填料,例如纤维型无机填料。本文所用术语“纤维型填料”可以指以单股计,相对于垂直长度(填料长度),具有相对高的水平长度(粒度、内径或外径)的填料,例如长宽比(竖直长度/水平长度)为5以上、10以上、20以上、30以上、40以上、50以上或100以上的填料。在纤维型填料中,长宽比(竖直长度/水平长度)可以为2,000以下、1,600以下、1,500以下、1,200以下、1,000以下、700以下、500以下或400以下。
纤维型填料可以为中空纤维型填料。术语“中空纤维型填料”可以指内部具有孔的填料,例如管形填料。当计算中空纤维型填料的长宽比时,水平长度可以为例如纤维的内径或外径。
纤维型填料,尤其是,中空纤维型填料具有比其他类型的填料(例如平面、球形或另外一种形状的填料)更低的结晶性,粒子间更小的相互作用和更高的分散性。依次,此类填料可以抑制组合物粘度的提高,并且较少发生聚集。此外,由于纤维型填料具有各向异性的结构,优选用于增强机械特性和抗龟裂特性,并具有优异的触变性,从而用较小的量有效地抑制荧光物质的沉淀。
纤维型填料的单股的粒径或中空纤维型填料的单股的内径或外径无特别限制,可以为例如大约0.5nm至1,000nm、0.5nm至800nm、0.5nm至600nm、0.5nm至500nm、0.5nm至300nm、0.5nm至200nm、1nm至150nm、1nm至100nm、1nm至80nm、1nm至60nm或1nm至50nm。
纤维型填料可以具有例如大约1.45以上的折射率。此外,纤维型填料可以满足等式1。
[等式1]
|X–Y|≤0.1
在等式1中,X为可固化组合物或其不包含填料的固化产物的折射率,Y为填料的折射率。
本发明所用术语“折射率”可以为例如相对于波长为450nm的光测量的折射率。在上述范围内,由于为应用至元件,所述组合物或固化产物的透明性得以保持,因而其亮度能够得到增强。在等式1中,|X–Y|可以为例如0.07以下或0.05以下。
伊毛缟石或多水高岭土可以用作纤维型填料。伊毛缟石为一种衍生自硅酸铝的中空纤维型化合物,并且由Al2SiO3(OH)4表示,多水高岭土也是一种衍生自硅酸铝的中空纤维型化合物,并且由Al2Si2O5(OH)4表示。
例如,相对于100重量份的聚有机硅氧烷(A),可固化组合物可以以0.5重量份至70重量份、1重量份至50重量份、5重量份至50重量份、10重量份至50重量份或10重量份至40重量份的量包含填料。由于纤维型填料的重量比控制在0.5重量份以上,因而能够增强所述组合物或固化产物的机械特性、抗龟裂性和耐热性,从而改善元件的可靠性。此外,由于重量比控制在70重量份以下,可以优异地保持可加工性。
可固化组合物还可以包含氢化硅烷化催化剂。氢化硅烷化催化剂可以用于促进氢化硅烷化反应。可以使用本领域中已知的任何常规组分作为氢化硅烷化催化剂。铂、钯、铑类催化剂可以用作此类催化剂。在本说明书中,考虑催化剂效率可以使用铂类催化剂,所述铂类催化剂可以为但不限于氯铂酸、四氯化铂、铂的烯烃复合物、铂的烯基硅氧烷复合物或铂的羰基复合物。
氢化硅烷化催化剂的含量无特别限制,只要氢化硅烷化催化剂以催化量包含在内,即能够起到催化剂作用的量即可。常规上,基于铂、钯或铑的原子量,氢化硅烷化催化剂可以以0.1ppm至100ppm,优选0.2ppm至100ppm的量使用。
可固化组合物还可以包括单独的增粘剂,或与聚有机硅氧烷(D)结合的增粘剂,以进一步增强对各种基板的粘合性。增粘剂为能够改善对组合物或固化产物的自粘性的组分,其尤其可以改善对金属和有机树脂的自粘性。
