CN107151127A - 一种瓷砖用环保彩色花香勾缝剂及其制备方法 - Google Patents
一种瓷砖用环保彩色花香勾缝剂及其制备方法 Download PDFInfo
- Publication number
- CN107151127A CN107151127A CN201710565639.8A CN201710565639A CN107151127A CN 107151127 A CN107151127 A CN 107151127A CN 201710565639 A CN201710565639 A CN 201710565639A CN 107151127 A CN107151127 A CN 107151127A
- Authority
- CN
- China
- Prior art keywords
- parts
- flower
- powder
- mixture
- environment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种瓷砖用环保彩色花香勾缝剂，包括以下重量份的原料：乳胶粉15‑25份、花朵提取液2‑4份、无机颜料1‑3份、白水泥20‑30份、矿物粉料50‑70份、吸附填土10‑18份、纳米二氧化钛粉末1‑3份、加工助剂5‑7份、碱抑制剂0.8‑1.4份、助粘剂2‑4份、防霉杀菌剂1‑3份、除甲醛助剂1‑3份、无机纤维3‑5份。本发明的勾缝剂具有良好的耐磨性、憎水性、耐候性，其粘结度高、防水抗渗、抗裂性好、可以抑制泛碱，能有效防止霉菌、藻类等微生物的侵蚀，此外还有花朵的清香；同时本发明的原料组分安全可靠，对环境无污染，且原料易得，成本较低，工艺简明，具有较高的实用价值和良好的应用前景。
Description
技术领域
本发明涉及建筑材料技术领域，具体涉及一种瓷砖用环保彩色花香勾缝剂及其制备方法。
背景技术
瓷砖勾缝剂又称填缝剂和嵌缝剂是用于填充瓷砖或石材间缝隙的接缝材料，与瓷砖、石材等装饰材料相配合提供美观的饰面及保证饰面砖之间的粘结和防渗。随着我国建筑业的快速发展，对瓷砖勾缝剂的要求越来越高，用量也越来越大。目前市场上的填缝剂大多采用乳液加水简单搅拌而成，将该填缝剂涂覆到底材上后，形成的膜既不透明，而且膜很薄，不利于该填缝剂起到防止墙面渗水的作用。
另一方面随着我国建筑业的快速发展，对瓷砖勾缝剂的要求越来越高，用量也越来越大。在勾缝剂的原料中，水泥是不可缺少的一部分。然而水泥因其刚性大、脆性碱性强，容易出现裂缝和泛碱，造成渗水和变色。
此外传统的勾缝材料主要以水泥、石英砂及各种助剂复配而成，普遍存在粘结力差、易脱落、防水性差、易泛碱，收缩率大、易开裂，颜色单一等问题，从而影响整个建筑的质量和美观。其次目前市场上的填缝剂大多采用乳液加水简单搅拌而成，将该填缝剂涂覆到底材上后，形成的膜既不透明，而且膜很薄，不利于该填缝剂起到防止墙面渗水的作用，另外，现有填缝剂固含量都低于20%，现有的瓷砖勾缝剂使用后，因水泥砂浆物料中含有游离的氢氧化钙多时，可导致建筑勾缝处表面泛碱，出现不美观的现象；另外，现有的勾缝剂不能有效防止霉菌、藻类等微生物的侵蚀；勾缝剂的柔韧性差、粘接力弱、耐水性和抗渗能力低。
发明内容
针对现有技术的缺陷，本发明的目的是提供一种瓷砖用环保彩色花香勾缝剂，该勾缝剂具有良好的耐磨性、憎水性、耐候性，其粘结度高、防水抗渗、抗裂性好、可以抑制泛碱，能有效防止霉菌、藻类等微生物的侵蚀，此外还有花朵的清香；同时本发明的原料组分安全可靠，对环境无污染，且原料易得，成本较低，工艺简明，具有较高的实用价值和良好的应用前景。
