CN103924769A - 一种防水实木地板及其制作方法 - Google Patents

一种防水实木地板及其制作方法 Download PDF

Info

Publication number
CN103924769A
CN103924769A CN201410188888.6A CN201410188888A CN103924769A CN 103924769 A CN103924769 A CN 103924769A CN 201410188888 A CN201410188888 A CN 201410188888A CN 103924769 A CN103924769 A CN 103924769A
Authority
CN
China
Prior art keywords
wooden floor
wood floor
waterproof
acrylic emulsion
silicone acrylic
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410188888.6A
Other languages
English (en)
Inventor
徐启旺
陈新明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HUZHOU CITY NANXUN HENGLI WOODEN PRODUCT FACTORY
Original Assignee
HUZHOU CITY NANXUN HENGLI WOODEN PRODUCT FACTORY
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HUZHOU CITY NANXUN HENGLI WOODEN PRODUCT FACTORY filed Critical HUZHOU CITY NANXUN HENGLI WOODEN PRODUCT FACTORY
Priority to CN201410188888.6A priority Critical patent/CN103924769A/zh
Publication of CN103924769A publication Critical patent/CN103924769A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种防水实木地板及其制作方法，包括木地板(1)，其特征在于：木地板(1)表面设有硅丙乳液渗透层(2)。本发明将硅丙乳液渗透到木地板的纤维导管中，使得木地板表面具有一层硅丙乳液渗透层，能够极大的提高木地板的耐水性，经试验，处理后的木地板用水浸泡24小时后，切开木地板检测，水分无法渗入木地板内部，因此本发明的木地板浸水后不变形、不缩胀，提高了木地板的使用寿命。同现有技术相比，本发明具有防水效果优越、持久，提高木地板稳定性的优点。

