CN103922385B - 一种氧化铈六边形纳米片状结构的制备方法 - Google Patents

一种氧化铈六边形纳米片状结构的制备方法 Download PDF

Info

Publication number
CN103922385B
CN103922385B CN201410193490.1A CN201410193490A CN103922385B CN 103922385 B CN103922385 B CN 103922385B CN 201410193490 A CN201410193490 A CN 201410193490A CN 103922385 B CN103922385 B CN 103922385B
Authority
CN
China
Prior art keywords
cerium oxide
shape structure
preparation
hexagonal nanosheet
nanosheet shape
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201410193490.1A
Other languages
English (en)
Other versions
CN103922385A (zh
Inventor
许海峰
蔡红
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Yancheng Mountain Fengruocao Decoration Co.,Ltd.
Yancheng Yidong Technology Service Co ltd
Original Assignee
Suzhou University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Suzhou University filed Critical Suzhou University
Priority to CN201410193490.1A priority Critical patent/CN103922385B/zh
Publication of CN103922385A publication Critical patent/CN103922385A/zh
Application granted granted Critical
Publication of CN103922385B publication Critical patent/CN103922385B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种氧化铈六边形纳米片状结构的制备方法，包括以下步骤：将1.4903g CeCl3·7H2O加入到10mL蒸馏水中，搅拌混合，为a液；将4.7430g尿素加入到15mL蒸馏水中，充分搅拌15-20min，与上述a液混合，充分搅拌30-35min，加入10mL乙二胺，再搅拌30-35min，转入50mL高温反应釜，在120-160℃下反应48h，反应结束后用水和酒精交替洗涤各3遍，最后在400℃下退火5h，即得所述氧化铈六边形纳米片状结构。本发明生产的纳米氧化铈纯净度高、形貌规范，尺寸均匀，不易团聚，环保，不添加大分子表面活性剂，原料简单，制备工艺和所需设备简单。

Description

一种氧化铈六边形纳米片状结构的制备方法
技术领域
本发明主要涉及纳米材料领域，尤其涉及一种氧化铈六边形纳米片状结构的制备方法。
背景技术
氧化铈可以广泛应用于抛光材料、催化剂、催化剂载体(助剂)、紫外线吸收剂、燃料电池电解质、汽车尾气吸收剂、电子陶瓷等；因此对氧化铈纳米材料进行了比较深入的研究，制备纳米氧化铈的方法也有很多，如高温煅烧法、水热合成法、溶液沉淀法、溶胶-凝胶法、微乳液法、有机铈盐热分解法等；但这些方法具有配方复杂，一般需要添加适合的表面活性剂或者沉淀剂，生产条件苛刻和成本高等缺点；
近年来，研究者们发现不同形貌的氧化铈具有不同的理化性质，因为为了不断提高氧化铈在各个领域的高效适用性，一种产量高、易控制、适于工业化生产的制备方法是很有必要的。
发明内容
本发明目的就是提供一种氧化铈六边形纳米片状结构的制备方法。
本发明是通过以下技术方案实现的：
一种氧化铈六边形纳米片状结构的制备方法，包括以下步骤：
(1)将1.4903g CeCl3·7H2O加入到10mL蒸馏水中，搅拌混合，为a液；
(2)将4.7430g尿素加入到15mL蒸馏水中，充分搅拌15-20min，与上述a液混合，充分搅拌30-35min，加入10mL乙二胺，再搅拌30-35min，转入50mL高温反应釜，在120-160℃下反应48h，反应结束后用水和酒精交替洗涤各3遍，最后在400℃下退火5h，即得所述氧化铈六边形纳米片状结构。
本发明的优点是：
本发明生产的纳米氧化铈纯净度高、形貌规范，尺寸均匀，直径为500-800nm，不易团聚，环保，不添加大分子表面活性剂，原料简单，制备工艺和所需设备简单。
附图说明
图1为氧化铈六边形纳米片状结构的XRD图；
图2为氧化铈六边形纳米片状结构的SEM图。
具体实施方式
实施例1
一种氧化铈六边形纳米片状结构的制备方法，包括以下步骤：
(1)将1.4903g CeCl3·7H2O加入到10mL蒸馏水中，搅拌混合，为a液；
(2)将4.7430g尿素加入到15mL蒸馏水中，充分搅拌15min，与上述a液混合，充分搅拌30min，加入10mL乙二胺，再搅拌30min，转入50mL高温反应釜，在120℃下反应48h，反应结束后用水和酒精交替洗涤各3遍，最后在400℃下退火5h，即得所述氧化铈六边形纳米片状结构，直径为500-800nm。
实施例2
一种氧化铈六边形纳米片状结构的制备方法，包括以下步骤：
(1)将1.4903g CeCl3·7H2O加入到10mL蒸馏水中，搅拌混合，为a液；
(2)将4.7430g尿素加入到15mL蒸馏水中，充分搅拌15min，与上述a液混合，充分搅拌30min，加入10mL乙二胺，再搅拌30min，转入50mL高温反应釜，在140℃下反应48h，反应结束后用水和酒精交替洗涤各3遍，最后在400℃下退火5h，即得所述氧化铈六边形纳米片状结构，直径为500-800nm。

Claims (1)

1.一种氧化铈六边形纳米片状结构的制备方法，其特征在于包括以下步骤：
(1)将1.4903g CeCl3·7H2O加入到10mL蒸馏水中，搅拌混合，为a液；
(2)将4.7430g尿素加入到15mL蒸馏水中，充分搅拌15-20min，与上述a液混合，充分搅拌30-35min，加入10mL乙二胺，再搅拌30-35min，转入50mL高温反应釜，在120-160℃下反应48h，反应结束后用水和酒精交替洗涤各3遍，最后在400℃下退火5h，即得所述氧化铈六边形纳米片状结构。
CN201410193490.1A 2014-05-08 2014-05-08 一种氧化铈六边形纳米片状结构的制备方法 Active CN103922385B (zh)