CN103274584A - 8.0mm 钢化玻璃的钢化加工方法 - Google Patents

8.0mm 钢化玻璃的钢化加工方法 Download PDF

Info

Publication number
CN103274584A
CN103274584A CN201310120901XA CN201310120901A CN103274584A CN 103274584 A CN103274584 A CN 103274584A CN 201310120901X A CN201310120901X A CN 201310120901XA CN 201310120901 A CN201310120901 A CN 201310120901A CN 103274584 A CN103274584 A CN 103274584A
Authority
CN
China
Prior art keywords
glass
temperature
carrying
minute
interval
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310120901XA
Other languages
English (en)
Inventor
张百庆
韩立平
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HEFEI CHENGXIN GLASS CO Ltd
Original Assignee
HEFEI CHENGXIN GLASS CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HEFEI CHENGXIN GLASS CO Ltd filed Critical HEFEI CHENGXIN GLASS CO Ltd
Priority to CN201310120901XA priority Critical patent/CN103274584A/zh
Publication of CN103274584A publication Critical patent/CN103274584A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种8.0mm钢化玻璃的钢化加工方法,包括以下步骤:将待加工玻璃水平放置到辊道上,通过辊道送到通道式钢化炉中,按区间依次进行热处理,采用高压风冷却至玻璃表面温度290-310℃;将玻璃加入到350-360℃硝酸钾熔盐中,加热时间3-4分钟;将玻璃加入150-160℃甘油溶液中冷却4-5分钟;取出玻璃后空冷。本发明通过采用分区间加热、冷处理,调节玻璃表面应力分布,保证了钢化玻璃的平整度,通过甘油溶液与硝酸钾熔盐处理,增加了玻璃表面的钢化度,降低了玻璃在冷却过程中自爆的机率,提高了钢化玻璃的成品率,满足了钢化玻璃的性能指标要求。

Description

8.0mm 钢化玻璃的钢化加工方法
技术领域
本发明属于玻璃制备领域,具体涉及钢化玻璃的制备工艺。 
技术背景
钢化玻璃由于具有较高机械强度、优良耐温急变性、良好的安全性等优点,使得其被广泛应用。现有钢化玻璃生产过程大多采用以空气为冷却介质的钢化工艺,使被加热玻璃通过大量空气在短时间内进行激冷处理,从而完成钢化过程。为了保证钢化玻璃的性能,通常需要在很短时间提供很大流量的空气,尤其在钢化较薄玻璃时更为明显,通常选用高风压、大流量的大功率风机同时吹风。 
目前玻璃钢化的方式也有化学钢化方式,化学钢化玻璃强度与物理钢化玻璃接近,但时间过长,效率低而生产成本高。 
发明内容
本发明的目的是提供一种8.0mm 钢化玻璃的钢化加工方法,玻璃表面应力均匀、弯曲度、碎片、钢化度均符合要求。 
本发明技术方案如下: 
8.0 mm 钢化玻璃的钢化加工方法,其特征在于包括以下步骤: 
(1)、将将玻璃水平放置到辊道上,通过辊道送到通道式钢化炉中,按区间依次进行热处理: 
第一区间:温度200-280℃,时间3-4分钟;第二区间:温度400-430℃,时间4-5分钟;第三区间:温度550-600℃,时间2-3分钟;第四区间:温度350-380℃,时间4-5分钟;第五区间:温度650-700℃,时间4-5分钟; 
(2)、采用高压风冷却至玻璃表面温度290-310℃; 
(3)、将玻璃加入到350-360℃硝酸钾熔盐中,加热时间3-4分钟; 
(4)、将玻璃加入150-160℃甘油溶液中冷却4-5分钟; 
(5)、取出玻璃后空冷。 
本发明通过采用分区间加热、冷处理,调节玻璃表面应力分布,保证了钢化玻璃的平整度,通过甘油溶液与硝酸钾熔盐处理,增加了玻璃表面的钢化度,降低了玻璃在冷却过程中自爆的机率,提高了钢化玻璃的成品率,满足了钢化玻璃的性能指标要求。 
具体实施方式
8.0 mm 钢化玻璃的钢化加工方法,包括依次进行以下步骤: 
(1)、将将玻璃水平放置到辊道上,通过辊道送到通道式钢化炉中,按区间依次进行热处理: 
第一区间:温度240-280℃,时间3-4分钟;第二区间:温度400-430℃,时间4-5分钟;第三区间:温度560-600℃,时间2-3分钟;第四区间:温度350-380℃,时间4-5分钟;第五区间:温度660-700℃,时间4-5分钟; 
(2)、采用高压风冷却至玻璃表面温度300-310℃; 
(3)、将玻璃加入到350-360℃硝酸钾熔盐中,加热时间4分钟; 
(4)、再将玻璃到出加入150-160℃甘油溶液中冷却5分钟; 
(5)、取出玻璃后空冷。 
将加工好的钢化玻璃进行检测,其弯曲度达到0.7‰,50×50mm 内碎片58 粒,符合标准;钢化度=3.6N/cm,自爆率在1~3‰。 

Claims (1)

1.8.0 mm 钢化玻璃的钢化加工方法,其特征在于包括以下步骤:
(1)、将将玻璃水平放置到辊道上,通过辊道送到通道式钢化炉中,按区间依次进行热处理:
第一区间:温度200-280℃,时间3-4分钟;第二区间:温度400-430℃,时间4-5分钟;第三区间:温度550-600℃,时间2-3分钟;第四区间:温度350-380℃,时间4-5分钟;第五区间:温度650-700℃,时间4-5分钟;
(2)、采用高压风冷却至玻璃表面温度290-310℃;
(3)、将玻璃加入到350-360℃硝酸钾熔盐中,加热时间3-4分钟;
(4)、将玻璃加入150-160℃甘油溶液中冷却4-5分钟;
(5)、取出玻璃后空冷。 
CN201310120901XA 2013-04-09 2013-04-09 8.0mm 钢化玻璃的钢化加工方法 Pending CN103274584A (zh)