CN104293279A - 一种制造防霉型有机硅密封胶的原料及其工艺 - Google Patents

一种制造防霉型有机硅密封胶的原料及其工艺 Download PDF

Info

Publication number
CN104293279A
CN104293279A CN201410500627.3A CN201410500627A CN104293279A CN 104293279 A CN104293279 A CN 104293279A CN 201410500627 A CN201410500627 A CN 201410500627A CN 104293279 A CN104293279 A CN 104293279A
Authority
CN
China
Prior art keywords
stir
hours
under
raw materials
sealant
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410500627.3A
Other languages
English (en)
Inventor
张建忠
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuxi tianli hardware spring factory
Original Assignee
Wuxi tianli hardware spring factory
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuxi tianli hardware spring factory filed Critical Wuxi tianli hardware spring factory
Priority to CN201410500627.3A priority Critical patent/CN104293279A/zh
Publication of CN104293279A publication Critical patent/CN104293279A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种制造防霉型有机硅密封胶的原料及其工艺，其原料包括：端羟基聚二甲基硅氧烷、甲基三丁酮肟硅烷、乙烯基三丁酮肟硅烷、碳酸钙、改性有机锡(催化剂)、白炭黑。采用本技术制造的密封胶是一种能有效抑制霉菌繁殖、生长的功能性有机硅密封胶，它的成功研制与开发，解决了以往密封胶的易变黄发黑的问题，使密封胶能长久保持稳定与美观，从而使之更适用于工业、建筑方面的应用，具有广阔的市场前景。

Description

一种制造防霉型有机硅密封胶的原料及其工艺
技术领域
本发明涉及密封胶制造领域，更具体的说是一种防霉型有机硅密封胶的原料、一种制造防霉型有机硅密封胶的工艺。 
背景技术
有机硅及其制得的有机硅材料，品种繁多，性能优异。目前品种牌号多达万种，常用的就有4000余种，大致可分为单体、中间体、产品及制品三大类。其中有机硅密封胶作为一种半有机半无机的高档密封材料，因其具有的卓越的耐候性、优异的耐高温性、耐化学性、环境友好等优点，广泛应用于建筑门窗、幕墙、汽车、道桥、电子及医疗等行业。防霉型有机硅密封胶是一种能有效抑制霉菌繁殖、生长的功能性有机硅密封胶，它的成功研制与开发，解决了以往密封胶的易变黄发黑的问题，使密封胶能长久保持稳定与美观，从而使之更适用于工业、建筑方面的应用。 
发明内容
本发明提供一种制造防霉型有机硅密封胶的原料及其工艺，为实现本发明的目的，本发明的技术方案如下： 
一种制造密封胶的原料，其原料包括：端羟基聚二甲基硅氧烷、甲基三丁酮肟硅烷、乙烯基三丁酮肟硅烷、碳酸钙、改性有机锡(催化剂)、白炭黑。
一种制造密封胶的工艺，其具体步骤包括： 
（1）加工有机硅基料
将5～7重量份表面已经被六甲基二硅氮烷或八甲基环四硅氧烷改性的、比表面积为120～200㎡/g的气相法白炭黑在搅拌条件下，加入60～100重量份粘度为为2000～10000mPa·S的端羟基二甲基硅氧烷中，以60～70转/分种的搅拌速度，搅拌3～4小时。静置8～9小时备用；
（2）制备基础胶料
80～100重量份的有机硅基料中，在60～70转/分搅拌速度下，搅拌2～3小时。静置备用；
（3）生产成品密封胶料
将上述基础胶料至于灌装机中，在真空度为2～8×10-4Pa条下，依次搅拌，加入3～5重量份硅烷偶联剂和2～3份催化剂，在60～70转/分的转速下，搅拌3～4小时。充入氮气，在氮气的保护及真空条件下，螺杆挤出灌装，制得单组份防霉有机硅密封剂。
优选的，步骤（2）中加入40%重量百分比的有机硅季铵盐菌剂和乙醇溶液3～6重量份。 
有益效果：本发明提供了一种制造防霉型有机硅密封胶的原料及其工艺，其原料包括：端羟基聚二甲基硅氧烷、甲基三丁酮肟硅烷、乙烯基三丁酮肟硅烷、碳酸钙、改性有机锡(催化剂)、白炭黑。采用本技术制造的密封胶是一种能有效抑制霉菌繁殖、生长的功能性有机硅密封胶，它的成功研制与开发，解决了以往密封胶的易变黄发黑的问题，使密封胶能长久保持稳定与美观，从而使之更适用于工业、建筑方面的应用，具有广阔的市场前景。 
具体实施方式
为使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解，下面结合具体实施方式，进一步阐述本发明。 
一种制造密封胶的原料，其原料包括：端羟基聚二甲基硅氧烷、甲基三丁酮肟硅烷、乙烯基三丁酮肟硅烷、碳酸钙、改性有机锡(催化剂)、白炭黑。 
所述原料制造密封胶的工艺，其具体步骤包括： 
（1）加工有机硅基料
将6重量份表面已经被六甲基二硅氮烷或八甲基环四硅氧烷改性的、比表面积为150㎡/g的气相法白炭黑在搅拌条件下，加入80重量份粘度为为7000mPa·S的端羟基二甲基硅氧烷中，以70转/分种的搅拌速度，搅拌4小时。静置9小时备用；
（2）制备基础胶料
加入40%重量百分比的有机硅季铵盐菌剂和乙醇溶液5重量份于90重量份的有机硅基料中，在70转/分搅拌速度下，搅拌3小时。静置备用；
（3）生产成品密封胶料
将上述基础胶料至于灌装机中，在真空度为6×10-4Pa条下，依次搅拌，加入4重量份硅烷偶联剂和3份催化剂，在70转/分的转速下，搅拌4小时。充入氮气，在氮气的保护及真空条件下，螺杆挤出灌装，制得单组份防霉有机硅密封剂。
本发明提供了一种制造防霉型有机硅密封胶的原料及其工艺，其原料包括：端羟基聚二甲基硅氧烷、甲基三丁酮肟硅烷、乙烯基三丁酮肟硅烷、碳酸钙、改性有机锡(催化剂)、白炭黑。采用本技术制造的密封胶是一种能有效抑制霉菌繁殖、生长的功能性有机硅密封胶，它的成功研制与开发，解决了以往密封胶的易变黄发黑的问题，使密封胶能长久保持稳定与美观，从而使之更适用于工业、建筑方面的应用，具有广阔的市场前景。 
以上所述仅为本发明的实施例，并非因此限制本发明的专利范围，凡是利用本发明说明书所作的等效结构或等效流程变换，或直接或间接运用在其他相关的技术领域，均同理包括在本发明的专利保护范围内。 

