CN103320821A - 一种碱性锌钴合金电镀液 - Google Patents

一种碱性锌钴合金电镀液 Download PDF

Info

Publication number
CN103320821A
CN103320821A CN2013102922254A CN201310292225A CN103320821A CN 103320821 A CN103320821 A CN 103320821A CN 2013102922254 A CN2013102922254 A CN 2013102922254A CN 201310292225 A CN201310292225 A CN 201310292225A CN 103320821 A CN103320821 A CN 103320821A
Authority
CN
China
Prior art keywords
parts
cobalt alloy
gram
alkaline zinc
sodium
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2013102922254A
Other languages
English (en)
Other versions
CN103320821B (zh
Inventor
葛黔峰
谭润清
袁丽红
魏雯
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guiyang Huake Electroplating Co Ltd
Original Assignee
Guiyang Huake Electroplating Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guiyang Huake Electroplating Co Ltd filed Critical Guiyang Huake Electroplating Co Ltd
Priority to CN201310292225.4A priority Critical patent/CN103320821B/zh
Publication of CN103320821A publication Critical patent/CN103320821A/zh
Application granted granted Critical
Publication of CN103320821B publication Critical patent/CN103320821B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种碱性锌钴合金电镀液，其特征在于：按重量计，在1000份电镀液中包括以下物质，氧化锌7-20份、氢氧化钠130-170份、硫酸钴3-12份、三乙醇胺15-25份、柠檬酸胺5-10份、酒石酸30-35份、苄基吡啶鎓羧酸钠0.1-0.6份、植酸钠0.1-0.5份、二甲胺2-5份、硫脲0.3-0.5份、洋茉莉醛0.02-0.05份，剩余为水。经申请人试验，通过本发明的电镀液配方得到的电镀产品，中性盐雾试验300小时不出白锈。同现有技术相比，具有合金成分钴含量容易控制，镀液深镀能力、均镀能力好，操作方便，镀液稳定等优点。