增粘剂可以为但不限于:具有至少一个或两个选自诸如乙烯基的烯基、(甲基)丙烯酰氧基、氢甲硅烷基(SiH基)、环氧基、烷氧基、烷氧基甲硅烷基、羰基和苯基的官能团的硅烷;或诸如具有2至30或4至20个硅原子的环状或直链硅氧烷的有机硅化合物。在本说明书中,可以额外混合至少一种增粘剂。
相对于100重量份的可固化组合物中另一种化合物(例如聚有机硅氧烷(A)、聚有机硅氧烷(B)和/或硅化合物(C)),所述组合物可以以0.1重量份至20重量份的含量包含增粘剂,但所述含量可以考虑期望的粘合性的改善适当改变。
可固化组合物还可以包含至少一种添加剂,所述添加剂包括:反应抑制剂,例如2-甲基-3-丁炔-2-醇、2-苯基-3-1-丁炔-2-醇、3-甲基-3-戊烯-1-炔、3,5-二甲基-3-己烯-1-炔、1,3,5,7-四甲基-1,3,5,7-四己烯基环四硅氧烷或乙炔基环己烷;无机填料,例如二氧化硅、氧化铝、氧化锆或二氧化钛;具有环氧基和/或烷氧基甲硅烷基的碳官能化硅烷,其部分水解-缩合产物或硅氧烷化合物;触变剂,例如能够与聚醚组合使用的雾相二氧化硅;提供导电性的试剂,例如银、铜、铝的金属粉末、或多种碳材料;或颜色调节剂,例如颜料或染料(必要时)。
可固化组合物还可以包含荧光物质。在此情况下,能够使用的荧光物质的种类无特别限制,例如,可以使用应用于发光二极管LED封装的常规种类的荧光物质,以实现白光。
本申请的另一个方面提供半导体元件,例如,光子半导体元件。示例性半导体元件可以由包含可固化组合物的固化产物的封装剂封装。由封装剂封装的半导体元件的例子包括二极管、晶体管、晶闸管、光电耦合器、CCD、固态图像提取二极管、单一IC、混合集成IC、LSI、VLSI或发光二极管(LED)。在一个实施方案中,半导体元件可以为LED。
LED可以通过在基板上堆叠半导体材料而形成。半导体材料可以为但不限于GaAs、GaP、GaAlAs、GaAsP、AlGaInP、GaN、InN、AlN、InGaAlN或SiC。此外,可以使用蓝宝石、尖晶石、SiC、Si、ZnO或GaN单晶作为基底。
此外,为了制备LED,当必要时,可以在基板与半导体材料之间形成一层缓冲层。GaN或AlN可以用作缓冲层。在基板上堆叠半导体材料的方法可以为但不特别限于MOCVD、HDVPE或液体生长。此外,LED的结构可以为例如包括MIS结、PN结和PIN结的单质结,异质结或双异质结。此外,可以使用单量子阱或多量子阱结构形成LED。
在一个实施方案中,LED的发射波长可以为例如250nm至550nm、300nm至500nm或330nm至470nm。发射波长可以指主发射峰波长。由于LED的发射波长设定在上述范围内,因而能够获得具有较长寿命、高能量效率和高色彩表现的白光LED。
LED可以使用所述组合物封装。此外,LED的封装可以仅用所述组合物进行,在某些情况下,另一种封装剂可以与所述组合物结合使用。当两种封装剂结合使用时,在使用所述组合物封装后,经封装的LED还可以由另外一种封装剂封装。或者,LED可以首先由其他封装剂封装,然后再用所述组合物封装。环氧树脂、硅树脂、丙烯酸树脂、脲树脂、酰亚胺树脂或玻璃可以用作其他封装剂。
