CN103421400A - 一种触摸屏uv固化可剥蓝胶及其制备方法 - Google Patents
一种触摸屏uv固化可剥蓝胶及其制备方法 Download PDFInfo
- Publication number
- CN103421400A CN103421400A CN201310388295XA CN201310388295A CN103421400A CN 103421400 A CN103421400 A CN 103421400A CN 201310388295X A CN201310388295X A CN 201310388295XA CN 201310388295 A CN201310388295 A CN 201310388295A CN 103421400 A CN103421400 A CN 103421400A
- Authority
- CN
- China
- Prior art keywords
- acrylic resin
- touch
- screen
- peelable blue
- barium sulfate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及触摸屏可剥蓝胶技术领域,具体涉及一种触摸屏UV固化可剥蓝胶及其制备方法,该种触摸屏UV固化可剥蓝胶由以下重量百分比的原料组成:有机氟硅改性丙烯酸树脂10-20%、酚醛环氧丙烯酸树脂5-15%、氨基丙烯酸树脂5-15%、脂肪族聚氨酯丙烯酸树脂5-15%、丙烯酸单体5-15%、光固化剂1-5%、二氧化硅0.1-1%、纳米硫酸钡15-25%、滑石粉10-20%、有机颜料铁蓝、群青蓝、钴蓝或酞菁蓝0.1-1%。本发明采用四种不同树脂相互配合,取长补短,制得的可剥蓝胶成膜性好,热固化成膜后具有良好的韧性、柔软性和耐酸碱性能;而且在触摸屏制作过程中导电膜保护工艺完成后,容易剥离,不会有残留在材料表面或者污染材料。
Description
技术领域
本发明涉及触摸屏可剥蓝胶技术领域,具体涉及一种触摸屏UV固化可剥蓝胶及其制备方法。
背景技术
随着信息技术和平面显示技术的迅速发展,触摸屏的应用越来越普遍。大到公共场所的信息查询系统,小到个人电脑、平板电脑、手机,触摸屏和我们的生活息息相关。在触摸屏的生产工艺过程中,需要通过使用可剥蓝胶对触摸屏玻璃进行多次的临时保护。可剥蓝胶主要应用于触摸屏中的透明导电玻璃、薄膜的ITO镀膜上,起到绝缘、防潮和保护。使用时通过丝网印刷在PET、ITO膜和ITO玻璃上,烘烤成膜后起到防止材料在后续生产过程中受到污染或划伤的作用,在触摸屏上、下线路粘合之前,可用简易方法剥离。
如申请号为201310003438.0的中国发明专利申请公开了一种触摸屏临时保护用UV固化可剥蓝胶及其制备方法,UV固化可剥蓝胶配方组成为:改性丙烯酸酯树脂50~70份,丙烯酸酯单体20~30份,光固化剂1.0-5.0份,触变剂0.1-1.0份,助剂0.1-5.0份,颜料0.1-1.0份;所述制备方法为:按配方比例准确称取各种原料,先将改性丙烯酸酯树脂、丙烯酸酯单体、光固化剂、助剂、颜料依次加入反应釜中搅拌,待搅拌均匀后,加入触变剂,分散均匀后出料。但上述保护胶耐酸碱性能差、柔韧性差、不易剥离、易残留。
