CN105419157A - 一种高性能改性塑料 - Google Patents
一种高性能改性塑料 Download PDFInfo
- Publication number
- CN105419157A CN105419157A CN201510873782.4A CN201510873782A CN105419157A CN 105419157 A CN105419157 A CN 105419157A CN 201510873782 A CN201510873782 A CN 201510873782A CN 105419157 A CN105419157 A CN 105419157A
- Authority
- CN
- China
- Prior art keywords
- parts
- performance modified
- modified plastics
- plastic
- alumine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
发明公开了一种高性能改性塑料，由以下成分制成：聚氯乙烯、聚丙烯、高铝矾土、铝粉、六铝酸钙、硅藻土、分散剂、热稳定剂、增塑剂。本发明改性塑料良好的力学性能，其抗拉强度好，抗冲击性能好，特别是缺口抗冲击好；通过在塑料中添加经过改性后的高铝矾土，主要提升塑料耐热抗老化性能；本发明通过采用经过处理的六铝酸钙，进一步提升塑料的耐候性，提高塑料在不同环境下的适应能力；本发明生产工艺简单，成本低，制作的塑料具有优异的热稳定性。
Description
技术领域
本发明涉及塑料制作领域，特别是涉及一种高性能改性塑料。
背景技术
市场上一般聚氯乙烯塑料，支化度较小，相对密度1.4左右，玻璃化温度77~90℃，170℃左右开始分解，对光和热的稳定性差，在100℃以上或经长时间阳光曝晒，就会分解而产生氯化氢，并进一步自动催化分解，引起变色，物理机械性能也迅速下降，脆性较大以及抗冲击性能较差等，这些不足使得其应用受到了限制。
发明内容
本发明的目的是提供一种高性能改性塑料，通过以下技术方案实现：
一种高性能改性塑料，按重量份计由以下成分制成：聚氯乙烯45份、聚丙烯25份、高铝矾土10份、铝粉8份、六铝酸钙6份、硅藻土5份、分散剂3份、热稳定剂2份、增塑剂2份。
进一步地，所述铝粉采用60-65℃的水浴加热处理1-1.5小时后，干燥。
进一步地，所述分散剂为六偏磷酸钠。
进一步地，所述热稳定剂为硬脂酸钙。
进一步地，所述增塑剂为柠檬酸酯。
进一步地，所述六铝酸钙与浓度为8.5%的纳米硫酸钡溶液共混加热处理2小时；所述纳米硫酸钡溶液中纳米硫酸钡的粒度为50-60nm。
进一步地，高铝矾土经过预处理：将高铝矾土与重量份为5份的煤矸石和重量份为0.5份的氧化铝粉末混合到一起，先进行混合研磨，再放入到1700℃温度下煅烧1小时。
进一步地，所述硅藻土经过改性处理：将硅藻土采用8.5%浓度的盐酸浸泡30分钟后，过滤，过滤，干燥，在300℃下煅烧40分钟后粉碎至80-100目。
本发明的有益效果是：本发明针对现有技术存在的上述不足，本发明改性塑料良好的力学性能，其抗拉强度好，抗冲击性能好，特别是缺口抗冲击好；通过在塑料中添加经过改性后的高铝矾土，主要提升塑料耐热抗老化性能；本发明通过采用经过处理的六铝酸钙，进一步提升塑料的耐候性，提高塑料在不同环境下的适应能力；本发明生产工艺简单，成本低，制作的塑料具有优异的热稳定性。
具体实施方式
一种高性能改性塑料，按重量份计由以下成分制成：聚氯乙烯45份、聚丙烯25份、高铝矾土10份、铝粉8份、六铝酸钙6份、硅藻土5份、分散剂3份、热稳定剂2份、增塑剂2份。
进一步地，所述铝粉采用60-65℃的水浴加热处理1-1.5小时后，干燥。
进一步地，所述分散剂为六偏磷酸钠。
进一步地，所述热稳定剂为硬脂酸钙。
进一步地，所述增塑剂为柠檬酸酯。
进一步地，所述六铝酸钙与浓度为8.5%的纳米硫酸钡溶液共混加热处理2小时；所述纳米硫酸钡溶液中纳米硫酸钡的粒度为50-60nm。
进一步地，高铝矾土经过预处理：将高铝矾土与重量份为5份的煤矸石和重量份为0.5份的氧化铝粉末混合到一起，先进行混合研磨，再放入到1700℃温度下煅烧1小时。
进一步地，所述硅藻土经过改性处理：将硅藻土采用8.5%浓度的盐酸浸泡30分钟后，过滤，过滤，干燥，在300℃下煅烧40分钟后粉碎至80-100目。
一种高性能改性塑料的制作方法，包括：
1）按重量份分别称取，聚氯乙烯45份、聚丙烯25份、高铝矾土10份、铝粉8份、六铝酸钙6份、硅藻土5份、分散剂3份、热稳定剂2份、增塑剂2份。
2）将聚氯乙烯、聚丙烯加热至熔融状态，与高铝矾土、铝粉、六铝酸钙、硅藻土混合，均匀搅拌30分钟后，再混合分散剂、热稳定剂和增塑剂，添加到挤出机中，挤压塑化而成均匀的塑料颗粒，挤出处理的工艺条件为：一区温度210-220℃，二区温度220-240℃，三区温度240-260℃，四区温度260-270℃，停留时间为2分钟。
本发明塑料的参数性能：
| 密度g/cm3 | 断裂伸长率% | 介电强度MV/m | 低温冲击脆化温度℃ | |
| 本发明塑料 | 1.40 | 105.4 | 22.5 | ≤-20 |
表1
本发明改性塑料性能测试：
表2
由表2可以看出，本发明塑料在性能上比一般聚氯乙烯塑料要优越很多。
Claims (8)
1.一种高性能改性塑料，其特征在于，按重量份计由以下成分制成：聚氯乙烯45份、聚丙烯25份、高铝矾土10份、铝粉8份、六铝酸钙6份、硅藻土5份、分散剂3份、热稳定剂2份、增塑剂2份。
2.根据权利要求1所述的一种高性能改性塑料，其特征在于，所述铝粉采用60-65℃的水浴加热处理1-1.5小时后，干燥。
3.根据权利要求1所述的一种高性能改性塑料，其特征在于，所述分散剂为六偏磷酸钠。
4.根据权利要求1所述的一种高性能改性塑料，其特征在于，所述热稳定剂为硬脂酸钙。
5.根据权利要求1所述的一种高性能改性塑料，其特征在于，所述增塑剂为柠檬酸酯。
6.根据权利要求1所述的一种高性能改性塑料，其特征在于，所述六铝酸钙与浓度为8.5%的纳米硫酸钡溶液共混加热处理2小时；所述纳米硫酸钡溶液中纳米硫酸钡的粒度为50-60nm。
7.根据权利要求1所述的一种高性能改性塑料，其特征在于，高铝矾土经过预处理：将高铝矾土与重量份为5份的煤矸石和重量份为0.5份的氧化铝粉末混合到一起，先进行混合研磨，再放入到1700℃温度下煅烧1小时。
8.根据权利要求1所述的一种高性能改性塑料，其特征在于，所述硅藻土经过改性处理：将硅藻土采用8.5%浓度的盐酸浸泡30分钟后，过滤，过滤，干燥，在300℃下煅烧40分钟后粉碎至80-100目。