CN103184456B - 一种环保型长寿命乳化防锈剂及其制备方法 - Google Patents

一种环保型长寿命乳化防锈剂及其制备方法 Download PDF

Info

Publication number
CN103184456B
CN103184456B CN201310066110.3A CN201310066110A CN103184456B CN 103184456 B CN103184456 B CN 103184456B CN 201310066110 A CN201310066110 A CN 201310066110A CN 103184456 B CN103184456 B CN 103184456B
Authority
CN
China
Prior art keywords
rust
environment
preventive agent
emulsification
antirust agent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310066110.3A
Other languages
English (en)
Other versions
CN103184456A (zh
Inventor
张乃庆
吴启东
陈立坤
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shandong Kerewo New Material Technology Co.,Ltd.
Original Assignee
Shanghai Jinzhao Energy Saving Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanghai Jinzhao Energy Saving Technology Co Ltd filed Critical Shanghai Jinzhao Energy Saving Technology Co Ltd
Priority to CN201310066110.3A priority Critical patent/CN103184456B/zh
Publication of CN103184456A publication Critical patent/CN103184456A/zh
Application granted granted Critical
Publication of CN103184456B publication Critical patent/CN103184456B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种环保型长寿命乳化防锈剂及其制备方法。该防锈剂由以下组分组成：ISO粘度等级在46#以下的白油40-50%，油酸二乙醇酰胺硼酸酯20-30%，失水山梨醇脂肪酸酯5-10%，十二烷基苯磺酸钠5-10%，N-油酰肌氨酸十八胺盐3-5%，环烷酸锌3-5%，壬基酚聚氧乙烯醚2-3%，苯并三氮唑0.5-1%，水5-10%。制备方法：称取苯并三氮唑和失水山梨醇脂肪酸酯充分搅拌透明后，依次加入白油、油酸二乙醇酰胺硼酸酯、N-油酰肌氨酸十八胺盐、环烷酸锌、壬基酚聚氧乙烯醚，以及预先与水混合好的十二烷基苯磺酸钠，在25-40℃的温度下充分搅拌30-60分钟至完全透明即得。本发明的防锈剂有很好的防锈性能，加水4-20倍后仍具有良好的防锈性能；同时，清洗方便，节能降耗，减少了对环境和工人的危害。