发明内容
本发明的目的在于针对现有技术的不足,提供一种柔韧性好、耐酸性强、易剥离、无残留的一种触摸屏UV固化可剥蓝胶及其制备方法。
为了实现上述目的,本发明采用如下技术方案:一种触摸屏UV固化可剥蓝胶,它由以下重量百分比的原料组成:
有机氟硅改性丙烯酸树脂 10-20%
酚醛环氧丙烯酸树脂 5-15%
氨基丙烯酸树脂 5-15%
脂肪族聚氨酯丙烯酸树脂 5-15%
丙烯酸单体 5-15%
光固化剂 1-5%
二氧化硅 0.1-1%
硫酸钡 15-25%
滑石粉 10-20%
有机颜料 0.1-1%,
上述各原料的重量百分比之和为100%。
有机氟硅改性丙烯酸树脂的制备方法可参见作者“时米超”在山东大学的硕士学位论文中发表的《有机氟硅改性丙烯酸树脂的合成及性能研究》。有机氟硅改性丙烯酸树脂耐热性、耐酸、耐盐性好。
优选的,它由以下重量百分比的原料组成:
有机氟硅改性丙烯酸树脂 10-15%
酚醛环氧丙烯酸树脂 8-10%
氨基丙烯酸树脂 10-15%
脂肪族聚氨酯丙烯酸树脂 8-10%
丙烯酸单体 5-10%
光固化剂 1-4%
二氧化硅 0.1-1%
硫酸钡 20-25%
滑石粉 10-15%
有机颜料 0.1-1%,
上述各原料的重量百分比之和为100%。
优选的,它由以下重量百分比的原料组成:
有机氟硅改性丙烯酸树脂 10-15%
酚醛环氧丙烯酸树脂 8-10%
氨基丙烯酸树脂 10-15%
脂肪族聚氨酯丙烯酸树脂 8-10 %
丙烯酸单体 10-15%
光固化剂 1-4%
二氧化硅 0.1-1%
硫酸钡 15-20%
滑石粉 15-20%
有机颜料 0.1-1%,
上述各原料的重量百分比之和为100%。
更为优选的,它由以下重量百分比的原料组成:
有机氟硅改性丙烯酸树脂 15%
酚醛环氧丙烯酸树脂 10%
氨基丙烯酸树脂 5%
脂肪族聚氨酯丙烯酸树脂 10%
丙烯酸单体 10%
光固化剂 4%
二氧化硅 1%
硫酸钡 25%
滑石粉 19%
有机颜料 1%。
优选的,所述光固化剂由质量比为1:1的二苯甲酮和邻苯甲酰苯甲酸甲酯组成。
优选的,所述硫酸钡为纳米硫酸钡。硫酸钡本身性质稳定,难溶于水、酸、碱或有机溶剂,纳米硫酸钡便于更好的分散到树脂基体中增强树脂基体的耐酸碱性,滑石粉有助于纳米硫酸钡分散的更均匀。
优选的,所述有机颜料为铁蓝、群青蓝、钴蓝或酞菁蓝。
一种触摸屏UV固化可剥蓝胶的制备方法,将配方量的有机氟硅改性丙烯酸树脂、酚醛环氧丙烯酸树脂、氨基丙烯酸树脂、脂肪族聚氨酯丙烯酸树脂、丙烯酸单体、光固化剂、二氧化硅、硫酸钡、滑石粉、有机颜料混合均匀后即得一种触摸屏UV固化可剥蓝胶。
本发明与现有技术相比较,有益效果在于:
(1)本发明采用有机氟硅改性丙烯酸树脂、酚醛环氧丙烯酸树脂、氨基丙烯酸树脂、脂肪族聚氨酯丙烯酸树脂四种树脂相互配合,取长补短,制得的可剥蓝胶成膜性好,热固化成膜后具有良好的韧性、柔软性和耐酸碱性能;而且在触摸屏制作过程中导电膜保护工艺完成后,容易剥离,不会有残留在材料表面或者污染材料。
