CN104086915A - 一种马达专用环保型pvc套管 - Google Patents
一种马达专用环保型pvc套管 Download PDFInfo
- Publication number
- CN104086915A CN104086915A CN201410269953.8A CN201410269953A CN104086915A CN 104086915 A CN104086915 A CN 104086915A CN 201410269953 A CN201410269953 A CN 201410269953A CN 104086915 A CN104086915 A CN 104086915A
- Authority
- CN
- China
- Prior art keywords
- parts
- sleeve pipe
- friendly pvc
- environment friendly
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及保护套管技术领域，它公开了一种马达专用环保型PVC套管，包括以下重量份的原料：PVC68—80份，TCPE20—32份，双季戊四醇酯或偏苯三酸三辛酯46—52份，碳酸钙磷石8—14份，稳定剂6—12份，硬脂酸盐0.5—1.2份，抗氧化剂0.5—1份。本发明采用PVC和TCPE共混之后混炼成胶粒，采用双季戊四醇酯或偏苯三酸三辛酯为增塑剂，采用碳酸钙磷石为阻燃剂，性能稳定，耐化学腐蚀性强，表面光滑，色泽均匀，绕线平整。
Description
技术领域
本发明涉及保护套管技术领域，尤其涉及到一种马达专用环保型PVC套管。
背景技术
马达套管在长期使用中易受磨损，老化，需要经常更换，目前市场上的马达套管大部分都是简单的用聚氯乙烯高分子聚合物为原料，经过注塑机高温注塑而成，但是该产品耐腐蚀性差，阻燃性差。
发明内容
本发明所要解决的技术问题是提供一种耐化学侵蚀，表面光滑，色泽均匀的马达专用环保型PVC套管。
为解决上述技术问题，本发明采用以下技术方案：
一种马达专用环保型PVC套管，其特征在于，包括以下重量份的原料：PVC68—80份，TCPE20—32份，双季戊四醇酯或偏苯三酸三辛酯46—52份，碳酸钙磷石8—14份，稳定剂6—12份，硬脂酸盐0.5—1.2份，抗氧化剂0.5—1份；
所述马达专用环保型PVC套管由以下顺序步骤制作而成，包括以下步骤：
(1)将PVC原料、TCPE原料混合后，在140—145℃下熔化，搅拌15—20分钟；
(2)向步骤(1)所得混合物中加入双季戊四醇酯或偏苯三酸三辛酯、碳酸钙磷石、稳定剂、硬脂酸盐和抗氧化剂，搅拌均匀加热至185—200℃，水冷却后加工成胶粒，并进行干燥处理；
(3)将干燥后的胶粒通过挤出机挤出成型；
(4)冷却后成卷包装。
优选的，所述马达专用环保型PVC套管包括以下重量份的原料：PVC70—80份，TCPE20—30份，双季戊四醇酯或偏苯三酸三辛酯8—52份，双酚A8—10份，硬脂酸盐0.5—1份，抗氧化剂0.5—0.8份。
优选的，所述稳定剂为双酚A。
优选的，所述PVC为105℃聚氯乙烯。
本发明与现有技术相比，具有以下优点：本发明采用PVC和TCPE共混之后混炼成胶粒，采用双季戊四醇酯或偏苯三酸三辛酯为增塑剂，采用碳酸钙磷石为阻燃剂，性能稳定，耐化学腐蚀性强，表面光滑，色泽均匀，绕线平整。
具体实施方式
下面结合具体实施方式对本发明的技术方案作进一步具体说明。
实施例一：
(1)将105℃PVC原料、TCPE原料混合后，在145℃下熔化，搅拌20分钟；