本发明解决技术问题采用如下技术方案：
本发明提供了一种瓷砖用环保彩色花香勾缝剂，包括以下重量份的原料：
乳胶粉15-25份、花朵提取液2-4份、无机颜料1-3份、白水泥20-30份、矿物粉料50-70份、吸附填土10-18份、纳米二氧化钛粉末1-3份、加工助剂5-7份、碱抑制剂0.8-1.4份、助粘剂2-4份、防霉杀菌剂1-3份、除甲醛助剂1-3份、无机纤维3-5份。
优选地，所述瓷砖用环保彩色花香勾缝剂包括以下重量份的原料：
乳胶粉20份、花朵提取液3份、无机颜料2份、白水泥25份、矿物粉料60份、吸附填土14份、纳米二氧化钛粉末2份、加工助剂6份、碱抑制剂1.1份、助粘剂3份、防霉杀菌剂2份、除甲醛助剂2份、无机纤维4份。
优选地，所述乳胶粉为丙烯酸酯乳胶粉和醋酸乙烯-乙烯乳胶粉按照重量比2:1组成的混合物；
所述无机纤维为玻璃纤维，所述无机纤维的规格为：长度5-7mm，直径为0.1-0.3mm。
优选地，所述花朵提取液为菊花提取液、金银花提取液、槐花提取液按照重量比3:1:2组成的混合物。
优选地，所述无机颜料为有色金属的氧化物和钛白粉按照重量比5:1组成的混合物。
优选地，所述矿物粉料为滑石粉、方解石粉、海泡石粉末按照重量比2:1:2组成的混合物；
所述吸附填土为凹凸棒土、膨润土、高岭土按照重量比5:1:1组成的混合物。
优选地，所述加工助剂为保水剂、消泡剂、固化剂按照重量比1:2:4组成的混合物；所述保水剂为羟乙基甲基纤维素，所述消泡剂为聚二甲基硅氧烷，所述固化剂为硫铝酸盐。
优选地，所述除甲醛助剂为几丁聚糖、2-咪唑烷酮按照重量比1:1组成的混合物，所述碱抑制剂为丙烯酸胶粉，所述助粘剂为聚乙烯醇，所述防霉杀菌剂为纳米铜和纳米银按照重量比5:1组成的混合物。
本发明还提供一种瓷砖用环保彩色花香勾缝剂的制备方法，包括以下步骤：
步骤一，按要求称量准备各组分原料；
步骤二，将矿物粉料、吸附填土、纳米二氧化钛粉末、无机纤维混合加入高速搅拌机中，转速为250-350r/min，搅拌25-35分钟，得到混合物A；
步骤三，将乳胶粉混合其重量20-30倍的水，混合花朵提取液加入高速搅拌机中，升温至35-45℃，转速为250-350r/min，搅拌20-30分钟，制得混合物B；
步骤四，将步骤三制得的混合物B、步骤二制备的混合物A、加工助剂、碱抑制剂、防霉杀菌剂、除甲醛助剂混合加入高速搅拌机中，转速为200-300r/min，搅拌15-25分钟，再升温至45-55℃，加入白水泥、助粘剂、无机颜料，继续搅拌30-40分钟，搅拌转速200-300r/min，制得发明的瓷砖用环保彩色花香勾缝剂。
优选地，所述瓷砖用环保彩色花香勾缝剂的制备步骤为：
步骤一，按要求称量准备各组分原料；
步骤二，将矿物粉料、吸附填土、纳米二氧化钛粉末、无机纤维混合加入高速搅拌机中，转速为300r/min，搅拌30分钟，得到混合物A；
步骤三，将乳胶粉混合其重量25倍的水，混合花朵提取液加入高速搅拌机中，升温至40℃，转速为300r/min，搅拌25分钟，制得混合物B；
步骤四，将步骤三制得的混合物B、步骤二制备的混合物A、加工助剂、碱抑制剂、防霉杀菌剂、除甲醛助剂混合加入高速搅拌机中，转速为250r/min，搅拌20分钟，再升温至50℃，加入白水泥、助粘剂、无机颜料，继续搅拌35分钟，搅拌转速250r/min，制得发明的瓷砖用环保彩色花香勾缝剂。
与现有技术相比，本发明具有如下的有益效果：
（1）本发明的一种瓷砖用环保彩色花香勾缝剂添加的矿物粉料和吸附填土，一方面可以降低勾缝剂的成本，减少水泥的使用量，能够形成致密的膏状弹性体，不受热涨、冻涨的侵害，另一方面能够吸收空气中的污染物，达到了较好的净化空气的作用。
