CN103352154A - 高强度铝合金线材及制备方法 - Google Patents

高强度铝合金线材及制备方法 Download PDF

Info

Publication number
CN103352154A
CN103352154A CN2013102717387A CN201310271738A CN103352154A CN 103352154 A CN103352154 A CN 103352154A CN 2013102717387 A CN2013102717387 A CN 2013102717387A CN 201310271738 A CN201310271738 A CN 201310271738A CN 103352154 A CN103352154 A CN 103352154A
Authority
CN
China
Prior art keywords
aluminium
silicon
zinc
tantalum
magnesium
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2013102717387A
Other languages
English (en)
Other versions
CN103352154B (zh
Inventor
周宏胜
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
TONGLING XINGYI METAL MATERIALS CO Ltd
Original Assignee
TONGLING XINGYI METAL MATERIALS CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TONGLING XINGYI METAL MATERIALS CO Ltd filed Critical TONGLING XINGYI METAL MATERIALS CO Ltd
Priority to CN201310271738.7A priority Critical patent/CN103352154B/zh
Publication of CN103352154A publication Critical patent/CN103352154A/zh
Application granted granted Critical
Publication of CN103352154B publication Critical patent/CN103352154B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种高强度铝合金线材及其制备方法，其特征在于含有以下重量百分比的成分：硅0.2-0.3、锌0.55-0.75、钽0.1-0.2、钛0.03-0.05、铁0.12-0.14、镁0.08-0.12、余量为铝。本发明原料中含有Si能够进一步提高铝合金线材的强度，本发明通过硅、锌、钽的配合，用量的优化，使得在提高强度的同时，不影响导电率。

Description

高强度铝合金线材及制备方法
技术领域
本发明属于合金线材制造技术领域，具体涉及一种用于输电线路上的高强度铝导线材及其制造工艺。
背景技术
以往，我国作为输电线用的电线主要成分是铜。但由于铜价格高，成本高，加上现在技术进步，铝合金导线的应用比例在不断的增加。现在输电线路上用的普通钢芯铝导线、铝包钢芯导线、耐热铝导线和高强铝导线等等。但现有的铝合金线材存在导电率不高、强度不高、不耐热、不同环境中导电率差异大、线耗高等一系列问题。
发明内容
本发明的目的是提供一种高强度铝合金线材及其制备方法，生产的铝合金线材能满足高强、高导和耐热的要求。
 本发明技术方案如下：
一种高强度铝合金线材，其特征在于含有以下重量百分比的成分：硅0.2-0.3、锌0.55-0.75、钽0.1-0.2、钛0.03-0.05、铁0.12-0.14、镁0.08-0.12、余量为铝。
高强度铝合金线材的制备方法，其特征在于包括以下步骤：
（1）、按硅、锌、钽质量比2：5：1的比例将硅、锌、钽粉末投入炉中熔化，精炼后浇注制取硅锌钽合金块；按钛、铁、镁按质量比3：10：6的比例将钛、铁、镁粉末投入炉中熔化，精炼后浇注制取钛铁镁合金块；
（2）、按原料配方，将铝块加入炉中升温至730-740℃下熔化，然后，再升温至780-790℃下，加入硅锌钽合金块后，充分混合后，再加入钛铁镁合金块及其它合金配料成分，充分混合后，通入精炼剂进行精炼、扒渣；再对铝液进行炉前化学快速分析，分析后根据配方中各组分的重量比调整铝液组分，对铝液进行补料；
（3）、保温：将步骤1 所得铝液在720-730℃下保温15-20min ；
（4）、连铸连轧成铝合金杆、拉丝机拉制成铝合金单线，控制润滑温度不高于90℃；
（5）、时效热处理，将铝合金单线放入240-250℃热处理炉中，处理时间为3-4h，再以3-4℃/分钟速率升温至290-310℃，保温2-3小时，再在120-130℃热处理炉中，处理时间为4-5小时。
本发明原料中含有Si 能够进一步提高铝合金线材的强度，本发明通过硅、锌、钽的配合，用量的优化，使得在提高强度的同时，不影响导电率。
本发明中稀土元素加入到铝合金中可起到微合金化的作用；此外，它与氢等气体和许多非金属有较强的亲和力，能生成熔点高的化合物，故它有一定的除氢、精炼、净化作用；同时，稀土元素化学活性极强，它可以在长大的晶粒界面上选择性地吸附，阻碍晶粒的生长，结果导致晶粒细化，有变质的作用。
本发明铝合金导线与现有的铝合金导线相比，同时具有高强度和高导电率，抗拉强度达到215Mpa 以上，导电率可达到60.0％IACS 以上，耐热性能长期运行达到180℃以上的高强度高导电率耐热铝合金导线，可以有效增加导线输电能力。
具体实施方式
一种高强度铝合金线材，含有以下重量百分比的成分：硅0.2-0.3、锌0.55-0.75、钽0.1-0.2、钛0.03-0.05、铁0.12-0.14、镁0.08-0.12、余量为铝。
高强度铝合金线材的制备方法，其特征在于包括以下步骤：
（1）、按硅、锌、钽质量比2：5：1的比例将硅、锌、钽粉末投入炉中熔化，精炼后浇注制取硅锌钽合金块；按钛、铁、镁按质量比3：10：6的比例将钛、铁、镁粉末投入炉中熔化，精炼后浇注制取钛铁镁合金块；
（2）、按原料配方，将铝块加入炉中升温至730-740℃下熔化，然后，再升温至780-790℃下，加入硅锌钽合金块后，充分混合后，再加入钛铁镁合金块及其它合金配料成分，充分混合后，通入精炼剂进行精炼、扒渣；再对铝液进行炉前化学快速分析，分析后根据配方中各组分的重量比调整铝液组分，对铝液进行补料；检测含量符合要求。
（3）、保温：将步骤1 所得铝液在720-730℃下保温15-20min ；
（4）、连铸连轧成铝合金杆、拉丝机拉制成铝合金单线，控制润滑温度不高于90℃；
（5）、时效热处理，将铝合金单线放入240-250℃热处理炉中，处理时间为3-4h，再以3-4℃/分钟速率升温至290-310℃，保温2-3小时，再在120-130℃热处理炉中，处理时间为4-5小时。
经测试其强度215Mpa，导电率为60.0％ IACS，长期耐热180℃强度残存率为81％，伸长率为3.11％，蠕变率低于0.01％。

