CN103881637A - 一种塑料粘合剂 - Google Patents
一种塑料粘合剂 Download PDFInfo
- Publication number
- CN103881637A CN103881637A CN201410106122.9A CN201410106122A CN103881637A CN 103881637 A CN103881637 A CN 103881637A CN 201410106122 A CN201410106122 A CN 201410106122A CN 103881637 A CN103881637 A CN 103881637A
- Authority
- CN
- China
- Prior art keywords
- parts
- epoxy resin
- sodium hydroxide
- aging agent
- zinc oxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种塑料粘合剂，其由以下重量份的原料制成：E-51环氧树脂100-200份，酚醛树脂30-50份，环己基苯基对苯二胺3-5份，氢氧化钠4-6份，氧化镁4-6份，氧化锌2-4份，防老剂1-3份，增强剂0.5-1份，稳定剂0.3-0.5份。本发明的有益效果在于：本发明以E-51环氧树脂为基本制备出塑料粘合剂，制备方法简单，具有良好的保存稳定性、粘结性和防老性，且固化快，便于塑料间的及时粘合，利于推广普及。
Description
技术领域
本发明属于粘合剂技术领域，尤其涉及一种塑料粘合剂。
背景技术
当今社会塑料因为其质轻价廉而受到人们的欢迎，市场中充斥着大量的塑料制品，塑料粘合剂也就应运而生。但现有的塑料粘合剂不仅生产工艺复杂，价格较高，而且其成品粘合剂粘结效果差，固化慢，给塑料粘合操作带来了极大的不便。
发明内容
本发明所要解决的技术问题是提供一种粘结效果好，固化较快的塑料粘合剂。
为解决上述技术问题，本发明采用的技术方案是：
一种塑料粘合剂，其由以下重量份的原料制成：E-51环氧树脂100-200份，酚醛树脂30-50份，环己基苯基对苯二胺3-5份，氢氧化钠4-6份，氧化镁4-6份，氧化锌2-4份，防老剂1-3份，增强剂0.5-1份，稳定剂0.3-0.5份。
优选的，上述塑料粘合剂由以下重量份的原料制成：E-51环氧树脂150份，酚醛树脂40份，环己基苯基对苯二胺4份，氢氧化钠5份，氧化镁5份，氧化锌3份，防老剂2份，增强剂0.8份，稳定剂0.4份。
制备上述塑料粘合剂的方法，包括以下步骤：先将E-51环氧树脂、酚醛树脂、环己基苯基对苯二胺、氢氧化钠、氧化镁和氧化锌放入反应釜内，在50-60℃的无氧环境下搅拌20-30分钟；然后放入防老剂、增强剂和稳定剂，加温至60-70℃，继续在无氧环境中搅拌40-50分钟；最后静置，冷却，并封装入库。
本发明的有益效果在于：本发明以E-51环氧树脂为基本制备出塑料粘合剂，制备方法简单，具有良好的保存稳定性、粘结性和防老性，且固化快，便于塑料间的及时粘合，利于推广普及。
具体实施方式：
下面结合各实施例对本发明作进一步的阐述，但不是对本发明的限制：
实施例1
一种塑料粘合剂，其由以下重量份的原料制成：E-51环氧树脂100份，酚醛树脂30份，环己基苯基对苯二胺3份，氢氧化钠4份，氧化镁4份，氧化锌2份，防老剂1份，增强剂0.5份，稳定剂0.3份。
制备上述塑料粘合剂的方法，包括以下步骤：先将E-51环氧树脂、酚醛树脂、环己基苯基对苯二胺、氢氧化钠、氧化镁和氧化锌放入反应釜内，在50℃的无氧环境下搅拌20分钟；然后放入防老剂、增强剂和稳定剂，加温至60℃，继续在无氧环境中搅拌40分钟；最后静置，冷却，并封装入库。
实施例2
一种塑料粘合剂，其由以下重量份的原料制成：E-51环氧树脂150份，酚醛树脂40份，环己基苯基对苯二胺4份，氢氧化钠5份，氧化镁5份，氧化锌3份，防老剂2份，增强剂0.8份，稳定剂0.4份。
制备上述塑料粘合剂的方法，包括以下步骤：先将E-51环氧树脂、酚醛树脂、环己基苯基对苯二胺、氢氧化钠、氧化镁和氧化锌放入反应釜内，在55℃的无氧环境下搅拌25分钟；然后放入防老剂、增强剂和稳定剂，加温至65℃，继续在无氧环境中搅拌45分钟；最后静置，冷却，并封装入库。
实施例3
一种塑料粘合剂，其由以下重量份的原料制成：E-51环氧树脂200份，酚醛树脂50份，环己基苯基对苯二胺5份，氢氧化钠6份，氧化镁6份，氧化锌4份，防老剂3份，增强剂1份，稳定剂0.5份。
制备上述塑料粘合剂的方法，包括以下步骤：先将E-51环氧树脂、酚醛树脂、环己基苯基对苯二胺、氢氧化钠、氧化镁和氧化锌放入反应釜内，在60℃的无氧环境下搅拌30分钟；然后放入防老剂、增强剂和稳定剂，加温至70℃，继续在无氧环境中搅拌50分钟；最后静置，冷却，并封装入库。
Claims (3)
1. 一种塑料粘合剂，其特征在于，由以下重量份的原料制成：E-51环氧树脂100-200份，酚醛树脂30-50份，环己基苯基对苯二胺3-5份，氢氧化钠4-6份，氧化镁4-6份，氧化锌2-4份，防老剂1-3份，增强剂0.5-1份，稳定剂0.3-0.5份。
2.根据权利要求1所述的一种塑料粘合剂，其特征在于，由以下重量份的原料制成：E-51环氧树脂150份，酚醛树脂40份，环己基苯基对苯二胺4份，氢氧化钠5份，氧化镁5份，氧化锌3份，防老剂2份，增强剂0.8份，稳定剂0.4份。
3.一种制备如根据权利要求1所述的塑料粘合剂的方法，其特征在于，包括以下步骤：先将E-51环氧树脂、酚醛树脂、环己基苯基对苯二胺、氢氧化钠、氧化镁5份和氧化锌放入反应釜内，在50-60℃的无氧环境下搅拌20-30分钟；然后放入防老剂、增强剂和稳定剂，加温至60-70℃，继续在无氧环境中搅拌40-50分钟；最后静置，冷却，并封装入库。