CN103508669A - 一种抗紫外线光伏玻璃及其应用 - Google Patents

一种抗紫外线光伏玻璃及其应用 Download PDF

Info

Publication number
CN103508669A
CN103508669A CN201310177804.4A CN201310177804A CN103508669A CN 103508669 A CN103508669 A CN 103508669A CN 201310177804 A CN201310177804 A CN 201310177804A CN 103508669 A CN103508669 A CN 103508669A
Authority
CN
China
Prior art keywords
photovoltaic glass
ultraviolet
solar photovoltaic
white
super
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201310177804.4A
Other languages
English (en)
Other versions
CN103508669B (zh
Inventor
邵景楚
徐国平
刘力武
刘四清
卿艳
王巍
李渊
杨燕参
李刚
杨敬仁
黎勇明
刘佑明
陈环艺
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hunan Qibin Solar Technology Co ltd
Original Assignee
ZHANGZHOU KIBING GLASS CO Ltd
Riverhead Qi Bingui Industry Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ZHANGZHOU KIBING GLASS CO Ltd, Riverhead Qi Bingui Industry Co Ltd filed Critical ZHANGZHOU KIBING GLASS CO Ltd
Priority to CN201310177804.4A priority Critical patent/CN103508669B/zh
Publication of CN103508669A publication Critical patent/CN103508669A/zh
Application granted granted Critical
Publication of CN103508669B publication Critical patent/CN103508669B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种抗紫外线超白光伏玻璃及其应用。该玻璃包括如下重量份的组分：SiO2 72.2-73.0重量份，Al2O3 0.1-1.0重量份、Na2O 14.3-15.3重量份、K2O 0.02-1.2重量份、CaO 9-12重量份、MgO 0.05-4.3重量份、Fe2O3 0.009-0.015重量份、CeO2 0.04-0.16重量份和SO3 0.02-0.18重量份。本发明的超白玻璃中含有0.04-0.16重量份的稀土金属氧化物CeO2，以及添加着色剂0.01-0.05重量份、Co3O4 0-0.1重量份，SrO 0.01-0.5重量份，MnO2 0-0.2重量份，Se 0-0.1重量份，使得该超白玻璃的抗紫外线能力大大提高、紫外线透射率低于55%、光透过率可提高至92%，显著降低了其封装的太阳能晶体硅电池及非晶硅电极板等的紫外线侵蚀作用、延长了太阳能电池组件使用寿命和太阳能电池光电转换效率。

Description

一种抗紫外线光伏玻璃及其应用
技术领域
本发明属于玻璃材料技术领域，具体涉及一种抗紫外线光伏玻璃及其应用。
背景技术
清洁再生能源技术的应用已经成为中国及全球能源战略发展的重要趋势，而太阳能是一种取之不竭的新能源。
利用太阳能发电的电池组件中多使用玻璃作为封装材料以防止其中的晶体硅或非晶体硅组件在紫外线的照射下老化而缩短其使用寿命，但现有技术中的封装玻璃的紫外线透过率仍然较高，无法有效抵御紫外线对晶体硅或非晶体硅组件的损害。另外，现有技术的超白玻璃透过率比较低，对太阳光大量吸收还不够，存在太阳能电池光电转换率低等缺陷。
发明内容
本发明的目的在于克服现有技术缺陷，提供一种抗紫外线光伏玻璃。
本发明的另一目的在于提供上述抗紫外线光伏玻璃的应用。
本发明的技术方案如下：
一种抗紫外线光伏玻璃，包括如下重量份的组分：
Figure BDA00003188754400021
在本发明的一个优选实施方案中，包括如下重量百分比的组分：
本发明的另一技术方案如下：
一种上述抗紫外线光伏玻璃作为太阳能电池封装材料的应用。
本发明的有益效果是：
1、本发明的抗紫外线光伏玻璃中含有0.04-0.16重量份的稀土金属氧化物CeO2，使得该抗紫外线光伏玻璃的抗紫外线能力大大提高，紫外线透射率低于55%，显著降低了其封装的太阳能晶体硅电池及非晶硅电极板等的紫外线侵蚀作用，延长了太阳能电池组件使用寿命；
2、本发明的抗紫外线光伏玻璃中含有0.01-0.015重量份的Fe2O3，保证了该抗紫外线光伏玻璃的超白特性，提高太阳光透过率至92%，降低光反射率，使得其封装的太阳能电池组件的光电转换效率得到提高；
3、本发明的抗紫外线光伏玻璃中含有0.02-0.1重量份的SO3，降低了生产该抗紫外线光伏玻璃的过程中含硫废气的排放量，有益于环境保护。
具体实施方式
以下通过具体实施方式对本发明的技术方案进行进一步的说明和描述。
实施例1
（1）按如下重量份称取各组分：
Figure BDA00003188754400032
Figure BDA00003188754400041
（2）将上述组分送入抗紫外线光伏玻璃窑炉中进行抗紫外线光伏玻璃的生产，具体工艺参数如下：熔化温度为1350-1450℃，澄清均化温度为1390-1430℃，成型温度为930-970℃，退火温度560-570℃，产品为平板玻璃。
实施例2
（1）按如下重量份称取各组分：
Figure BDA00003188754400042
Figure BDA00003188754400051
（2）将上述组分送入抗紫外线光伏玻璃窑炉中进行抗紫外线光伏玻璃的生产，具体工艺参数如下：熔化温度为1350-1450℃，澄清均化温度为1390-1430℃，成型温度为930-970℃，退火温度560-570℃，产品为平板玻璃。
实施例3
（1）按如下重量份称取各组分：
Figure BDA00003188754400052
Figure BDA00003188754400061
（2）将上述组分送入抗紫外线光伏玻璃窑炉中进行抗紫外线光伏玻璃的生产，具体工艺参数如下：熔化温度为1350-1450℃，澄清均化温度为1390-1430℃，成型温度为930-970℃，退火温度560-570℃，产品为平板玻璃。
实施例4
（1）按如下重量百分比称取各组分：
Figure BDA00003188754400062
（2）将上述组分送入抗紫外线光伏玻璃窑炉中进行抗紫外线光伏玻璃的生产，具体工艺参数如下：熔化温度为1350-1450℃，澄清均化温度为1390-1430℃，成型温度为930-970℃，退火温度560-570℃，产品为平板玻璃。
以上所述，仅为本发明的较佳实施例而已，故不能依此限定本发明实施的范围，即依本发明专利范围及说明书内容所作的等效变化与修饰，皆应仍属本发明涵盖的范围内。

Claims (3)

1.一种抗紫外线光伏玻璃，其特征在于：包括如下重量份的组分：
Figure FDA00003188754300011
2.如权利要求1所述的一种抗紫外线光伏玻璃，其特征在于：包括如下重量百分比的组分：
Figure FDA00003188754300012
Figure FDA00003188754300021
3.一种权利要求1所述的抗紫外线光伏玻璃作为太阳能电池封装材料的应用。
CN201310177804.4A 2013-05-14 2013-05-14 一种抗紫外线超白光伏玻璃及其应用 Active CN103508669B (zh)