CN107043211A - 一种全氧燃烧窑炉光伏玻璃配方 - Google Patents

一种全氧燃烧窑炉光伏玻璃配方 Download PDF

Info

Publication number
CN107043211A
CN107043211A CN201710041578.5A CN201710041578A CN107043211A CN 107043211 A CN107043211 A CN 107043211A CN 201710041578 A CN201710041578 A CN 201710041578A CN 107043211 A CN107043211 A CN 107043211A
Authority
CN
China
Prior art keywords
weight
parts
formula
oxygen combustion
cullet
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710041578.5A
Other languages
English (en)
Inventor
严养情
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Rainbow (Hefei) photovoltaic Co., Ltd.
Original Assignee
Hefei Rainbow New Energy Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hefei Rainbow New Energy Co Ltd filed Critical Hefei Rainbow New Energy Co Ltd
Priority to CN201710041578.5A priority Critical patent/CN107043211A/zh
Publication of CN107043211A publication Critical patent/CN107043211A/zh
Pending legal-status Critical Current

Abstract

本发明提供一种全氧燃烧窑炉光伏玻璃的配方，包括30%‑40%的碎玻璃及60%‑70%配合料。配合料主要包括下述氧化物组成：SiO270.5‑73.5重量份；Na2O 12.8‑13.8重量份；CaO 8.5‑9.5重量份；MgO 3.1‑3.5重量份；AL2O3 0.9‑1.3重量份；SB2O3 0.13‑0.23重量份；将上述化合物熔解制成玻璃，本发明提供了一种在全氧燃烧窑炉内低成本、便于生产的光伏玻璃配方，节约资源，保护环境。

