CN103088691A - 一种经向接结三层造纸网的生产工艺 - Google Patents
一种经向接结三层造纸网的生产工艺 Download PDFInfo
- Publication number
- CN103088691A CN103088691A CN2012105412780A CN201210541278A CN103088691A CN 103088691 A CN103088691 A CN 103088691A CN 2012105412780 A CN2012105412780 A CN 2012105412780A CN 201210541278 A CN201210541278 A CN 201210541278A CN 103088691 A CN103088691 A CN 103088691A
- Authority
- CN
- China
- Prior art keywords
- net
- warp
- parallel
- monofilament
- adopts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种经向接结三层造纸网的生产工艺,包括步骤线材购入、线材检验、整经、递头、织网、验网、一次定型、切网、插接、二次定型、成品检验、包装入库等步骤。本发明由原纬连接SSB三层网改变为经连接SSB三层网,通过在织造时经线的张力大,使连接线有规律的紧密的连接在上下两层网中,不易产生相互搓动、滑移。由此网面结构紧密、稳定、网孔排列规则均匀,不易变形,为造纸成型带来了许多优越性。
Description
技术领域
本发明涉及一种造纸网,具体涉及一种经向接结三层造纸网的生产工艺。
背景技术
造纸用聚酯成形网从组织结构的发展来看,历经了单层网、1.5层网、两层网、2.5层网到现在广泛使用的3层网。所谓的3层网即分别由两组独立的经纬线系统各自交织形成上层、下层两个组织结构,按照纬向、经向不同的连接方式将两层紧密、有效地结合在一起,形成一个具有平整细腻的抄纸面和耐磨损的纸机面完美统一的造纸成形网品种。目前市场多使用纬线自身绑定的SSB网(self support binding),该网种虽然在纸张效果、节能、运行性上取得了比2.5层网更好的效果,但由于纬线连接SSB网在纸机运转过程中容易使网体上下层产生位移,造成脱水孔变形、网体自身上下层间磨损,影响浆料的留着和脱水的一致性及稳定性。为此,我公司研制开发了经向接结的三层造纸网,该网的生产使用两个经轴,经线在进行各自系统交织的同时还和彼系统的纬线交织,由于经线在织造过程中张力大、可控易调节,网体上下层结构紧密稳定,纸机上使用后在出纸匀度、防止纤维流失、脱水、寿命等方面取得明显效果。
发明内容
本发明的目的在于针对现有技术的不足,提供一种经向接结三层造纸网的生产工艺。
本发明采用的技术方案如下:
一种经向接结三层造纸网的生产工艺,包括以下步骤:
(1)线材购入
根据生产计划要求,按型号、品质、数量进口德国优质抗水解聚酯单丝、PET单丝和PA单丝;
(2)线材检验
根据生产计划要求的线径、热缩、拉伸强度、耐酸碱度等指标逐项检验,根据具体生产要求分批次抽检和全检,本产品检验指标如下:
经线: Ф0.24-0.26mm,拉伸强度:850-950N/mm2,热缩值:14-15%,
纬线一:Ф0.24-0.26mm,拉伸强度:550-600N/mm2 ,热缩值:2-3%,
纬线二:Φ0.45m-0.55mm,拉伸强度:550-650N/mm2 热缩值:9-11%,
纬线三:Φ0.45-0.55mm,拉伸强度:450-500N/mm2 热缩值:9-11%,其中,经线一、纬线一采用抗水解聚酯单丝,纬线二采用PET单丝,纬线三采用PA单丝 ;
(3)整经
要求每根单丝张力均匀一致,整经速度:40-50m/min,张力:70-80公斤/环;
(4)递头