(2)本发明添加的硫酸钡与以上四种树脂的配合,大大增强了本发明的耐酸碱性能,添加的滑石粉可一方面可以改善热塑性成膜树脂的塑性和柔韧性,另一方面可以作为硫酸钡的分散剂,便于硫酸钡均匀分散到树脂基体中。
具体实施方式
下面结合实施例对本发明作进一步的说明。
实施例1。
一种触摸屏UV固化可剥蓝胶,它由以下重量百分比的原料组成:
有机氟硅改性丙烯酸树脂15%、酚醛环氧丙烯酸树脂10%、氨基丙烯酸树脂7%、脂肪族聚氨酯丙烯酸树脂5%、丙烯酸单体15%、光固化剂二苯甲酮1%和邻苯甲酰苯甲酸甲酯1%、二氧化硅0.1%、纳米硫酸钡25%、滑石粉20%、有机颜料铁蓝0.9%。
一种触摸屏UV固化可剥蓝胶的制备方法,将配方量的有机氟硅改性丙烯酸树脂、酚醛环氧丙烯酸树脂、氨基丙烯酸树脂、脂肪族聚氨酯丙烯酸树脂、丙烯酸单体、光固化剂、二氧化硅、硫酸钡、滑石粉、有机颜料混合均匀后即得一种触摸屏UV固化可剥蓝胶。
实施例2。
一种触摸屏UV固化可剥蓝胶,它由以下重量百分比的原料组成:
有机氟硅改性丙烯酸树脂10%、酚醛环氧丙烯酸树脂15%、氨基丙烯酸树脂15%、脂肪族聚氨酯丙烯酸树脂5%、丙烯酸单体14%、光固化剂二苯甲酮2.5%和邻苯甲酰苯甲酸甲酯2.5%、二氧化硅0.9%、纳米硫酸钡15%、滑石粉20%、有机颜料酞菁蓝0.1%。
一种触摸屏UV固化可剥蓝胶的制备方法,将配方量的有机氟硅改性丙烯酸树脂、酚醛环氧丙烯酸树脂、氨基丙烯酸树脂、脂肪族聚氨酯丙烯酸树脂、丙烯酸单体、光固化剂、二氧化硅、硫酸钡、滑石粉、有机颜料混合均匀后即得一种触摸屏UV固化可剥蓝胶。
实施例3。
一种触摸屏UV固化可剥蓝胶,它由以下重量百分比的原料组成:
有机氟硅改性丙烯酸树脂15%、酚醛环氧丙烯酸树脂10%、氨基丙烯酸树脂5%、脂肪族聚氨酯丙烯酸树脂10%、丙烯酸单体10%、光固化剂二苯甲酮2%和邻苯甲酰苯甲酸甲酯2%、二氧化硅1%、纳米硫酸钡25%、滑石粉19%、有机颜料钴蓝1%。
一种触摸屏UV固化可剥蓝胶的制备方法,将配方量的有机氟硅改性丙烯酸树脂、酚醛环氧丙烯酸树脂、氨基丙烯酸树脂、脂肪族聚氨酯丙烯酸树脂、丙烯酸单体、光固化剂、二氧化硅、硫酸钡、滑石粉、有机颜料混合均匀后即得一种触摸屏UV固化可剥蓝胶。
实施例4。
一种触摸屏UV固化可剥蓝胶,它由以下重量百分比的原料组成:
有机氟硅改性丙烯酸树脂20%、酚醛环氧丙烯酸树脂5%、氨基丙烯酸树脂5%、脂肪族聚氨酯丙烯酸树脂15%、丙烯酸单体5%、光固化剂二苯甲酮2%和邻苯甲酰苯甲酸甲酯2%、二氧化硅0.5%、纳米硫酸钡25%、滑石粉20%、有机颜料铁蓝、群青蓝、钴蓝或酞菁蓝0.5%。
一种触摸屏UV固化可剥蓝胶的制备方法,将配方量的有机氟硅改性丙烯酸树脂、酚醛环氧丙烯酸树脂、氨基丙烯酸树脂、脂肪族聚氨酯丙烯酸树脂、丙烯酸单体、光固化剂、二氧化硅、硫酸钡、滑石粉、有机颜料混合均匀后即得一种触摸屏UV固化可剥蓝胶。
实施例5。
一种触摸屏UV固化可剥蓝胶,它由以下重量百分比的原料组成:
有机氟硅改性丙烯酸树脂15%、酚醛环氧丙烯酸树脂10%、氨基丙烯酸树脂10%、脂肪族聚氨酯丙烯酸树脂10%、丙烯酸单体10%、光固化剂二苯甲酮1%和邻苯甲酰苯甲酸甲酯1%、二氧化硅0.8%、纳米硫酸钡22%、滑石粉20%、有机颜料酞菁蓝0.2%。