Description

一种全氧燃烧窑炉光伏玻璃配方
技术领域
本发明涉及玻璃制造领域，具体涉及一种全氧燃烧窑炉光伏玻璃的配方。
背景技术
太阳能光伏发电在在新能源发展中具有巨大优势，太阳能被认为是取之不尽、用之不竭的能源，它无需开采、运输，只要有阳光的地方就能利用，并且无毒、无污染、无碳排放，光伏玻璃组为光伏组件的必要材料，其高透过率对组件有直接影响，目前采用普通的浮法工艺和压延工艺无法达到高透过率，传统窑炉采用煤炭能源，严重影响环境质量，因此，本领域需要开发一种环境友好、低成本的光伏玻璃配方及制造方法。
发明内容
为了克服上述中现有技术存在的不足，本发明本发明内容第一目的在于开发一种低成本、高效益、高透过率的光伏玻璃组合物。
本发明内容第二目的在于生产过程中使用对环境无害化的能源。
本发明内容第三目的在于开发一种低成本、高效益的光伏玻璃制备方法。
本发明的目的是通过以下方案实现的：一种全氧燃烧窑炉光伏玻璃的配方，包括碎玻璃和配合料，其特征在于：按照重量比，30%-40%的碎玻璃和60%-70%配合料，其中配合料按照重量计，包括下述氧化物组成：SiO270.5-73.5重量份； Na2O 12.8-13.8重量份；CaO8.5-9.5重量份； MgO 3.1-3.5重量份； AL2O3 0.9-1.3重量份；SB2O3 0.13-0.23重量份。
优选的，配方按照重量比34%的碎玻璃，66%的配合料混合。
优选的，所述的碎玻璃为无色碎玻璃。
一种全氧燃烧窑炉光伏玻璃的配方的制作方法，其特征在于：所述碎玻璃和配合料组合物组分经充分混合后在全氧燃烧的窑炉内融化，融化后经压延处理和退火处理得到光伏玻璃，包括原料输送-称量-混合-熔化（全氧燃烧窑炉）-压延-退火-裁切-钢化-镀膜-检验-包装，所述的窑炉选用日融化量在250t/d至750t/d的玻璃窑炉。
本发明有益效果为：
（1）低成本、高效益、高透过率，使得光伏组件利用价值最大化；
（2）采用天然气加热生产，生产过程中降低环境污染；
（3）降低生产难度，节约成本。
具体实施方式
一种全氧燃烧窑炉光伏玻璃的配方，包括碎玻璃和配合料，其特征在于：按照重量比，30%-40%的碎玻璃和60%-70%配合料，其中配合料按照重量计，包括下述氧化物组成：SiO270.5-73.5重量份； Na2O 12.8-13.8重量份；CaO 8.5-9.5重量份； MgO 3.1-3.5重量份； AL2O3 0.9-1.3重量份；SB2O3 0.13-0.23重量份,优选的配方按照重量比34%的碎玻璃，66%的配合料混合，所述的碎玻璃为无色碎玻璃。
实施例1
一种全氧燃烧窑炉光伏玻璃的配方，包括碎玻璃和配合料，按照重量比，30%的碎玻璃和70%配合料，其中配合料按照重量计，包括下述氧化物组成：SiO270.5重量份； Na2O 12.8重量份；CaO 8.5重量份； MgO 3.1重量份； AL2O3 0.9重量份；SB2O3 0.13重量份。
其中，所述的碎玻璃为无色碎玻璃。
实施例2
一种全氧燃烧窑炉光伏玻璃的配方，包括碎玻璃和配合料，按照重量比，34%的碎玻璃和66%配合料，其中配合料按照重量计，包括下述氧化物组成：SiO272重量份； Na2O 13.3重量份；CaO 9重量份； MgO 3.3重量份； AL2O3 1.1重量份；SB2O3 0.18重量份。
其中，所述的碎玻璃为无色碎玻璃。
实施例3
一种全氧燃烧窑炉光伏玻璃的配方，包括碎玻璃和配合料，按照重量比，40%的碎玻璃和60%配合料，其中配合料按照重量计，包括下述氧化物组成：SiO273.5重量份； Na2O 13.8重量份；CaO 9.5重量份； MgO 3.5重量份； AL2O3 1.3重量份；SB2O3 0.23重量份。
其中，所述的碎玻璃为无色碎玻璃。
上述实施例2中所制得光伏玻璃，根据JC T 2170-2013 太阳能光伏组件用减反射膜玻璃 ，玻璃可见光透射比、太阳光直接透射比、太阳能总透射比、紫外线透射比的测定，所述光伏玻璃透过率（以3.2mm计）≥91.6%，达到光伏组件各方面实用性能最佳状态。
根据上述所述的一种全氧燃烧窑炉光伏玻璃的配方，本发明还提供一种用于制备一种全氧燃烧窑炉光伏玻璃的配方的制造方法，该方法将实施例1-3所得到的配方组分，经过充分混合以后，进入到全氧燃烧的窑炉内融化，全氧燃烧采用天然气配合氧气燃烧，天然气作为清洁能源，相较于煤炭能源，可有效减低污染物的排放，达到清洁生产的目的，融化以后经过玻璃生产中常规的压延和退火处理，即可得到光伏玻璃，窑炉选用日融化量在250t/d至750t/d的玻璃窑炉，具体步骤包括：原料输送-称量-混合-熔化（全氧燃烧窑炉）-压延-退火-裁切-钢化-镀膜-检验-包装，即可得到想要的大小规格型号的光伏玻璃，满足实际需要。
最后应说明的是：以上实施例仅用以说明本发明而并非限制本发明所描述的技术方案；因此，尽管本说明书参照上述的各个实施例对本发明已进行了详细的说明，但是，本领域的普通技术人员应当理解，仍然可以对本发明进行修改或等同替换；而一切不脱离本发明的精神和范围的技术方案及其改进，均应涵盖在本发明的权利要求范围中。

Claims (5)

1.一种全氧燃烧窑炉光伏玻璃的配方，包括碎玻璃和配合料，其特征在于：按照重量比，30%-40%的碎玻璃和60%-70%配合料，其中配合料按照重量计，包括下述氧化物组成：SiO270.5-73.5重量份； Na2O 12.8-13.8重量份；CaO 8.5-9.5重量份； MgO 3.1-3.5重量份； AL2O3 0.9-1.3重量份；SB2O3 0.13-0.23重量份。
2.根据权利要求1所述的一种全氧燃烧窑炉光伏玻璃的配方，其特征在于：所述的配方按照重量比34%的碎玻璃，66%的配合料混合。
3.根据权利要求1所述的一种全氧燃烧窑炉光伏玻璃的配方，其特征在于：所述的碎玻璃为无色碎玻璃。
4.根据权利要求1、2或3所述的一种全氧燃烧窑炉光伏玻璃的配方的制作方法，其特征在于：所述的碎玻璃和配合料组合物组分经充分混合后在全氧燃烧的窑炉内融化，融化后经压延处理和退火处理得到光伏玻璃，具体步骤包括：配方原料输送-称量-混合-熔化（全氧燃烧窑炉）-压延-退火-裁切-钢化-镀膜-检验-包装。
5.根据权利要求4所述的一种全氧燃烧窑炉光伏玻璃的配方的制作方法，其特征在于：所述的窑炉选用日融化量在250t/d至750t/d的玻璃窑炉。
CN201710041578.5A 2017-01-20 2017-01-20 一种全氧燃烧窑炉光伏玻璃配方 Pending CN107043211A (zh)