CN103160868A - 一种用于生产含硫活性镍的电解液及其使用方法 - Google Patents

一种用于生产含硫活性镍的电解液及其使用方法 Download PDF

Info

Publication number
CN103160868A
CN103160868A CN2011104253138A CN201110425313A CN103160868A CN 103160868 A CN103160868 A CN 103160868A CN 2011104253138 A CN2011104253138 A CN 2011104253138A CN 201110425313 A CN201110425313 A CN 201110425313A CN 103160868 A CN103160868 A CN 103160868A
Authority
CN
China
Prior art keywords
nickel
electrolyte
active
sulfur
electrolytic solution
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2011104253138A
Other languages
English (en)
Inventor
何跃林
曹文玲
高扬
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Angang Heavy Machinery Co Ltd
Original Assignee
Angang Heavy Machinery Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Angang Heavy Machinery Co Ltd filed Critical Angang Heavy Machinery Co Ltd
Priority to CN2011104253138A priority Critical patent/CN103160868A/zh
Publication of CN103160868A publication Critical patent/CN103160868A/zh
Pending legal-status Critical Current

Abstract

本发明涉及活性电解镍生产领域，特别涉及一种用于生产含硫活性镍的电解液及其使用方法，其特征在于，以配制1升电解液计算，其各组分含量如下：硫酸镍或氨基磺酸镍180-380g；氯化镍8-50g；硼酸20-50g；十二烷基硫酸钠0.02-0.1g；苯亚基磺酸钠1-10g；余量为水。上述电解液的使用方法，其具体工艺参数如下：电解液PH为4.0-4.5，电解温度50-55℃，阴极电流DK 4-8A/dm2。与现有技术相比，本发明的有益效果是：本发明生产的含硫活性镍，含硫活性镍的形状类似纽扣，直径25-28mm，厚度8-8.1mm，化学成分为99.98％的镍，0.02％硫，产品性能稳定，成分均匀。

Description

一种用于生产含硫活性镍的电解液及其使用方法
技术领域
本发明涉及活性电解镍生产领域，特别涉及一种用于生产含硫活性镍的电解液及其使用方法。
背景技术
目前，我国电镀镍行业主要采用电解镍作为阳极材料，含硫活性镍具有高活性、易溶解、电流效率高、不易钝化等优点在功能性电镀镍尤其是电铸镍行业备受青睐。目前市场上流通的含硫活性镍多为进口，国际市场含硫活性镍的杂质太多、使用后阳极泥严重污染电镀液；镍废料通过沉淀、过滤、萃取等方法不可避免在活性镍制造过程中带进杂质，这些杂质带到电解液中严重影响功能性电镀镍及镍合金的产品质量。
发明内容
本发明的目的在于提供一种用于生产含硫活性镍的电解液及其使用方法，克服现有技术的不足，降低含硫活性镍中的杂质含量，生产镍含量为99.98％、硫含量为0.02％的镍扣。
本发明是采用以下技术方案实现的：
一种用于生产含硫活性镍的电解液，以配制1升电解液计算，其各组分含量如下：
硫酸镍或氨基磺酸镍180-380g，作为电解液的主盐，起到导电载体；
氯化镍8-50g，活化阳极，防止阳极钝化，提高电流效率；
硼酸20-50g，作为缓冲剂；
十二烷基硫酸钠0.02-0.1g，起润湿作用；
苯亚基磺酸钠1-10g，能增加产品中的硫含量；
水余量。
上述的电解液的使用方法，其具体工艺参数如下：
电解液PH为4.0-4.5，电解温度50-55℃，阴极电流DK 4-8A/dm2。
与现有技术相比，本发明的有益效果是：本发明生产的含硫活性镍，含硫活性镍的形状类似纽扣，直径25-28mm，厚度8-8.1mm，化学成分为99.98％的镍，0.02％硫，产品性能稳定，成分均匀。
具体实施方式
下面结合实施例对本发明做进一步说明。
实施例1
一种用于生产含硫活性镍的电解液，以配制1升电解液为例，其各组分含量如下：
硫酸镍或氨基磺酸镍360g；
氯化镍45g；
硼酸40g；
十二烷基硫酸钠0.03g；
苯亚基磺酸钠2g；
水余量。
实施例2
一种用于生产含硫活性镍的电解液，以配制1升电解液为例，其各组分含量如下：
硫酸镍或氨基磺酸镍190g；
氯化镍10g；
硼酸25g；
十二烷基硫酸钠0.09g；
苯亚基磺酸钠8g；
水余量。
实施例3
硫酸镍或氨基磺酸镍270g/l；
氯化镍18g/l；
硼酸31g/l；
十二烷基硫酸钠0.06g；
苯亚基磺酸钠5.5g；
水余量。
上述实施例中生产的含硫活性镍的形状类似纽扣，直径25-28mm，厚度8.0-8.1mm，化学成分为99.98％的镍、0.02％硫。电解时，阳极为电解镍板，电解液PH为4.0-4.5，电解温度50-55℃，阴极电流DK 4-8A/dm2，生产周期为5天。

Claims (2)

1.一种用于生产含硫活性镍的电解液，其特征在于，以配制1升电解液计算，其各组分含量如下：
硫酸镍或氨基磺酸镍180-380g，
氯化镍8-50g，
硼酸20-50g，
十二烷基硫酸钠0.02-0.1g，
苯亚基磺酸钠1-10g，
水余量。
2.权利要求1所述的电解液的使用方法，其特征在于，其具体工艺参数如下：
电解液PH为4.0-4.5，电解温度50-55℃，阴极电流DK 4-8A/dm2。
CN2011104253138A 2011-12-17 2011-12-17 一种用于生产含硫活性镍的电解液及其使用方法 Pending CN103160868A (zh)