Description

一种防水实木地板及其制作方法
技术领域
本发明涉及一种防水实木地板及其制作方法，属于木地板技术领域。
背景技术
实木地板稳定性差，受潮或被水浸泡后容易发霉、变形，使用效果不好。现有技术中虽然有对实木地板的防水处理工艺，比如在地板表面喷涂防水剂，在地板外部安装防水套等，但一些工艺防水效果无法持久，一些工艺太过复杂，实施效果不理想。
发明内容
本发明的目的在于，提供一种防水实木地板及其制作方法。防水效果好，稳定持久。
本发明的技术方案。防水实木地板，包括木地板，木地板表面设有硅丙乳液渗透层。
前述的防水实木地板，所述硅丙乳液渗透层为纳米硅丙乳液渗透层。
防水实木地板的制作方法，包括下述步骤：
A、制作木地板基板，将木材制片，侧面制作榫口和榫头；
B、干燥，将木地板基板进行加热处理，温度为110-130度，时间为3-6小时；
C、将木地板基板放入硅丙乳液中进行渗透，渗透压力为0.2-0.4Mpa，时间为1-2小时，渗透后打磨木地板基板表面至平整；
D、将渗透后的木地板基板养护2-7天；
E、对木地板基板进行上漆、抛光处理，得到木地板。
前述的防水实木地板的制作方法，所述硅丙乳液为纳米硅丙乳液。
前述的防水实木地板的制作方法，步骤B中，所述加热温度为120度，时间为4-5小时。
前述的防水实木地板的制作方法，步骤C中，所述渗透压力为0.3Mpa，时间为1.5小时。
前述的防水实木地板的制作方法，步骤D中，所述养护时间为4天。
硅丙乳液结合了有机硅耐高温性、耐候性、耐化学品性，疏水、表面能低不易污染性和丙烯酸类树脂的高保色性、柔韧性、附着性，采用纳米级硅丙乳液，能够更好的渗透到木地板的纤维导管中。本发明将硅丙乳液渗透到木地板的纤维导管中，使得木地板表面具有一层硅丙乳液渗透层，能够极大的提高木地板的耐水性，经试验，处理后的木地板用水浸泡24小时后，切开木地板检测，水分无法渗入木地板内部，因此本发明的木地板浸水后不变形、不缩胀，提高了木地板的使用寿命。同现有技术相比，本发明具有防水效果优越、持久，提高木地板稳定性的优点。
附图说明
附图1为本发明的结构示意图。
具体实施方式
本发明的实施例1。防水实木地板的制作方法如下：
A、采用现有技术制作木地板基板，将木材制片，然后在木板侧面制作出榫口和榫头，得到木地板基板。
B、干燥：将木地板基板进行加热处理，温度为110-130度，时间为3-6小时，不仅降低木地板的含水率，还能改善木地板基板的渗透性。热处理温度过高，时间过长，基板容易变形、开裂，因此要注意加热的温度时间，并在加热过程中仔细观察。
C、将木地板基板放入硅丙乳液中进行渗透，然后加压，渗透压力为0.2-0.4Mpa，时间为1-2小时，渗透后打磨木地板基板表面至平整；采用的硅丙乳液采购现有成品。
D、将渗透后的木地板基板养护2-7天。
E、采用现有技术对木地板基板进行上漆、抛光处理，得到木地板。
制作得到的防水实木地板，如图1所示，其木地板1表面形成硅丙乳液渗透层2，能够防止水进入木地板内部。
本发明的实施例2。防水实木地板的制作方法如下：
A、采用现有技术制作木地板基板，将木材制片，然后在木板侧面制作出榫口和榫头，得到木地板基板。
B、干燥，将木地板基板进行加热处理，温度为120度，时间为4-5小时。
C、将木地板基板放入硅丙乳液中进行渗透，渗透压力为0.3Mpa，时间为1.5小时，渗透后打磨木地板基板表面至平整。
D、将渗透后的木地板基板养护4天。
E、采用现有技术对木地板基板进行上漆、抛光处理，得到木地板成品。
制作得到的防水实木地板，其木地板1表面形成纳米硅丙乳液渗透层2。
本发明的实施例3。防水实木地板的制作方法如下：
A、采用现有技术制作木地板基板，将木材制片，然后在木板侧面制作出榫口和榫头，得到木地板基板。
B、干燥，将木地板基板进行加热处理，温度为125度，时间为4小时；
C、将木地板基板放入硅丙乳液中进行渗透，渗透压力为0.3Mpa，时间为1.5小时，渗透后打磨木地板基板表面至平整；
D、将渗透后的木地板基板养护4天；
E、采用现有技术对木地板基板进行上漆、抛光处理，得到木地板成品。
制作得到的防水实木地板，其木地板1表面形成纳米硅丙乳液渗透层2。
本发明的实施例4。防水实木地板的制作方法如下：
A、采用现有技术制作木地板基板，将木材制片，然后在木板侧面制作出榫口和榫头，得到木地板基板。
B、干燥，将木地板基板进行加热处理，温度为115度，时间为5.5小时。
C、将木地板基板放入硅丙乳液中进行渗透，渗透压力为0.3Mpa，时间为1.2小时，渗透后打磨木地板基板表面至平整。
D、将渗透后的木地板基板养护4天。
E、采用现有技术对木地板基板进行上漆、抛光处理，得到木地板成品。
制作得到的防水实木地板，其木地板1表面形成纳米硅丙乳液渗透层2。

Claims (7)

1.一种防水实木地板，包括木地板(1)，其特征在于：木地板(1)表面设有硅丙乳液渗透层(2)。
2.根据权利要求1所述的防水实木地板，其特征在于：所述硅丙乳液渗透层(2)为纳米硅丙乳液渗透层。
3.如权利要求1或2所述的防水实木地板的制作方法，其特征在于：包括下述步骤：
A、制作木地板基板，将木材制片，侧面制作榫口和榫头；
B、干燥，将木地板基板进行加热处理，温度为110-130度，时间为3-6小时；
C、将木地板基板放入硅丙乳液中进行渗透，渗透压力为0.2-0.4Mpa，时间为1-2小时，渗透后打磨木地板基板表面至平整；
D、将渗透后的木地板基板养护2-7天；
E、对木地板基板进行上漆、抛光处理，得到木地板。
4.根据权利要求3所述的防水实木地板的制作方法，其特征在于：所述硅丙乳液为纳米硅丙乳液。
5.根据权利要求3所述的防水实木地板的制作方法，其特征在于：步骤B中，所述加热温度为120度，时间为4-5小时。
6.根据权利要求3所述的防水实木地板的制作方法，其特征在于：步骤C中，所述渗透压力为0.3Mpa，时间为1.5小时。
7.根据权利要求3所述的防水实木地板的制作方法，其特征在于：步骤D中，所述养护时间为4天。
CN201410188888.6A 2014-05-06 2014-05-06 一种防水实木地板及其制作方法 Pending CN103924769A (zh)