CN1036790C - 一种防水胶及其制备方法 - Google Patents
一种防水胶及其制备方法 Download PDFInfo
- Publication number
- CN1036790C CN1036790C CN95106924A CN95106924A CN1036790C CN 1036790 C CN1036790 C CN 1036790C CN 95106924 A CN95106924 A CN 95106924A CN 95106924 A CN95106924 A CN 95106924A CN 1036790 C CN1036790 C CN 1036790C
- Authority
- CN
- China
- Prior art keywords
- parts
- liquid
- glue
- stirred
- ethylene glycol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
一种防水胶及其制备方法。本发明属于防水胶的组成及其制备方法。本发明的特点是以苯丙乳液、磷酸三丁酯、乙二醇、氯化石蜡、白乳胶和丙烯酸为其原料,分成两组混合搅拌,再合并搅拌反应,形成终产品。本发明的防水胶防水性能较好、用途广泛、耐老化时间长、制作工艺简单。
Description
本发明属于一种防水胶及其制备方法,特别是多用途的防水胶及其制备方法。
现有的防水胶在通常情况下性能还是比较令人满意的,但普遍存在的问题是其用途单一、耐老化时间较短、价格较高及制作工艺复杂,尤其使人们不满的是在寒冷气候下易发生脆裂现象,完全失去了防水性能。
本发明的目的是提供一种多用途的防水胶,其用途广泛、防水性能较好、耐老化时间长、制作工艺简单,它不仅可作为堵漏胶使用,还可作为防水涂料和粘贴用胶使用。
实现本发明的技术方案是:以苯丙乳液、磷酸三丁酯、乙二醇、氯化石蜡、白乳胶和丙烯酸为其生产原料,首先将苯丙乳液、磷酸三丁酯、乙二醇和氯化石蜡混合搅拌反应,形成A液,然后又混合白乳胶和丙烯酸,搅拌反应,形成B液,最后加温搅拌A、B两液,形成终产品。
本发明的具体配方比例及其制作工艺如下:
(1)以重量计,将20~50份的苯丙乳液、2~5份磷酸三丁酯、4~7份乙二醇和10~40份氯化石蜡加入反应釜中,搅拌10分钟后停机,在18~22℃下反应24小时,形成A液;
(2)将20~60份白乳胶和24~54份丙烯酸加入反应釜中,搅拌10分钟,在12~15℃下反应8小时,构成B液;
(3)先将A液加入反应釜中搅拌3~5分钟,再把B液加入反应釜中搅拌10分钟,然后升温至60~80℃,反应4小时即构成本发明所述的终产品。
本发明所述的防水胶用途比较广泛,它可作为粘贴墙纸、标签用胶,可用来在墙柱或墙面上粘贴大理石、瓷砖等,还可用作屋面及落水口处的防水处理、水池及落水管道的堵漏、各种植绒用胶等。本防水胶的生产工艺简单、施工操作容易,产品的性能较稳定,有较好的粘结力、伸缩率、抗水性能、耐寒性及耐老化性。本防水胶的使用寿命可达30年之久,可在-40℃的低温下不发生脆裂现象,其延伸率可达到500%,即使用于落水口处的防水堵漏,也很容易施工。此外,通过调整胶中的掺水量或白乳胶量,本产品可重复粘贴物品。
下面,列举几个本发明的具体实施例,对其技术方案作进一步描述。
实施例1:管道堵漏胶的制备
以重量计,取苯丙乳液50份(可采用北京东方化工厂BC01牌号的苯丙乳液,或云南省武定县新兴涂料厂生产的)、磷酸三丁酯2份、乙二醇7份、氯化石蜡10份,搅拌制得第一组A液,再取白乳胶40份(可用贵州有机化工厂的“水晶”牌,或昆明精细化工厂生产的)、丙烯酸30份搅拌得到第二组B液,将A液和B液混合搅拌反应,即可制得最终产品。
实施例2:标签、墙纸等粘贴用胶的制备
以重量计,取苯丙乳液30份、磷酸三丁酯3份、乙二醇5份、氯化石蜡20份,搅拌制得第一组A液、再取白乳胶20份、丙烯酸30份搅拌得到第二组B液,将A液和B液混合搅拌反应,即可制得混合胶液,取出92%的该混合胶液,加入8%的水高速搅拌合成,制得终产品。
实施例3:屋面防水胶的制备
以重量计,取苯丙乳液20份、磷酸三丁酯2份、乙二醇4份、氯化石蜡30份,搅拌制得第一组A液,再取白乳胶25份、丙烯酸24份搅拌得到第二组B液,将A液和B液混合搅拌反应,即可制得混合胶液。取按重量比60%的该混合胶液,加入40%重量的8%的聚乙烯醇胶水混合均匀待用;又取重量比50%的重质碳酸钙与占重量50%的8%的聚乙烯醇胶水搅拌混合均匀,再将两者搅拌均匀制成终产品。
Claims (2)
1.一种防水胶,其特征是以苯丙乳液、磷酸三丁酯、乙二醇、氯化石蜡、白乳胶和丙烯酸为原料,首先按重量之比将苯丙乳液20~50份、磷酸三丁酯2~5份、乙二醇4~7份和氯化石蜡10~40份混合搅拌反应,形成A液,然后又将白乳胶20~60份和丙烯酸24~54份混合,搅拌反应,形成B液,最后加温搅拌A、B两液,形成终产品。
2.根据权利要求1的一种防水胶的制备方法,其特征是按以下步骤制备:
(1)按重量计,将20~50份的苯丙乳液、2~5份磷酸三丁酯、4~7份乙二醇和10~40份氯化石蜡加入反应釜中,搅拌10分钟,在18~22℃下反应24小时,形成A液;
(2)将20~60份白乳胶和24~54份丙烯酸加入反应釜中,搅拌10分钟,在12~15℃下反应8小时,构成B液;
(3)先将A液加入反应釜中搅拌3~5分钟,再把B液加入反应釜中搅拌10分钟,然后升温至60~80℃,反应4小时,最后生成终产品。