CN103665661B - 一种硬质pvc发泡板及其制备方法 - Google Patents
一种硬质pvc发泡板及其制备方法 Download PDFInfo
- Publication number
- CN103665661B CN103665661B CN201310636801.2A CN201310636801A CN103665661B CN 103665661 B CN103665661 B CN 103665661B CN 201310636801 A CN201310636801 A CN 201310636801A CN 103665661 B CN103665661 B CN 103665661B
- Authority
- CN
- China
- Prior art keywords
- foamed board
- hard pvc
- pvc foamed
- mixing
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种硬质PVC发泡板及其制备方法，硬质PVC发泡板以重量组分计包括：PVC？80-95份，加工助剂ACR？5-10份，碳酸钙5-10份，滑石粉0.5-2份，二氧化钛1-3份，AC发泡剂0.3-1份，苯乙烯2-8份，石蜡2-6份，硬脂酸0.5-1份；制备方法为将各组分于混合搅拌机中混合均匀，然后于双螺杆挤出机中进行挤出，螺杆温度为160-170℃，口模温度为165-180℃，螺杆转速为20-30转/分钟。本发明提供的硬质PVC发泡板伸长率达到了14%以上，拉伸强度达到了19MPa以上，弯曲强度达到了16MPa以上，缺口冲击强度达到了42KJ/M2以上，邵氏硬度D型达到了58以上。
Description
技术领域
本发明属于化工材料领域，具体涉及一种硬质PVC发泡板及其制备方法。
背景技术
PVC发泡板又称为雪弗板和安迪板，其化学成分是聚氯乙烯。广泛应用于客车、火车车厢顶棚、箱体芯层、内部装潢用板、建筑物外墙板、内装饰用板、办公室、住宅、公共场所建筑物隔间，商用装饰架、无尘室用板、吊顶板、网板印刷、电脑刻字、广告标示、展板、标志用板相册板等行业及化工防腐工程、热成型件、冷库用板、特殊保冷工程、环保用板模、运动器材、养殖用材、海滨防潮设施、耐水材料、美工材料及各种轻便隔板代替玻璃天棚等。目前使用的PVC发泡板硬度不够大，在需要承重的领域应用受到限制，因此需要开发一种硬度较大的PVC发泡板来拓展其应用。
发明内容
本发明的目的在于为了克服以上现有技术的不足而提供一种硬质PVC发泡板及其制备方法。
本发明是通过以下技术手段实现的：
一种硬质PVC发泡板，以重量组分计包括：PVC80-95份，加工助剂ACR5-10份，碳酸钙5-10份，滑石粉0.5-2份，二氧化钛1-3份，AC发泡剂0.3-1份，苯乙烯2-8份，石蜡2-6份，硬脂酸0.5-1份。
所述的硬质PVC发泡板，可以优选为以重量组分计包括：PVC86-90份，加工助剂ACR6-8份，碳酸钙5-6份，滑石粉0.6-1份，二氧化钛1-2份，AC发泡剂0.3-0.6份，苯乙烯3-5份，石蜡3-5份，硬脂酸0.7-0.9份。
一种以上所述的硬质PVC发泡板的制备方法，可以按照以下步骤进行制备：
（1）按照重量份称取各组分；
（2）将各组分于混合搅拌机中混合，搅拌速度为50-60转/分钟，110-120℃混合15-20分钟，然后搅拌降温至50-60℃混合10-20分钟；
（3）将步骤（2）混合后的物料于双螺杆挤出机中进行挤出，其中螺杆温度为160-170℃，口模温度为165-180℃，螺杆转速为20-30转/分钟。
具体实施方式：
实施例1
一种硬质PVC发泡板，以重量组分计包括：PVC80份，加工助剂ACR5份，碳酸钙5份，滑石粉0.5份，二氧化钛1份，AC发泡剂0.3份，苯乙烯2份，石蜡2份，硬脂酸0.5份。
