CN103555141A - 一种高耐水耐油性粉末涂料 - Google Patents

一种高耐水耐油性粉末涂料 Download PDF

Info

Publication number
CN103555141A
CN103555141A CN201310516015.9A CN201310516015A CN103555141A CN 103555141 A CN103555141 A CN 103555141A CN 201310516015 A CN201310516015 A CN 201310516015A CN 103555141 A CN103555141 A CN 103555141A
Authority
CN
China
Prior art keywords
parts
powder paint
raw material
powder
add
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310516015.9A
Other languages
English (en)
Inventor
徐曙
万鹏程
徐磊
马千里
吴晓明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI MINGDU ELECTRICAL Co Ltd
Original Assignee
ANHUI MINGDU ELECTRICAL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI MINGDU ELECTRICAL Co Ltd filed Critical ANHUI MINGDU ELECTRICAL Co Ltd
Priority to CN201310516015.9A priority Critical patent/CN103555141A/zh
Publication of CN103555141A publication Critical patent/CN103555141A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种高耐水耐油性粉末涂料，它是由下述重量份的原料组成的：E-12环氧树脂55-60、石英玻璃纤维2-4、丙烯醇3-4、六溴环十二烷1-2、三甘醇二异辛酸酯2-3、三甲基六亚甲基二胺4-10、聚四氟乙烯蜡4-6、点花扩散剂RC4011-3、辛基硫醇锡0TM-17N0.6-1、氟化钙2-3、亚甲基二萘磺酸钠1-2、复合填料5-10；本发明的粉末涂料具有很高的耐水耐油性，耐化学腐蚀性强，涂装固化方便，特别适用于各种塑料、木材、木塑类壳体。

Description

一种高耐水耐油性粉末涂料
技术领域
    本发明主要涉及一种涂料，尤其涉及一种高耐水耐油性粉末涂料。
背景技术
粉末涂料是一种新型的不含溶剂100％固体粉末状涂料。具有不用溶剂、无污染、节省能源和资源、减轻劳动强度和涂膜机械强度高等特点。粉末涂料的种类有两大类：热塑性粉末涂料和热固性粉末涂料。粉末涂料的品种虽然没有像溶剂型涂料那样繁多，但可做为粉末涂料的聚合物树脂也很多。
发明内容
本发明目的就是为了提供一种高耐水耐油性粉末涂料。
本发明是通过以下技术方案实现的：
一种高耐水耐油性粉末涂料，其特征在于它是由下述重量份的原料组成的：
E-12环氧树脂55-60、石英玻璃纤维2-4、丙烯醇3-4、六溴环十二烷1-2、三甘醇二异辛酸酯2-3、三甲基六亚甲基二胺4-10、聚四氟乙烯蜡4-6、点花扩散剂 RC401 1-3、辛基硫醇锡0TM-17N 0.6-1、氟化钙2-3、亚甲基二萘磺酸钠1-2、复合填料5-10；
所述的复合填料是由下述重量份的原料组成的：
红土35-40、矿粉5-7、陶瓷粉4-6、酚A聚碳酸酯2-3、乙撑双硬脂酰胺1-2、木质素磺酸钙0.6-1、抗氧剂1010 0.1-0.2；
将上述木质素磺酸钙加入到10-15倍水中，搅拌混合后加入陶瓷粉、矿粉，在100-120℃下保温搅拌至水干，加入酚A聚碳酸酯，升高温度为180-200℃，200-300转/分搅拌分散4-6分钟，得预混料；将上述红土在700-800℃下煅烧2-3小时后与上述预混料混合，球磨1-2小时，加入剩余各原料，充分球磨，即得所述粘结助剂。
一种高耐水耐油性粉末涂料的制备方法，包括以下步骤：
将上述玻璃纤维、竹炭粉、纳米铝矾土混合，搅拌均匀后加入硅烷偶联剂kh550，600-1000转/分搅拌分散5-7分钟，加入剩余各原料，通过挤出机中熔融挤出，压片，风冷、磨粉，过120-160目筛，即得所述高耐水耐油性粉末涂料。
本发明的优点是：
    本发明的粉末涂料具有很高的耐水耐油性，耐化学腐蚀性强，涂装固化方便，特别适用于各种塑料、木材、木塑类壳体。
具体实施方式
实施例1，
一种高耐水耐油性粉末涂料，它是由下述重量份（公斤）的原料组成的：
E-12环氧树脂60、石英玻璃纤维2、丙烯醇3-4、六溴环十二烷2、三甘醇二异辛酸酯3、三甲基六亚甲基二胺10、聚四氟乙烯蜡6、点花扩散剂 RC401 1、辛基硫醇锡0TM-17N 1、氟化钙3、亚甲基二萘磺酸钠2、复合填料5；
所述的复合填料是由下述重量份的原料组成的：
红土40、矿粉5、陶瓷粉6、酚A聚碳酸酯3、乙撑双硬脂酰胺2、木质素磺酸钙0.6、抗氧剂1010 0.2；
将上述木质素磺酸钙加入到15倍水中，搅拌混合后加入陶瓷粉、矿粉，在120℃下保温搅拌至水干，加入酚A聚碳酸酯，升高温度为200℃，300转/分搅拌分散4分钟，得预混料；将上述红土在700℃下煅烧2小时后与上述预混料混合，球磨2小时，加入剩余各原料，充分球磨，即得所述粘结助剂。
一种高耐水耐油性粉末涂料的制备方法，包括以下步骤：
将上述玻璃纤维、竹炭粉、纳米铝矾土混合，搅拌均匀后加入硅烷偶联剂kh550，1000转/分搅拌分散5分钟，加入剩余各原料，通过挤出机中熔融挤出，压片，风冷、磨粉，过160目筛，即得所述高耐水耐油性粉末涂料。
性能测试：
铅笔硬度测试：2H 无划伤；
弯曲硬度测试：0T 弯通过；
耐盐雾测试：1000 小时腐蚀力不大于1 级。

