CN103398889B - 一种双相不锈钢-碳钢复合板的显微组织显示方法 - Google Patents

一种双相不锈钢-碳钢复合板的显微组织显示方法 Download PDF

Info

Publication number
CN103398889B
CN103398889B CN201310368367.4A CN201310368367A CN103398889B CN 103398889 B CN103398889 B CN 103398889B CN 201310368367 A CN201310368367 A CN 201310368367A CN 103398889 B CN103398889 B CN 103398889B
Authority
CN
China
Prior art keywords
mordant
ethyl alcohol
microstructure
absolute ethyl
display packing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310368367.4A
Other languages
English (en)
Other versions
CN103398889A (zh
Inventor
芮乐顺
业成
周玉华
夏志敏
李志强
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nanjing Boiler & Pressure Vessel Supervision And Inspection Institute
NANJING JINCHUANG NON-FERROUS METAL TECHNOLOGY DEVELOPMENT Co Ltd
Original Assignee
Nanjing Boiler & Pressure Vessel Supervision And Inspection Institute
NANJING JINCHUANG NON-FERROUS METAL TECHNOLOGY DEVELOPMENT Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nanjing Boiler & Pressure Vessel Supervision And Inspection Institute, NANJING JINCHUANG NON-FERROUS METAL TECHNOLOGY DEVELOPMENT Co Ltd filed Critical Nanjing Boiler & Pressure Vessel Supervision And Inspection Institute
Priority to CN201310368367.4A priority Critical patent/CN103398889B/zh
Publication of CN103398889A publication Critical patent/CN103398889A/zh
Application granted granted Critical
Publication of CN103398889B publication Critical patent/CN103398889B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种双相不锈钢-碳钢复合板的显微组织显示方法。所述方法如下：将磨制、抛光好的试样用第一腐蚀剂显示出双相钢的组织，流水冲洗干净、喷上无水乙醇，迅速干燥，再用第二腐蚀剂腐蚀出碳钢或低合金钢的组织，流水冲洗干净、喷上无水乙醇，迅速干燥。腐蚀剂以体积百分比计，所述第一腐蚀剂为铁氰化钾、氢氧化钾以及余量的水，所述第二腐蚀剂为体积4%硝酸酒精溶液4ml硝酸+96ml的无水乙醇。