以上所述的硬质PVC发泡板按照以下步骤进行制备：
（1）按照重量份称取各组分；
（2）将各组分于混合搅拌机中混合，搅拌速度为50转/分钟，110℃混合15分钟，然后搅拌降温至50℃混合10分钟；
（3）将步骤（2）混合后的物料于双螺杆挤出机中进行挤出，其中螺杆温度为160℃，口模温度为165℃，螺杆转速为20转/分钟。
实施例2
一种硬质PVC发泡板，以重量组分计包括：PVC86份，加工助剂ACR6份，碳酸钙5份，滑石粉0.6份，二氧化钛1份，AC发泡剂0.3份，苯乙烯3份，石蜡3份，硬脂酸0.7份。
以上所述的硬质PVC发泡板按照以下步骤进行制备：
（1）按照重量份称取各组分；
（2）将各组分于混合搅拌机中混合，搅拌速度为52转/分钟，113℃混合16分钟，然后搅拌降温至55℃混合12分钟；
（3）将步骤（2）混合后的物料于双螺杆挤出机中进行挤出，其中螺杆温度为165℃，口模温度为168℃，螺杆转速为25转/分钟。
实施例3
一种硬质PVC发泡板，以重量组分计包括：PVC88份，加工助剂ACR7份，碳酸钙5份，滑石粉0.8份，二氧化钛1.5份，AC发泡剂0.5份，苯乙烯4份，石蜡4份，硬脂酸0.8份。
以上所述的硬质PVC发泡板按照以下步骤进行制备：
（1）按照重量份称取各组分；
（2）将各组分于混合搅拌机中混合，搅拌速度为55转/分钟，118℃混合20分钟，然后搅拌降温至55℃混合16分钟；
（3）将步骤（2）混合后的物料于双螺杆挤出机中进行挤出，其中螺杆温度为165℃，口模温度为172℃，螺杆转速为26转/分钟。
实施例4
一种硬质PVC发泡板，以重量组分计包括：PVC90份，加工助剂ACR8份，碳酸钙6份，滑石粉1份，二氧化钛2份，AC发泡剂0.6份，苯乙烯5份，石蜡5份，硬脂酸0.9份。
以上所述的硬质PVC发泡板按照以下步骤进行制备：
（1）按照重量份称取各组分；
（2）将各组分于混合搅拌机中混合，搅拌速度为60转/分钟，118℃混合20分钟，然后搅拌降温至60℃混合20分钟；
（3）将步骤（2）混合后的物料于双螺杆挤出机中进行挤出，其中螺杆温度为168℃，口模温度为178℃，螺杆转速为30转/分钟。
实施例5
一种硬质PVC发泡板，以重量组分计包括：PVC95份，加工助剂ACR10份，碳酸钙10份，滑石粉2份，二氧化钛3份，AC发泡剂1份，苯乙烯8份，石蜡6份，硬脂酸1份。
以上所述的硬质PVC发泡板按照以下步骤进行制备：
（1）按照重量份称取各组分；
（2）将各组分于混合搅拌机中混合，搅拌速度为60转/分钟，120℃混合20分钟，然后搅拌降温至60℃混合20分钟；
（3）将步骤（2）混合后的物料于双螺杆挤出机中进行挤出，其中螺杆温度为170℃，口模温度为180℃，螺杆转速为30转/分钟。相对密度0.6-0.8，拉伸强度12MPa，伸长率15%，弯曲强度15MPa，邵氏硬度D55，
对以上实施例制备得到的硬质PVC发泡板进行性能测试，结果见下表：
从以上试验结果可以看出，本发明提供的硬质PVC发泡板伸长率达到了14%以上，拉伸强度达到了19MPa以上，弯曲强度达到了16MPa以上，缺口冲击强度达到了42KJ/M2以上，邵氏硬度D型达到了58以上。
Claims (1)
1.一种硬质PVC发泡板，其特征在于，以重量组分计包括：PVC86-90份，加工助剂ACR6-8份，碳酸钙5-6份，滑石粉0.6-1份，二氧化钛1-2份，AC发泡剂0.3-0.6份，苯乙烯3-5份，石蜡3-5份，硬脂酸0.7-0.9份；
所述的硬质PVC发泡板的制备方法，按照以下步骤进行制备：
（1）按照重量份称取各组分；
（2）将各组分于混合搅拌机中混合，搅拌速度为50-60转/分钟，110-120℃混合15-20分钟，然后搅拌降温至50-60℃混合10-20分钟；
（3）将步骤（2）混合后的物料于双螺杆挤出机中进行挤出，其中螺杆温度为160-170℃，口模温度为165-180℃，螺杆转速为20-30转/分钟。