根据织物穿综图,表经里经相互间隔采用顺穿法依次穿入各综框;
(5)织网
按照织物组织图进行织网,完全组织经线采用16综片织造,表经:里经=1:1,完全组织纬线为24行,表纬:里纬=2:1,其中里纬采用PET和PA间隔1:1使用,表层组织采用3/1斜纹,里层组织采用3/1纬重平组织,经密33-36根/cm,总纬密33-38根/cm;
(6)验网
对织造网进行预检验,处理网体瑕疵、并进行情况登记,为合理切网提供依据;
(7)一次定型
根据圈数设置定型针板速度、加热温度,纵向张力根据网子宽度乘以设定值,计算出纵向总张力输入定型机进行拉伸控制,横向拉幅器按设定值值输入定型机进行收缩控制,使网子定型后达到规定伸长、收缩和透气、提高网子的稳定性和使用寿命;
(8)切网
按用户要求的网型、透气、规格切网,切网前必须要根据生产工作票进行严格预检,避开有问题的网体,合理拼切,保证成网率;
(9)插接
通过插接工序,将切好的网体两端拆掉一定宽度的纬线,分别将螺旋环编织进网体里,最后用专门的连接线通过螺旋环将网子连接起来;
(10)二次定型
二次定型主要处理插口平整,上机运转一圈,网口平整即可,温度为150-160℃,长度按20米以下拉长5-6公分,20米以上拉长10-12公分,横向张力保持在150-160公斤左右,速度为3-4米/分钟;
(11)成品检验
参照聚酯网行业标准GB/T 26455-2011,进行全面复检,长、宽、透气、经密、纬密、网子平整度、接口强度等,不符合要求的坚决不放行,保证提供给客户的是优质合格品;
(12)包装入库
包装箱按规范定制,穿丝、合格证、按规定放入,包装箱外观型号规格、方向、防潮标志、轻拿轻放等标识清楚。
本发明的有益效果:
(1)本发明由原纬连接SSB三层网改变为经连接SSB三层网,通过在织造时经线的张力大,使连接线有规律的紧密的连接在上下两层网中,不易产生相互搓动、滑移。由此网面结构紧密、稳定、网孔排列规则均匀,不易变形,为造纸成型带来了许多优越性;
(2)本发明采用所选用的抗水解单丝,具有绝对的稳定性和耐磨及抗污染的性能,完全能够适应高速、高温、湿热的环境下使用要求,保障了网体的强度和使用寿命。
附图说明
图1为本发明造纸网生产流程。
图2为本发明一次定型工艺参数。
图3为本发明造纸网织物组织图。
具体实施方式
本发明的目的在于针对现有技术的不足,提供一种经向接结三层造纸网的生产工艺。
本发明采用的技术方案如下:
一种经向接结三层造纸网的生产工艺,包括以下步骤:
(1)线材购入
根据生产计划要求,按型号、品质、数量进口德国优质抗水解聚酯单丝、PET单丝和PA单丝;
(2)线材检验
根据生产计划要求的线径、热缩、拉伸强度、耐酸碱度等指标逐项检验,根据具体生产要求分批次抽检和全检,本产品检验指标如下:
经线: Ф0.25mm,拉伸强度:920N/mm2,热缩值:15%,
纬线一:Ф0.25mm,拉伸强度:580N/mm2 ,热缩值:2.5%,
纬线二:Φ0.50mm,拉伸强度:630N/mm2 热缩值:10%,
纬线三:Φ0.50mm,拉伸强度:480N/mm2 热缩值:10%,其中,经线一、纬线一采用抗水解聚酯单丝,纬线二采用PET单丝,纬线三采用PA单丝 ;
(3)整经
要求每根单丝张力均匀一致,整经速度:40m/min,张力:80公斤/环;
(4)递头
根据织物穿综图,表经里经相互间隔采用顺穿法依次穿入各综框;
(5)织网
按照织物组织图进行织网,完全组织经线采用16综片织造,表经:里经=1:1,完全组织纬线为24行,表纬:里纬=2:1,其中里纬采用PET和PA间隔1:1使用,表层组织采用3/1斜纹,里层组织采用3/1纬重平组织,经密35根/cm,总纬密36根/cm;
(6)验网
对织造网进行预检验,处理网体瑕疵、并进行情况登记,为合理切网提供依据;
(7)一次定型
