CN103540052A - 一种防紫外线电线电缆料及其制备方法 - Google Patents

一种防紫外线电线电缆料及其制备方法 Download PDF

Info

Publication number
CN103540052A
CN103540052A CN201310426217.4A CN201310426217A CN103540052A CN 103540052 A CN103540052 A CN 103540052A CN 201310426217 A CN201310426217 A CN 201310426217A CN 103540052 A CN103540052 A CN 103540052A
Authority
CN
China
Prior art keywords
ultraviolet
powder
cable material
compounded mix
preparation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310426217.4A
Other languages
English (en)
Inventor
许义彬
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JING FENG GROUP
Original Assignee
JING FENG GROUP
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JING FENG GROUP filed Critical JING FENG GROUP
Priority to CN201310426217.4A priority Critical patent/CN103540052A/zh
Publication of CN103540052A publication Critical patent/CN103540052A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种防紫外线电线电缆料及其制备方法，其由下列重量份的原料制成：SG-2型PVC80-90、聚对苯二甲酸二乙酯20-30、双酚A聚碳酸酯10-15、4,4'二苯基甲烷二异氰酸酯1-2、玉石粉5-8、磷酸二苯异辛酯3-6、三盐基硫酸铅0.5-1.5、聚乙烯蜡2-3、加工助剂ACR-4011.5-2.5、紫外线吸收剂UV-5311-1.5、紫外线吸收剂UV-90.5-1、滑石粉10-15、聚磷酸铵4-8、纳米海泡石5-10、硫酸镁晶须10-15、复合填料4-6。本发明电缆料不仅具有优异的防紫外线性能，提高电缆料的耐光照老化性，还具有良好的物理机械性能，柔软抗撕裂，高耐磨，耐高低温，耐酸碱。

Description

一种防紫外线电线电缆料及其制备方法
技术领域
本发明涉及一种电缆料及其制备方法，具体涉及一种防紫外线电线电缆料及其制备方法。
背景技术
随着电线电缆市场需求的不断扩大以及我国对PVC科研开发的不断深入，极大地存进了PVC在电缆料的推广应用，用量居于有机材料之手。但是，现有的PVC电缆料还存在着抗紫外线差一大缺点，紫外线是危害塑料PVC电缆的大主要危害之一，每年造成许多事故发生，在经济上造成巨大损失，因此开展研究防紫外线剂PVC电缆料十分重要。
发明内容
本发明的目的在于针对现有技术中存在的不足，提供一种防紫外线电线电缆料及其制备方法。该电缆料物理机械性能好、耐紫外线光照老化性能优异、使用寿命长。
为了实现上述发明目的，本发明采用的技术方案为：
一种防紫外线电线电缆料，由下列重量份的原料制成：SG-2型PVC80-90、聚对苯二甲酸二乙酯20-30、双酚A聚碳酸酯10-15、4,4'二苯基甲烷二异氰酸酯1-2、玉石粉5-8、磷酸二苯异辛酯3-6、三盐基硫酸铅0.5-1.5、聚乙烯蜡2-3、加工助剂ACR-4011.5-2.5、紫外线吸收剂UV-5311-1.5、紫外线吸收剂UV-90.5-1、滑石粉10-15、聚磷酸铵4-8、纳米海泡石5-10、硫酸镁晶须10-15、复合填料4-6；
所述复合填料的制备方法如下：a.取下列重量份的原料：铝矾土10-15、重晶石8-12、纳米氮化钛5-10、乙烯基三乙氧基硅烷1-2、纳米锌粉2-3、赤泥4-6、硬脂酸2-3、抗氧剂10351-2；b、将高岭土、天青石在500-550℃下煅烧3-5h，冷却至室温后，与纳米氮化钛、赤泥一并加入适量水中研磨，70-80℃水浴加热1-2h，然后加浓度为10-15%盐酸溶液调PH为4.0-5.5，研磨浆料至400-500目筛后，再加浓度为8-12%氢氧化钠溶液调为中性，过滤水洗，喷雾干燥，得粉末；c、将上述所得粉末与其它剩余成分混合，研磨混合均匀即得。
防紫外线电线电缆料的制备方法，包括以下步骤：
（1）将聚对苯二甲酸二乙酯、双酚A聚碳酸酯、4,4'二苯基甲烷二异氰酸酯、玉石粉、磷酸二苯异辛酯、紫外线吸收剂UV-9、复合填料投入高速混合机中，1500-2000rpm高速搅拌3-6min，然后将混合料加入180-240℃的双螺杆挤出机塑化造粒制得复合填料母粒；
（2）将挤塑机升温至140-170℃，加入SG-2型PVC、复合填料、三盐基硫酸铅、聚磷酸铵、加工助剂ACR-401，混炼3-4min，再加入聚乙烯蜡、滑石粉、纳米海泡石，混炼2-3min，最后加入硫酸镁晶须、紫外线吸收剂UV-531，混炼1-2min，然后挤出造粒，经振动筛过筛后，最后冷却包装即可。
本发明的有益效果：
本发明电缆料不仅具有优异的防紫外线性能，提高电缆料的耐光照老化性，还具有良好的物理机械性能，柔软抗撕裂，高耐磨，耐高低温，耐酸碱。经检测，其各项性能均超过国家标准，完全符合企业的使用要求，具有巨大的经济前景和社会效益。
具体实施方式
一种防紫外线电线电缆料，由下列重量(kg)的原料制成：SG-2型PVC80、聚对苯二甲酸二乙酯25、双酚A聚碳酸酯12、4,4'二苯基甲烷二异氰酸酯1.5、玉石粉6、磷酸二苯异辛酯4、三盐基硫酸铅1、聚乙烯蜡2、加工助剂ACR-4012、紫外线吸收剂UV-5311.5、紫外线吸收剂UV-90.8、滑石粉12、聚磷酸铵6、纳米海泡石8、硫酸镁晶须12、复合填料5；
所述复合填料的制备方法如下：a.取下列重量份的原料：铝矾土15、重晶石10、纳米氮化钛6、乙烯基三乙氧基硅烷1.5、纳米锌粉2、赤泥5、硬脂酸2、抗氧剂10351.5；b、将高岭土、天青石在530℃下煅烧4h，冷却至室温后，与纳米氮化钛、赤泥一并加入适量水中研磨，80℃水浴加热1h，然后加浓度为10%盐酸溶液调PH为5.5，研磨浆料至500目筛后，再加浓度为10%氢氧化钠溶液调为中性，过滤水洗，喷雾干燥，得粉末；c、将上述所得粉末与其它剩余成分混合，研磨混合均匀即得。
防紫外线电线电缆料的制备方法，包括以下步骤：
（1）将聚对苯二甲酸二乙酯、双酚A聚碳酸酯、4,4'二苯基甲烷二异氰酸酯、玉石粉、磷酸二苯异辛酯、紫外线吸收剂UV-9、复合填料投入高速混合机中，2000rpm高速搅拌4min，然后将混合料加入180-240℃的双螺杆挤出机塑化造粒制得复合填料母粒；
（2）将挤塑机升温至140-170℃，加入SG-2型PVC、复合填料、三盐基硫酸铅、聚磷酸铵、加工助剂ACR-401，混炼3min，再加入聚乙烯蜡、滑石粉、纳米海泡石，混炼2min，最后加入硫酸镁晶须、紫外线吸收剂UV-531，混炼1min，然后挤出造粒，经振动筛过筛后，最后冷却包装即可。
制得的电缆料的性能测试结果如下：
Figure BDA0000383607490000031

