CN103571064A - 一种电缆用三元乙丙橡胶/聚氯乙烯塑料复合护套料及其制备方法 - Google Patents
一种电缆用三元乙丙橡胶/聚氯乙烯塑料复合护套料及其制备方法 Download PDFInfo
- Publication number
- CN103571064A CN103571064A CN201310464708.8A CN201310464708A CN103571064A CN 103571064 A CN103571064 A CN 103571064A CN 201310464708 A CN201310464708 A CN 201310464708A CN 103571064 A CN103571064 A CN 103571064A
- Authority
- CN
- China
- Prior art keywords
- parts
- polyvinyl chloride
- sheath material
- preparation
- rubber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种电缆用三元乙丙橡胶/聚氯乙烯塑料复合护套料及其制备方法,其由以下重量份的原料制成:三元乙丙橡胶50-70、SG-3型聚氯乙烯树脂30-40、SBS15-20、氧化锌2-3、硬脂酸1-2、邻苯二甲酸二辛酯10-15、环氧油酸丁酯5-10、煅烧陶土10-15、炭黑N66015-20、偏硼酸钡4-8、玻璃微珠3-6、乙撑双硬脂酰胺3-5、氯化石蜡4-8、双巯基乙酸异辛酯二正辛基1-2、十溴二苯乙烷8-12、不溶性硫磺3-5等。本发明护套料具有优良的韧性、弹性、耐油性、耐热性、耐酸碱性、耐老化性等性能,经久耐用,且原料来源广泛低廉,生产工艺简单,生产成本低,具有良好的市场前景和巨大的经济效益。
Description
技术领域
本发明涉及一种电缆护套料及其制备方法,具体涉及一种电缆用三元乙丙橡胶/聚氯乙烯塑料复合护套料及其制备方法。
背景技术
电缆护套是电缆不可缺少的中间结构部分,起着保护电缆的作用,保证电缆的通电安全,让铜丝和水、空气等介质隔绝,避免出现漏电现象。橡胶聚氯乙烯复合护套因其良好的弹性手感、物理机械性能以及绝缘性能,广泛应用于矿用电缆、电梯电缆等领域。但是现有橡胶聚氯乙烯复合护套料的生产成本普遍较高,如何在不降低产品的性能同时降低生产成本是企业亟待解决的问题。
发明内容
本发明的目的在于针对现有技术的不足,提供一种成本低廉、加工性能好、综合性能优异的电缆用三元乙丙橡胶/聚氯乙烯塑料复合护套料及其制备方法。
本发明采用的技术方案如下:
一种电缆用三元乙丙橡胶/聚氯乙烯塑料复合护套料,由以下重量份的原料制成:三元乙丙橡胶50-70、SG-3型聚氯乙烯树脂30-40、SBS15-20、氧化锌2-3、硬脂酸1-2、邻苯二甲酸二辛酯10-15、环氧油酸丁酯5-10、煅烧陶土10-15、炭黑N660 15-20、偏硼酸钡4-8、玻璃微珠3-6、乙撑双硬脂酰胺3-5、氯化石蜡4-8、双巯基乙酸异辛酯二正辛基1-2、十溴二苯乙烷8-12、不溶性硫磺3-5、三烯丙基异氰酸酯2-3、二丁基二硫代氨基甲酸锌1-2、2-硫醇基甲基苯并咪唑2-3、N,N'-二正丁基硫脲1-2、复合填料3-5;
所述复合填料的制备方法如下:a、按重量比4-8:3-6:2-4称取高岭土、硅藻土、白云石粉碎、混合均匀后湿法球磨18-24h,再在110-120℃下烘干,然后在550-580℃下煅烧1-2h,冷却至室温后加入适量的水打浆制成浓度为40-50%的浆液,然后加浓度为10-15%的盐酸溶液调节浆液PH至4.0-5.0,70-80℃水浴加热2-3h,再用浓度为15-20%的氢氧化钠溶液调节浆液PH至中性,然后加入浆液重量1-2%的十二烷基苯磺酸钠、2-3%的六偏磷酸钠、3-5%的聚丙烯酸、2-3%的水溶性硅溶胶、1-2%的羟乙基纤维素和0.5-1%的乙二醇丁醚醋酸酯,高速研磨20-30min,烘干,过300-400目筛;b、上述过筛后的粉末中加入1-2%的纳米氮化铝、2-3%的乙烯基硅油、3-4%的季戊四醇硬脂酸酯、1-2%的玉石粉,高速剪切分散10-15min即可。
一种电缆用三元乙丙橡胶/聚氯乙烯塑料复合护套料的制备方法,包括以下步骤:
(1)将SG-3型聚氯乙烯树脂、SBS、邻苯二甲酸二辛酯、复合填料、玻璃微珠乙撑双硬脂酰胺、氧化锌、硬脂酸加入密炼机中,在55-65℃下混炼3-4min,得混合料A;
(2)将三元乙丙橡胶、环氧油酸丁酯、煅烧陶土、炭黑N660、偏硼酸钡、氯化石蜡、十溴二苯乙烷加入密炼机中,在70-75℃下混炼4-6min;得混合料B;
(3)将上述制得的混合料A和混合料B一起送入开炼机中混合均匀,再加入其余原料,在85-90℃下混炼3-5min,降温至40℃以下时出片;
