CN105419728A - 一种刹车片摩擦材料的混合料 - Google Patents
一种刹车片摩擦材料的混合料 Download PDFInfo
- Publication number
- CN105419728A CN105419728A CN201510908149.4A CN201510908149A CN105419728A CN 105419728 A CN105419728 A CN 105419728A CN 201510908149 A CN201510908149 A CN 201510908149A CN 105419728 A CN105419728 A CN 105419728A
- Authority
- CN
- China
- Prior art keywords
- parts
- weight
- fiber
- following component
- friction material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种刹车片摩擦材料的混合料，涉及刹车片技术领域，其特征在于：按重量份包括以下组分，粘结剂5～8份，增加纤维10～15份，摩擦性能调节剂5～10份，填料60～80份，所述的粘结剂按重量份包括以下组分：酚醛树脂30～40份、顺丁橡胶16～26份、邻苯二甲酸二辛酯3～8份、丁酯3～8份和马来酸苷2～3份；所述的增加纤维按重量份包括以下组分：钢纤维18～20份、碳化硅晶须10～16份、芳纶2～3份和钼纤维3～8份。本发明的摩擦系数高、耐磨性好，热稳定性高，使用寿命长。
Description
技术领域
本发明涉及刹车片技术领域，具体涉及一种刹车片摩擦材料的混合料。
背景技术
在整个汽车工业中，制动(刹车)片是一种举足轻重、不可缺少的零部件，如果缺少它，汽车在公路上的行驶安全将无法保障，况且，该产品既是安全件，又是易损件。在正常情况下一辆车每年至少要更换一套刹车片。刹车片主要材料以各种纤维(石棉、复合纤维、陶瓷纤维、钢纤维、铜纤维、芳纶纤维等)为基材，以树脂为粘合剂混入有机和无机粉状填料粘合而成。摩擦块由摩擦材料、粘合剂组成，刹车时被挤压在刹车盘或刹车鼓上产生摩擦，从而达到车辆减速刹车的目的。由于摩擦作用，摩擦块会逐渐被磨损，一般来讲成本越低的刹车片磨损得越快。摩擦材料使用完后要及时更换刹车片，否则钢板与刹车盘就会直接接触，最终会丧失刹车效果并损坏刹车盘。现有的用于摩擦块的摩擦材料比较简单，热稳定性和摩擦系数低，不耐磨使用寿命低。
发明内容
本发明所要解决的技术问题在于提供一种摩擦系数高、耐磨性好，热稳定性高，使用寿命长的刹车片摩擦材料的混合料。
本发明所要解决的技术问题采用以下技术方案来实现：
一种刹车片摩擦材料的混合料，其特征在于：按重量份包括以下组分，
所述的粘结剂按重量份包括以下组分：酚醛树脂30～40份、顺丁橡胶16～26份、邻苯二甲酸二辛酯3～8份、丁酯3～8份和马来酸苷2～3份；改善树脂的高温性能。为了更大的提高粘结剂的高温性能。
所述的增加纤维按重量份包括以下组分：钢纤维18～20份、碳化硅晶须10～16份、芳纶2～3份和钼纤维3～8份；可以降低材料的密度、减小其磨损量，但同时也会降低材料的摩擦系数。为了提高摩擦材料在各温度段的稳定性及其纤维和粘结剂的亲和性能。
所述的摩擦性能调节剂按重量份包括以下组分：石墨8～10份、二硫化硅3～5份和白炭黑1～3份。增加了摩擦材料的摩擦系数，调节材料的热稳定性能以及其工作稳定性。
所述的填料按重量份包括以下组分：滑石粉5～10份、云母粉3～8份、铜粉1～2份和硫酸钡0.5～0.6份。它既能降低摩擦系数又能减少偶材料的磨损，从而提高摩擦材料的使用寿命。加入铜粉，它的作用是可以在摩擦材料和对偶间形成转移膜，既能提高摩擦力矩和稳定摩擦系数，有能减小对对偶件的损伤，提高整个摩擦副的耐摩性能。加入硫酸钡，可以提高材料的密度。
本发明的有益效果是：本发明的摩擦系数高、耐磨性好，热稳定性高，使用寿命长。
具体实施方式
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解，下面结合具体实施例，进一步阐述本发明。
一种刹车片摩擦材料的混合料，按重量份包括以下组分，
粘结剂按重量份包括以下组分：酚醛树脂30～40份、顺丁橡胶16～26份、邻苯二甲酸二辛酯3～8份、丁酯3～8份和马来酸苷2～3份；
增加纤维按重量份包括以下组分：钢纤维18～20份、碳化硅晶须10～16份、芳纶2～3份和钼纤维3～8份。
摩擦性能调节剂按重量份包括以下组分：石墨8～10份、二硫化硅3～5份和白炭黑1～3份。
填料按重量份包括以下组分：滑石粉5～10份、云母粉3～8份、铜粉1～2份和硫酸钡0.5～0.6份。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (3)
1.一种刹车片摩擦材料的混合料，其特征在于：按重量份包括以下组分，
所述的粘结剂按重量份包括以下组分：酚醛树脂30～40份、顺丁橡胶16～26份、邻苯二甲酸二辛酯3～8份、丁酯3～8份和马来酸苷2～3份；
所述的增加纤维按重量份包括以下组分：钢纤维18～20份、碳化硅晶须10～16份、芳纶2～3份和钼纤维3～8份。
2.根据权利要求1所述的一种刹车片摩擦材料的混合料，其特征在于：所述的摩擦性能调节剂按重量份包括以下组分：石墨8～10份、二硫化硅3～5份和白炭黑1～3份。
3.根据权利要求1所述的一种刹车片摩擦材料的混合料，其特征在于：所述的填料按重量份包括以下组分：滑石粉5～10份、云母粉3～8份、铜粉1～2份和硫酸钡0.5～0.6份。