Claims (2)

1.一种防紫外线电线电缆料，其特征在于，由下列重量份的原料制成：SG-2型PVC 80-90、聚对苯二甲酸二乙酯20-30、双酚A聚碳酸酯10-15、4,4'二苯基甲烷二异氰酸酯1-2、玉石粉5-8、磷酸二苯异辛酯 3-6、三盐基硫酸铅0.5-1.5、聚乙烯蜡2-3、加工助剂ACR-401 1.5-2.5、紫外线吸收剂UV-531 1-1.5、紫外线吸收剂UV-9 0.5-1、滑石粉 10-15、聚磷酸铵 4-8、纳米海泡石5-10、硫酸镁晶须10-15、复合填料4-6；
所述复合填料的制备方法如下：a.取下列重量份的原料：铝矾土10-15、重晶石8-12、纳米氮化钛5-10、乙烯基三乙氧基硅烷1-2、纳米锌粉2-3、赤泥4-6、硬脂酸2-3、抗氧剂1035 1-2；b、将高岭土、天青石在500-550℃下煅烧3-5h，冷却至室温后，与纳米氮化钛、赤泥一并加入适量水中研磨，70-80℃水浴加热1-2h，然后加浓度为10-15%盐酸溶液调PH为4.0-5.5，研磨浆料至400-500目筛后，再加浓度为8-12%氢氧化钠溶液调为中性，过滤水洗，喷雾干燥，得粉末；c、将上述所得粉末与其它剩余成分混合，研磨混合均匀即得。
2.如权利要求1所述的防紫外线电线电缆料的制备方法，其特征在于包括以下步骤：
将聚对苯二甲酸二乙酯、双酚A聚碳酸酯、4,4'二苯基甲烷二异氰酸酯、玉石粉、磷酸二苯异辛酯、紫外线吸收剂UV-9、复合填料投入高速混合机中，1500-2000rpm高速搅拌3-6min，然后将混合料加入180-240℃的双螺杆挤出机塑化造粒制得复合填料母粒；
将挤塑机升温至140-170℃，加入SG-2型PVC、复合填料、三盐基硫酸铅、聚磷酸铵、加工助剂ACR-401，混炼3-4min，再加入聚乙烯蜡、滑石粉、纳米海泡石，混炼2-3min，最后加入硫酸镁晶须、紫外线吸收剂UV-531，混炼1-2min，然后挤出造粒，经振动筛过筛后，最后冷却包装即可。
CN201310426217.4A 2013-09-17 2013-09-17 一种防紫外线电线电缆料及其制备方法 Pending CN103540052A (zh)