(2)向步骤(1)所得混合物中加入双季戊四醇酯、碳酸钙磷石、双酚A、硬脂酸盐和抗氧化剂，搅拌均匀加热至1200℃，水冷却后加工成胶粒，并进行干燥处理；
(3)将干燥后的胶粒通过挤出机挤出成型；
(4)冷却后成卷包装。
实施例二：
(1)将105℃PVC原料、TCPE原料混合后，在140℃下熔化，搅拌15分钟；
(2)向步骤(1)所得混合物中加入偏苯三酸三辛酯、碳酸钙磷石、双酚A、硬脂酸盐和抗氧化剂，搅拌均匀加热至185℃，水冷却后加工成胶粒，并进行干燥处理；
(3)将干燥后的胶粒通过挤出机挤出成型；
(4)冷却后成卷包装。
实施例三：
(1)将105℃PVC原料、TCPE原料混合后，在143℃下熔化，搅拌18分钟；
(2)向步骤(1)所得混合物中加入双季戊四醇酯、碳酸钙磷石、双酚A、硬脂酸盐和抗氧化剂，搅拌均匀加热至190℃，水冷却后加工成胶粒，并进行干燥处理；
(3)将干燥后的胶粒通过挤出机挤出成型；
(4)冷却后成卷包装。
实施例四：
(1)将105℃PVC原料、TCPE原料混合后，在142℃下熔化，搅拌17分钟；
(2)向步骤(1)所得混合物中加入双季戊四醇酯、碳酸钙磷石、双酚A、硬脂酸盐和抗氧化剂，搅拌均匀加热至188℃，水冷却后加工成胶粒，并进行干燥处理；
(3)将干燥后的胶粒通过挤出机挤出成型；
(4)冷却后成卷包装。
实施例五：
(1)将105℃PVC原料、TCPE原料混合后，在144℃下熔化，搅拌18分钟；
(2)向步骤(1)所得混合物中加入偏苯三酸三辛酯、碳酸钙磷石、双酚A、硬脂酸盐和抗氧化剂，搅拌均匀加热至195℃，水冷却后加工成胶粒，并进行干燥处理；
(3)将干燥后的胶粒通过挤出机挤出成型；
(4)冷却后成卷包装。
本发明与现有技术相比，具有以下优点：本发明采用PVC和TCPE共混之后混炼成胶粒，采用双季戊四醇酯或偏苯三酸三辛酯为增塑剂，采用碳酸钙磷石为阻燃剂，性能稳定，耐化学腐蚀性强，表面光滑，色泽均匀，绕线平整。
为进一步说明本发明的基本性能，将本发明产品进行了下表实验：
最后所应说明的是，以上具体实施方式仅用以说明本发明的技术方案而非限制，尽管参照较佳实施例对本发明进行了详细说明，本领域的普通技术人员应当理解，可以对本发明的技术方案进行修改或者等同替换，而不脱离本发明技术方案的精神和范围，其均应涵盖在本发明的权利要求范围当中。
Claims (4)
1.一种马达专用环保型PVC套管，其特征在于，包括以下重量份的原料：PVC68—80份，TCPE20—32份，双季戊四醇酯或偏苯三酸三辛酯46—52份，碳酸钙磷石8—14份，稳定剂6—12份，硬脂酸盐0.5—1.2份，抗氧化剂0.5—1份；
所述马达专用环保型PVC套管由以下顺序步骤制作而成，包括以下步骤：
(1)将PVC原料、TCPE原料混合后，在140—145℃下熔化，搅拌15—20分钟；
(2)向步骤(1)所得混合物中加入双季戊四醇酯或偏苯三酸三辛酯、碳酸钙磷石、稳定剂、硬脂酸盐和抗氧化剂，搅拌均匀加热至185—200℃，水冷却后加工成胶粒，并进行干燥处理；
(3)将干燥后的胶粒通过挤出机挤出成型；
(4)冷却后成卷包装。
2.根据权利要求1所述的马达专用环保型PVC套管，其特征在于，包括以下重量份的原料：PVC70—80份，TCPE20—30份，双季戊四醇酯或偏苯三酸三辛酯8—52份，双酚A8—10份，硬脂酸盐0.5—1份，抗氧化剂0.5—0.8份。
3.根据权利要求1所述的马达专用环保型PVC套管，其特征在于，所述稳定剂为双酚A。
4.根据权利要求1所述的马达专用环保型PVC套管，其特征在于，所述PVC为105℃聚氯乙烯。