为了用所述组合物封装LED,例如,(可以使用)包括先将组合物注入模具,浸渍LED固定于其中的引线框,然后固化所述组合物的方法。或者,可以使用将组合物注入模具(其中插有LED)然后固化所述组合物的方法。可以使用分配器注入,传递模塑或注塑作为注入组合物的方法。此外,作为其他封装方法,可以包括,将组合物滴落于LED之上,通过丝网印刷或使用掩模涂覆所述组合物,然后固化所述组合物的方法,以及将组合物注入杯(LED通过分配器设置于其底部)中然后固化组合物的方法。
此外,必要时组合物可以用作将LED固定至引线端或封装的芯片粘合材料,或者LED之上的钝化层或封装基板。
当有必要固化所述组合物时,固化无特别限制,可以通过例如将组合物保持在60℃至200℃下10分钟至5小时而进行,或者在适当温度适当时间下以两步以上的步骤进行。
封装剂的形状无特别限制,例如,可以为弹形镜片、平面或薄膜的形状。
此外,根据本领域已知的常规方法,可以对LED的性能进行额外的强化。为强化性能,例如,可以使用在LED的背面上设置反射层或光照聚集层的方法,在其底部形成互补着色部分的方法,在LED上设置吸收比主发射峰短的波长的光的吸光层的方法,封装LED然后用轻质材料模塑LED的方法,将LED插入待固定的通孔的方法,或者通过倒装晶片接触法使LED与引线构件接触以由基底方向提取光的方法。
LED可以有效应用于,例如,液晶显示器(LCD)的背光、灯、各种传感器、打印机与复印机的光源、汽车仪表的光源、信号灯、指示灯、显示装置、平面型LED的光源、显示器、装饰灯或多种照明。
有益效果
本申请的可固化组合物表现出优异的可加工性和可操作性。此外,可固化组合物在固化后表现优异的光提取效率、硬度、耐热冲击性、抗湿性、透气性和粘合性。此外,可固化组合物能够提供表现长期耐久性和可靠性,并且即使在苛刻条件下,也不会产生白化和表面粘性的固化产物。
具体实施方式
下文将参照实施例与对比实施例进一步详细说明本申请的可固化组合物,但所述可固化组合物的范围并不限于以下实施例。下文中,缩写“Vi”指乙烯基,缩写“Ph”指苯基,缩写“Me”指甲基,缩写“Ep”指3-环氧丙氧基丙基。
1.透光率的测量
实施例与对比实施例的可固化材料的透光率通过如下方法评价。将可固化组合物注入以大约1mm彼此间隔开的两块玻璃基板之间,并在150℃下固化1小时,从而制备厚度为1mm的平面样品。随后,使用UV-VIS光度计在室温下测量样品在厚度方向上相对于450nm波长的透光率,然后根据以下标准评价。
<评价透光率的标准>
○:85%以上的透光率
△:75%以上并小于85%的透光率
×:小于75%的透光率
2.元件特性评价
使用聚邻苯二甲酰胺(PPA)制备的7030 LED封装来评价元件特性。具体地,使可固化组合物在PPA杯中分散,在70℃下保持30分钟,然后在150℃下固化1小时,从而制备表面贴装的LED。之后,根据以下方法进行测试。
(1)热冲击测试
将LED保持在-40℃下30分钟,并在85℃下再保持30分钟,将其设定为一个循环。将此过程重复200次,即,200个循环,然后将LED保持在室温下。考察剥离状态以评价耐热冲击性。为进行评价,如上所述测试由相同的可固化组合物制备的20个LED,表1示出表现剥离的LED的数目,(剥离的LED数目/LED总数(20))。
(2)长期耐久性测试
在85℃和85%的相对湿度的条件下,提供30mA的电流的同时,运行所制备的LED500小时。随后,测量运行后亮度相对运行前初始亮度的降低率,并根据以下标准进行评价。
<评价标准>
A:相对于初始亮度,5%以下的亮度降低率
B:相对于初始亮度,大于5%且7%以下的亮度降低率