Claims (2)

1.一种高强度铝合金线材，其特征在于含有以下重量百分比的成分：硅0.2-0.3、锌0.55-0.75、钽0.1-0.2、钛0.03-0.05、铁0.12-0.14、镁0.08-0.12、余量为铝。
2.根据权利要求1所述的高强度铝合金线材的制备方法，其特征在于包括以下步骤：
（1）、按硅、锌、钽质量比2：5：1的比例将硅、锌、钽粉末投入炉中熔化，精炼后浇注制取硅锌钽合金块；按钛、铁、镁按质量比3：10：6的比例将钛、铁、镁粉末投入炉中熔化，精炼后浇注制取钛铁镁合金块；
（2）、按原料配方，将铝块加入炉中升温至730-740℃下熔化，然后，再升温至780-790℃下，加入硅锌钽合金块后，充分混合后，再加入钛铁镁合金块及其它合金配料成分，充分混合后，通入精炼剂进行精炼、扒渣；再对铝液进行炉前化学快速分析，分析后根据配方中各组分的重量比调整铝液组分，对铝液进行补料；
（3）、保温：将步骤1 所得铝液在720-730℃下保温15-20min ；
（4）、连铸连轧成铝合金杆、拉丝机拉制成铝合金单线，控制润滑温度不高于90℃；
（5）、时效热处理，将铝合金单线放入240-250℃热处理炉中，处理时间为3-4h，再以3-4℃/分钟速率升温至290-310℃，保温2-3小时，再在120-130℃热处理炉中，处理时间为4-5小时。
CN201310271738.7A 2013-07-01 2013-07-01 高强度铝合金线材及制备方法 Active CN103352154B (zh)