CN105419154A - 一种耐热改性塑料 - Google Patents

一种耐热改性塑料 Download PDF

Info

Publication number
CN105419154A
CN105419154A CN201510852589.2A CN201510852589A CN105419154A CN 105419154 A CN105419154 A CN 105419154A CN 201510852589 A CN201510852589 A CN 201510852589A CN 105419154 A CN105419154 A CN 105419154A
Authority
CN
China
Prior art keywords
parts
plastic
heatproof
modification
plastic according
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510852589.2A
Other languages
English (en)
Inventor
闫海玲
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Bengbu Haiming Die Casting Machine Co Ltd
Original Assignee
Bengbu Haiming Die Casting Machine Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Bengbu Haiming Die Casting Machine Co Ltd filed Critical Bengbu Haiming Die Casting Machine Co Ltd
Priority to CN201510852589.2A priority Critical patent/CN105419154A/zh
Publication of CN105419154A publication Critical patent/CN105419154A/zh
Pending legal-status Critical Current

Abstract

发明公开了一种耐热改性塑料，由以下成分制成：聚氯乙烯、聚丙烯、高铝矾土、铝粉、柠檬酸钠、红柱石、分散剂、热稳定剂、增塑剂。本发明改性塑料良好的力学性能，其抗拉强度好，抗冲击性能好；通过在塑料中添加经过改性后的高铝矾土，主要提升塑料耐热抗老化性能；本发明通过采用经过改性液处理的红柱石，能够提高塑料的可模压性，并且提高了塑料的耐候性和化学稳定性；本发明生产工艺简单，成本低，制作的塑料具有优异的热稳定性。

Description

一种耐热改性塑料
技术领域
本发明涉及塑料制作领域，特别是涉及一种耐热改性塑料。
背景技术
市场上一般聚氯乙烯塑料，支化度较小，相对密度1.4左右，玻璃化温度77~90℃，170℃左右开始分解，对光和热的稳定性差，在100℃以上或经长时间阳光曝晒，就会分解而产生氯化氢，并进一步自动催化分解，引起变色，物理机械性能也迅速下降，脆性较大以及抗冲击性能较差等，这些不足使得其应用受到了限制。
发明内容
本发明的目的是提供一种耐热改性塑料，通过以下技术方案实现：
一种耐热改性塑料，按重量份计由以下成分制成：聚氯乙烯40份、聚丙烯20份、高铝矾土8份、铝粉5份、柠檬酸钠6份、红柱石8份、分散剂3份、热稳定剂2份、增塑剂2份。
进一步地，所述铝粉采用60-65℃的水浴加热处理1-1.5小时后，干燥。
进一步地，所述分散剂为六偏磷酸钠。
进一步地，所述热稳定剂为硬脂酸钙。
进一步地，所述增塑剂为柠檬酸酯。
进一步地，高铝矾土经过预处理：将高铝矾土与重量份为5份的煤矸石和重量份为0.5份的氧化铝粉末混合到一起，先进行混合研磨，再放入到1700℃温度下煅烧1小时。
进一步地，所述红柱石经过改性液的处理：将红柱石浸泡到改性液中，加热至70-80℃，并以300r/min转速搅拌1.5小时后，过滤，干燥，研磨成粉末；所述改性液按重量百分比计由以下成分制成：二氧化硅纳米颗粒2%、氧化铝纳米颗粒3%、钛白粉粒子4.5%、聚丙烯酸钠10%其余为水。
本发明的有益效果是：本发明针对现有技术存在的上述不足，本发明改性塑料良好的力学性能，其抗拉强度好，抗冲击性能好；通过在塑料中添加经过改性后的高铝矾土，主要提升塑料耐热抗老化性能；本发明通过采用经过改性液处理的红柱石，能够提高塑料的可模压性，并且提高了塑料的耐候性和化学稳定性；本发明生产工艺简单，成本低，制作的塑料具有优异的热稳定性。
具体实施方式
一种耐热改性塑料，按重量份计由以下成分制成：聚氯乙烯40份、聚丙烯20份、高铝矾土8份、铝粉5份、柠檬酸钠6份、红柱石8份、分散剂3份、热稳定剂2份、增塑剂2份。
进一步地，所述铝粉采用60-65℃的水浴加热处理1-1.5小时后，干燥。
进一步地，所述分散剂为六偏磷酸钠。
进一步地，所述热稳定剂为硬脂酸钙。
进一步地，所述增塑剂为柠檬酸酯。
进一步地，高铝矾土经过预处理：将高铝矾土与重量份为5份的煤矸石和重量份为0.5份的氧化铝粉末混合到一起，先进行混合研磨，再放入到1700℃温度下煅烧1小时。
进一步地，所述红柱石经过改性液的处理：将红柱石浸泡到改性液中，加热至70-80℃，并以300r/min转速搅拌1.5小时后，过滤，干燥，研磨成粉末；所述改性液按重量百分比计由以下成分制成：二氧化硅纳米颗粒2%、氧化铝纳米颗粒3%、钛白粉粒子4.5%、聚丙烯酸钠10%其余为水。
一种耐热改性塑料的制作方法，包括：
1）按重量份分别称取，聚氯乙烯40份、聚丙烯20份、高铝矾土8份、铝粉5份、柠檬酸钠6份、红柱石8份、分散剂3份、热稳定剂2份、增塑剂2份。
2）将聚氯乙烯、聚丙烯加热至熔融状态，与高铝矾土、铝粉、柠檬酸钠、红柱石混合，均匀搅拌30分钟后，再混合分散剂、热稳定剂和增塑剂，添加到挤出机中，挤压塑化而成均匀的塑料颗粒，挤出处理的工艺条件为：一区温度210-220℃，二区温度220-240℃，三区温度240-260℃，四区温度260-270℃，停留时间为2分钟。
本发明塑料的参数性能：
密度g/cm3 断裂伸长率% 介电强度MV/m 低温冲击脆化温度℃
本发明塑料 1.38 289.4 20.4 ≤-20
表1
本发明改性塑料性能测试：
表2
由表2可以看出，本发明塑料在性能上比一般聚氯乙烯塑料要优越很多。

