CN103223580A - 废旧铣刀的再生工艺 - Google Patents

废旧铣刀的再生工艺 Download PDF

Info

Publication number
CN103223580A
CN103223580A CN2013101336532A CN201310133653A CN103223580A CN 103223580 A CN103223580 A CN 103223580A CN 2013101336532 A CN2013101336532 A CN 2013101336532A CN 201310133653 A CN201310133653 A CN 201310133653A CN 103223580 A CN103223580 A CN 103223580A
Authority
CN
China
Prior art keywords
temperature
milling cutter
time
waste
hours
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2013101336532A
Other languages
English (en)
Inventor
周静波
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHANGSHU SANJUN PRECISION CUTTING TOOLS FACTORY
Original Assignee
CHANGSHU SANJUN PRECISION CUTTING TOOLS FACTORY
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHANGSHU SANJUN PRECISION CUTTING TOOLS FACTORY filed Critical CHANGSHU SANJUN PRECISION CUTTING TOOLS FACTORY
Priority to CN2013101336532A priority Critical patent/CN103223580A/zh
Publication of CN103223580A publication Critical patent/CN103223580A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种废旧铣刀的再生工艺，包括如下步骤：1)将废旧铣刀进行外圆磨，除去废旧铣刀表面的氧化层以及杂质，形成初坯；2)对初坯进行热处理：低温预热的温度为545℃-565℃，保温2.5h；中温预热的温度为845℃-865℃，保温15min-25min；高温加热的温度为1285℃-1305℃，保温105s-125s；第一次回火的温度为555℃-575℃，回火时间为2h-3h，保温1.5h-2.5h，然后空冷至室温；第二次回火的温度为555℃-575℃，回火时间为1.5h-2.5h，然后空冷至室温；第三次回火的温度为555℃-575℃，回火时间为1.5h-2.5h，然后空冷至室温；3)热处理后的初坯再次进行外圆磨，使其直径达到成品直径；4)在开槽机上进行开槽；5)开槽后清边；7)清边后进行开刃，制得成品铣刀。本发明能将废旧铣刀加工再生成合格的新铣刀。

Description

废旧铣刀的再生工艺
技术领域
本发明涉及废旧铣刀的再生工艺。
背景技术
铣刀，是用于铣削加工的、具有一个或多个刀齿的旋转刀具。工作时各刀齿依次间歇地切去工件的余量。铣刀主要用于在铣床上加工平面、台阶、沟槽、成形表面和切断工件等。
铣刀的大量应用也产生了大量的废旧铣刀，不对废旧铣刀再利用会造成很大浪费。
发明内容
本发明的目的在于提供一种废旧铣刀的再生工艺，其能将废旧铣刀加工再生成合格的新铣刀。
为实现上述目的，本发明的技术方案是设计一种废旧铣刀的再生工艺，包括如下步骤：
1)将废旧铣刀进行外圆磨，除去废旧铣刀表面的氧化层以及杂质，形成初坯；
2)对初坯进行热处理：低温预热的温度为545℃-565℃，保温2.5h；中温预热的温度为845℃-865℃，保温15min-25min；高温加热的温度为1285℃-1305℃，保温105s-125s；第一次回火的温度为555℃-575℃，回火时间为2h-3h，保温1.5h-2.5h，然后空冷至室温；第二次回火的温度为555℃-575℃，回火时间为1.5h-2.5h，然后空冷至室温；第三次回火的温度为555℃-575℃，回火时间为1.5h-2.5h，然后空冷至室温；
3)热处理后的初坯再次进行外圆磨，使其直径达到成品直径；
4)在开槽机上进行开槽；
5)开槽后清边；
7)清边后进行开刃，制得成品铣刀。
本发明的优点和有益效果在于：提供一种废旧铣刀的再生工艺，其能将废旧铣刀加工再生成合格的新铣刀。
具体实施方式
下面结合实施例，对本发明的具体实施方式作进一步描述。以下实施例仅用于更加清楚地说明本发明的技术方案，而不能以此来限制本发明的保护范围。
本发明具体实施的技术方案是：
实施例1
一种废旧铣刀的再生工艺，包括如下步骤：
1)将废旧铣刀进行外圆磨，除去废旧铣刀表面的氧化层以及杂质，形成初坯；
2)对初坯进行热处理：低温预热的温度为545℃，保温2.5h；中温预热的温度为845℃，保温15min；高温加热的温度为1285℃，保温105s；第一次回火的温度为555℃，回火时间为2h，保温1.5h，然后空冷至室温；第二次回火的温度为555℃，回火时间为1.5h，然后空冷至室温；第三次回火的温度为555℃，回火时间为1.5h，然后空冷至室温；
3)热处理后的初坯再次进行外圆磨，使其直径达到成品直径；
4)在开槽机上进行开槽；
5)开槽后清边；
7)清边后进行开刃，制得成品铣刀。
实施例2
一种废旧铣刀的再生工艺，包括如下步骤：
1)将废旧铣刀进行外圆磨，除去废旧铣刀表面的氧化层以及杂质，形成初坯；
2)对初坯进行热处理：低温预热的温度为555℃，保温2.5h；中温预热的温度为855℃，保温18min；高温加热的温度为1295℃，保温115s；第一次回火的温度为565℃，回火时间为2.5h，保温2h，然后空冷至室温；第二次回火的温度为565℃，回火时间为2h，然后空冷至室温；第三次回火的温度为565℃，回火时间为2h，然后空冷至室温；
3)热处理后的初坯再次进行外圆磨，使其直径达到成品直径；
4)在开槽机上进行开槽；
5)开槽后清边；
7)清边后进行开刃，制得成品铣刀。
实施例3
一种废旧铣刀的再生工艺，包括如下步骤：
1)将废旧铣刀进行外圆磨，除去废旧铣刀表面的氧化层以及杂质，形成初坯；
2)对初坯进行热处理：低温预热的温度为565℃，保温2.5h；中温预热的温度为865℃，保温25min；高温加热的温度为1305℃，保温125s；第一次回火的温度为575℃，回火时间为3h，保温2.5h，然后空冷至室温；第二次回火的温度为575℃，回火时间为2.5h，然后空冷至室温；第三次回火的温度为575℃，回火时间为2.5h，然后空冷至室温；
3)热处理后的初坯再次进行外圆磨，使其直径达到成品直径；
4)在开槽机上进行开槽；
5)开槽后清边；
7)清边后进行开刃，制得成品铣刀。
以上所述仅是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明技术原理的前提下，还可以做出若干改进和润饰，这些改进和润饰也应视为本发明的保护范围。

Claims (1)

1.废旧铣刀的再生工艺，其特征在于，包括如下步骤：
1)将废旧铣刀进行外圆磨，除去废旧铣刀表面的氧化层以及杂质，形成初坯；
2)对初坯进行热处理：低温预热的温度为545℃-565℃，保温2.5h；中温预热的温度为845℃-865℃，保温15min-25min；高温加热的温度为1285℃-1305℃，保温105s-125s；第一次回火的温度为555℃-575℃，回火时间为2h-3h，保温1.5h-2.5h，然后空冷至室温；第二次回火的温度为555℃-575℃，回火时间为1.5h-2.5h，然后空冷至室温；第三次回火的温度为555℃-575℃，回火时间为1.5h-2.5h，然后空冷至室温；
3)热处理后的初坯再次进行外圆磨，使其直径达到成品直径；
4)在开槽机上进行开槽；
5)开槽后清边；
7)清边后进行开刃，制得成品铣刀。
CN2013101336532A 2013-04-16 2013-04-16 废旧铣刀的再生工艺 Pending CN103223580A (zh)