CN103524934B - 一种耐溶剂聚氯乙烯电缆护套料及其制备方法 - Google Patents

一种耐溶剂聚氯乙烯电缆护套料及其制备方法 Download PDF

Info

Publication number
CN103524934B
CN103524934B CN201310461455.9A CN201310461455A CN103524934B CN 103524934 B CN103524934 B CN 103524934B CN 201310461455 A CN201310461455 A CN 201310461455A CN 103524934 B CN103524934 B CN 103524934B
Authority
CN
China
Prior art keywords
polyvinyl chloride
oxide
sheath material
add
solvent resistance
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310461455.9A
Other languages
English (en)
Other versions
CN103524934A (zh
Inventor
何成龙
何源
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hangzhou Yongtong New Material Co., Ltd
Original Assignee
Wuhu Spaceflight Special Cable Factory Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuhu Spaceflight Special Cable Factory Co Ltd filed Critical Wuhu Spaceflight Special Cable Factory Co Ltd
Priority to CN201310461455.9A priority Critical patent/CN103524934B/zh
Publication of CN103524934A publication Critical patent/CN103524934A/zh
Application granted granted Critical
Publication of CN103524934B publication Critical patent/CN103524934B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种耐溶剂聚氯乙烯电缆护套料及其制备方法，其由以下重量份的原料制成：SG-5型聚氯乙烯树脂60-80、双酚A聚碳酸酯20-30、聚甲基丙烯酸甲酯5-10、氧化锌1-2、氧化钙2-3、异丙基三（二辛基焦磷酸酰氧基）钛酸酯0.5-1、邻苯二甲酸二乙酯10-15、三盐基硫酸铅2-3、三氧化二锑8-12、三氧化钼5-10、硬脂酸钡1-2、硬脂酸钙2-3、尼龙酸二异丁酯5-10、抗氧剂1076？1-2、沉淀硫酸钡10-15、硅灰石5-10、复合填料3-6。本发明护套料具有优异的耐溶剂性，在二甲苯、丙酮等溶剂中浸泡7天，不溶胀，且具有良好的拉伸强度和断裂伸长率，拉伸强度≥15MPa，断裂伸长率≥350％。

Description

一种耐溶剂聚氯乙烯电缆护套料及其制备方法
技术领域
本发明涉及一种电缆护套料及其制备方法，具体涉及一种耐溶剂聚氯乙烯电缆护套料及其制备方法。
背景技术
电缆护套是电缆不可缺少的中间结构部分，起着保护电缆的作用，保证电缆的通电安全，让铜丝和水、空气等介质隔绝，避免出现漏电现象。聚氯乙烯材料因具有优良的物理机械性能、柔韧性，价格便宜，并且加工性能优异，被广泛用于电缆护套层。但是现有的聚氯乙烯电缆护套料遇到溶剂后容易发生开裂现象，从而影响电缆的使用性能。
发明内容
本发明的目的在于针对现有技术的不足，提供一种耐溶剂聚氯乙烯电缆护套料及其制备方法。该护套料具有优良的强度、伸长性能和耐溶剂性。
本发明采用的技术方案如下：
一种耐溶剂聚氯乙烯电缆护套料，由以下重量份的原料制成：SG-5型聚氯乙烯树脂60-80、双酚A聚碳酸酯20-30、聚甲基丙烯酸甲酯5-10、氧化锌1-2、氧化钙2-3、异丙基三（二辛基焦磷酸酰氧基）钛酸酯0.5-1、邻苯二甲酸二乙酯10-15、三盐基硫酸铅2-3、三氧化二锑8-12、三氧化钼5-10、硬脂酸钡1-2、硬脂酸钙2-3、尼龙酸二异丁酯5-10、抗氧剂10761-2、沉淀硫酸钡10-15、硅灰石5-10、复合填料3-6；
所述复合填料的制备方法如下：a、按重量比4-6:3-5:2-3称取膨润土、重晶石、独居石，再加入膨润土重量2-3%的煤粉、1-2%的活性炭，混合均匀后540-560℃煅烧3-5h，冷却至常温后粉碎粒径至15μm以下，然后加水打浆制成浓度为40-50%的浆液，加入浓度为10-15%的盐酸溶液调节浆液PH至4.5-5.5，70-80℃水浴加热2-3h，再用浓度为10-15%的氢氧化钠溶液调节PH至中性，然后加入浆液重量2-3%的壬基酚聚氧乙烯醚、3-4%的十二烷基硫酸钠、2-3%的N,N-二(羟基乙基)椰油酰胺、1-2%的粉煤灰、2-3%的聚乙二醇和3-5%的硅酸钠，高速研磨浆料粒径至10μm以下，喷雾干燥成粉末；b、向上述制得的粉末中加入2-3%的玉石粉、1-2%的锆英粉、3-4%的聚丙烯酸钠、1-2%的壳聚糖和0.5-1%的四异丙基二(二辛基亚磷酸酰氧基)钛酸酯，高速剪切分散10-15min即可。
一种耐溶剂聚氯乙烯电缆护套料的制备方法，包括以下步骤：将高速捏合机加热至55-65℃，加入双酚A聚碳酸酯、聚甲基丙烯酸甲酯、邻苯二甲酸二乙酯、氧化钙、复合填料，捏合2-4min；然后升温至80-90℃，加入聚氯乙烯树脂、氧化锌、三氧化二锑、三氧化钼、尼龙酸二异丁酯、沉淀硫酸钡、硅灰石，捏合4-6min，再加入其余原料，继续捏合1-2min，降温至45℃以下即可出料；然后将混合料投入双螺杆挤出机进行挤出造粒，双螺杆挤出机的工作温度为150-170℃，最后经风冷、筛选磁选、计量、包装，即得所需的护套料。
本发明的有益效果：
本发明护套料具有优异的耐溶剂性，在二甲苯、丙酮等溶剂中浸泡7天，不溶胀，且具有良好的拉伸强度和断裂伸长率，拉伸强度≥15MPa，断裂伸长率≥350％。
具体实施方式
一种耐溶剂聚氯乙烯电缆护套料，由以下重量（kg）的原料制成：SG-5型聚氯乙烯树脂70、双酚A聚碳酸酯30、聚甲基丙烯酸甲酯8、氧化锌1.5、氧化钙2.5、异丙基三（二辛基焦磷酸酰氧基）钛酸酯0.7、邻苯二甲酸二乙酯12、三盐基硫酸铅2、三氧化二锑10、三氧化钼8、硬脂酸钡2、硬脂酸钙2、尼龙酸二异丁酯7、抗氧剂10761.5、沉淀硫酸钡15、硅灰石8、复合填料4；
所述复合填料的制备方法如下：a、按重量比5:4:2称取膨润土、重晶石、独居石，再加入膨润土重量2%的煤粉、1.5%的活性炭，混合均匀后550℃煅烧4h，冷却至常温后粉碎粒径至15μm以下，然后加水打浆制成浓度为40-50%的浆液，加入浓度为15%的盐酸溶液调节浆液PH至5.0，75℃水浴加热3h，再用浓度为15%的氢氧化钠溶液调节PH至中性，然后加入浆液重量3%的壬基酚聚氧乙烯醚、3%的十二烷基硫酸钠、2%的N,N-二(羟基乙基)椰油酰胺、1.5%的粉煤灰、2%的聚乙二醇和4%的硅酸钠，高速研磨浆料粒径至10μm以下，喷雾干燥成粉末；b、向上述制得的粉末中加入2%的玉石粉、1.5%的锆英粉、3%的聚丙烯酸钠、1.5%的壳聚糖和0.6%的四异丙基二(二辛基亚磷酸酰氧基)钛酸酯，高速剪切分散10min即可。
一种耐溶剂聚氯乙烯电缆护套料的制备方法，包括以下步骤：将高速捏合机加热至55-65℃，加入双酚A聚碳酸酯、聚甲基丙烯酸甲酯、邻苯二甲酸二乙酯、氧化钙、复合填料，捏合3min；然后升温至80-90℃，加入聚氯乙烯树脂、氧化锌、三氧化二锑、三氧化钼、尼龙酸二异丁酯、沉淀硫酸钡、硅灰石，捏合5min，再加入其余原料，继续捏合2min，降温至45℃以下即可出料；然后将混合料投入双螺杆挤出机进行挤出造粒，双螺杆挤出机的工作温度为150-170℃，最后经风冷、筛选磁选、计量、包装，即得所需的护套料。
制得的护套料的性能测试结果如下：