Description

一种环保型长寿命乳化防锈剂及其制备方法
技术领域
本发明属于金属防锈技术领域，具体涉及一种环保型长寿命乳化防锈剂及其制备方法。
背景技术
传统的金属中长期防锈一般使用防锈油进行涂刷处理防锈，防锈油的使用量大，成本高，从节能环保的角度看，也是一种极不环保的行为，特别是一些还要进行后道工序加工的零部件，用防锈油防锈后，清洗比较困难。
目前市面上还有一些硼酸盐、磷酸盐、羧酸盐类的水性防锈剂，由于防锈时间很短，只能做短期防锈。还有用亚硝酸钠作为水性防锈剂使用的，虽然有一定的防锈效果，但是亚硝酸钠有致癌性，很多国家禁止使用。
发明内容
本发明的目的在于克服现有技术的不足，提供一种环保型长寿命乳化防锈剂及其制备方法。该环保型水性防锈剂加水4-20倍使用，仍具有良好的防锈性能。
为实现上述目的，本发明采用了如下技术方案：
一种环保型长寿命乳化防锈剂，按重量百分比计由以下组分组成：
上述的白油主要是C16-C30的烷烃混合物，化学性能稳定，本发明所使用的白油作为基础油使用，要求ISO粘度等级在46#以下的；
上述的油酸二乙醇酰胺硼酸酯具有优良的防锈性能，同时有较好的自乳化性；
上述失水山梨醇脂肪酸酯的防锈性能优异，同时又是一种亲油型的非离子表面活性剂，其商品名为司盘，常见的商品型号有：S-20，S-40，S-60，S-80，S-85等，本发明中要求使用液体的司盘产品（以便于溶解苯并三氮唑），因此选用S-20、S-80或S-85，优选S-80；
上述十二烷基苯磺酸钠的防锈性能较好，同时是一种亲水型的阴离子表面活性剂；
上述N-油酰肌氨酸十八胺盐是优良的防锈缓蚀剂，同时又是一种两性离子表面活性剂；
上述环烷酸锌的防锈性能优异，同时还可作为亲油型阴离子表面活性剂使用；
上述壬基酚聚氧乙烯醚是非离子型表面活性剂，本发明中主要使用OP-9或TX-10；
上述苯并三氮唑对有色金属的防锈防腐性能优越，苯并三氮唑为固体，能较好地溶解于液体的失水山梨醇脂肪酸酯中；
上述少量的水的存在可以使乳化防锈剂的母液更加稳定。
一种上述环保型长寿命乳化防锈剂的制备方法为：按所述重量百分比称取苯并三氮唑和失水山梨醇脂肪酸酯充分搅拌透明后，依次加入按所述重量百分比称取的白油、油酸二乙醇酰胺硼酸酯、N-油酰肌氨酸十八胺盐、环烷酸锌、壬基酚聚氧乙烯醚，以及预先与水混合好的十二烷基苯磺酸钠，在25-40℃的温度下充分搅拌30-60分钟，至混合液完全透明后，即可包装入库。
一种上述环保型长寿命乳化防锈剂的使用方法：按重量比加4-20倍的水搅拌乳化后使用。
本发明的有益效果：
本发明的环保型长寿命乳化防锈剂，具有很好的防锈性能；该环保型水性防锈剂加水4-20倍使用，仍具有良好的防锈性能，可用于中、长期防锈；同时，清洗方便，节能降耗，减少了对环境和工人的危害。
具体实施方式
下面结合实施例对本发明作进一步的说明。
实施例1
称取1kg苯并三氮唑和10kg的失水山梨醇脂肪酸酯（S-80）充分搅拌透明后，依次加入40kg的46#白油、25kg油酸二乙醇酰胺硼酸酯、5kg的N-油酰肌氨酸十八胺盐、3kg的环烷酸锌、3kg壬基酚聚氧乙烯醚(TX-10)，以及预先与8kg水混合好的5kg十二烷基苯磺酸钠，在40℃的温度下充分搅拌30分钟，至完全透明，包装即得环保型长寿命乳化防锈剂。
本防锈剂原液，根据GB/T2361-1992试验方法做温热实验（14天），结果0级，符合防锈油的技术指标。
本防锈剂原液，根据SH/T0081-1991进行盐雾试验结果：96小时，0级，符合防锈油相关技术指标。
实施例2
称取0.5kg苯并三氮唑和5kg的失水山梨醇脂肪酸酯（S-80）充分搅拌透明后，依次加入50kg的32#白油、20kg油酸二乙醇酰胺硼酸酯、3kg的N-油酰肌氨酸十八胺盐、5kg的环烷酸锌、2kg壬基酚聚氧乙烯醚(OP-9)，以及预先和7kg水混合好的7.5kg十二烷基苯磺酸钠，在25℃的温度下充分搅拌60分钟，至完全透明，包装即得环保型长寿命乳化防锈剂。
本防锈剂按重量比5%防锈剂+95%的蒸馏水，用GB/T11143-2008试验方法做液相锈蚀（蒸馏水）实验，结果合格。
本防锈剂按重量比5%防锈剂+95%的蒸馏水，根据GB/T2361-1992试验方法做温热实验（7天），结果1级。
本防锈剂按重量比5%防锈剂+95%的蒸馏水，根据SH/T0081-1991进行盐雾试验结果：24小时，0级。
实施例3
称取0.6kg苯并三氮唑和6kg的失水山梨醇脂肪酸酯（S-20）充分搅拌透明后，依次加入45kg的22#白油、22kg油酸二乙醇酰胺硼酸酯、4kg的N-油酰肌氨酸十八胺盐、4kg的环烷酸锌、2.4kg壬基酚聚氧乙烯醚(OP-9)，以及预先和10kg水混合好的6kg十二烷基苯磺酸钠，在35℃的温度下充分搅拌45分钟，至完全透明，包装即得环保型长寿命乳化防锈剂。
本防锈剂按重量比10%防锈剂+90%的蒸馏水，用GB/T11143-2008试验方法做液相锈蚀（蒸馏水）实验，结果合格。
本防锈剂按重量比10%防锈剂+90%蒸馏水，根据GB/T2361-1992试验方法做温热实验（7天），结果1级。
本防锈剂按重量比10%防锈剂+90%蒸馏水，根据SH/T0081-1991进行盐雾试验结果：48小时，0级。
实施例4
称取0.7kg苯并三氮唑和7kg的失水山梨醇脂肪酸酯（S-80）充分搅拌透明后，依次加入43kg的10#白油、20kg油酸二乙醇酰胺硼酸酯、4kg的N-油酰肌氨酸十八胺盐、4kg的环烷酸锌、2.3kg壬基酚聚氧乙烯醚(TX-10)，以及预先和9kg水混合好的10kg十二烷基苯磺酸钠，在30℃的温度下充分搅拌50分钟，至完全透明，包装即得环保型长寿命乳化防锈剂。
本防锈剂按重量比15%防锈剂+85%的蒸馏水，用GB/T11143-2008试验方法做液相锈蚀（蒸馏水）实验，结果合格。
本防锈剂按重量比15%防锈剂+85%蒸馏水，根据GB/T2361-1992试验方法做温热实验（7天），结果0级。
本防锈剂按重量比15%防锈剂+85%蒸馏水，根据SH/T0081-1991进行盐雾试验结果：48小时，0级。
实施例5
称取0.8kg苯并三氮唑和5kg的失水山梨醇脂肪酸酯（S-85）充分搅拌透明后，依次加入44kg的5#白油、30kg油酸二乙醇酰胺硼酸酯、3kg的N-油酰肌氨酸十八胺盐、3.2kg的环烷酸锌、2kg壬基酚聚氧乙烯醚(TX-10)，以及预先和5kg水混合好的7kg十二烷基苯磺酸钠，在36℃的温度下充分搅拌40分钟，至完全透明，包装即得环保型长寿命乳化防锈剂。
本防锈剂按重量比20%防锈剂+80%的蒸馏水，用GB/T11143-2008试验方法做液相锈蚀（蒸馏水）实验，结果合格。
本防锈剂按重量比20%防锈剂+80%蒸馏水，根据GB/T2361-1992试验方法做温热实验（7天），结果0级。
本防锈剂按重量比20%防锈剂+80%蒸馏水，根据GB/T5096-1985铜片腐蚀（3h,50℃），结果1a级。