Claims (2)

1.一种高耐水耐油性粉末涂料，其特征在于它是由下述重量份的原料组成的：
E-12环氧树脂55-60、石英玻璃纤维2-4、丙烯醇3-4、六溴环十二烷1-2、三甘醇二异辛酸酯2-3、三甲基六亚甲基二胺4-10、聚四氟乙烯蜡4-6、点花扩散剂 RC401 1-3、辛基硫醇锡0TM-17N 0.6-1、氟化钙2-3、亚甲基二萘磺酸钠1-2、复合填料5-10；
所述的复合填料是由下述重量份的原料组成的：
红土35-40、矿粉5-7、陶瓷粉4-6、酚A聚碳酸酯2-3、乙撑双硬脂酰胺1-2、木质素磺酸钙0.6-1、抗氧剂1010 0.1-0.2；
将上述木质素磺酸钙加入到10-15倍水中，搅拌混合后加入陶瓷粉、矿粉，在100-120℃下保温搅拌至水干，加入酚A聚碳酸酯，升高温度为180-200℃，200-300转/分搅拌分散4-6分钟，得预混料；将上述红土在700-800℃下煅烧2-3小时后与上述预混料混合，球磨1-2小时，加入剩余各原料，充分球磨，即得所述粘结助剂。
2.一种如权利要求1所述的高耐水耐油性粉末涂料的制备方法，其特征在于包括以下步骤：
将上述玻璃纤维、竹炭粉、纳米铝矾土混合，搅拌均匀后加入硅烷偶联剂kh550，600-1000转/分搅拌分散5-7分钟，加入剩余各原料，通过挤出机中熔融挤出，压片，风冷、磨粉，过120-160目筛，即得所述高耐水耐油性粉末涂料。
CN201310516015.9A 2013-10-28 2013-10-28 一种高耐水耐油性粉末涂料 Pending CN103555141A (zh)