根据圈数设置定型针板速度、加热温度,纵向张力根据网子宽度乘以设定值,计算出纵向总张力输入定型机进行拉伸控制,横向拉幅器按设定值值输入定型机进行收缩控制,使网子定型后达到规定伸长、收缩和透气、提高网子的稳定性和使用寿命;
(8)切网
按用户要求的网型、透气、规格切网,切网前必须要根据生产工作票进行严格预检,避开有问题的网体,合理拼切,保证成网率;
(9)插接
通过插接工序,将切好的网体两端拆掉一定宽度的纬线,分别将螺旋环编织进网体里,最后用专门的连接线通过螺旋环将网子连接起来;
(10)二次定型
二次定型主要处理插口平整,上机运转一圈,网口平整即可,温度为155℃,长度按20米以下拉长6公分,20米以上拉长12公分,横向张力保持在160公斤左右,速度为3米/分钟;
(11)成品检验
参照聚酯网行业标准GB/T 26455-2011,进行全面复检,长、宽、透气、经密、纬密、网子平整度、接口强度等,不符合要求的坚决不放行,保证提供给客户的是优质合格品;
(12)包装入库
包装箱按规范定制,穿丝、合格证、按规定放入,包装箱外观型号规格、方向、防潮标志、轻拿轻放等标识清楚。
本发明经向接结三层造纸网与纬连接三层成型网相比,网子纹路排列规则整齐、网体密实挺度好、网面平整、寿命有明显提高。
Claims (1)
1.一种经向接结三层造纸网的生产工艺,其特征在于包括以下步骤:
(1)线材购入
根据生产计划要求,按型号、品质、数量进口德国优质抗水解聚酯单丝、PET单丝和PA单丝;
(2)线材检验
根据生产计划要求的线径、热缩、拉伸强度、耐酸碱度等指标逐项检验,根据具体生产要求分批次抽检和全检,本产品检验指标如下:
经线: Ф0.24-0.26mm,拉伸强度:850-950N/mm2,热缩值:14-15%,
纬线一:Ф0.24-0.26mm,拉伸强度:550-600N/mm2 ,热缩值:2-3%,
纬线二:Φ0.45m-0.55mm,拉伸强度:550-650N/mm2 热缩值:9-11%,
纬线三:Φ0.45-0.55mm,拉伸强度:450-500N/mm2 热缩值:9-11%,其中,经线一、纬线一采用抗水解聚酯单丝,纬线二采用PET单丝,纬线三采用PA单丝 ;
(3)整经
要求每根单丝张力均匀一致,整经速度:40-50m/min,张力:70-80公斤/环;
(4)递头
根据织物穿综图,表经里经相互间隔采用顺穿法依次穿入各综框;
(5)织网
按照织物组织图进行织网,完全组织经线采用16综片织造,表经:里经=1:1,完全组织纬线为24行,表纬:里纬=2:1,其中里纬采用PET和PA间隔1:1使用,表层组织采用3/1斜纹,里层组织采用3/1纬重平组织,经密33-36根/cm,总纬密33-38根/cm;
(6)验网
对织造网进行预检验,处理网体瑕疵、并进行情况登记,为合理切网提供依据;
(7)一次定型
根据圈数设置定型针板速度、加热温度,纵向张力根据网子宽度乘以设定值,计算出纵向总张力输入定型机进行拉伸控制,横向拉幅器按设定值值输入定型机进行收缩控制,使网子定型后达到规定伸长、收缩和透气、提高网子的稳定性和使用寿命;
(8)切网
按用户要求的网型、透气、规格切网,切网前必须要根据生产工作票进行严格预检,避开有问题的网体,合理拼切,保证成网率;
(9)插接
通过插接工序,将切好的网体两端拆掉一定宽度的纬线,分别将螺旋环编织进网体里,最后用专门的连接线通过螺旋环将网子连接起来;
(10)二次定型
二次定型主要处理插口平整,上机运转一圈,网口平整即可,温度为150-160℃,长度按20米以下拉长5-6公分,20米以上拉长10-12公分,横向张力保持在150-160公斤左右,速度为3-4米/分钟;
(11)成品检验
参照聚酯网行业标准GB/T 26455-2011,进行全面复检,长、宽、透气、经密、纬密、网子平整度、接口强度等,不符合要求的坚决不放行,保证提供给客户的是优质合格品;
(12)包装入库
包装箱按规范定制,穿丝、合格证、按规定放入,包装箱外观型号规格、方向、防潮标志、轻拿轻放等标识清楚。