Description

一种碱性锌钴合金电镀液
 
技术领域
本发明涉及一种碱性锌钴合金电镀液，属于合金电镀技术领域。
背景技术
锌合金电镀近年来发展迅猛，如锌铁合金电镀、锌镍合金电镀及锌钴合金电镀等技术，由于优异的耐腐蚀性能，应用越来越广泛；锌钴合金电镀具有镀层含钴量少，耐蚀性高，容易钝化成彩色、白色、黑色和橄榄色等各种颜色等优点。现有的锌钴合金电镀多为氯化物类型，存在着电镀厚度不足，不够均匀，电镀液不够稳定等缺点。
发明内容
本发明的目的在于，提供一种深镀能力、均镀能力好，操作方便，镀液稳定的碱性锌钴合金电镀液，以克服现有技术的不足。
本发明的技术方案。碱性锌钴合金电镀液，按重量计，在1000份电镀液中包括以下物质，氧化锌7-20份、氢氧化钠130-170份、硫酸钴3-12份、三乙醇胺15-25份、柠檬酸胺5-10份、酒石酸30-35份、苄基吡啶鎓羧酸钠0.1-0.6份、植酸钠0.1-0.5份、二甲胺2-5份、硫脲0.3-0.5份、洋茉莉醛0.02-0.05份，剩余为水。
前述的碱性锌钴合金电镀液，按重量计，在1000份电镀液中包括以下物质，氧化锌10-16份、氢氧化钠140-160份、硫酸钴6-9份、三乙醇胺17-23份、柠檬酸胺7-8份、酒石酸31-34份、苄基吡啶鎓羧酸钠0.2-0.5份、植酸钠0.2-0.4份、二甲胺3-4份、硫脲0.3-0.5份、洋茉莉醛0.03-0.04份，剩余为水。
前述的碱性锌钴合金电镀液，按重量计，在1000份电镀液中包括以下物质，氧化锌13-14份、氢氧化钠150份、硫酸钴7-8份、三乙醇胺20份、柠檬酸胺7-8份、酒石酸32-33份、苄基吡啶鎓羧酸钠0.3-0.4份、植酸钠0.3份、二甲胺3-4份、硫脲0.4份、洋茉莉醛0.03-0.04份，剩余为水。 
本发明的碱性锌钴合金电镀具有良好的深镀能力和均镀能力，镀层脆性小，合金成分钴含量容易控制等优点，电镀操作更方便，镀液使用寿命长。经申请人试验，通过本发明的电镀液配方得到的电镀产品，中性盐雾试验300小时不出白锈。同现有技术相比，具有合金成分钴含量容易控制，镀液深镀能力、均镀能力好，操作方便，镀液稳定等优点。
具体实施方式
本发明的实施例1。本发明的技术方案。碱性锌钴合金电镀液，以配置一升电镀液为例，在1升烧杯中加入300毫升水，加入氧化锌7-20克，搅拌均匀；缓慢加入氢氧化钠130-170克，搅拌至全部溶解，溶液清澈后，补充水400毫升降温到室温；将苄基吡啶鎓羧酸钠0.1-0.6克、植酸钠0.1-0.5克、二甲胺2-5克、硫脲0.3-0.5克、洋茉莉醛0.02-0.05克分别加入烧杯中；在另一个烧杯中加入200毫升水，将三乙醇胺15-25克、柠檬酸胺5-10克、酒石酸30-35克加入后搅拌至完全溶解，再加入硫酸钴3-12克搅拌至完全溶解；将2个烧杯中的溶液混合，用水补充至1升，得到电镀液。使用时，将需要电镀的产品放入电镀液中，按照0.2安/平方分米电流通电15分钟即可。
本发明的实施例2。碱性锌钴合金电镀液，以配置一升电镀液为例，在1升烧杯中加入300毫升水，加入氧化锌10-16克，搅拌均匀；缓慢加入氢氧化钠140-160克，搅拌至全部溶解，溶液清澈后，补充水400毫升降温到室温；将苄基吡啶鎓羧酸钠0.2-0.5克、植酸钠0.2-0.4克、二甲胺3-4克、硫脲0.3-0.5克、洋茉莉醛0.03-0.04克分别加入烧杯中；在另一个烧杯中加入200毫升水，将三乙醇胺17-23克、柠檬酸胺7-8克、酒石酸31-34克加入后搅拌至完全溶解，再加入硫酸钴6-9克搅拌至完全溶解；将2个烧杯中的溶液混合，用水补充至1升，得到电镀液。
本发明的实施例3。碱性锌钴合金电镀液，以配置一升电镀液为例，在1升烧杯中加入300毫升水，加入氧化锌13-14克，搅拌均匀；缓慢加入氢氧化钠150克，搅拌至全部溶解，溶液清澈后，补充水400毫升降温到室温；将苄基吡啶鎓羧酸钠0.3-0.4克、植酸钠0.3克、二甲胺3-4克、硫脲0.4克、洋茉莉醛0.03-0.04克分别加入烧杯中；在另一个烧杯中加入200毫升水，将三乙醇胺20克、柠檬酸胺7-8克、酒石酸32-33克加入后搅拌至完全溶解，再加入硫酸钴7-8克搅拌至完全溶解；将2个烧杯中的溶液混合，用水补充至1升，得到电镀液。

Claims (3)

1.一种碱性锌钴合金电镀液，其特征在于：按重量计，在1000份电镀液中包括以下物质，氧化锌7-20份、氢氧化钠130-170份、硫酸钴3-12份、三乙醇胺15-25份、柠檬酸胺5-10份、酒石酸30-35份、苄基吡啶鎓羧酸钠0.1-0.6份、植酸钠0.1-0.5份、二甲胺2-5份、硫脲0.3-0.5份、洋茉莉醛0.02-0.05份，剩余为水。
2.根据权利要求1所述的碱性锌钴合金电镀液，其特征在于：按重量计，在1000份电镀液中包括以下物质，氧化锌10-16份、氢氧化钠140-160份、硫酸钴6-9份、三乙醇胺17-23份、柠檬酸胺7-8份、酒石酸31-34份、苄基吡啶鎓羧酸钠0.2-0.5份、植酸钠0.2-0.4份、二甲胺3-4份、硫脲0.3-0.5份、洋茉莉醛0.03-0.04份，剩余为水。
3.根据权利要求2所述的碱性锌钴合金电镀液，其特征在于：按重量计，在1000份电镀液中包括以下物质，氧化锌13-14份、氢氧化钠150份、硫酸钴7-8份、三乙醇胺20份、柠檬酸胺7-8份、酒石酸32-33份、苄基吡啶鎓羧酸钠0.3-0.4份、植酸钠0.3份、二甲胺3-4份、硫脲0.4份、洋茉莉醛0.03-0.04份，剩余为水。
CN201310292225.4A 2013-07-12 2013-07-12 一种碱性锌钴合金电镀液 Expired - Fee Related CN103320821B (zh)