（2）本发明的一种瓷砖用环保彩色花香勾缝剂添加的花朵提取液，主要为菊花提取液、金银花提取液、槐花提取液，使得制备的勾缝剂具有植物花香，具有安神愉悦的功能；添加的加工助剂主要为保水剂、消泡剂、固化剂，能使产品的保水率高、收缩率小，增强了产品的抗裂性和粘结性。
（3）本发明的一种瓷砖用环保彩色花香勾缝剂添加了除甲醛助剂、碱抑制剂、助粘剂、防霉杀菌剂，其中除甲醛助剂提高了产品去除甲醛等有毒有害物质的能力，碱抑制剂提高了勾缝剂的防水抗渗和抑制泛碱性能，保障了其耐候持久性能，助粘剂能提高其柔韧性、粘结力、耐水性和抗渗能力，防霉杀菌剂可防止霉菌、藻类等微生物的侵蚀。
（4）本发明的一种瓷砖用环保彩色花香勾缝剂添加无机纤维为玻璃纤维，可以有效增强勾缝剂的耐久性，使其不掉渣、抗水、耐碱耐磨以及耐玷污，提高了其抗收缩和抗裂性等性能。
（5）本发明的一种瓷砖用环保彩色花香勾缝剂具有良好的耐磨性、憎水性、耐候性，其粘结度高、防水抗渗、抗裂性好、可以抑制泛碱，能有效防止霉菌、藻类等微生物的侵蚀，此外还有花朵的清香；同时本发明的原料组分安全可靠，对环境无污染，且原料易得，成本较低，工艺简明，具有较高的实用价值和良好的应用前景。
具体实施方式
下面结合具体实施例，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例1.
本实施例的一种瓷砖用环保彩色花香勾缝剂，包括以下重量份的原料：
乳胶粉15份、花朵提取液2份、无机颜料1份、白水泥20份、矿物粉料50份、吸附填土10份、纳米二氧化钛粉末1份、加工助剂5份、碱抑制剂0.8份、助粘剂2份、防霉杀菌剂1份、除甲醛助剂1份、无机纤维3份。
本实施例中的乳胶粉为丙烯酸酯乳胶粉和醋酸乙烯-乙烯乳胶粉按照重量比2:1组成的混合物；
所述无机纤维为玻璃纤维，所述无机纤维的规格为：长度5-7mm，直径为0.1-0.3mm。
本实施例中的花朵提取液为菊花提取液、金银花提取液、槐花提取液按照重量比3:1:2组成的混合物。
本实施例中的无机颜料为有色金属的氧化物和钛白粉按照重量比5:1组成的混合物。
本实施例中的矿物粉料为滑石粉、方解石粉、海泡石粉末按照重量比2:1:2组成的混合物；
所述吸附填土为凹凸棒土、膨润土、高岭土按照重量比5:1:1组成的混合物。
本实施例中的加工助剂为保水剂、消泡剂、固化剂按照重量比1:2:4组成的混合物；所述保水剂为羟乙基甲基纤维素，所述消泡剂为聚二甲基硅氧烷，所述固化剂为硫铝酸盐。
本实施例中的除甲醛助剂为几丁聚糖、2-咪唑烷酮按照重量比1:1组成的混合物，所述碱抑制剂为丙烯酸胶粉，所述助粘剂为聚乙烯醇，所述防霉杀菌剂为纳米铜和纳米银按照重量比5:1组成的混合物。
本实施例的一种瓷砖用环保彩色花香勾缝剂的制备方法，包括以下步骤：
步骤一，按要求称量准备各组分原料；
步骤二，将矿物粉料、吸附填土、纳米二氧化钛粉末、无机纤维混合加入高速搅拌机中，转速为250r/min，搅拌35分钟，得到混合物A；
步骤三，将乳胶粉混合其重量20倍的水，混合花朵提取液加入高速搅拌机中，升温至35℃，转速为250r/min，搅拌20分钟，制得混合物B；
步骤四，将步骤三制得的混合物B、步骤二制备的混合物A、加工助剂、碱抑制剂、防霉杀菌剂、除甲醛助剂混合加入高速搅拌机中，转速为200r/min，搅拌15分钟，再升温至45℃，加入白水泥、助粘剂、无机颜料，继续搅拌30分钟，搅拌转速200r/min，制得发明的瓷砖用环保彩色花香勾缝剂。
实施例2.
