CN105111632A - 一种新型改性聚氯乙烯塑料 - Google Patents

一种新型改性聚氯乙烯塑料 Download PDF

Info

Publication number
CN105111632A
CN105111632A CN201510615361.1A CN201510615361A CN105111632A CN 105111632 A CN105111632 A CN 105111632A CN 201510615361 A CN201510615361 A CN 201510615361A CN 105111632 A CN105111632 A CN 105111632A
Authority
CN
China
Prior art keywords
parts
polyvinyl chloride
modified
igelite
plastics
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510615361.1A
Other languages
English (en)
Inventor
申自俭
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jieshou Ruiqi Plastic Co Ltd
Original Assignee
Jieshou Ruiqi Plastic Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jieshou Ruiqi Plastic Co Ltd filed Critical Jieshou Ruiqi Plastic Co Ltd
Priority to CN201510615361.1A priority Critical patent/CN105111632A/zh
Publication of CN105111632A publication Critical patent/CN105111632A/zh
Pending legal-status Critical Current

Abstract

发明公开了一种新型改性聚氯乙烯塑料，由以下成分制成：聚氯乙烯、丙烯酸树脂、改性玻璃纤维、铝粉、松脂岩、硅藻土、碳酸钙、分散剂、热稳定剂、增塑剂。本发明针对现有技术存在的上述不足，(1)本发明通过在塑料中添加经过改性后的松脂岩与硅藻土，主要提升塑料的抗冲击强度与耐热老化性能；(2)配合采用改性处理后的玻璃纤维，配合使用改性的碳酸钙，能够提升聚氯乙烯塑料的抗拉强度，增强其减摩耐磨性能，还能提高其耐候性能；(3)本发明通过采用高温处理的铝粉，进一步提升塑料的耐热性；（4）本发明生产工艺简单，成本低，制作的塑料具有优异的热稳定性。

Description

一种新型改性聚氯乙烯塑料
技术领域
本发明涉及塑料制作领域，特别是涉及一种新型改性聚氯乙烯塑料。
背景技术
市场上一般聚氯乙烯塑料，支化度较小，相对密度1.4左右，玻璃化温度77~90℃，170℃左右开始分解，对光和热的稳定性差，在100℃以上或经长时间阳光曝晒，就会分解而产生氯化氢，并进一步自动催化分解，引起变色，物理机械性能也迅速下降，脆性较大以及抗冲击性能较差等，这些不足使得其应用受到了限制。
发明内容
本发明的目的是提供一种新型改性聚氯乙烯塑料，通过以下技术方案实现：
一种新型改性聚氯乙烯塑料，按重量份计由以下成分制成：聚氯乙烯40份、丙烯酸树脂30份、改性玻璃纤维6份、铝粉8份、松脂岩6份、硅藻土5份、碳酸钙3份、分散剂3份、热稳定剂2份、增塑剂2份。
进一步地，所述铝粉经过200℃有氧煅烧。
进一步地，所述分散剂为六偏磷酸钠。
进一步地，所述热稳定剂为二盐基亚磷酸铅。
进一步地，所述增塑剂为柠檬酸酯。
进一步地，所述松脂岩经过改性处理：将铝酸三异丙酯溶于液体石蜡中，配制成3-5%浓度的铝酸三异丙酯，再加入烘干的松脂岩，研磨1-1.5小时后，在100℃下恒温30分钟，冷却至室温，过滤，干燥。
进一步地，所述硅藻土经过改性处理：将硅藻土采用5%浓度的盐酸浸泡30分钟后，过滤，再采用5%氢氧化钠溶液浸泡，并加热至沸腾，持续10分钟后，自然冷却至室温，过滤，干燥，粉碎至50-100目。
进一步地，所述改性玻璃纤维的制作方法为，将玻璃纤维在65-70℃下浸泡在0.5-1%浓度的硅烷偶联剂2-3小时后，添加羧甲基纤维素钠，加热至85-90℃，持续1-1.5小时，过滤，干燥。
进一步地，所述碳酸钙采用1-2%浓度甲基丙烯酸溶液浸泡1小时后，过滤，用去离子水清洗，然后再用1-2%聚丁基丙烯酸溶液浸泡，加热至85-90℃，保持1-2小时后，冷却至室温，过滤，用去离子水清洗，干燥，粉碎至50-100目粉末。
本发明的有益效果是：本发明针对现有技术存在的上述不足，(1)本发明通过在塑料中添加经过改性后的松脂岩与硅藻土，主要提升塑料的抗冲击强度与耐热老化性能；(2)配合采用改性处理后的玻璃纤维，配合使用改性过的碳酸钙，能够提升聚氯乙烯塑料的抗拉强度，增强其减摩耐磨性能，还能提高其耐候性能；(3)本发明通过采用高温处理的铝粉，进一步提升塑料的耐热性；（4）本发明生产工艺简单，成本低，制作的塑料具有优异的热稳定性。
具体实施方式
一种新型改性聚氯乙烯塑料，按重量份计由以下成分制成：聚氯乙烯40份、丙烯酸树脂30份、改性玻璃纤维6份、铝粉8份、松脂岩6份、硅藻土5份、碳酸钙3份、分散剂3份、热稳定剂2份、增塑剂2份。
进一步地，所述铝粉经过200℃有氧煅烧。
进一步地，所述分散剂为六偏磷酸钠。
进一步地，所述热稳定剂为二盐基亚磷酸铅。
进一步地，所述增塑剂为柠檬酸酯。
进一步地，所述松脂岩经过改性处理：将铝酸三异丙酯溶于液体石蜡中，配制成3-5%浓度的铝酸三异丙酯，再加入烘干的松脂岩，研磨1-1.5小时后，在100℃下恒温30分钟，冷却至室温，过滤，干燥。
进一步地，所述硅藻土经过改性处理：将硅藻土采用5%浓度的盐酸浸泡30分钟后，过滤，再采用5%氢氧化钠溶液浸泡，并加热至沸腾，持续10分钟后，自然冷却至室温，过滤，干燥，粉碎至50-100目。
进一步地，所述改性玻璃纤维的制作方法为，将玻璃纤维在65-70℃下浸泡在0.5-1%浓度的硅烷偶联剂2-3小时后，添加羧甲基纤维素钠，加热至85-90℃，持续1-1.5小时，过滤，干燥。
进一步地，所述碳酸钙采用1-2%浓度甲基丙烯酸溶液浸泡1小时后，过滤，用去离子水清洗，然后再用1-2%聚丁基丙烯酸溶液浸泡，加热至85-90℃，保持1-2小时后，冷却至室温，过滤，用去离子水清洗，干燥，粉碎至50-100目粉末。
一种新型改性聚氯乙烯塑料的制作方法，包括：
1）按重量份分别称取，聚氯乙烯40份、丙烯酸树脂30份、改性玻璃纤维6份、铝粉8份、松脂岩6份、硅藻土5份、碳酸钙3份、分散剂3份、热稳定剂2份、增塑剂2份。
进一步地，所述铝粉经过200℃有氧煅烧。
2）将聚氯乙烯与丙烯酸树脂加热至熔融状态，与铝粉、松脂岩、硅藻土、改性玻璃纤维、碳酸钙混合，均匀搅拌30分钟后，再混合分散剂、热稳定剂和增塑剂，添加到挤出机中，挤压塑化而成均匀的塑料，挤出处理的工艺条件为：一区温度210-220℃，二区温220-240℃，三区温240-260℃，四区温度260-270℃，停留时间为2分钟。
本发明塑料的参数性能:
密度g/cm3 断裂伸长率% 介电强度MV/m 低温冲击脆化温度℃
本发明塑料 1.53 301.9 23.6 ≤-24
表1
本发明改性聚氯乙烯塑料性能测试：
表2
由表2可以看出，本发明塑料在性能上比一般聚氯乙烯塑料要优越很多。

