CN104278517B - 人工合成纤维后整理平滑助剂及其制备、浸渍方法 - Google Patents
人工合成纤维后整理平滑助剂及其制备、浸渍方法 Download PDFInfo
- Publication number
- CN104278517B CN104278517B CN201410546600.8A CN201410546600A CN104278517B CN 104278517 B CN104278517 B CN 104278517B CN 201410546600 A CN201410546600 A CN 201410546600A CN 104278517 B CN104278517 B CN 104278517B
- Authority
- CN
- China
- Prior art keywords
- final finishing
- weight portions
- pet
- slip aids
- moisturizing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及一种PET纤维后整理平滑助剂,在70℃温度下,把5~30重量份的由对苯二甲酸二甲酯、PEO-PPO嵌段聚醚和乙二醇通过酯交换熔融缩聚而成的聚醚型聚酯嵌段共聚物和50~100重量份的水均匀混合,冷却降温至常温,调节PH值呈弱酸性后,加入10~30重量份的三元共聚硅油,恒温搅拌使其混合均匀,调节PH值呈弱酸性后,即可得到产品,将PET纤维充分浸入PET纤维后整理保湿助剂的浸渍液中,浸渍参数如下:浴比3~5%o.w.f;药/水比1/100~2/100;浸泡温度35℃;浸泡时间18~20分钟;将浸渍后的纤维取出,离心脱水、烘干即可。本发明的后整理保湿助剂,浸渍使用简单方便,浸渍处理后具有抗静电性强,滋润滑爽,保湿持久性强的特点,生产设备简单,成本低。
Description
[技术领域]
本发明涉及纤维整理助剂,具体涉及一种PET纤维后整理平滑助剂及其制备、浸渍方法。
[背景技术]
由于真发原材料限制,合成纤维在发制品行业运用越来越多。但合成纤维与真发蛋白纤维手感差别较大,因此在合成纤维发制品完成前,大都要经过各种有机硅类助剂进行浸泡处理,赋予其较好的柔软,滋润,平滑,丰满的手感。但由于大多硅油本身含有的亲水性基团较少,并且对合成纤维的吸附能力较差,导致合成纤维产品出现干燥,打结,保湿持久性差,易产生静电的问题,不能满足产品滋润的手感要求,严重影响了产品质量。
[发明内容]
本发明的目的是解决现有技术中纤维后处理后容易出现干燥,打结,保湿持久性差,易产生静电的问题。
为了实现上述目的,本发明提供一种人工合成纤维后整理平滑助剂,包含以下组分:
a.5~30重量份的由对苯二甲酸二甲酯、PEO-PPO嵌段聚醚和乙二醇通过酯交换熔融缩聚而成的聚醚型聚酯嵌段共聚物;
b.10~30重量份三元共聚硅油;
c.50~100重量份的去离子水。
本发明提供的有人工合成纤维(PET)后整理保湿助剂各组份分子结构和配比的设计思路是使合成纤维浸渍处理后具有抗静电性强、滋润滑爽,保湿持久性强的性能特点。其机理是采用相似相容的化学原理,运用与合成纤维(PET)大分子结构相似的聚醚型聚酯嵌段共聚物,增强助剂与纤维的亲和力,增大纤维对药品的吸附量,使纤维表面的亲水基团成倍增加,最终达到较好的保湿效果。三元共聚硅油的加入旨在辅助提升产品的柔软性和平滑性。
本发明还包括一种PET纤维后整理保湿助剂的制备方法,在70℃温度下,把5~30重量份的由对苯二甲酸二甲酯、PEO-PPO嵌段聚醚和乙二醇通过酯交换熔融缩聚而成的聚醚型聚酯嵌段共聚物和50~100重量份的水均匀混合,冷却降温至常温,调节PH值呈弱酸性后,加入10~30重量份的三元共聚硅油,恒温搅拌使其混合均匀,调节PH值呈弱酸性后,即可得到产品。
