CN103128296A - 一种金属锡粉的生产方法 - Google Patents

一种金属锡粉的生产方法 Download PDF

Info

Publication number
CN103128296A
CN103128296A CN2011103854908A CN201110385490A CN103128296A CN 103128296 A CN103128296 A CN 103128296A CN 2011103854908 A CN2011103854908 A CN 2011103854908A CN 201110385490 A CN201110385490 A CN 201110385490A CN 103128296 A CN103128296 A CN 103128296A
Authority
CN
China
Prior art keywords
metal
additive
tin powder
pressure
metal tin
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2011103854908A
Other languages
English (en)
Other versions
CN103128296B (zh
Inventor
曾明军
孟庆芳
莫正彬
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Chongqing You Yanchongye novel material company limited
Original Assignee
CHONGQING SMELTTED Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHONGQING SMELTTED Co Ltd filed Critical CHONGQING SMELTTED Co Ltd
Priority to CN201610272558.4A priority Critical patent/CN105728736B/zh
Priority to CN201110385490.8A priority patent/CN103128296B/zh
Priority to CN201610272165.3A priority patent/CN105689729B/zh
Priority to CN201610273255.4A priority patent/CN105855557B/zh
Publication of CN103128296A publication Critical patent/CN103128296A/zh
Application granted granted Critical
Publication of CN103128296B publication Critical patent/CN103128296B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种金属锡粉的生产方法，包括金属熔化、雾化等步骤，金属熔化过程熔融锡液的温度控制在295～310℃，在所述雾化过程中加入苯并三氮唑添加剂，其加入量占熔化后的金属锡液重量的0.005%～0.008%，雾化过程通入的高压空气气流量控制在约7～8.2m3/min。本发明通过在雾化法生产金属锡粉过程中选择一种添加剂，利用添加剂自身的性质，添加剂与金属的相互作用以及雾化的有利环境，使得添加剂气化在金属锡粉表面形成一层防止氧化和结块的保护层；应用本发明方法生产的锡粉产品，采用常规包装、金属锡粉产品氧化变质率可有效控制在0.8%～3.5%，采用常规包装生产成本得到有效地降低、生产体系安全性好，退货率大大得到降低，经济效益显著。