Claims (1)

1.一种耐溶剂聚氯乙烯电缆护套料，其特征在于，由以下重量份的原料制成：SG-5型聚氯乙烯树脂60-80、双酚A聚碳酸酯20-30、聚甲基丙烯酸甲酯5-10、氧化锌1-2、氧化钙2-3、异丙基三（二辛基焦磷酸酰氧基）钛酸酯0.5-1、邻苯二甲酸二乙酯10-15、三盐基硫酸铅2-3、三氧化二锑8-12、三氧化钼5-10、硬脂酸钡1-2、硬脂酸钙2-3、尼龙酸二异丁酯5-10、抗氧剂10761-2、沉淀硫酸钡10-15、硅灰石5-10、复合填料3-6；
所述复合填料的制备方法如下：
a、按重量比4-6:3-5:2-3称取膨润土、重晶石、独居石，再加入膨润土重量2-3%的煤粉、1-2%的活性炭，混合均匀后540-560℃煅烧3-5h，冷却至常温后粉碎粒径至15μm以下，然后加水打浆制成浓度为40-50%的浆液，加入浓度为10-15%的盐酸溶液调节浆液pH至4.5-5.5，70-80℃水浴加热2-3h，再用浓度为10-15%的氢氧化钠溶液调节pH至中性，然后加入浆液重量2-3%的壬基酚聚氧乙烯醚、3-4%的十二烷基硫酸钠、2-3%的N,N-二(羟基乙基)椰油酰胺、1-2%的粉煤灰、2-3%的聚乙二醇和3-5%的硅酸钠，高速研磨浆料粒径至10μm以下，喷雾干燥成粉末；
b、向上述制得的粉末中加入2-3%的玉石粉、1-2%的锆英粉、3-4%的聚丙烯酸钠、1-2%的壳聚糖和0.5-1%的四异丙基二(二辛基亚磷酸酰氧基)钛酸酯，高速剪切分散10-15min即可；
所述的耐溶剂聚氯乙烯电缆护套料的制备方法包括以下步骤：将高速捏合机加热至55-65℃，加入双酚A聚碳酸酯、聚甲基丙烯酸甲酯、邻苯二甲酸二乙酯、氧化钙、复合填料，捏合2-4min；然后升温至80-90℃，加入聚氯乙烯树脂、氧化锌、三氧化二锑、三氧化钼、尼龙酸二异丁酯、沉淀硫酸钡、硅灰石，捏合4-6min，再加入其余原料，继续捏合1-2min，降温至45℃以下即可出料；然后将混合料投入双螺杆挤出机进行挤出造粒，双螺杆挤出机的工作温度为150-170℃，最后经风冷、筛选磁选、计量、包装，即得所需的护套料。
CN201310461455.9A 2013-09-30 2013-09-30 一种耐溶剂聚氯乙烯电缆护套料及其制备方法 Active CN103524934B (zh)