CN103602312A - 刹车片专用耐磨材料 - Google Patents

刹车片专用耐磨材料 Download PDF

Info

Publication number
CN103602312A
CN103602312A CN201310580041.8A CN201310580041A CN103602312A CN 103602312 A CN103602312 A CN 103602312A CN 201310580041 A CN201310580041 A CN 201310580041A CN 103602312 A CN103602312 A CN 103602312A
Authority
CN
China
Prior art keywords
parts
phenolic resin
resistant material
special wear
brake pad
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310580041.8A
Other languages
English (en)
Inventor
王玉庆
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
QINGDAO GUANGLIANDA PRECISION MACHINERY Co Ltd
Original Assignee
QINGDAO GUANGLIANDA PRECISION MACHINERY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by QINGDAO GUANGLIANDA PRECISION MACHINERY Co Ltd filed Critical QINGDAO GUANGLIANDA PRECISION MACHINERY Co Ltd
Priority to CN201310580041.8A priority Critical patent/CN103602312A/zh
Publication of CN103602312A publication Critical patent/CN103602312A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种刹车片专用耐磨材料，由下列重量份的材料组成：一种刹车片专用耐磨材料，其特征在于，由下列重量份的材料组成：腰果壳油改性酚醛树脂10～20份；钛酸钾晶须5～8份；芳纶短纤维2～5份；摩擦粉10～12份；氧化钙5～10份；硅灰石纤维3～6份；摩擦粉5～8份；云母10～12份；碳化硅2～4份。采用了腰果壳油改性酚醛树脂，用其代替普通酚醛树脂作为刹车片材料的有机载体，消除了普通酚醛树脂存在的耐热烧蚀性差、磨耗高、抗冲击强度低等缺点，可以避免普通酚醛树脂对盘式刹车片摩擦材料带来的性能缺陷，以提高盘式刹车片摩擦材料的整体性能。

Description

刹车片专用耐磨材料
技术领域
本发明涉及一种刹车片专用耐磨材料。
背景技术
摩擦材料是一种应用在动力机械上，依靠摩擦作用来执行制动和传动功能的部件材料。它主要包括制动器衬片（刹车片）和离合器面片（离合器片）。刹车片用于制动，离合器片用于传动。任何机械设备与运动的各种车辆都必须要有制动或传动装置。摩擦材料是这种制动或传动装置上的关键性部件。它最主要的功能是通过摩擦来吸收或传递动力，它们使机械设备与各种机动车辆能够安全可靠地工作。所以说摩擦材料是一种应用广泛又甚关键的材料。现有的用于刹车片的摩擦材料种类繁多，最为常用的是树脂基摩擦材料，但这类树脂基体在工作温度较高时易发生严重的热分解，使其摩擦磨损性能严重衰退，降低使用寿命。
发明内容
 针对现有技术存在的不足，本发明所要解决的技术问题是，提供一种提高了摩擦材料的摩擦系数，减少了制动噪音，减轻了高温时摩擦材料的热衰退性的刹车片专用耐磨材料。
为解决上述技术问题，本发明所采取的技术方案是：一种刹车片专用耐磨材料，其特征在于，由下列重量份的材料组成：
腰果壳油改性酚醛树脂          10～20份；
钛酸钾晶须                     5～8份；
芳纶短纤维                     2～5份；
摩擦粉                         10～12份；
氧化钙                         5～10份；
硅灰石纤维                     3～6份；
摩擦粉                         5～8份；
云母                           10～12份；
碳化硅                         2～4份。
上述的刹车片专用耐磨材料，其特征在于，由下列重量份的材料组成：
腰果壳油改性酚醛树脂           15份；
钛酸钾晶须                     7份；
芳纶短纤维                     3份；
摩擦粉                         11份；
氧化钙                         8份；
硅灰石纤维                     5份；
摩擦粉                         7份；
云母                           11份；
碳化硅                         3份。
本发明刹车片用耐磨材料的优点是：采用了腰果壳油改性酚醛树脂，用其代替普通酚醛树脂作为刹车片材料的有机载体，消除了普通酚醛树脂存在的耐热烧蚀性差、磨耗高、抗冲击强度低等缺点，可以避免普通酚醛树脂对盘式刹车片摩擦材料带来的性能缺陷，以提高盘式刹车片摩擦材料的整体性能。
具体实施方式
下面结合具体实施例对本发明做进一步详细说明；
实施例1：
一种刹车片专用耐磨材料，其特征在于，由下列重量份的材料组成：
腰果壳油改性酚醛树脂          10～20份；
钛酸钾晶须                     5～8份；
芳纶短纤维                     2～5份；
摩擦粉                         10～12份；
氧化钙                         5～10份；
硅灰石纤维                     3～6份；
摩擦粉                         5～8份；
云母                           10～12份；
碳化硅                         2～4份。
本发明优选实施例: 一种刹车片专用耐磨材料，其特征在于，由下列重量份的材料组成：
腰果壳油改性酚醛树脂           15份；
钛酸钾晶须                     7份；
芳纶短纤维                     3份；
摩擦粉                         11份；
氧化钙                         8份；
硅灰石纤维                     5份；
摩擦粉                         7份；
云母                           11份；
碳化硅                         3份。
当然，上述说明并非是对本发明的限制，本发明也并不限于上述举例，本技术领域的普通技术人员，在本发明的实质范围内，作出的变化、改型、添加或替换，都应属于本发明的保护范围。

Claims (2)

1.一种刹车片专用耐磨材料，其特征在于，由下列重量份的材料组成：
腰果壳油改性酚醛树脂          10～20份；
钛酸钾晶须                     5～8份；
芳纶短纤维                     2～5份；
摩擦粉                         10～12份；
氧化钙                         5～10份；
硅灰石纤维                     3～6份；
摩擦粉                         5～8份；
云母                           10～12份；
碳化硅                         2～4份。
2.一种刹车片专用耐磨材料，其特征在于，由下列重量份的材料组成：
腰果壳油改性酚醛树脂           15份；
钛酸钾晶须                     7份；
芳纶短纤维                     3份；
摩擦粉                         11份；
氧化钙                         8份；
硅灰石纤维                     5份；
摩擦粉                         7份；
云母                           11份；
碳化硅                         3份。
CN201310580041.8A 2013-11-19 2013-11-19 刹车片专用耐磨材料 Pending CN103602312A (zh)