Claims (9)

1.一种新型改性聚氯乙烯塑料，其特征在于，按重量份计由以下成分制成：聚氯乙烯40份、丙烯酸树脂30份、改性玻璃纤维6份、铝粉8份、松脂岩6份、硅藻土5份、碳酸钙3份、分散剂3份、热稳定剂2份、增塑剂2份。
2.根据权利要求1所述的一种新型改性聚氯乙烯塑料，其特征在于，所述铝粉经过200℃有氧煅烧。
3.根据权利要求1所述的一种新型改性聚氯乙烯塑料，其特征在于，所述分散剂为六偏磷酸钠。
4.根据权利要求1所述的一种新型改性聚氯乙烯塑料，其特征在于，所述热稳定剂为二盐基亚磷酸铅。
5.根据权利要求1所述的一种新型改性聚氯乙烯塑料，其特征在于，所述增塑剂为柠檬酸酯。
6.根据权利要求1所述的一种新型改性聚氯乙烯塑料，其特征在于，所述松脂岩经过改性处理：将铝酸三异丙酯溶于液体石蜡中，配制成3-5%浓度的铝酸三异丙酯，再加入烘干的松脂岩，研磨1-1.5小时后，在100℃下恒温30分钟，冷却至室温，过滤，干燥。
7.根据权利要求1所述的一种新型改性聚氯乙烯塑料，其特征在于，所述硅藻土经过改性处理：将硅藻土采用5%浓度的盐酸浸泡30分钟后，过滤，再采用5%氢氧化钠溶液浸泡，并加热至沸腾，持续10分钟后，自然冷却至室温，过滤，干燥，粉碎至50-100目。
8.根据权利要求1所述的一种新型改性聚氯乙烯塑料，特在在于，所述改性玻璃纤维的制作方法为，将玻璃纤维在65-70℃下浸泡在0.5-1%浓度的硅烷偶联剂2-3小时后，添加羧甲基纤维素钠，加热至85-90℃，持续1-1.5小时，过滤，干燥。
9.根据权利要求1所述的一种新型改性塑料，其特征在于，所述碳酸钙采用1-2%浓度甲基丙烯酸溶液浸泡1小时后，过滤，用去离子水清洗，然后再用1-2%聚丁基丙烯酸溶液浸泡，加热至85-90℃，保持1-2小时后，冷却至室温，过滤，用去离子水清洗，干燥，粉碎至50-100目粉末。
CN201510615361.1A 2015-09-24 2015-09-24 一种新型改性聚氯乙烯塑料 Pending CN105111632A (zh)