Description

一种双相不锈钢-碳钢复合板的显微组织显示方法
一、技术领域
本发明属于金相样品制备领域，更具体地讲，涉及一种双相不锈钢-碳钢复合板的显微组织显示方法
二、背景技术
通过爆炸复合技术使两种性能不同的材料相互复合在一起形成一种兼有两种材料性能的复合材料，大大扩展了现有材料的性能及应用范围。因此在各个领域有着广泛的应用。众所周知，双相不锈钢与碳钢或低合金钢两种材料的耐腐蚀性能差异很大，不能用同一种试剂把两种材料的组织都显示出来，而且能把双相不锈钢的组织腐蚀出来的试剂，很可能对碳钢或低合金钢造成过腐蚀，而能把碳钢或低合金钢的组织腐蚀出来的试剂，对双相不锈钢不腐蚀。因此找到适合的试剂，用适当的方法把两种材料的组织都能有效的显示出来是非常必要。对于研究焊接面的组织以及焊接对组织的影响有重要意义。
三、发明内容
针对用一种试剂不能把两种材料的组织都显示出来的不足，本发明的目的在于提供一种双相不锈钢-碳钢复合板的显微组织显示方法，以期获得良好的金相显微组织显示效果。
为了实现上述目的，本发明提供了一种双相不锈钢-碳钢复合板的显微组织显示方法，所述方法如下：
将磨制、抛光好的试样在加热至80～90℃的第一腐蚀剂中浸蚀1～2min，显微组织显示后迅速流水冲洗、喷无水乙醇、吹干；再用滴管滴第二腐蚀剂于试样抛光面上，组织显示后迅速流水冲洗、喷无水乙醇、并吹干后观察试样。
所述的双相不锈钢-碳钢复合板的显微组织显示方法，其特征在于，所述第一腐蚀剂为10克铁氰化钾+10克氢氧化钾+100ml蒸馏水，所述第二腐蚀剂为4ml硝酸+96ml的无水乙醇。
本发明的有益效果：
本发明所需的耗材均为常规的金相实验室耗材，所需化学药品也便于采购，成本低、操作简便，应用本发明所提供的组织显示方法，可以制备并显示双相不锈钢-碳钢或低合金钢爆炸焊接复合板两种材料结合面及结合面处波峰波谷的显微组织，显示效果清晰良好。
四、附图说明
图1.是根据本发明示例所获得的双相不锈钢-碳钢复合板的熔合线波峰波谷形貌照片，放大10倍；
图2.是根据本发明示例所获得的双相不锈钢-碳钢复合板的显微组织照片，放大100倍；
图3.是根据本发明示例所获得的双相不锈钢-碳钢复合板的显微组织照片，放大400倍。
五、具体实施方式
实施例1：一种双相不锈钢-碳钢复合板的显微组织显示方法，其特征在于显示方法如下：
将磨制、抛光好的试样在加热至80℃的第一腐蚀剂(10克铁氰化钾+10克氢氧化钾+100ml蒸馏水)中浸蚀1min，显微组织显示后迅速流水冲洗、喷无水乙醇、吹干；再用滴管滴第二腐蚀剂(4ml硝酸+96ml的无水乙醇)于试样抛光面上，组织显示后迅速流水冲洗、喷无水乙醇、并吹干后用光学显微镜观察试样。
实施例2：一种双相不锈钢-碳钢复合板的显微组织显示方法，其特征在于显示方法如下：
将磨制、抛光好的试样在加热至85℃的第一腐蚀剂(10克铁氰化钾+10克氢氧化钾+100ml蒸馏水)中浸蚀1.5min，显微组织显示后迅速流水冲洗、喷无水乙醇、吹干；再用滴管滴第二腐蚀剂(4ml硝酸+96ml的无水乙醇)于试样抛光面上，组织显示后迅速流水冲洗、喷无水乙醇、并吹干后用光学显微镜观察试样。
实施例3：一种双相不锈钢-碳钢复合板的显微组织显示方法，其特征在于显示方法如下：
将磨制、抛光好的试样在加热至90℃的第一腐蚀剂(10克铁氰化钾+10克氢氧化钾+100ml蒸馏水)中浸蚀2min，显微组织显示后迅速流水冲洗、喷无水乙醇、吹干；再用滴管滴第二腐蚀剂(4ml硝酸+96ml的无水乙醇)于试样抛光面上，组织显示后迅速流水冲洗、喷无水乙醇、并吹干后观察试样。

Claims (1)

1.一种双相不锈钢-碳钢复合板的显微组织显示方法，其特征在于本发明采用第一腐蚀剂和第二腐蚀剂组合，使耐蚀性能差异很大的两种材料的显微组织先后都能显示出来，可以同时观察到两种材料清晰的显微组织，所述显示方法步骤如下：
首先将磨制、抛光好的试样在加热至80～90℃的第一腐蚀剂中浸蚀1～2min，显微组织显示后迅速流水冲洗、喷淋无水乙醇、吹干；再用滴管滴第二腐蚀剂于试样抛光面上，组织显示后迅速流水冲洗、喷淋无水乙醇、并吹干后观察试样，其中所述第一腐蚀剂为10克铁氰化钾+10克氢氧化钾+100ml蒸馏水，所述第二腐蚀剂为4ml硝酸+96ml的无水乙醇。
CN201310368367.4A 2013-08-21 2013-08-21 一种双相不锈钢-碳钢复合板的显微组织显示方法 Active CN103398889B (zh)