CN103360869A - 一种高附着力镜面油墨 - Google Patents

一种高附着力镜面油墨 Download PDF

Info

Publication number
CN103360869A
CN103360869A CN2013102830591A CN201310283059A CN103360869A CN 103360869 A CN103360869 A CN 103360869A CN 2013102830591 A CN2013102830591 A CN 2013102830591A CN 201310283059 A CN201310283059 A CN 201310283059A CN 103360869 A CN103360869 A CN 103360869A
Authority
CN
China
Prior art keywords
parts
adhesion
ink
mirror effect
adhesive force
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2013102830591A
Other languages
English (en)
Inventor
沈届秋
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SUZHO AOTU COLOR PRINTING FACTORY
Original Assignee
SUZHO AOTU COLOR PRINTING FACTORY
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SUZHO AOTU COLOR PRINTING FACTORY filed Critical SUZHO AOTU COLOR PRINTING FACTORY
Priority to CN2013102830591A priority Critical patent/CN103360869A/zh
Publication of CN103360869A publication Critical patent/CN103360869A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种高附着力镜面油墨，其原料的重量份数组成为：环氧丙烯酸树脂80-150份、乙二醇单丁醚20-80份、纳米级铝粉60-120份、色料20-50份、分散剂1-10份、消泡剂1-10份、附着力促进剂1-10份。所述色料为永固黄、酞菁蓝、金光红中的一种或几种的混合物；所述分散剂为聚乙烯蜡。所述消泡剂为聚二甲基硅氧烷。本发明提供的油墨制造工艺简单、印刷效果良好、镜面光泽优异，且与基材的附着力较高，不易脱落，可广泛应用于电器、家具的装饰。

Description

一种高附着力镜面油墨
技术领域
本发明涉及一种油墨，尤其涉及一种高附着力镜面油墨。
背景技术
近年来，科技水平不断进步，人类生活水平持续提高，人们对家居装饰的要求也越来越高，对于装饰表面除了要求具有丰富的色彩和立体感外，还要求表面具有镜面效果。目前，市场上已出现多种镜面油墨，然而据大多数镜面油墨制造工艺简单、镜面效果不佳，而且附着力较低，一段时间后容易出现油膜脱落的现象，影响使用以及美观。
发明内容
解决的技术问题：针对现有技术的不足，本发明提供了一种高附着力镜面油墨，其制造工艺简单、印刷效果良好、镜面光泽优异，且与基材的附着力较高。
技术方案：本发明提供了一种高附着力镜面油墨，其原料的重量份数组成为：环氧丙烯酸树脂80-150份、乙二醇单丁醚20-80份、纳米级铝粉60-120份、色料20-50份、分散剂1-10份、消泡剂1-10份、附着力促进剂1-10份。
所述色料为永固黄、酞菁蓝、金光红中的一种或几种的混合物。
所述分散剂为聚乙烯蜡。所述消泡剂为聚二甲基硅氧烷。
作为优选方案，上述高附着力镜面油墨，其原料的重量份数组成为：环氧丙烯酸树脂100-120份、乙二醇单丁醚40-60份、纳米级铝粉80-100份、色料30-40份、分散剂4-8份、消泡剂4-8份、附着力促进剂4-8份。
有益效果：本发明制造工艺简单、印刷效果良好、镜面光泽优异。通过添加附着力促进剂，增强了油墨与基材的附着力，印刷后油膜不易脱落，可广泛应用于电器、家具的装饰。
具体实施方式
下面通过实施例的方式进一步说明本说明，本发明的范围并不因此局限于下述实施例。
实施例1
环氧丙烯酸树脂                 100份
乙二醇单丁醚                   40份
纳米级铝粉                     80份
永固黄                         30份
聚乙烯蜡                       4份
聚二甲基硅氧烷                 4份
附着力促进剂                   4份
将上述原料按重量份数混合加入搅拌机，先高速搅拌1小时，再低速搅拌30分钟，使原料完全混合，将上述混合均匀的物料经三辊机研磨分散后得到黄色镜面油墨。
实施例2
环氧丙烯酸树脂                 110份
乙二醇单丁醚                   50份
纳米级铝粉                     90份
酞菁蓝                         35份
聚乙烯蜡                       6份
聚二甲基硅氧烷                 6份
附着力促进剂                   6份
将上述原料按重量份数混合加入搅拌机，先高速搅拌1小时，再低速搅拌30分钟，使原料完全混合，将上述混合均匀的物料经三辊机研磨分散后得到蓝色镜面油墨。
实施例3
环氧丙烯酸树脂                 120份
乙二醇单丁醚                   60份
纳米级铝粉                     100份
金光红                         40份
聚乙烯蜡                       8份
聚二甲基硅氧烷                 8份
附着力促进剂                   8份
将上述原料按重量份数混合加入搅拌机，先高速搅拌1小时，再低速搅拌30分钟，使原料完全混合，将上述混合均匀的物料经三辊机研磨分散后得到红色镜面油墨。
实施例4
环氧丙烯酸树脂                 110份
乙二醇单丁醚                   50份
纳米级铝粉                     90份
永固黄                         35份
聚乙烯蜡                       6份
聚二甲基硅氧烷                 6份
附着力促进剂                   6份
将上述原料按重量份数混合加入搅拌机，先高速搅拌1小时，再低速搅拌30分钟，使原料完全混合，将上述混合均匀的物料经三辊机研磨分散后得到黄色镜面油墨。
实施例5
环氧丙烯酸树脂                 110份
乙二醇单丁醚                   50份
纳米级铝粉                     90份
金光红                         35份
聚乙烯蜡                       6份
聚二甲基硅氧烷                 6份
附着力促进剂                   6份
将上述原料按重量份数混合加入搅拌机，先高速搅拌1小时，再低速搅拌30分钟，使原料完全混合，将上述混合均匀的物料经三辊机研磨分散后得到红色镜面油墨。
对上述各实施例制得的镜面油墨进行性能测试，测试结果如下：
测试项目 实施例1 实施例2 实施例3 实施例4 实施例5
颜色 黄 蓝 红 黄 红
细度（μm）
Figure 302136DEST_PATH_IMAGE002
10
Figure 219276DEST_PATH_IMAGE002
10
Figure 185964DEST_PATH_IMAGE002
10
Figure 581173DEST_PATH_IMAGE002
10
Figure 333229DEST_PATH_IMAGE002
10
附着力（划格法） 100/100 100/100 100/100 100/100 100/100

Claims (5)

1.一种高附着力镜面油墨，其特征在于原料的重量份数组成为：环氧丙烯酸树脂80-150份、乙二醇单丁醚20-80份、纳米级铝粉60-120份、色料20-50份、分散剂1-10份、消泡剂1-10份、附着力促进剂1-10份。
2.根据权利要求1所述的一种高附着力镜面油墨，其特征在于：所述色料为永固黄、酞菁蓝、金光红中的一种或几种的混合物。
3.根据权利要求1所述的一种高附着力镜面油墨，其特征在于：所述分散剂为聚乙烯蜡。
4.根据权利要求1所述的一种高附着力镜面油墨，其特征在于：所述消泡剂为聚二甲基硅氧烷。
5.根据权利要求1所述的一种高附着力镜面油墨，其特征在于它由下列重量份数的原料组成：环氧丙烯酸树脂100-120份、乙二醇单丁醚40-60份、纳米级铝粉80-100份、色料30-40份、分散剂4-8份、消泡剂4-8份、附着力促进剂4-8份。
CN2013102830591A 2013-07-08 2013-07-08 一种高附着力镜面油墨 Pending CN103360869A (zh)