一种触摸屏UV固化可剥蓝胶的制备方法,将配方量的有机氟硅改性丙烯酸树脂、酚醛环氧丙烯酸树脂、氨基丙烯酸树脂、脂肪族聚氨酯丙烯酸树脂、丙烯酸单体、光固化剂、二氧化硅、硫酸钡、滑石粉、有机颜料混合均匀后即得一种触摸屏UV固化可剥蓝胶。
实施例6。
一种触摸屏UV固化可剥蓝胶,它由以下重量百分比的原料组成:
有机氟硅改性丙烯酸树脂18%、酚醛环氧丙烯酸树脂15%、氨基丙烯酸树脂15%、脂肪族聚氨酯丙烯酸树脂15%、丙烯酸单体15%、光固化剂二苯甲酮0.5%和邻苯甲酰苯甲酸甲酯0.5%、二氧化硅0.4%、纳米硫酸钡10%、滑石粉10%、有机颜料酞菁蓝0.6%。
一种触摸屏UV固化可剥蓝胶的制备方法,将配方量的有机氟硅改性丙烯酸树脂、酚醛环氧丙烯酸树脂、氨基丙烯酸树脂、脂肪族聚氨酯丙烯酸树脂、丙烯酸单体、光固化剂、二氧化硅、硫酸钡、滑石粉、有机颜料混合均匀后即得一种触摸屏UV固化可剥蓝胶。
成膜性测试
将印刷好有本发明可剥蓝胶的ITO玻璃或ITO膜置于UV灯下照射固化后取出,观察成膜情况,包括边缘缩墨、缩孔、膜龟裂、指触成膜是否干爽。如果成膜没有上述任何一种情况,记为“○”;如果成膜有上述任何一种情况,记为“△”,如果成膜有上述两种或两种情况以上,记为“×”
粘附可剥性测试
将本发明可剥蓝胶丝印于玻璃基板25mm*20cm,并在UV灯下照射固化成膜, 然后测试该膜对玻璃的180°剥离力,单位“gf/inch”。当剥离力在10-30gf/inch时剥离无残留则粘附可剥性最好,记为“○”;当剥离力小于10gf/inch时可剥无残留但粘附性较差,记为“△”;当剥离力大于30gf/inch时则粘附性好难剥离有残留,记为“×”。
耐酸/碱性测试
将取镀有ITO 导电膜层的玻璃(聚酯膜)基板6 片,丝印前测试ITO导电膜的电阻值记为“R0”。然后将本发明可剥蓝胶通过200 目的丝印网板印刷于上述的ITO 基板,UV灯下照射固化成膜;接着将板材各3片分别浸泡在10% 的硝酸溶液和10%的氢氧化钠溶液中,浸泡条件为:温度为25℃,浸泡时间为1小时。最后将这些板材取出并撕去本发明可剥蓝胶其ITO导电膜的阻值,记为“R”。当R/R0小于等于1.05 则有很好的耐酸碱性,记为“○”;当R/R0大于1.05而小于1.1 则耐酸碱性良好,记为“△”;当R/R0大于等于1.1则耐酸碱性较差,记为“×”。
耐热高温测试
将本发明可剥蓝胶丝印于玻璃基板,并在UV灯下照射固化成膜,然后将其置于热烘烤150℃×2 小时,观察膜是否收缩、龟裂、泛黄等现象;如有没有上述现象表明耐热性好,记为“○”;如果有少量泛黄或微量收缩表明耐热性一般,记为“△”;如果上述三种现象同时存在表明耐热性较差,记为“×”。
绝缘电阻测试
将本发明可剥蓝胶丝印于玻璃基板,并于并在UV灯下照射固化成膜,然后将膜整块剥离用ZC-90G 高绝缘电阻测量仪(上海太欧电子有限公司制)测试可剥离保护油墨的绝缘电阻值,电阻值越大则绝缘效果也好,一般认为当绝缘电阻≥ 1011Ω时已经具有良好的绝缘性能。