Claims (3)

1.一种制造防霉型密封胶的原料，其特征在于，其原料包括：端羟基聚二甲基硅氧烷、甲基三丁酮肟硅烷、乙烯基三丁酮肟硅烷、碳酸钙、改性有机锡(催化剂)、白炭黑。
2.一种利用权利要求1所述原料制造密封胶的工艺，其特征在于，其具体步骤包括：
（1）加工有机硅基料
将5～7重量份表面已经被六甲基二硅氮烷或八甲基环四硅氧烷改性的、比表面积为120～200㎡/g的气相法白炭黑在搅拌条件下，加入60～100重量份粘度为为2000～10000mPa·S的端羟基二甲基硅氧烷中，以60～70转/分种的搅拌速度，搅拌3～4小时，静置8～9小时备用；
（2）制备基础胶料
80～100重量份的有机硅基料中，在60～70转/分搅拌速度下，搅拌2～3小时,静置备用；
（3）生产成品密封胶料
将上述基础胶料至于灌装机中，在真空度为2～8×10-4Pa条下，依次搅拌，加入3～5重量份硅烷偶联剂和2～3份催化剂，在60～70转/分的转速下，搅拌3～4小时，充入氮气，在氮气的保护及真空条件下，螺杆挤出灌装，制得单组份防霉有机硅密封剂。
3.根据权利要求2所述的一种密封胶制造工艺，其特征在于，步骤（2）中加入40%重量百分比的有机硅季铵盐菌剂和乙醇溶液3～6重量份。
CN201410500627.3A 2014-09-26 2014-09-26 一种制造防霉型有机硅密封胶的原料及其工艺 Pending CN104293279A (zh)