CN103333615A - 一种浅色松香及其生产方法 - Google Patents
一种浅色松香及其生产方法 Download PDFInfo
- Publication number
- CN103333615A CN103333615A CN201310222861XA CN201310222861A CN103333615A CN 103333615 A CN103333615 A CN 103333615A CN 201310222861X A CN201310222861X A CN 201310222861XA CN 201310222861 A CN201310222861 A CN 201310222861A CN 103333615 A CN103333615 A CN 103333615A
- Authority
- CN
- China
- Prior art keywords
- rosin
- metal catalyst
- pale
- production method
- pale rosin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种浅色松香及其生产方法,该浅色松香重量组份为:特级松香95~100千克、脱色剂0.1~0.4千克,非贵金属催化剂0.1~0.5千克;其生产方法包括下列步骤:A、将特级松香溶解后,进入蒸馏釜,同时投入脱色剂和非贵金属催化剂,在200℃~220℃温度下带真空蒸馏进行初馏;B、将初馏后的物料加温至270℃±10℃带真空蒸馏进行中馏;3、将中馏后的物料降温至140~160℃后即可。采用本发明,通过脱色剂进行脱色,又通过非贵金属催化剂进行了部分歧化,使浅色松香的能达到一号色至无色之间,同时稳定性得到了很大程度的提高,可以直接应用在对色泽要求较高的某些胶黏剂和涂料行业。
Description
技术领域
本发明涉及一种浅色松香及其生产方法。
背景技术
目前市场上的所谓的无色松香颜色在二号色左右,颜色较深、稳定性较差、应用范围较小,尤其不适用于某些胶黏剂和涂料行业。
发明内容
本发明的目的是提供能达到一号色至无色之间,且稳定性好的一种浅色松香及其生产方法。
本发明采取的技术方案是:一种浅色松香,其特征在于其重量组份为:特级松香 95~100千克、脱色剂0.1~0.4千克,非贵金属催化剂0.1~0.5千克。
所述的一种浅色松香的生产方法,其特征在于它包括下列步骤:A、将特级松香溶解后,进入蒸馏釜,同时投入脱色剂和非贵金属催化剂,在200℃~220℃温度下带真空蒸馏进行初馏;B、将初馏后的物料加温至270℃±10℃带真空蒸馏进行中馏;3、将中馏后的物料降温至140~160℃后即可。
采用本发明,通过脱色剂进行脱色,又通过非贵金属催化剂进行了部分歧化,使浅色松香的能达到一号色至无色之间,同时稳定性得到了很大程度的提高,可以直接应用在对色泽要求较高的某些胶黏剂和涂料行业。
具体实施方式
下面结合具体的实施例对本发明作进一步说明。该浅色松香的生产方法包括下列步骤:
一、将特级松香95~100千克溶解后,进入蒸馏釜,同时投入脱色剂0.1~0.4千克,非贵金属催化剂0.1~0.5千克,在200℃~220℃温度下带真空蒸馏进行初馏,去除其中重油;
二、将经过初馏后的物料加温至270℃±10℃带真空蒸馏进行中馏,去除其中的黑香;
三、将经过中馏后的物料降温至140~160℃后放入镀锌铁桶进行包装即可;
通过上述蒸馏过程中添加的脱色剂和非贵金属催化剂,使浅色松香在精制的同时进行了脱色和歧化处理,使浅色松香的色泽达到一号色至无色之间,且稳定性得到了很大程度的提高,可以直接应用在对色泽要求较高的某些胶黏剂和涂料行业。
Claims (2)
1.一种浅色松香,其特征在于其重量组份为:特级松香 95~100千克、脱色剂0.1~0.4千克,非贵金属催化剂0.1~0.5千克。
2.根据权利要求1所述的一种浅色松香,其特征在于其生产方法包括下列步骤:A、将特级松香溶解后,进入蒸馏釜,同时投入脱色剂和非贵金属催化剂,在200℃~220℃温度下带真空蒸馏进行初馏;B、将初馏后的物料加温至270℃±10℃带真空蒸馏进行中馏;3、将中馏后的物料降温至140~160℃后即可。