CN105063621B - 一种镁合金金相腐蚀剂 - Google Patents

一种镁合金金相腐蚀剂 Download PDF

Info

Publication number
CN105063621B
CN105063621B CN201510476698.9A CN201510476698A CN105063621B CN 105063621 B CN105063621 B CN 105063621B CN 201510476698 A CN201510476698 A CN 201510476698A CN 105063621 B CN105063621 B CN 105063621B
Authority
CN
China
Prior art keywords
magnesium alloy
etching agent
parts
acid
oxalic acid
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201510476698.9A
Other languages
English (en)
Other versions
CN105063621A (zh
Inventor
张清
陈君
李全安
李萍
朱利敏
张兴渊
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Henan University of Science and Technology
Original Assignee
Henan University of Science and Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Henan University of Science and Technology filed Critical Henan University of Science and Technology
Priority to CN201510476698.9A priority Critical patent/CN105063621B/zh
Publication of CN105063621A publication Critical patent/CN105063621A/zh
Application granted granted Critical
Publication of CN105063621B publication Critical patent/CN105063621B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种镁合金金相腐蚀剂，属于镁合金金相试验技术领域。本发明的镁合金金相腐蚀剂由草酸和如下体积份数的组分组成：质量百分比浓度为68％的硝酸1‑3份、质量百分比浓度为98％的醋酸2‑4份、乙醇100份；所述草酸的量为每100mL乙醇采用10‑15g的草酸。本发明的镁合金金相腐蚀剂可以快速、有效地对镁合金进行腐蚀，而且腐蚀时间可精确控制。