耐水性测试
将本发明可剥蓝胶丝印于玻璃基板,并在UV灯下照射固化成膜,然后将其浸泡50℃温水中24 小时,观察是否有脱膜、翘边、泛白等现象;如果没有上述现象,耐水记为“○”,如果有任何一种上述现象,耐水性记为“×”。
将实施例1-6的触摸屏UV固化可剥蓝胶进行上述各种测试,各项性能见表1。
表1
通过表1可以看出,本发明可剥蓝胶的具有良好的成膜性、粘附可剥性、耐酸性、耐碱性、耐水性、绝缘性能、耐高温性。
最后应当说明的是,以上实施例仅用以说明本发明的技术方案,而非对本发明保护范围的限制,尽管参照较佳实施例对本发明作了详细地说明,本领域的普通技术人员应当理解,可以对本发明的技术方案进行修改或者等同替换,而不脱离本发明技术方案的实质和范围。
Claims (8)
1.一种触摸屏UV固化可剥蓝胶,其特征在于:它由以下重量百分比的原料组成:
有机氟硅改性丙烯酸树脂 10-20%
酚醛环氧丙烯酸树脂 5-15%
氨基丙烯酸树脂 5-15%
脂肪族聚氨酯丙烯酸树脂 5-15%
丙烯酸单体 5-15%
光固化剂 1-5%
二氧化硅 0.1-1%
硫酸钡 15-25%
滑石粉 10-20%
有机颜料 0.1-1%。
2.根据权利要求1所述的一种触摸屏UV固化可剥蓝胶,其特征在于:它由以下重量百分比的原料组成:
有机氟硅改性丙烯酸树脂 10-15%
酚醛环氧丙烯酸树脂 8-10%
氨基丙烯酸树脂 10-15%
脂肪族聚氨酯丙烯酸树脂 8-10%
丙烯酸单体 5-10%
光固化剂 1-4%
二氧化硅 0.1-1%
硫酸钡 20-25%
滑石粉 10-15%
有机颜料 0.1-1%。
3.根据权利要求1所述的一种触摸屏UV固化可剥蓝胶,其特征在于:它由以下重量百分比的原料组成:
有机氟硅改性丙烯酸树脂 10-15%
酚醛环氧丙烯酸树脂 8-10%
氨基丙烯酸树脂 10-15%
脂肪族聚氨酯丙烯酸树脂 8-10 %
丙烯酸单体 10-15%
光固化剂 1-4%
二氧化硅 0.1-1%
硫酸钡 15-20%
滑石粉 15-20%
有机颜料 0.1-1%。
4.根据权利要求1所述的一种触摸屏UV固化可剥蓝胶,其特征在于:它由以下重量百分比的原料组成:
有机氟硅改性丙烯酸树脂 15%
酚醛环氧丙烯酸树脂 10%
氨基丙烯酸树脂 5%
脂肪族聚氨酯丙烯酸树脂 10%
丙烯酸单体 10%
光固化剂 4%
二氧化硅 1%
硫酸钡 25%
滑石粉 19%
有机颜料 1%。
5.根据权利要求1所述的一种触摸屏UV固化可剥蓝胶,其特征在于:所述光固化剂由质量比为1:1的二苯甲酮和邻苯甲酰苯甲酸甲酯组成。
6.根据权利要求1所述的一种触摸屏UV固化可剥蓝胶,其特征在于:所述硫酸钡为纳米硫酸钡。
7.根据权利要求1所述的一种触摸屏UV固化可剥蓝胶,其特征在于:所述有机颜料为铁蓝、群青蓝、钴蓝或酞菁蓝。
8.权利要求1-7任一项所述的一种触摸屏UV固化可剥蓝胶的制备方法,其特征在于:将配方量的有机氟硅改性丙烯酸树脂、酚醛环氧丙烯酸树脂、氨基丙烯酸树脂、脂肪族聚氨酯丙烯酸树脂、丙烯酸单体、光固化剂、二氧化硅、硫酸钡、滑石粉、有机颜料混合均匀后即得一种触摸屏UV固化可剥蓝胶。