(4)将上述制得的片料置于平板硫化机中在160-180℃下硫化10-15min,然后置于烘箱中在145-165℃下二次硫化2-3h,即得所需的护套料。
本发明的有益效果:
本发明护套料综合性能优异,具有优良的韧性、弹性、耐油性、耐热性、耐酸碱性、耐老化性等性能,经久耐用,且原料来源广泛低廉,生产工艺简单,生产成本低,具有良好的市场前景和巨大的经济效益。
具体实施方式
一种电缆用三元乙丙橡胶/聚氯乙烯塑料复合护套料,由以下重量(kg)的原料制成:三元乙丙橡胶60、SG-3型聚氯乙烯树脂40、SBS15、氧化锌2、硬脂酸1.5、邻苯二甲酸二辛酯12、环氧油酸丁酯8、煅烧陶土15、炭黑N660 18、偏硼酸钡6、玻璃微珠4、乙撑双硬脂酰胺3、氯化石蜡6、双巯基乙酸异辛酯二正辛基1.5、十溴二苯乙烷10、不溶性硫磺4、三烯丙基异氰酸酯2、二丁基二硫代氨基甲酸锌1.5、2-硫醇基甲基苯并咪唑2、N,N'-二正丁基硫脲1、复合填料4;
所述复合填料的制备方法如下:a、按重量比6:3:2称取高岭土、硅藻土、白云石粉碎、混合均匀后湿法球磨18h,再在110℃下烘干,然后在550℃下煅烧2h,冷却至室温后加入适量的水打浆制成浓度为50%的浆液,然后加浓度为15%的盐酸溶液调节浆液PH至5.0,80℃水浴加热2h,再用浓度为15%的氢氧化钠溶液调节浆液PH至中性,然后加入浆液重量1%的十二烷基苯磺酸钠、2%的六偏磷酸钠、3%的聚丙烯酸、2%的水溶性硅溶胶、1%的羟乙基纤维素和0.5%的乙二醇丁醚醋酸酯,高速研磨20min,烘干,过300目筛;b、上述过筛后的粉末中加入1%的纳米氮化铝、2%的乙烯基硅油、3%的季戊四醇硬脂酸酯、1%的玉石粉,高速剪切分散10min即可。
一种电缆用三元乙丙橡胶/聚氯乙烯塑料复合护套料的制备方法,包括以下步骤:
(1)将SG-3型聚氯乙烯树脂、SBS、邻苯二甲酸二辛酯、复合填料、玻璃微珠乙撑双硬脂酰胺、氧化锌、硬脂酸加入密炼机中,在60℃下混炼3min,得混合料A;
(2)将三元乙丙橡胶、环氧油酸丁酯、煅烧陶土、炭黑N660、偏硼酸钡、氯化石蜡、十溴二苯乙烷加入密炼机中,在75℃下混炼5min;得混合料B;
(3)将上述制得的混合料A和混合料B一起送入开炼机中混合均匀,再加入其余原料,在90℃下混炼4min,降温至40℃以下时出片;
(4)将上述制得的片料置于平板硫化机中在170℃下硫化12min,然后置于烘箱中在150℃下二次硫化3h,即得所需的护套料。
制得的护套料的性能测试结果如下:
Claims (2)
1.一种电缆用三元乙丙橡胶/聚氯乙烯塑料复合护套料,其特征在于,由以下重量份的原料制成:三元乙丙橡胶50-70、SG-3型聚氯乙烯树脂30-40、SBS 15-20、氧化锌2-3、硬脂酸1-2、邻苯二甲酸二辛酯10-15、环氧油酸丁酯5-10、煅烧陶土10-15、炭黑N660 15-20、偏硼酸钡 4-8、玻璃微珠3-6、乙撑双硬脂酰胺 3-5、氯化石蜡 4-8、双巯基乙酸异辛酯二正辛基1-2、十溴二苯乙烷8-12、不溶性硫磺3-5、三烯丙基异氰酸酯2-3、二丁基二硫代氨基甲酸锌1-2、2-硫醇基甲基苯并咪唑 2-3、N,N'-二正丁基硫脲 1-2、复合填料 3-5;
所述复合填料的制备方法如下:a、按重量比4-8:3-6:2-4称取高岭土、硅藻土、白云石粉碎、混合均匀后湿法球磨18-24h,再在110-120℃下烘干,然后在550-580℃下煅烧1-2h,冷却至室温后加入适量的水打浆制成浓度为40-50%的浆液,然后加浓度为10-15%的盐酸溶液调节浆液PH至4.0-5.0,70-80℃水浴加热2-3h,再用浓度为15-20%的氢氧化钠溶液调节浆液PH至中性,然后加入浆液重量1-2%的十二烷基苯磺酸钠、2-3%的六偏磷酸钠、3-5%的聚丙烯酸、2-3%的水溶性硅溶胶、1-2%的羟乙基纤维素和0.5-1%的乙二醇丁醚醋酸酯,高速研磨20-30min,烘干,过300-400目筛;b、上述过筛后的粉末中加入1-2%的纳米氮化铝、2-3%的乙烯基硅油、3-4%的季戊四醇硬脂酸酯、1-2%的玉石粉,高速剪切分散10-15min即可。
2.如权利要求1所述的电缆用三元乙丙橡胶/聚氯乙烯塑料复合护套料的制备方法,其特征在于包括以下步骤:
(1)将SG-3型聚氯乙烯树脂、SBS、邻苯二甲酸二辛酯、复合填料、玻璃微珠乙撑双硬脂酰胺、氧化锌、硬脂酸加入密炼机中,在55-65℃下混炼3-4min,得混合料A;
(2)将三元乙丙橡胶、环氧油酸丁酯、煅烧陶土、炭黑N660、偏硼酸钡、氯化石蜡、十溴二苯乙烷加入密炼机中,在70-75℃下混炼4-6min;得混合料B;
(3)将上述制得的混合料A和混合料B一起送入开炼机中混合均匀,再加入其余原料,在85-90℃下混炼3-5min,降温至40℃以下时出片;
(4)将上述制得的片料置于平板硫化机中在160-180℃下硫化10-15min,然后置于烘箱中在145-165℃下二次硫化2-3h,即得所需的护套料。