本实施例的一种瓷砖用环保彩色花香勾缝剂，包括以下重量份的原料：
乳胶粉25份、花朵提取液4份、无机颜料3份、白水泥30份、矿物粉料70份、吸附填土18份、纳米二氧化钛粉末3份、加工助剂7份、碱抑制剂1.4份、助粘剂4份、防霉杀菌剂3份、除甲醛助剂3份、无机纤维5份。
本实施例中的乳胶粉为丙烯酸酯乳胶粉和醋酸乙烯-乙烯乳胶粉按照重量比2:1组成的混合物；
所述无机纤维为玻璃纤维，所述无机纤维的规格为：长度5-7mm，直径为0.1-0.3mm。
本实施例中的花朵提取液为菊花提取液、金银花提取液、槐花提取液按照重量比3:1:2组成的混合物。
本实施例中的无机颜料为有色金属的氧化物和钛白粉按照重量比5:1组成的混合物。
本实施例中的矿物粉料为滑石粉、方解石粉、海泡石粉末按照重量比2:1:2组成的混合物；
所述吸附填土为凹凸棒土、膨润土、高岭土按照重量比5:1:1组成的混合物。
本实施例中的加工助剂为保水剂、消泡剂、固化剂按照重量比1:2:4组成的混合物；所述保水剂为羟乙基甲基纤维素，所述消泡剂为聚二甲基硅氧烷，所述固化剂为硫铝酸盐。
本实施例中的除甲醛助剂为几丁聚糖、2-咪唑烷酮按照重量比1:1组成的混合物，所述碱抑制剂为丙烯酸胶粉，所述助粘剂为聚乙烯醇，所述防霉杀菌剂为纳米铜和纳米银按照重量比5:1组成的混合物。
本实施例的一种瓷砖用环保彩色花香勾缝剂的制备方法，包括以下步骤：
步骤一，按要求称量准备各组分原料；
步骤二，将矿物粉料、吸附填土、纳米二氧化钛粉末、无机纤维混合加入高速搅拌机中，转速为350r/min，搅拌35分钟，得到混合物A；
步骤三，将乳胶粉混合其重量30倍的水，混合花朵提取液加入高速搅拌机中，升温至45℃，转速为350r/min，搅拌30分钟，制得混合物B；
步骤四，将步骤三制得的混合物B、步骤二制备的混合物A、加工助剂、碱抑制剂、防霉杀菌剂、除甲醛助剂混合加入高速搅拌机中，转速为300r/min，搅拌25分钟，再升温至55℃，加入白水泥、助粘剂、无机颜料，继续搅拌40分钟，搅拌转速300r/min，制得发明的瓷砖用环保彩色花香勾缝剂。
实施例3.