C:相对于初始亮度,大于7%且9%以下的亮度降低率
D:相对于初始亮度,大于9%的亮度降低率
实施例1
通过混合由式A至式D表示的化合物(共混量:式A:70g,式B:200g,式C:70g,式D:4g)制备能够通过氢化硅烷化固化的可固化组合物。此处,式A的聚有机硅氧烷通过如下方法制备:在催化剂(例如四甲基氢氧化铵(TMAH))的存在下,在大约115℃下,使八甲基环四硅氧烷和八苯基环四硅氧烷的混合物与二乙烯基四甲基二硅氧烷反应大约20小时,除式A的聚有机硅氧烷之外的其他化合物通过已知合成方法制备。随后,将催化剂(铂(0)-1,3-二乙烯基-1,1,3,3-四甲基二硅氧烷)以10ppm Pt(0)的含量混入组合物中,并将20g平均外径为约2mm,长度为约400nm的中空型伊毛缟石均匀混合,从而制备可固化组合物。
[式A]
(ViMe2SiO1/2)2(Me2SiO2/2)18(Ph2SiO2/2)14
[式B]
(ViMe2SiO1/2)2(Ph2SiO2/2)0.4(PhSiO3/2)6
[式C]
(HMe2SiO1/2)2(Ph2SiO2/2)1.5
[式D]
(ViMe2SiO1/2)2(EpSiO3/2)3(MePhSiO2/2)20
实施例2
通过混合由式E、F、C和D表示的化合物(共混量:式E:70g,式F:200g,式C:70g,式D:4g)制备能够通过氢化硅烷化固化的可固化组合物。此处,式E的聚有机硅氧烷通过如下方法制备,在催化剂(例如四甲基氢氧化铵(TMAH))的存在下,使八甲基环四硅氧烷和四甲基四苯基环四硅氧烷的混合物与二乙烯基四甲基二硅氧烷反应,除式E的聚有机硅氧烷之外的其他化合物通过已知合成方法制备。随后,将催化剂(铂(0)-1,3-二乙烯基-1,1,3,3-四甲基二硅氧烷)以10ppm Pt(0)的含量混入组合物中,并将大约20g平均内径为大约50mm,长度为大约8,000nm的中空型多水高岭土均匀混合,从而制备可固化组合物。
[式E]
(ViMe2SiO1/2)2(PhMeSiO2/2)26(Me2SiO2/2)4
[式F]
(ViMe2SiO1/2)2(MePhSiO2/2)0.4(PhSiO3/2)6
[式C]
(HMe2SiO1/2)2(Ph2SiO2/2)1.5
[式D]
(ViMe2SiO1/2)2(EpSiO3/2)3(MePhSiO2/2)20
实施例3
通过混合由式G、H、C和D表示的化合物(共混量:式G:70g,式H:200g,式C:70g,式D:4g)制备能够通过氢化硅烷化固化的可固化组合物。此处,式G的聚有机硅氧烷通过如下方法制备,使用例如四甲基氢氧化铵(TMAH))的催化剂,在合适的温度下,使八甲基环四硅氧烷和八苯基环四硅氧烷、八苯基-多面低聚倍半硅氧烷(八苯基-POSS)与二乙烯基四甲基二硅氧烷的混合物反应,其他化合物通过已知合成方法制备。随后,将催化剂(铂(0)-1,3-二乙烯基-1,1,3,3-四甲基二硅氧烷)以10ppm Pt(0)的含量混入组合物中,并将大约20g平均内径为大约30mm,长度为大约10,000nm的中空型多水高岭土均匀混合,从而制备可固化组合物。
[式G]
(ViMe2SiO1/2)2(Me2SiO2/2)10(Ph2SiO2/2)10(PhSiO3/2)3
[式H]
(ViMe2SiO1/2)2(MePhSiO2/2)0.4(PhSiO3/2)6
[式C]
(HMe2SiO1/2)2(Ph2SiO2/2)1.5