Claims (7)

1.一种耐热改性塑料，其特征在于，按重量份计由以下成分制成：聚氯乙烯40份、聚丙烯20份、高铝矾土8份、铝粉5份、柠檬酸钠6份、红柱石8份、分散剂3份、热稳定剂2份、增塑剂2份。
2.根据权利要求1所述的一种耐热改性塑料，其特征在于，所述铝粉采用60-65℃的水浴加热处理1-1.5小时后，干燥。
3.根据权利要求1所述的一种耐热改性塑料，其特征在于，所述分散剂为六偏磷酸钠。
4.根据权利要求1所述的一种耐热改性塑料，其特征在于，所述热稳定剂为硬脂酸钙。
5.根据权利要求1所述的一种耐热改性塑料，其特征在于，所述增塑剂为柠檬酸酯。
6.根据权利要求1所述的一种耐热改性塑料，其特征在于，高铝矾土经过预处理：将高铝矾土与重量份为5份的煤矸石和重量份为0.5份的氧化铝粉末混合到一起，先进行混合研磨，再放入到1700℃温度下煅烧1小时。
7.根据权利要求1所述的一种耐热改性塑料，其特征在于，所述红柱石经过改性液的处理：将红柱石浸泡到改性液中，加热至70-80℃，并以300r/min转速搅拌1.5小时后，过滤，干燥，研磨成粉末；所述改性液按重量百分比计由以下成分制成：二氧化硅纳米颗粒2%、氧化铝纳米颗粒3%、钛白粉粒子4.5%、聚丙烯酸钠10%其余为水。
CN201510852589.2A 2015-11-27 2015-11-27 一种耐热改性塑料 Pending CN105419154A (zh)