本实施例的一种瓷砖用环保彩色花香勾缝剂，包括以下重量份的原料：
乳胶粉20份、花朵提取液3份、无机颜料2份、白水泥25份、矿物粉料60份、吸附填土14份、纳米二氧化钛粉末2份、加工助剂6份、碱抑制剂1.1份、助粘剂3份、防霉杀菌剂2份、除甲醛助剂2份、无机纤维4份。
本实施例中的乳胶粉为丙烯酸酯乳胶粉和醋酸乙烯-乙烯乳胶粉按照重量比2:1组成的混合物；
所述无机纤维为玻璃纤维，所述无机纤维的规格为：长度5-7mm，直径为0.1-0.3mm。
本实施例中的花朵提取液为菊花提取液、金银花提取液、槐花提取液按照重量比3:1:2组成的混合物。
本实施例中的无机颜料为有色金属的氧化物和钛白粉按照重量比5:1组成的混合物。
本实施例中的矿物粉料为滑石粉、方解石粉、海泡石粉末按照重量比2:1:2组成的混合物；
所述吸附填土为凹凸棒土、膨润土、高岭土按照重量比5:1:1组成的混合物。
本实施例中的加工助剂为保水剂、消泡剂、固化剂按照重量比1:2:4组成的混合物；所述保水剂为羟乙基甲基纤维素，所述消泡剂为聚二甲基硅氧烷，所述固化剂为硫铝酸盐。
本实施例中的除甲醛助剂为几丁聚糖、2-咪唑烷酮按照重量比1:1组成的混合物，所述碱抑制剂为丙烯酸胶粉，所述助粘剂为聚乙烯醇，所述防霉杀菌剂为纳米铜和纳米银按照重量比5:1组成的混合物。
本实施例的一种瓷砖用环保彩色花香勾缝剂的制备方法，包括以下步骤：
步骤一，按要求称量准备各组分原料；
步骤二，将矿物粉料、吸附填土、纳米二氧化钛粉末、无机纤维混合加入高速搅拌机中，转速为300r/min，搅拌30分钟，得到混合物A；
步骤三，将乳胶粉混合其重量25倍的水，混合花朵提取液加入高速搅拌机中，升温至40℃，转速为300r/min，搅拌25分钟，制得混合物B；
步骤四，将步骤三制得的混合物B、步骤二制备的混合物A、加工助剂、碱抑制剂、防霉杀菌剂、除甲醛助剂混合加入高速搅拌机中，转速为250r/min，搅拌20分钟，再升温至50℃，加入白水泥、助粘剂、无机颜料，继续搅拌35分钟，搅拌转速250r/min，制得发明的瓷砖用环保彩色花香勾缝剂。
以上各实施例制备的瓷砖用环保彩色花香勾缝剂的性能测试结果如下：
| 抗耐碱性 | 防水性（水珠法） | 吸水比% | |
| 实施例1 | 54h无异常 | 5滴水珠30分钟后保持原状 | 1.1 |
| 实施例2 | 49h无异常 | 5滴水珠30分钟后保持原状 | 1.2 |
| 实施例3 | 51h无异常 | 5滴水珠30分钟后保持原状 | 1.1 |
| 对比例 | 34h异常泛白 | 5滴水珠30分钟后水珠变小 | 7.6 |
本发明的一种瓷砖用环保彩色花香勾缝剂具有良好的耐磨性、憎水性、耐候性，其粘结度高、防水抗渗、抗裂性好、可以抑制泛碱，能有效防止霉菌、藻类等微生物的侵蚀，此外还有花朵的清香；同时本发明的原料组分安全可靠，对环境无污染，且原料易得，成本较低，工艺简明，具有较高的实用价值和良好的应用前景。
对于本领域技术人员而言，显然本发明不限于上述示范性实施例的细节，而且在不背离本发明的精神或基本特征的情况下，能够以其他的具体形式实现本发明。因此，无论从哪一点来看，均应将实施例看作是示范性的，而且是非限制性的，本发明的范围由所附权利要求而不是上述说明限定，因此旨在将落在权利要求的等同要件的含义和范围内的所有变化囊括在本发明内。
此外，应当理解，虽然本说明书按照实施方式加以描述，但并非每个实施方式仅包含一个独立的技术方案，说明书的这种叙述方式仅仅是为清楚起见，本领域技术人员应当将说明书作为一个整体，各实施例中的技术方案也可以经适当组合，形成本领域技术人员可以理解的其他实施方式。
Claims (10)
1.一种瓷砖用环保彩色花香勾缝剂，其特征在于，包括以下重量份的原料：