[式D]
(ViMe2SiO1/2)2(EpSiO3/2)3(MePhSiO2/2)20
实施例4
通过混合由式I、J、C和D表示的化合物(共混量:式I:70g,式J:200g,式C:70g,式D:4g)制备能够通过氢化硅烷化固化的可固化组合物。此处,式I的聚有机硅氧烷通过如下方法制备,在催化剂(例如四甲基氢氧化铵(TMAH))的存在下,使八甲基环四硅氧烷和八苯基环四硅氧烷的混合物与二乙烯基四甲基二硅氧烷反应,除此之外的其他化合物通过已知合成方法制备。随后,催化剂(铂(0)-1,3-二乙烯基-1,1,3,3-四甲基二硅氧烷)以10ppm Pt(0)的含量混入组合物中,并将大约20g的平均内径为大约40mm,长度为大约5,000nm的中空型多水高岭土均匀混合,从而制备可固化组合物。
[式I]
(ViMe2SiO1/2)2(Me2SiO2/2)14(Ph2SiO2/2)16
[式J]
(ViMe2SiO1/2)2(Ph2SiO2/2)0.4(PhSiO3/2)6
[式C]
(HMe2SiO1/2)2(Ph2SiO2/2)1.5
[式D]
(ViMe2SiO1/2)2(EpSiO3/2)3(MePhSiO2/2)20
对比实施例1
以与实施例1中所述相同的方法制备可固化组合物,不同的是,未混合伊毛缟石。
对比实施例2
以与实施例1中所述相同的方法制备可固化组合物,不同的是,未混合伊毛缟石,以及使用平均粒径为大约20nm的二氧化硅粒子。
对比实施例3
以与实施例1中所述相同的方法制备可固化组合物,不同的是,未混合伊毛缟石,以及使用玻璃鳞片(REP-015,Nippon Itarahas)。.
对比实施例4
以与实施例1中所述相同的方法制备可固化组合物,不同的是,未混合伊毛缟石,使用蒙脱石粘土。
测量实施例和对比实施例中制备的可固化组合物的物理性质并总结于表1中。
[表1]
Claims (19)
1.一种可固化组合物,包含:
含有聚有机硅氧烷的聚合产物,所述聚有机硅氧烷包含具有脂族不饱和键的官能团,具有式2的硅氧烷单元和式3的硅氧烷单元,并且所述聚有机硅氧烷中式2的硅氧烷单元相对于全部双官能硅氧烷单元的摩尔比为30%以上;和
纤维形状的填料:
[式2]
(R1R2SiO2/2)
[式3]
(R3 2SiO2/2)
其中,R1和R2各自独立地为环氧基、烷基、烯基或炔基,R3为芳基,
所述填料为中空纤维的形状,并且
所述纤维形状的填料满足等式1,
[等式1]
|X–Y|≤0.1
在等式1中,X为所述可固化组合物或其不包含填料的固化产物的折射率,Y为所述纤维形状的填料的折射率。
2.根据权利要求1所述的可固化组合物,其中,R1和R2各自独立地为烷基。
3.根据权利要求1所述的可固化组合物,其中,式3的硅氧烷单元相对于所述聚有机硅氧烷中包含芳基的双官能硅氧烷单元的摩尔比为70%以上。
4.根据权利要求1所述的可固化组合物,其中,所述聚有机硅氧烷具有式4的平均组成式:
[式4]
(R4 3SiO1/2)a(R4 2SiO2/2)b(R4SiO3/2)c(SiO4/2)d
其中,在至少一个R4为烯基并且至少一个R4为芳基的情况下,R4各自独立地为环氧基、烷基、烯基、炔基或芳基;a和b各自独立地为正数,c和d各自独立地为0或正数,b/(b+c+d)为0.7至1。
5.根据权利要求1所述的可固化组合物,其中,所述聚有机硅氧烷具有式5的平均组成式:
[式5]
