CN103952944A - 一种仿荷叶格拉辛离型纸的制备方法 - Google Patents

一种仿荷叶格拉辛离型纸的制备方法 Download PDF

Info

Publication number
CN103952944A
CN103952944A CN201410191611.9A CN201410191611A CN103952944A CN 103952944 A CN103952944 A CN 103952944A CN 201410191611 A CN201410191611 A CN 201410191611A CN 103952944 A CN103952944 A CN 103952944A
Authority
CN
China
Prior art keywords
lotus leaf
release liners
release paper
preparation
laxin
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410191611.9A
Other languages
English (en)
Other versions
CN103952944B (zh
Inventor
於险峰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Ji Xiangbao (taicang) Material Science And Technology Development Co Ltd
Original Assignee
Ji Xiangbao (taicang) Material Science And Technology Development Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ji Xiangbao (taicang) Material Science And Technology Development Co Ltd filed Critical Ji Xiangbao (taicang) Material Science And Technology Development Co Ltd
Priority to CN201410191611.9A priority Critical patent/CN103952944B/zh
Publication of CN103952944A publication Critical patent/CN103952944A/zh
Application granted granted Critical
Publication of CN103952944B publication Critical patent/CN103952944B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种仿荷叶格拉辛离型纸的制备方法，包括以下步骤：将格拉辛原纸的双面印制荷叶图案，并进行电晕预处理和超级压光，然后将离型剂涂布在印制有荷叶图案的格拉辛原纸上得到仿荷叶格拉辛离型纸，最后将涂布好的仿荷叶格拉辛离型纸烘干即得。本发明的制备方法简单可行，通过采用钯碳酸钙做催化剂，生产效率更高，而且没有毒副作用，相比贵金属催化剂更有利。另外本发明制备的仿荷叶格拉辛离型纸不仅可长时间保存、而且能够锁住食品的营养成分以及风味，而且本产品无毒、无味、食品级离型纸，适合各种食品包装，而且抗菌率达到了100%。

Description

一种仿荷叶格拉辛离型纸的制备方法
技术领域
    本发明涉及离型纸的制备方法，具体涉及一种仿荷叶格拉辛离型纸的制备方法。
背景技术
荷叶为自然种植作物，产量有限，而且目前有很多食品要用到荷叶进行包装，而随着使用荷叶的量越来越大，目前种植根本无法满足需求，另外，由于荷叶无法长时间保存，韧性不高，包装食品后也容易破裂，而且在包装有粘性的食品的时候，荷叶会与食品产生粘连，在食用起来也极为不便。特别是我们在做荷叶包鸡、虾等一些含油脂量较高的食品的时候，油脂容易渗出荷叶，导致鸡、虾等的营养流失，而且风味也丢失。
发明内容
发明目的：针对现有技术的不足，本发明的目的是提供一种仿荷叶格拉辛离型纸的制备方法。本发明制备的仿荷叶格拉辛离型纸容易储藏、运输，防止粘连，还可长时间保存食品的风味，锁住食品的营养，基本可以替代普通的荷叶进行包装食品。
技术方案：为了解决上述问题，本发明的技术方案是提供一种仿荷叶格拉辛离型纸的制备方法，包括以下步骤：将格拉辛原纸的双面印制荷叶图案，并进行电晕预处理和超级压光，然后将离型剂涂布在印制有荷叶图案的格拉辛原纸上得到仿荷叶格拉辛离型纸，最后将涂布好的仿荷叶格拉辛离型纸烘干即得。
其中，上述格拉辛原纸的厚度为60~90g/m2，平滑度大于85秒，纵向抗张强度大于等于55N/15mm，横向抗张强度大于等于45 N/15mm。
其中，上述超级压光的步骤为：将电晕预处理过的印制有荷叶图案的格拉辛原纸经过温度为180-245℃加热架桥、温度为310-360℃加热熔融后，再加5Mpa-20Mpa的压力将其挤出。
其中，上述离型剂包括2~5重量份的食品级硅油、1~2重量份的碳酸钙、5~15重量份的棕榈油。
其中，上述离型剂的涂布量为0.35~0.55g/m2。
其中，上述烘干工序在70~90℃分区段烘干，中间温度为85~90℃， 两头温度为70~85℃，烘干时间控制20~25s。
上述的制备方法制备得到的仿荷叶格拉辛离型纸。
有益效果：本发明的制备方法简单可行，通过采用钯碳酸钙做催化剂，生产效率更高，而且没有毒副作用，相比贵金属催化剂更有利。另外本发明制备的仿荷叶格拉辛离型纸不仅可长时间保存、而且能够锁住食品的营养成分以及风味，而且本产品无毒、无味、食品级离型纸，适合各种食品包装，而且抗菌率达到了100%。
具体实施方式
下面结合具体实施方式，进一步阐述本发明。
实施例1：仿荷叶格拉辛离型纸的制备
一种仿荷叶格拉辛离型纸的制备方法，包括以下步骤：将格拉辛原纸的双面印制荷叶图案，格拉辛原纸的厚度为60g/m2，平滑度大于85秒，纵向抗张强度55N/15mm，横向抗张强度45 N/15mm；并进行电晕预处理和超级压光，超级压光的步骤为：将电晕预处理过的印制有荷叶图案的格拉辛原纸经过温度为180℃加热架桥、温度为310℃加热熔融后，再加5Mpa的压力将其挤出；然后将离型剂涂布在印制有荷叶图案的格拉辛原纸上得到仿荷叶格拉辛离型纸，最后将涂布好的仿荷叶格拉辛离型纸烘干即得；离型剂包括2重量份的食品级硅油、1重量份的碳酸钙、5重量份的棕榈油；离型剂的涂布量为0.35g/m2；烘干工序在70~90℃分区段烘干，中间温度为85℃， 两头温度为70℃，烘干时间控制20s。
 