乳胶粉15-25份、花朵提取液2-4份、无机颜料1-3份、白水泥20-30份、矿物粉料50-70份、吸附填土10-18份、纳米二氧化钛粉末1-3份、加工助剂5-7份、碱抑制剂0.8-1.4份、助粘剂2-4份、防霉杀菌剂1-3份、除甲醛助剂1-3份、无机纤维3-5份。
2.根据权利要求1所述的一种瓷砖用环保彩色花香勾缝剂，其特征在于，所述瓷砖用环保彩色花香勾缝剂包括以下重量份的原料：
乳胶粉20份、花朵提取液3份、无机颜料2份、白水泥25份、矿物粉料60份、吸附填土14份、纳米二氧化钛粉末2份、加工助剂6份、碱抑制剂1.1份、助粘剂3份、防霉杀菌剂2份、除甲醛助剂2份、无机纤维4份。
3.根据权利要求1或2所述的一种瓷砖用环保彩色花香勾缝剂，其特征在于，所述乳胶粉为丙烯酸酯乳胶粉和醋酸乙烯-乙烯乳胶粉按照重量比2:1组成的混合物；
所述无机纤维为玻璃纤维，所述无机纤维的规格为：长度5-7mm，直径为0.1-0.3mm。
4.根据权利要求1或2所述的一种瓷砖用环保彩色花香勾缝剂，其特征在于，所述花朵提取液为菊花提取液、金银花提取液、槐花提取液按照重量比3:1:2组成的混合物。
5.根据权利要求1或2所述的一种瓷砖用环保彩色花香勾缝剂，其特征在于，所述无机颜料为有色金属的氧化物和钛白粉按照重量比5:1组成的混合物。
6.根据权利要求1或2所述的一种瓷砖用环保彩色花香勾缝剂，其特征在于，所述矿物粉料为滑石粉、方解石粉、海泡石粉末按照重量比2:1:2组成的混合物；
所述吸附填土为凹凸棒土、膨润土、高岭土按照重量比5:1:1组成的混合物。
7.根据权利要求1或2所述的一种瓷砖用环保彩色花香勾缝剂，其特征在于，所述加工助剂为保水剂、消泡剂、固化剂按照重量比1:2:4组成的混合物；所述保水剂为羟乙基甲基纤维素，所述消泡剂为聚二甲基硅氧烷，所述固化剂为硫铝酸盐。
8.根据权利要求1或2所述的一种瓷砖用环保彩色花香勾缝剂，其特征在于，所述除甲醛助剂为几丁聚糖、2-咪唑烷酮按照重量比1:1组成的混合物，所述碱抑制剂为丙烯酸胶粉，所述助粘剂为聚乙烯醇，所述防霉杀菌剂为纳米铜和纳米银按照重量比5:1组成的混合物。
9.一种制备如权利要求1或2所述瓷砖用环保彩色花香勾缝剂的方法，其特征在于，包括以下步骤：
步骤一，按要求称量准备各组分原料；
步骤二，将矿物粉料、吸附填土、纳米二氧化钛粉末、无机纤维混合加入高速搅拌机中，转速为250-350r/min，搅拌25-35分钟，得到混合物A；
步骤三，将乳胶粉混合其重量20-30倍的水，混合花朵提取液加入高速搅拌机中，升温至35-45℃，转速为250-350r/min，搅拌20-30分钟，制得混合物B；
步骤四，将步骤三制得的混合物B、步骤二制备的混合物A、加工助剂、碱抑制剂、防霉杀菌剂、除甲醛助剂混合加入高速搅拌机中，转速为200-300r/min，搅拌15-25分钟，再升温至45-55℃，加入白水泥、助粘剂、无机颜料，继续搅拌30-40分钟，搅拌转速200-300r/min，制得发明的瓷砖用环保彩色花香勾缝剂。
10.根据权利要求9所述的一种瓷砖用环保彩色花香勾缝剂的制备方法，其特征在于，所述步骤为：
步骤一，按要求称量准备各组分原料；
步骤二，将矿物粉料、吸附填土、纳米二氧化钛粉末、无机纤维混合加入高速搅拌机中，转速为300r/min，搅拌30分钟，得到混合物A；
步骤三，将乳胶粉混合其重量25倍的水，混合花朵提取液加入高速搅拌机中，升温至40℃，转速为300r/min，搅拌25分钟，制得混合物B；
步骤四，将步骤三制得的混合物B、步骤二制备的混合物A、加工助剂、碱抑制剂、防霉杀菌剂、除甲醛助剂混合加入高速搅拌机中，转速为250r/min，搅拌20分钟，再升温至50℃，加入白水泥、助粘剂、无机颜料，继续搅拌35分钟，搅拌转速250r/min，制得发明的瓷砖用环保彩色花香勾缝剂。