Claims (5)

1.一种环保型长寿命乳化防锈剂，其特征在于，按重量百分比计由以下组分组成：
所述白油为ISO粘度等级在46以下的C16-C30的烷烃混合物；所述失水山梨醇脂肪酸酯为S-20、S-80或S-85。
2.如权利要求1所述的环保型长寿命乳化防锈剂，其特征在于：所述壬基酚聚氧乙烯醚为OP-9或TX-10。
3.如权利要求1或2所述的环保型长寿命乳化防锈剂，其特征在于：所述失水山梨醇脂肪酸酯为S-80。
4.一种如权利要求1-3所述的环保型长寿命乳化防锈剂的制备方法，其特征在于，按所述重量百分比称取苯并三氮唑和失水山梨醇脂肪酸酯充分搅拌透明后，依次加入按所述重量百分比称取的白油、油酸二乙醇酰胺硼酸酯、N-油酰肌氨酸十八胺盐、环烷酸锌、壬基酚聚氧乙烯醚，以及预先与水混合好的十二烷基苯磺酸钠，在25-40℃的温度下充分搅拌30-60分钟，至混合液完全透明后即得。
5.一种如权利要求1-3所述的环保型长寿命乳化防锈剂的使用方法，其特征在于，将上述乳化防锈剂按重量比加4-20倍的水搅拌乳化后使用。
CN201310066110.3A 2013-03-01 2013-03-01 一种环保型长寿命乳化防锈剂及其制备方法 Active CN103184456B (zh)