CN104311914A - 汽车发动机衬套 - Google Patents

汽车发动机衬套 Download PDF

Info

Publication number
CN104311914A
CN104311914A CN201410538444.0A CN201410538444A CN104311914A CN 104311914 A CN104311914 A CN 104311914A CN 201410538444 A CN201410538444 A CN 201410538444A CN 104311914 A CN104311914 A CN 104311914A
Authority
CN
China
Prior art keywords
parts
gel
automotive engine
component
environment
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410538444.0A
Other languages
English (en)
Other versions
CN104311914B (zh
Inventor
张安民
许容毅
张辉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SHANDONG TOGET BRAKE SYSTEM Co.,Ltd.
Original Assignee
Anhui Aofeng Auto Parts Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Aofeng Auto Parts Co Ltd filed Critical Anhui Aofeng Auto Parts Co Ltd
Priority to CN201410538444.0A priority Critical patent/CN104311914B/zh
Publication of CN104311914A publication Critical patent/CN104311914A/zh
Application granted granted Critical
Publication of CN104311914B publication Critical patent/CN104311914B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种汽车发动机衬套，涉及汽车配件技术领域，由以下重量份数的组分构成：顺丁橡胶20份、天然橡胶15份、氟橡胶4份、硬脂酸钡4份、聚苯醚10份、桐油2份、气相法白炭黑5份、植物胶5份、二异氰酸酯5份、聚环氧乙烷5份、聚酰胺纤维5份、催化剂5份、碳酸钙5份、凹凸棒粉5份、薄荷油2份、改性硅胶5份；配制时将各组分一同送入反应容器中，在80-90℃环境下搅拌30分钟制得胶料，再送入模具成型即可；本发明成本低，配制方法简单，安全环保，可延长寿命长达3倍以上，减震性能明显提高，使用安全可靠。

Description

汽车发动机衬套
技术领域
本发明涉及汽车配件技术领域，尤其涉及一种汽车发动机衬套。
背景技术
汽车发动机衬套包括有衬套本体，衬套本体内开有连通的上下孔，现有技术中的发动机衬套通常采取用天然胶橡胶和顺丁橡胶混炼而制成的优质胶料经过混合后一体注塑成型，再经过硫化机模压而制成优质全橡胶制品，在便用性能上也可以可达到预期的便用要求。但是，其耐磨性不好，减震效果不好，使用年限不长，需要改进。
发明内容
本发明所要解决的技术问题在于提供一种成本低，使用效果佳的汽车发动机衬套。
本发明所要解决的技术问题采用以下技术方案来实现：
一种汽车发动机衬套，由以下重量份数的组分构成：顺丁橡胶20份、天然橡胶15份、氟橡胶4份、硬脂酸钡4份、聚苯醚10份、桐油2份、气相法白炭黑5份、植物胶5份、二异氰酸酯5份、聚环氧乙烷5份、聚酰胺纤维5份、催化剂5份、碳酸钙5份、凹凸棒粉5份、薄荷油2份、改性硅胶5份；配制时将各组分一同送入反应容器中，在80-90℃环境下搅拌30分钟制得胶料，再送入模具成型即可；
上述改性硅胶是将粉体硅胶投入反应釜中，加温至80℃，再投入茶叶生物碱、羟丙基-β-环糊精及石墨烯，搅拌均匀，在90℃保温30分钟，制得改性硅胶；其中粉体硅胶与茶叶生物碱、羟丙基-β-环糊精及石墨烯的质量比为80:5:5:10；
上述催化剂是由以下重量份数的组分构成：苦参碱4-6份、酒石酸4-6份、羟基乙酸4-6份、尿素4-6份、稀土2份、氧化铝微粉2份、硬脂酸3份、玉米淀粉5份、松香皂2份；制备时将各组分混匀，在120-125℃环境下热处理30分钟即可。
本发明的有益效果是：本发明成本低，配制方法简单，安全环保，可延长寿命长达3倍以上，减震性能明显提高，使用安全可靠。
具体实施方式
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解，下面结合具体实施例，进一步阐述本发明。
实施例1
一种汽车发动机衬套，由以下重量份数的组分构成：顺丁橡胶20份、天然橡胶15份、氟橡胶4份、硬脂酸钡4份、聚苯醚10份、桐油2份、气相法白炭黑5份、植物胶5份、二异氰酸酯5份、聚环氧乙烷5份、聚酰胺纤维5份、催化剂5份、碳酸钙5份、凹凸棒粉5份、薄荷油2份、改性硅胶5份；配制时将各组分一同送入反应容器中，在80-90℃环境下搅拌30分钟制得胶料，再送入模具成型即可；
上述改性硅胶是将粉体硅胶投入反应釜中，加温至80℃，再投入茶叶生物碱、羟丙基-β-环糊精及石墨烯，搅拌均匀，在90℃保温30分钟，制得改性硅胶；其中粉体硅胶与茶叶生物碱、羟丙基-β-环糊精及石墨烯的质量比为80:5:5:10；
上述催化剂是由以下重量份数的组分构成：苦参碱4-6份、酒石酸4-6份、羟基乙酸4-6份、尿素4-6份、稀土2份、氧化铝微粉2份、硬脂酸3份、玉米淀粉5份、松香皂2份；制备时将各组分混匀，在120-125℃环境下热处理30分钟即可。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。

Claims (1)

1.一种汽车发动机衬套，其特征在于，由以下重量份数的组分构成：顺丁橡胶20份、天然橡胶15份、氟橡胶4份、硬脂酸钡4份、聚苯醚10份、桐油2份、气相法白炭黑5份、植物胶5份、二异氰酸酯5份、聚环氧乙烷5份、聚酰胺纤维5份、催化剂5份、碳酸钙5份、凹凸棒粉5份、薄荷油2份、改性硅胶5份；配制时将各组分一同送入反应容器中，在80-90℃环境下搅拌30分钟制得胶料，再送入模具成型即可；
上述改性硅胶是将粉体硅胶投入反应釜中，加温至80℃，再投入茶叶生物碱、羟丙基-β-环糊精及石墨烯，搅拌均匀，在90℃保温30分钟，制得改性硅胶；其中粉体硅胶与茶叶生物碱、羟丙基-β-环糊精及石墨烯的质量比为80:5:5:10；
上述催化剂是由以下重量份数的组分构成：苦参碱4-6份、酒石酸4-6份、羟基乙酸4-6份、尿素4-6份、稀土2份、氧化铝微粉2份、硬脂酸3份、玉米淀粉5份、松香皂2份；制备时将各组分混匀，在120-125℃环境下热处理30分钟即可。
CN201410538444.0A 2014-10-13 2014-10-13 汽车发动机衬套 Active CN104311914B (zh)