本发明还包括上述PET纤维后整理保湿助剂的浸渍方法,包括以下步骤:
将PET纤维充分浸入PET纤维后整理保湿助剂的浸渍液中,浸渍参数如下:
浴比3--5%(o.w.f);
用量mL(药/水)1/100--2/100;
浸泡温度35℃;
浸泡时间18—20分钟;
将浸渍后的纤维取出,离心脱水、烘干即可。
本发明提供的人工合成纤维(PET)后整理保湿助剂,能与水任意比稀释,浸渍使用简单方便,浸渍处理后具有抗静电性强,滋润滑爽,保湿持久性强的特点,生产设备简单,成本低。
[具体实施方式]
下面结合实施例对本发明作进一步说明。
实施例1
1、纤维整理保湿助剂组分配方(以重量份数计):8份聚醚型聚酯嵌段共聚物、24份三元共聚硅油、68份去离子水。
2、制备方法:
在70℃温度下,把8份聚醚酯嵌段共聚物和适量40份的去离子水在乳化机中搅拌0.5小时,得到均匀的液体,冷却降温至常温,调节PH值呈弱酸性后,再按比例将24份三元共聚硅油与28份去离子水加入,搅拌均匀,恒温搅拌0.5小时使其混合均匀,调节PH值呈弱酸性后,即可得到产品。
其中的聚酯-聚醚型多嵌段共聚物采用的是常规的聚酯-聚醚型多嵌段共聚物,其生产工艺和产品都是清楚的,其反应机理一般如下:
与在180~200度,催化剂的条件下进行酯交换反应得到预聚体,然后预聚体又在250度左右,催化剂的条件下进行缩聚反应,最后获得如下式的聚酯-聚醚型多嵌段共聚物:
3、浸渍使用方法:
取1500毫升35℃的软化水,加入15克上述制得的产品搅拌,使其在水中充分溶解,得浸渍液;取待处理纤维300克,放入浸渍液,浸泡20分钟;把浸渍后的纤维捞出,离心脱水后烘干即可。
实施例2
1、纤维前整理助剂组分配方(以重量份数计):20份聚醚酯嵌段共聚物、16份三元共聚硅油、64份去离子水。
2、制备方法:
在70℃温度下,把20份聚醚酯嵌段共聚物和适量40份的去离子水在乳化机中搅拌0.5小时,得到均匀的液体,冷却降温至常温,调节PH值呈弱酸性后,再按比例将16份三元共聚硅油与24份去离子水加入,搅拌均匀,恒温搅拌0.5小时使其混合均匀,调节PH值呈弱酸性后,即可得到产品3、浸渍使用方法:
取1000毫升35℃的软化水,加入15克上述制得的产品搅拌,使其在水中充分溶解,得浸渍液;取待处理纤维300克,放入浸渍液,浸泡18分钟;把浸渍后的纤维捞出,离心脱水后烘干即可。
以上为本发明的较佳实施例,凡依本发明技术方案所作的改变,所产生的功能作用未超出本发明技术方案的范围时,均属于本发明的保护范围。
Claims (3)
1.一种PET纤维后整理平滑助剂,其特征在于由以下组分组成:
a.5~30重量份的由对苯二甲酸二甲酯、PEO-PPO嵌段聚醚和乙二醇通过酯交换熔融缩聚而成的聚醚型聚酯嵌段共聚物;
b.10~30重量份三元共聚硅油;
c.50~100重量份的去离子水。
2.一种PET纤维后整理平滑助剂的制备方法,其特征在于在70℃温度下,把5~30重量份的由对苯二甲酸二甲酯、PEO-PPO嵌段聚醚和乙二醇通过酯交换熔融缩聚而成的聚醚型聚酯嵌段共聚物和50~100重量份的水均匀混合,冷却降温至常温,调节pH值呈弱酸性后,加入10~30重量份的三元共聚硅油,恒温搅拌使其混合均匀,调节pH值呈弱酸性后,即可得到产品。
3.一种权利要求1所述PET纤维后整理平滑助剂的浸渍方法,其特征在于包括以下步骤:
将PET纤维充分浸入PET纤维后整理保湿助剂的浸渍液中,浸渍参数如下:
将浸渍后的纤维取出,离心脱水、烘干即可。