Description

一种金属锡粉的生产方法
技术领域
本发明涉及一种金属粉末的生产方法，具体涉及一种金属锡粉的雾化生产方法，属于冶金技术领域。
背景技术
目前金属锡粉的生产采用气体雾化法，其基本的生产工艺是：第一步，金属的熔化，熔化温度比金属熔点高50℃～100℃；第二步，在雾化设备中，利用0.3MP～1.2MP的高压空气雾化金属液流，制得合乎相应规格、要求的粉末；第三步，冷却集粉；第四步，经冷却的粉末进行筛分；第五步，产品真空包装。
由于目前雾化法生产的金属锡粉暴露在空气中易氧化变质，因此采用真空包装，但在现有的生产技术状况下生产的产品，存在以下问题：1、真空包装容易出现各种的漏气情况，造成粉末的氧化；2、真空包装由于内外压力差，锡粉末和锡粉末很容易结块；3、氧化和结块的粉重新加工增加大量的成本，同时粉末的挥发和飞扬，造成金属损失，挥发和飞扬还容易造成重金属中毒。
发明内容
本发明的目的在于提供一种金属锡粉的生产方法，该方法制得的金属锡粉抗氧化性能佳、适合进行常规包装，同时避免了真空包装结块的问题；该方法工艺简单、易于控制、安全性好。
本发明的目的是通过如下技术方案实现的：
一种金属锡粉的生产方法，包括金属熔化、雾化等步骤，其特征在于：金属熔化过程熔融锡液的温度控制在295～310℃，在所述雾化过程中加入苯并三氮唑添加剂，其加入量占熔化后的金属锡液重量的0.005％～0.008％，雾化过程通入的高压空气气流量控制在7～8.2m3/min。该方法制得的-180目级金属锡粉，应用于摩擦材料领域。
上述苯并三氮唑添加剂，其分子式：C6H5N3，外观是白色、微黄或微红色针状结晶，分子量119.0，沸点：204℃(压力2KPa)，熔点：100℃，为市售产品。
Figure BDA0000113328800000011
发明人采用雾化法生产应用于摩擦材料领域的-180目级金属锡粉的研发过程中，选择了多种添加剂防止金属粉末产品的氧化，但要么制得的金属粉末产品采用常规包装后发生氧化的产品至少达45％以上，无法推广、产品抗氧化效果不理想达不到工业生产的要求；要么出现安全性问题、整个生产过程不好控制。发明人做了大量的实验研究，最终选择了苯并三氮唑添加剂、并在雾化过程中添加，同时苯并三氮唑的加入量也很有讲究，控制在本发明的用量范围使得生产过程的安全性好、同时最终金属粉末产品的抗氧化能力佳，最后生产的金属粉末产品采用常规包装，其氧化变质率仅为2.7～3.5％左右。
为了进一步提高制得的金属锡粉产品的抗氧化能力，上述苯并三氮唑添加剂的加入温度为210～283℃、压力为0.8～0.95个标准大气压；可使得生产的金属粉末产品采用常规包装，其氧化变质率仅为2.0～2.5％左右。
更优选地，为了进一步提高安全性能及金属锡粉产品的抗氧化能力，上述苯并三氮唑添加剂的加入温度为250～275℃，金属液流雾化过程中通入高压空气的压力为0.5～0.7Mpa，金属熔化过程熔融锡液的温度控制在300～310℃；生产的金属粉末产品采用常规包装，其氧化变质率仅为1.5～2％左右。
具体地说，一种金属锡粉的生产方法，包括金属熔化、雾化等步骤，其特征在于：在所述雾化过程中加入苯并三氮唑添加剂，其加入量占熔化后的金属液重量的0.006％～0.007％，所述苯并三氮唑添加剂的加入温度为250～275℃、压力为0.8～0.95个标准大气压，金属液流雾化过程中通入高压空气的压力为0.6～0.7Mpa、高压气流量为7.5～8.2m3/min，金属熔化过程熔融锡液的温度控制在300～310℃；整个生产过程中系统安全性好、易于控制，同时生产的金属粉末产品只需采用常规包装，其氧化变质率仅为0.8～1.5％左右。
本发明具有如下的有益效果：
本发明通过在雾化法生产金属锡粉过程中选择一种添加剂，利用添加剂自身的性质，添加剂与金属锡的相互作用以及雾化的有利环境，使得添加剂气化在锡粉表面形成一层防止氧化和结块的保护层；通过生产实践，应用本发明方法生产的-180目级金属锡粉主要应用于摩擦材料领域，如：摩托车/汽车刹车片、机械转动防摩擦部位等，采用常规包装、因为氧化和结块发生的退货减少了98％以上，金属锡粉产品氧化变质率可有效控制在0.8％～3.5％，采用常规包装生产成本得到有效地降低、生产体系安全性好，退货率大大得到降低，经济效益显著，同时员工的工作环境得到改善、身心健康得到保证。
具体实施方式
下面通过实施例对本发明进行具体的描述，有必要在此指出的是以下实施例只用于对本发明进行进一步说明，不能理解为对本发明保护范围的限制，该领域的技术熟练人员可以根据上述本发明内容对本发明作出一些非本质的改进和调整。
实施例1
一种金属锡粉的生产方法，按下述步骤进行：
a.在金属熔化炉中溶解得到金属锡液流，熔融锡液的温度控制在300～310℃；
b.雾化过程中加入的金属锡液流直径在2.5～2.8mm；将压力为0.6～0.7Mpa、气流量为7.5～8.2m3/min的高压空气通入雾化设备中将金属锡液流雾化，同时通入苯并三氮唑添加剂，所述苯并三氮唑添加剂加入量占进入雾化设备的金属液流重量的0.006％～0.007％，所述苯并三氮唑添加剂的加入温度为264～275℃、压力为0.8～0.95个标准大气压；
c.冷却至常温集粉；
d.筛分、经常规包装成袋备用或待售。
上述方法生产过程中安全性好；制得的金属锡粉氧化变质率仅为0.8～1.5％，销售后几乎不存在退货，常规包装，经济效益显著。
实施例2～6：按以下步骤及工艺生产金属粉末，其余同实施例1。
Figure BDA0000113328800000031
上述方法制得的金属锡粉氧化变质率仅为1.0～3.5％，常规包装，经济效益显著；制备过程中安全性好。

Claims (4)

1.一种金属锡粉的生产方法，包括金属熔化、雾化等步骤，其特征在于：金属熔化过程熔融锡液的温度控制在295～310℃，在所述雾化过程中加入苯并三氮唑添加剂，其加入量占熔化后的金属锡液重量的0.005%～0.008%，雾化过程通入的高压空气气流量控制在约7～8.2m3/min。
2.如权利要求1所述的生产方法，其特征在于：所述述苯并三氮唑添加剂的加入温度为210～283℃、压力为0.8～0.95个标准大气压。
3.如权利要求1、2或3所述的生产方法，其特征在于：所述苯并三氮唑添加剂的加入温度为250～275℃，金属液流雾化过程中通入高压空气的压力为0.5～0.7Mpa，金属熔化过程熔融锡液的温度控制在300～310℃。
4.如权利要求1所述的生产方法，其特征在于：在所述雾化过程中加入苯并三氮唑添加剂，其加入量占熔化后的金属液重量的0.006%～0.007%，所述苯并三氮唑添加剂的加入温度为250～275℃、压力为0.8～0.95个标准大气压，金属液流雾化过程中通入高压空气的压力为0.6～0.7Mpa、高压气流量为7.5～8.2m3/min，金属熔化过程熔融锡液的温度控制在300～310℃。
CN201110385490.8A 2011-11-28 2011-11-28 一种金属锡粉的生产方法 Active CN103128296B (zh)