(R5R6 2SiO1/2)e(R7R8SiO2/2)f(R9 2SiO2/2)g(R10SiO3/2)h
其中,R5为烷基、烯基、炔基或芳基,R6为具有1至4个碳原子的烷基,R7和R8各自独立地为烷基、烯基、环氧基或芳基,R9为环氧基或芳基,e为正数,f、g和h各自独立地为0或正数,(f+g)/(f+g+h)为0.7至1。
6.根据权利要求1所述的可固化组合物,其中,所述聚有机硅氧烷包含式1的单元:
[式1]
其中,Ra和Rb各自独立地为烷基、烯基或芳基,Rc为烷基或芳基。
7.根据权利要求1所述的可固化组合物,其中,所述聚合产物为包含式6的化合物的混合物的聚合产物:
[式6]
其中,Rd和Re各自独立地为环氧基、烷基、烯基、炔基或芳基,并且o为3至6。
8.根据权利要求1所述的可固化组合物,其中,所述聚合产物为包含式7和式8的化合物的混合物的聚合产物:
[式7]
[式8]
其中,Rf和Rg各自为环氧基或烷基,Rh和Ri各自为环氧基或芳基,p为3至6的数,q为3至6的数。
9.根据权利要求7和8中任一项所述的可固化组合物,其中,所述混合物还包含具有式9或式10的平均组成式的聚有机硅氧烷:
[式9]
[RjSiO3/2]
[式10]
[RkRl 2SiO1/2]p[RmSiO3/2]q
其中,Rj、Rk和Rm各自独立地为环氧基、烷基、烯基、炔基或芳基,Rl为具有1个碳原子至4个碳原子的烷基,p为1至3,q为1至10。
10.根据权利要求1所述的可固化组合物,其中,所述纤维形状的填料的长宽比为50以上。
11.根据权利要求1所述的可固化组合物,其中,所述中空纤维形状的填料的单股内径或外径为0.5nm至1,000nm。
12.根据权利要求1所述的可固化组合物,其中,所述纤维形状的填料的折射率为1.45以上。
13.根据权利要求1所述的可固化组合物,其中,所述中空纤维形状的填料为伊毛缟石或多水高岭土。
14.根据权利要求1所述的可固化组合物,其中,相对于100重量份的所述聚有机硅氧烷,以0.5至70重量份的量包含所述纤维形状的填料。
15.根据权利要求1所述的可固化组合物,还包含:具有式12的平均组成式的聚有机硅氧烷:
[式12]
(R11 3SiO1/2)a(R11 2SiO2/2)b(R11SiO3/2)c(SiO4/2)d
其中,在至少一个R11为烯基并且至少一个R11为芳基的情况下,R11各自独立地为环氧基、烷基、烯基、炔基或芳基;a为正数,b为0或正数,c为正数,d为0或正数,b/(b+c+d)小于0.65,c/(c+d)为0.8以上。
16.根据权利要求1所述的可固化组合物,其中,所述可固化组合物还包含式13的化合物,或具有式14的平均组成式的化合物:
[式13]
R12 3SiO(R12 2SiO)nSiR12 3
[式14]
(R13 3SiO1/2)a(R13 2SiO2/2)b(R13SiO3/2)c(SiO2)d
其中,在至少两个R12为氢原子并且至少一个R12为芳基的情况下,R12各自独立地为氢、烷基、烯基、炔基或芳基;在至少两个R13为氢原子并且至少一个R13为芳基的情况下,n为1至100,R13各自独立地为氢、烷基、烯基、炔基或芳基;以及a为正数,b为0或正数,c为正数,d为0或正数。
17.一种光子半导体,其通过固化的权利要求1所述的可固化组合物封装。
18.一种液晶显示器,其在背光单元中包括权利要求17所述的光子半导体。
19.一种照明装置,包括权利要求17所述的光子半导体。