CN103214169A - 5.0mm 钢化玻璃的钢化加工方法 - Google Patents
5.0mm 钢化玻璃的钢化加工方法 Download PDFInfo
- Publication number
- CN103214169A CN103214169A CN2013101209170A CN201310120917A CN103214169A CN 103214169 A CN103214169 A CN 103214169A CN 2013101209170 A CN2013101209170 A CN 2013101209170A CN 201310120917 A CN201310120917 A CN 201310120917A CN 103214169 A CN103214169 A CN 103214169A
- Authority
- CN
- China
- Prior art keywords
- glass
- temperature
- minute
- toughened
- interval
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种5.0mm钢化玻璃的钢化加工方法,包括以下步骤:将待加工玻璃水平放置到辊道上,通过辊道送到通道式钢化炉中,按区间依次进行热处理,采用高压风冷却至玻璃表面温度280-300℃;将玻璃加入150-160℃、12-15%的硝酸钾甘油溶液冷却3-5分钟;将玻璃加入到200-210℃甘油中处理4-6分钟;取出后用50-60℃水雾冷却至室温。本发明通过采用分区间加热、冷处理,调节玻璃表面应力分布,保证了钢化玻璃的平整度,通过硝酸钾甘油溶液与甘油、水雾处理,增加了玻璃表面的钢化度,降低了玻璃在冷却过程中自爆的机率,提高了钢化玻璃的成品率,满足了钢化玻璃的性能指标要求。
Description
技术领域
本发明属于玻璃制备领域,具体涉及钢化玻璃的制备工艺。
技术背景
钢化玻璃由于具有较高机械强度、优良耐温急变性、良好的安全性等优点,使得其被广泛应用。现有钢化玻璃生产过程大多采用以空气为冷却介质的钢化工艺,使被加热玻璃通过大量空气在短时间内进行激冷处理,从而完成钢化过程。为了保证钢化玻璃的性能,通常需要在很短时间提供很大流量的空气,尤其在钢化较薄玻璃时更为明显,通常选用高风压、大流量的大功率风机同时吹风。
目前玻璃钢化的方式也有化学钢化方式,化学钢化玻璃强度与物理钢化玻璃接近,但时间过长,效率低而生产成本高。
发明内容
本发明的目的是提供一种5.0mm 钢化玻璃的钢化加工方法,玻璃表面应力均匀、弯曲度、碎片、钢化度均符合要求。
本发明技术方案如下:
5.0 mm 钢化玻璃的钢化加工方法,其特征在于包括以下步骤:
(1)、将将玻璃水平放置到辊道上,通过辊道送到通道式钢化炉中,按区间依次进行热处理:
第一区间:温度220-260℃,时间2-3分钟;第二区间:温度380-420℃,时间4-5分钟;第三区间:温度280-320℃,时间3-4分钟;第四区间:温度520-580℃,时间4-5分钟;第五区间:温度650-700℃,时间5-6分钟;
(2)、采用高压风冷却至玻璃表面温度280-300℃;
(3)、将玻璃加入150-160℃、12-15%的硝酸钾甘油溶液冷却3-5分钟;
(4)、将玻璃加入到200-210℃甘油中处理4-6分钟;
(5)、取出后用50-60℃水雾冷却至室温。
本发明通过采用分区间加热、冷处理,调节玻璃表面应力分布,保证了钢化玻璃的平整度,通过硝酸钾甘油溶液与甘油、水雾处理,增加了玻璃表面的钢化度,降低了玻璃在冷却过程中自爆的机率,提高了钢化玻璃的成品率,满足了钢化玻璃的性能指标要求。
具体实施方式
5.0 mm 钢化玻璃的钢化加工方法,包括依次进行以下步骤:
(1)、将将玻璃水平放置到辊道上,通过辊道送到通道式钢化炉中,按区间依次进行热处理:
第一区间:温度250-260℃,时间2-3分钟;第二区间:温度380-400℃,时间4-5分钟;第三区间:温度280-310℃,时间3-4分钟;第四区间:温度520-540℃,时间4-5分钟;第五区间:温度680-700℃,时间5-6分钟;
(2)、采用高压风冷却至玻璃表面温度290-300℃;
(3)、将玻璃加入150-160℃、15%的硝酸钾甘油溶液冷却5分钟;
(4)、将玻璃加入到200-210℃甘油中处理6分钟;
(5)、取出后用60℃热水雾冷却至室温。
将加工好的钢化玻璃进行检测,其弯曲度达到0.5‰,50×50mm 内碎片59 粒,符合标准;钢化度=3.8N/cm,自爆率在1~3‰。
Claims (1)
1.5.0 mm 钢化玻璃的钢化加工方法,其特征在于包括以下步骤:
(1)、将将玻璃水平放置到辊道上,通过辊道送到通道式钢化炉中,按区间依次进行热处理:
第一区间:温度220-260℃,时间2-3分钟;第二区间:温度380-420℃,时间4-5分钟;第三区间:温度280-320℃,时间3-4分钟;第四区间:温度520-580℃,时间4-5分钟;第五区间:温度650-700℃,时间5-6分钟;
(2)、采用高压风冷却至玻璃表面温度280-300℃;
(3)、将玻璃加入150-160℃、12-15%的硝酸钾甘油溶液冷却3-5分钟;
(4)、将玻璃加入到200-210℃甘油中处理4-6分钟;
(5)、取出后用50-60℃水雾冷却至室温。