CN103352156B - 防止热裂铝合金线材及制备方法 - Google Patents
防止热裂铝合金线材及制备方法 Download PDFInfo
- Publication number
- CN103352156B CN103352156B CN201310272671.9A CN201310272671A CN103352156B CN 103352156 B CN103352156 B CN 103352156B CN 201310272671 A CN201310272671 A CN 201310272671A CN 103352156 B CN103352156 B CN 103352156B
- Authority
- CN
- China
- Prior art keywords
- aluminium
- titanium
- beryllium
- cerium
- lanthanum
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
一种防止热裂铝合金线材及其制备方法,其特征在于其中含有下列重量百分比的成分:钛0.02-0.032、铜0.8-1.0、铍0.021-0.032、铈0.12-0.15、镨0.03-0.04、钕0.011-0.013、镧0.022-0.025、余量为铝。本发明铝合金中加入微量的钛,能显著细化铝合金的晶粒组织,提高合金的机械性能,降低合金的热裂倾向,但会降低导电率。本发明通过钛与铜、铍等的配合,改善其导电率,达到较好的效果。
Description
技术领域
本发明属于合金线材制造技术领域,具体涉及一种用于输电线路上的高强度、高导电率以及防止热裂铝合金线材及其制造工艺。
背景技术
以往,我国作为输电线用的电线主要成分是铜。但由于铜价格高,成本高,加上现在技术进步,铝合金导线的应用比例在不断的增加。现在输电线路上用的普通钢芯铝导线、铝包钢芯导线、耐热铝导线和高强铝导线等等。但现有的铝合金线材存在导电率不高、强度不高、不耐热、不同环境中导电率差异大、线耗高等一系列问题。
发明内容
本发明的目的是提供一种防止热裂铝合金线材及其制备方法,生产的铝合金线材能满足高强、高导和防热裂的要求。
本发明技术方案如下:
一种防止热裂铝合金线材,其特征在于其中含有下列重量百分比的成分:钛0.02-0.032、铜0.8-1.0、铍0.021-0.032、铈0.12-0.15、镨0.03-0.04、钕0.011-0.013、镧0.022-0.025、余量为铝。
防止热裂铝合金线材的制备方法,其特征在于包括以下步骤:
(1)、按钛、铍、铈质量比2:2:1的比例将钛、铍、铈粉末投入炉中熔化,精炼后浇注制取钛铍铈合金块;按镨、钕、镧按质量比3:1:2的比例将镨、钕、镧粉末投入炉中熔化,精炼后浇注制取镨钕镧合金块;
(2)、按原料配方,将铝块加入炉中升温至730-740℃下熔化,然后,再升温至780-790℃下,加入钛铍铈合金块后,充分混合后,再加入镨钕镧合金块及其它合金配料成分,充分混合后,通入精炼剂进行精炼、扒渣;再对铝液进行炉前化学快速分析,分析后根据配方中各组分的重量比调整铝液组分,对铝液进行补料;
(3)、保温:将步骤1所得铝液在720-730℃下保温15-20min;
(4)、连铸连轧成铝合金杆、拉丝机拉制成铝合金单线,控制润滑温度不高于90℃;
(5)、时效热处理,放入320-330℃热处理炉中处理4-5小时,然后,以4-5℃/分钟速率降温至130-140℃,保温3-4小时,再以6-8℃/分钟速度升温至220-230℃,保温2-3小时;再自然冷却至室温即可。
本发明铝合金中加入微量的钛,能显著细化铝合金的晶粒组织,提高合金的机械性能,降低合金的热裂倾向,但会降低导电率。本发明通过钛与铜、铍等的配合,改善其导电率,达到较好的效果。
本发明中稀土元素加入到铝合金中可起到微合金化的作用;此外,它与氢等气体和许多非金属有较强的亲和力,能生成熔点高的化合物,故它有一定的除氢、精炼、净化作用;同时,稀土元素化学活性极强,它可以在长大的晶粒界面上选择性地吸附,阻碍晶粒的生长,结果导致晶粒细化,有变质的作用。
本发明铝合金导线与现有的铝合金导线相比,同时具有高强度和高导电率,抗拉强度达到225Mpa以上,导电率可达到61.0%IACS以上,耐热性能长期运行达到100℃以上的高强度高导电率耐热铝合金导线,可以有效增加导线输电能力。
具体实施方式
一种防止热裂铝合金线材,其中含有下列重量百分比的成分:钛0.02-0.032、铜0.8-1.0、铍0.021-0.032、铈0.12-0.15、镨0.03-0.04、钕0.011-0.013、镧0.022-0.025、余量为铝。
防止热裂铝合金线材的制备方法,其特征在于包括以下步骤:
(1)、按钛、铍、铈质量比2:2:1的比例将钛、铍、铈粉末投入炉中熔化,精炼后浇注制取钛铍铈合金块;按镨、钕、镧按质量比3:1:2的比例将镨、钕、镧粉末投入炉中熔化,精炼后浇注制取镨钕镧合金块;
(2)、按原料配方,将铝块加入炉中升温至730-740℃下熔化,然后,再升温至780-790℃下,加入钛铍铈合金块后,充分混合后,再加入镨钕镧合金块及其它合金配料成分,充分混合后,通入精炼剂进行精炼、扒渣;再对铝液进行炉前化学快速分析,分析后根据配方中各组分的重量比调整铝液组分,对铝液进行补料;
(3)、保温:将步骤1所得铝液在720-730℃下保温15-20min;
(4)、连铸连轧成铝合金杆、拉丝机拉制成铝合金单线,控制润滑温度不高于90℃;
(5)、时效热处理,放入320-330℃热处理炉中处理4-5小时,然后,以4-5℃/分钟速率降温至130-140℃,保温3-4小时,再以6-8℃/分钟速度升温至220-230℃,保温2-3小时;再自然冷却至室温即可。
经测试其强度225Mpa,导电率为61.0%IACS,长期耐热180℃强度残存率为82%,伸长率为2.91%,蠕变率低于0.01%。
Claims (2)
1.一种防止热裂铝合金线材,其特征在于其中含有下列重量百分比的成分:钛0.02-0.032、铜0.8-1.0、铍0.021-0.032、铈0.12-0.15、镨0.03-0.04、钕0.011-0.013、镧0.022-0.025、余量为铝。
2.根据权利要求1所述的防止热裂铝合金线材的制备方法,其特征在于包括以下步骤:
(1)、按钛、铍、铈质量比2:2:1的比例将钛、铍、铈粉末投入炉中熔化,精炼后浇注制取钛铍铈合金块;按镨、钕、镧按质量比3:1:2的比例将镨、钕、镧粉末投入炉中熔化,精炼后浇注制取镨钕镧合金块;
(2)、按原料配方,将铝块加入炉中升温至730-740℃下熔化,然后,再升温至780-790℃下,加入钛铍铈合金块后,充分混合后,再加入镨钕镧合金块及其它合金配料成分,充分混合后,通入精炼剂进行精炼、扒渣;再对铝液进行炉前化学快速分析,分析后根据配方中各组分的重量比调整铝液组分,对铝液进行补料;
(3)、保温:将步骤(2)所得铝液在720-730℃下保温15-20min;
(4)、连铸连轧成铝合金杆、拉丝机拉制成铝合金单线,控制润滑温度不高于90℃;
(5)、时效热处理,放入320-330℃热处理炉中处理4-5小时,然后,以4-5℃/分钟速率降温至130-140℃,保温3-4小时,再以6-8℃/分钟速度升温至220-230℃,保温2-3小时;再自然冷却至室温即可。