Description

一种镁合金金相腐蚀剂
技术领域
本发明涉及一种镁合金金相腐蚀剂，属于镁合金金相试验技术领域。
背景技术
镁合金作为实际应用中最轻的金属材料，具有密度小、比强度高、比刚度高、切削加工性能好等特点，具有其他材料不可替代的优势，在许多领域都得到了广泛的应用。
由于材料成分的差别、热处理工艺的差别，往往会得到不同类型的镁合金组织，进而导致最终合金的性能也有所差别。为了获得所需要的镁合金，就要在镁合金的研究和生产中，对合金的金相组织进行观察，并结合性能测试数据，及时调整合金的成分和热处理工艺。镁合金的金相试验通常采用化学浸蚀法，即采用合适的金相腐蚀剂实现镁合金组织的显示。
现有技术中的镁合金金相腐蚀剂，通常是由硝酸、盐酸、水组成，由于这种腐蚀剂腐蚀性较强，而镁合金的耐腐蚀性非常差，因此，在腐蚀过程中，合金的晶界难以清楚地显示。而且，镁合金在腐蚀过程中的腐蚀时间非常难以精确控制，时间过短，晶界难以清洗显示出来，腐蚀时间过长，则会在金相试样表面形成一层难以除去的氧化物薄膜，导致表面模糊不清，第二相难以辨认，对金相组织的观察和分析产生严重的影响。因此，需要对镁合金金相腐蚀剂进行有效改进，以提高镁合金金相组织观察和分析的准确性。
发明内容
本发明的目的在于提供一种腐蚀效果好且腐蚀时间可精确控制的镁合金金相腐蚀剂。
为了实现以上目的，本发明的镁合金金相腐蚀剂的技术方案如下：
一种镁合金金相腐蚀剂，由草酸和如下体积份数的组分组成：质量百分比浓度为68％的硝酸1-3份、质量百分比浓度为98％的醋酸2-4份、乙醇100份；所述草酸的量为每100mL乙醇采用10-15g的草酸。
本发明的镁合金金相腐蚀剂的组分包括硝酸、草酸、醋酸，其中硝酸为强酸，草酸为中强酸，醋酸为弱酸，三者协同作用，保证了腐蚀剂的酸性适中，而且草酸的量相对于硝酸和醋酸的来说较多一些，避免了酸性过强或过弱，保证了腐蚀剂的腐蚀速度适中，避免腐蚀速度过快或者过慢，增强了腐蚀时间的可控制性。
为了进一步提高本发明的镁合金金相腐蚀剂的腐蚀效果，所述镁合金金相腐蚀剂由草酸和如下体积份数的组分组成：质量百分比浓度为68％的硝酸2份、质量百分比浓度为98％的醋酸3份、乙醇100份；所述草酸的量为每100mL乙醇采用12g的草酸。
将上述硝酸、草酸、醋酸加入乙醇中，混匀即得所述镁合金金相腐蚀剂。配制方法简单，而且各组分均为常规试剂，可以使本发明的镁合金金相腐蚀剂的使用更加方便。
将抛光后的镁合金试样在所述镁合金金相腐蚀剂中浸泡5-10s，用乙醇清洗，在空气中晾干或者用滤纸吸干，即得腐蚀后的镁合金试样。
本发明的镁合金金相腐蚀剂能够控制腐蚀的速度呈现均匀稳定的态势，使腐蚀时间能够较为精确地控制，整体上也缩短了腐蚀时间，使用本发明的镁合金金相腐蚀剂的腐蚀时间只需5-10s。使用本发明的金相腐蚀剂，能够清晰地显示镁合金的金相组织。特别的，本发明的金相腐蚀剂对热处理态镁合金具有良好的效果，能够使其金相组织清晰地显示出来。
具体实施方式
下面结合具体实施例对本发明的技术方案进行进一步的说明。各实施例中涉及的硝酸、草酸、醋酸及乙醇均为市售产品。
实施例1
本实施例的镁合金金相腐蚀剂，由如下组分组成：质量百分比浓度为68％的硝酸1mL、草酸15g、质量百分比浓度为98％的醋酸4mL、乙醇100mL。
将100mL乙醇加入烧杯中，加入1mL质量百分比浓度为68％的硝酸、15g草酸、4mL质量百分比浓度为98％的醋酸，搅拌混合均匀即得镁合金金相腐蚀剂。
将抛光后的镁合金试样浸入上述制备好的镁合金金相腐蚀剂中，浸蚀5s，取出，用乙醇冲洗，在空气中晾干，即得到腐蚀后的镁合金试样。
实施例2
本实施例的镁合金金相腐蚀剂，由如下组分组成：质量百分比浓度为68％的硝酸2mL、草酸12g、质量百分比浓度为98％的醋酸3mL、乙醇100mL。
将100mL乙醇加入烧杯中，加入2mL质量百分比浓度为68％的硝酸、12g草酸、3mL质量百分比浓度为98％的醋酸，搅拌混合均匀即得镁合金金相腐蚀剂。
将抛光后的镁合金试样浸入上述制备好的镁合金金相腐蚀剂中，浸蚀7s，取出，用乙醇冲洗，在空气中晾干，即得到腐蚀后的镁合金试样。
实施例3
本实施例的镁合金金相腐蚀剂，由如下组分组成：质量百分比浓度为68％的硝酸3mL、草酸10g、质量百分比浓度为98％的醋酸2mL、乙醇100mL。
将100mL乙醇加入烧杯中，加入3mL质量百分比浓度为68％的硝酸、10g草酸、2mL质量百分比浓度为98％的醋酸，搅拌混合均匀即得镁合金金相腐蚀剂。
将抛光后的镁合金试样浸入上述制备好的镁合金金相腐蚀剂中，浸蚀10s，取出，用乙醇冲洗，用滤纸吸干，即得到腐蚀后的镁合金试样。
本发明的镁合金金相腐蚀剂的腐蚀时间短，使用本发明的镁合金金相腐蚀剂的腐蚀时间只需5-10s，而且能够精确控制。特别的，本发明的金相腐蚀剂对热处理态镁合金具有良好的效果，能够使其金相组织清晰地显示出来。

Claims (2)

1.一种镁合金金相腐蚀剂，其特征在于，由草酸和如下体积份数的组分组成：质量百分比浓度为68%的硝酸1-2份、质量百分比浓度为98%的醋酸3-4份、乙醇100份；所述草酸的量为每100mL乙醇采用12-15g的草酸。
2.如权利要求1所述的镁合金金相腐蚀剂，其特征在于，由草酸和如下体积份数的组分组成：质量百分比浓度为68%的硝酸2份、质量百分比浓度为98%的醋酸3份、乙醇100份；所述草酸的量为每100mL乙醇采用12g的草酸。
CN201510476698.9A 2015-08-06 2015-08-06 一种镁合金金相腐蚀剂 Expired - Fee Related CN105063621B (zh)