CN103146878A - 一种锌铝铁钢水炉外精炼剂及其制备方法 - Google Patents
一种锌铝铁钢水炉外精炼剂及其制备方法 Download PDFInfo
- Publication number
- CN103146878A CN103146878A CN2013100429417A CN201310042941A CN103146878A CN 103146878 A CN103146878 A CN 103146878A CN 2013100429417 A CN2013100429417 A CN 2013100429417A CN 201310042941 A CN201310042941 A CN 201310042941A CN 103146878 A CN103146878 A CN 103146878A
- Authority
- CN
- China
- Prior art keywords
- powder
- aluminium
- zinc
- molten steel
- refining agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种锌铝铁钢水炉外精炼剂及其制备方法,其组成原料的重量份为:碳酸钠20-25、三氧化二铝28-32、氧化锌15-17、重晶石13-15、铝粉4-6、改性钾长石粉6-10和硅灰石粉12-15;本发明的原料中添加了重晶石、铝粉、改性钾长石粉和硅灰石粉,变废为宝,充分利用了其吸附性能,精炼剂脱硫、脱磷效果好,减少了回磷现象,同时,其中三氧化二铝含量高,降低了生产成本。
Description
技术领域
本发明涉及炼钢技术领域,具体涉及一种锌铝铁钢水炉外精炼剂及其制备方法。
背景技术
目前,对炼钢生产率和成本以及钢铁产品质量提出了越来越高的要求,为适合这一要求,炉外精炼特别是钢包炉精炼成为现代精炼流程中的重要生产工序,在各冶金企业得到广泛应用,钢包炉精炼的一个主要冶金功能是利用精炼剂对钢液进行精炼,以达到降低钢水中氧、硫和夹杂物含量的目的,提高钢的性能,精炼剂品种很多。
发明内容
本发明的目的在于提供一种锌铝铁钢水炉外精炼剂及其制备方法,本发明精炼剂配方中增加了重晶石、铝粉、改性钾长石粉和硅灰石粉,充分利用了其吸附性能,精炼剂脱硫、脱磷效果好,成本低。
为了实现上述目的本发明采用如下技术方案:
锌铝铁钢水炉外精炼剂,其组成原料的重量份为:碳酸钠20-25、三氧化二铝28-32、氧化锌15-17、重晶石13-15、铝粉4-6、改性钾长石粉6-10和硅灰石粉12-15。
锌铝铁钢水炉外精炼剂,其组成原料的重量份为:碳酸钠22、三氧化二铝30、氧化锌16、重晶石14、铝粉5、改性钾长石粉8和硅灰石粉14。
锌铝铁钢水炉外精炼剂的制备方法,包括以下步骤:
(1)破碎:用破碎机将各原料分别破碎;
(2)混合:将破碎好的各原料按配方要求混合,并用球磨机混合均匀;
(3)过筛:用100目筛网将混合均匀的原料过筛;
(4)干燥:将过筛后的原料放在烘箱中烘烤,去除水分,烘烤温度为95-115℃,根据水分的挥发程度控制烘烤时间。
所述的改性钾长石粉的制备方法如下:
a、钾长石粉加热熔化;
b、加入相当于其重量2-3%的氟化钙粉、1-2%的铁粉、2-3%的竹炭粉、3-5%的氧化镁粉,搅拌均匀,冲入冷水中,烘干粉碎成超细粉末。
本发明的有益效果:
本发明的原料中添加了重晶石、铝粉、改性钾长石粉和硅灰石粉,变废为宝,充分利用了其吸附性能,精炼剂脱硫、脱磷效果好,减少了回磷现象,同时,其中三氧化二铝含量高,降低了生产成本。
具体实施方式
实施例1:锌铝铁钢水炉外精炼剂,其组成原料的重量份(kg)为:碳酸钠22、三氧化二铝30、氧化锌16、重晶石14、铝粉5、改性钾长石粉8和硅灰石粉14。
锌铝铁钢水炉外精炼剂的制备方法,包括以下步骤:
(1)破碎:用破碎机将各原料分别破碎;
(2)混合:将破碎好的各原料按配方要求混合,并用球磨机混合均匀;
(3)过筛:用100目筛网将混合均匀的原料过筛;
(4)干燥:将过筛后的原料放在烘箱中烘烤,去除水分,烘烤温度为105℃,根据水分的挥发程度控制烘烤时间。
所述的改性钾长石粉的制备方法如下:
a、钾长石粉加热熔化;
b、加入相当于其重量2%的氟化钙粉、2%的铁粉、3%的竹炭粉、5%的氧化镁粉,搅拌均匀,冲入冷水中,烘干粉碎成超细粉末。
下面结合上述的精炼剂的制备实施例,具体描述本发明的炼钢精炼剂的使用方法:
采用实施例1 所述的精炼剂,按常规投加方法,分二次投加,试验钢水包有1-5号,脱硫、硫磷效果如下表:
1号:钢水条件:S 0.033%,P 0.171% ;脱硫率58%,脱磷率58%;
2号:钢水条件:S 0.036%,P 0.174% ;脱硫率55%,脱磷率54%;
3号:钢水条件:S 0.039%,P 0.177% ;脱硫率43%,脱磷率52%;
4号:钢水条件:S 0.041%,P 0.172% ;脱硫率51%,脱磷率57%;
5号:钢水条件:S 0.044%,P 0.169% ;脱硫率47%,脱磷率61%。
说明本发明精炼剂有较高的脱硫、硫磷率,且稳定性好,成本较低,能基本满足钢厂技术要求。
Claims (4)
1.一种锌铝铁钢水炉外精炼剂,其特征在于其组成原料的重量份为:碳酸钠20-25、三氧化二铝28-32、氧化锌15-17、重晶石13-15、铝粉4-6、改性钾长石粉6-10和硅灰石粉12-15。
2.根据权利要求1所述的锌铝铁钢水炉外精炼剂,其特征在于其组成原料的重量份为:碳酸钠22、三氧化二铝30、氧化锌16、重晶石14、铝粉5、改性钾长石粉8和硅灰石粉14。
3.一种如权利要求1所述的锌铝铁钢水炉外精炼剂的制备方法,其特征在于包括以下步骤:
(1)破碎:用破碎机将各原料分别破碎;
(2)混合:将破碎好的各原料按配方要求混合,并用球磨机混合均匀;
(3)过筛:用100目筛网将混合均匀的原料过筛;
(4)干燥:将过筛后的原料放在烘箱中烘烤,去除水分,烘烤温度为95-115℃,根据水分的挥发程度控制烘烤时间。
4.根据权利要求1所述的锌铝铁钢水炉外精炼剂,其特征在于:所述的改性钾长石粉的制备方法如下:
a、钾长石粉加热熔化;
b、加入相当于其重量2-3%的氟化钙粉、1-2%的铁粉、2-3%的竹炭粉、3-5%的氧化镁粉,搅拌均匀,冲入冷水中,烘干粉碎成超细粉末。