实施例2
一种仿荷叶格拉辛离型纸的制备方法，包括以下步骤：将格拉辛原纸的双面印制荷叶图案，并进行电晕预处理和超级压光，然后将离型剂涂布在印制有荷叶图案的格拉辛原纸上得到仿荷叶格拉辛离型纸，最后将涂布好的仿荷叶格拉辛离型纸烘干即得。格拉辛原纸的厚度为90g/m2，平滑度大于85秒，纵向抗张强度60N/15mm，横向抗张强度55 N/15mm。超级压光的步骤为：将电晕预处理过的印制有荷叶图案的格拉辛原纸经过温度为245℃加热架桥、温度为360℃加热熔融后，再加20Mpa的压力将其挤出。离型剂包括5重量份的食品级硅油、2重量份的碳酸钙、15重量份的棕榈油。离型剂的涂布量为0.55g/m2。烘干工序在70~90℃分区段烘干，中间温度为90℃， 两头温度为85℃，烘干时间控制25s。
 
实施例3
一种仿荷叶格拉辛离型纸的制备方法，包括以下步骤：将格拉辛原纸的双面印制荷叶图案，并进行电晕预处理和超级压光，然后将离型剂涂布在印制有荷叶图案的格拉辛原纸上得到仿荷叶格拉辛离型纸，最后将涂布好的仿荷叶格拉辛离型纸烘干即得。格拉辛原纸的厚度为75g/m2，平滑度大于85秒，纵向抗张强度70N/15mm，横向抗张强度60 N/15mm。超级压光的步骤为：将电晕预处理过的印制有荷叶图案的格拉辛原纸经过温度为200℃加热架桥、温度为330℃加热熔融后，再加10Mpa的压力将其挤出。离型剂包括3重量份的食品级硅油、1重量份的碳酸钙、10重量份的棕榈油。离型剂的涂布量为0.45g/m2。烘干工序在70~90℃分区段烘干，中间温度为87℃， 两头温度为75℃，烘干时间控制22s。
实施例1~3制备得到的仿荷叶格拉辛离型纸的检测参数：
以上所述仅是本发明的优选实施方式，应当指出：对于本技术领域的普通技术人员来说，在不脱离本发明原理的前提下，还可以做出若干改进和润饰，这些改进和润饰也应视为本发明的保护范围。

Claims (7)

1.一种仿荷叶格拉辛离型纸的制备方法，其特征在于，包括以下步骤：将格拉辛原纸的双面印制荷叶图案，并进行电晕预处理和超级压光，然后将离型剂涂布在印制有荷叶图案的格拉辛原纸上得到仿荷叶格拉辛离型纸，最后将涂布好的仿荷叶格拉辛离型纸烘干即得。
2.根据权利要求1所述的一种仿荷叶格拉辛离型纸的制备方法，其特征在于，所述格拉辛原纸的厚度为60~90g/m2，平滑度大于85秒，纵向抗张强度大于等于55N/15mm，横向抗张强度大于等于45 N/15mm。
3.根据权利要求1所述的一种仿荷叶格拉辛离型纸的制备方法，其特征在于，所述超级压光的步骤为：将电晕预处理过的印制有荷叶图案的格拉辛原纸经过温度为180-245℃加热架桥、温度为310-360℃加热熔融后，再加5Mpa-20Mpa的压力将其挤出。
4.根据权利要求1所述的一种仿荷叶格拉辛离型纸的制备方法，其特征在于，所述离型剂包括2~5重量份的食品级硅油、1~2重量份的钯碳酸钙、5~15重量份的棕榈油。
5.根据权利要求1所述的一种仿荷叶格拉辛离型纸的制备方法，其特征在于，所述离型剂的涂布量为0.35~0.55g/m2。
6.根据权利要求1所述的一种仿荷叶格拉辛离型纸的制备方法，其特征在于，所述烘干工序在70~90℃分区段烘干，中间温度为85~90℃， 两头温度为70~85℃，烘干时间控制20~25s。
7.权利要求1~6任一项所述的制备方法制备得到的仿荷叶格拉辛离型纸。
CN201410191611.9A 2014-05-08 2014-05-08 一种仿荷叶格拉辛离型纸的制备方法 Active CN103952944B (zh)