CN103059451A - 一种阻燃柔软的聚氯乙烯电线电缆材料 - Google Patents

一种阻燃柔软的聚氯乙烯电线电缆材料 Download PDF

Info

Publication number
CN103059451A
CN103059451A CN2011103203786A CN201110320378A CN103059451A CN 103059451 A CN103059451 A CN 103059451A CN 2011103203786 A CN2011103203786 A CN 2011103203786A CN 201110320378 A CN201110320378 A CN 201110320378A CN 103059451 A CN103059451 A CN 103059451A
Authority
CN
China
Prior art keywords
polyvinyl chloride
parts
cable material
flame
retardant flexible
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2011103203786A
Other languages
English (en)
Inventor
朱雪忠
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHANGSHU CHIKUSHI MACHINERY Co Ltd
Original Assignee
CHANGSHU CHIKUSHI MACHINERY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHANGSHU CHIKUSHI MACHINERY Co Ltd filed Critical CHANGSHU CHIKUSHI MACHINERY Co Ltd
Priority to CN2011103203786A priority Critical patent/CN103059451A/zh
Publication of CN103059451A publication Critical patent/CN103059451A/zh
Pending legal-status Critical Current

Abstract

一种阻燃柔软的聚氯乙烯电线电缆材料，属于热塑性材料技术领域。其是由以下的重量份数的原料组成：聚氯乙烯树脂90～120份；增塑剂20～40份；矿物填料5～10份；金属氧化物5～10份；阻燃剂5～15份；抗氧剂0.8～1.4份；稳定剂2～4份；润滑剂0.5～1份。本发明的阻燃柔软的聚氯乙烯电线电缆材料具有如下的性能：抗张强度≥10MPa,断裂伸长率≥250%，阻燃性可以达到UL-94-V-0(3mm)。

Description

一种阻燃柔软的聚氯乙烯电线电缆材料
技术领域：
本发明属于热塑性材料技术领域，具体设计一种阻燃柔软的聚氯乙烯电线电缆材料。
背景技术：
聚氯乙烯是一种很好的材料，被广泛用于各个行。如：制鞋、包装、日用、电器、电力电线等。尽管聚氯乙烯分子链中含氯等元素，但是很多要求高阻燃的电线电缆中，聚氯乙烯仍然是达不到阻燃要求，为了提高材料的阻燃性，增加很多的阻燃剂，这样对材料的硬度有影响，而发明人想到了，即不大幅增加聚氯乙烯电线电缆硬度又能增加其阻燃性，经过大量试验，本发明人提出了一种阻燃的柔软的聚氯乙烯电线电缆材料。
发明内容：
本发明的任务在于提供一种阻燃柔软的聚氯乙烯电线电缆材料，其具有较好的加工性，较好的强度和伸长性能，较好的阻燃性，还有柔软的手感。
本发明的任务是这样来完成的，一种阻燃柔软的聚氯乙烯电线电缆材料，其是由以下的重量份数的原料组成：
聚氯乙烯树脂      90～120份；
增塑剂            20～40份；
矿物填料          5～10份；
金属氧化物        5～10份；
阻燃剂            5～15份；
抗氧剂            0.8～1.4份；
稳定剂            2～4份；
润滑剂            0.5～1份。
在本发明的一个实施例中，所述的聚氯乙烯树脂是指K值为73～74的软聚氯乙烯树脂。
在本发明的另一个实施例中，所述的增塑剂是指邻苯二甲酸二辛酯和磷酸二苯异辛酯中的任意一种。
在本发明的又一个实施例中，所述的矿物填料是指碳酸钙和氢氧化铝中的任意一种。
在本发明的再一个实施例中，所述的金属氧化物是指三氧化二锑和三氧化钼中得任意一种。
在本发明的还一个实施例中，所述的阻燃剂是指氯化石蜡和十溴二苯乙烷中的任意一种。
在本发明的更而一个实施例中，所述的抗氧剂是指2.4二叔丁基苯基-亚磷酸三酯、硫代二丙酸二月桂酯、硫代二丙酸二硬脂醇酯中的任意一种。
在本发明的进而一个实施例中，所述的稳定剂是指三碱式硫酸铅。
在本发明的更进而一个实施例中，所述的润滑剂是指硬脂酸和硬脂酸钡中的任意一个。
本发明的阻燃柔软的聚氯乙烯电线电缆材料具有如下的性能：抗张强度≥10MPa，断裂伸长率≥250％，阻燃性可以达到UL-94-V-0(3mm)。
具体实施方式
实施例1：
一种阻燃柔软的聚氯乙烯电线电缆材料是由以下重量份数的原料组成：
聚氯乙烯树脂                91份；
邻苯二甲酸二辛酯            22份；
碳酸钙                      5份；
三氧化二锑                  10份；
氯化石蜡                    5.2份；
2.4二叔丁基苯基-亚磷酸三酯  0.8份；
三碱式硫酸铅                2.2份；
硬脂酸钡                    0.5份。
将上述组份准确称量后，依次加入高速混合机中进行混合，混合均匀后，转移至双螺杆塑炼机上塑炼，待塑炼均匀后再经水冷拉条后切粒，然后进入离心干燥机进行干燥后，最后进行包装。
实施例2：
一种阻燃柔软的聚氯乙烯电线电缆材料是由以下重量份数的原料组成：
聚氯乙烯树脂        99份；
磷酸二苯异辛酯      25份；
氢氧化铝            6.2份；
三氧化钼            8.8份；
十溴二苯乙烷        8.9份；
硫代二丙酸二月桂酯  0.9份；
三碱式硫酸铅        2.6份；
硬脂酸              0.7份；
炭黑(着色剂)        2份。
将上述组份准确称量后，依次加入高速混合机中进行混合，混合均匀后，转移至双螺杆塑炼机上塑炼，待塑炼均匀后再经水冷拉条后切粒，然后进入离心干燥机进行干燥后，最后进行包装，即得到黑色阻燃柔软的聚氯乙烯电线电缆料。
实施例3：
一种阻燃柔软的聚氯乙烯电线电缆材料是由以下重量份数的原料组成：
聚氯乙烯树脂            105份；
磷酸二苯异辛酯          30份；
碳酸钙                  7.8份；
三氧化二锑              6.9份；
氯化石蜡                12份；
硫代二丙酸二硬脂醇酯    1.2份；
三碱式硫酸铅            3.3份；
硬脂酸                  0.8份；
氧化铁红(着色剂)        2份。
将上述组份准确称量后，依次加入高速混合机中进行混合，混合均匀后，转移至双螺杆塑炼机上塑炼，待塑炼均匀后再经水冷拉条后切粒，然后进入离心干燥机进行干燥后，最后进行包装，即得到红色阻燃柔软的聚氯乙烯电线电缆料。
实施例4：
一种阻燃柔软的聚氯乙烯电线电缆材料是由以下重量份数的原料组成：
聚氯乙烯树脂          113份；
磷酸二苯异辛酯        35份；
碳酸钙                9.2份；
三氧化锑              5.3份；
十溴二苯乙烷          14.8份；
硫代二丙酸二硬脂醇酯  1.3份；
三碱式硫酸铅      3.7份；
硬脂酸钡          0.9份；
酞氰绿(着色剂)    3份。
将上述组份准确称量后，依次加入高速混合机中进行混合，混合均匀后，转移至双螺杆塑炼机上塑炼，待塑炼均匀后再经水冷拉条后切粒，然后进入离心干燥机进行干燥后，最后进行包装，即得到绿色阻燃柔软的聚氯乙烯电线电缆料。
实施例5：
一种阻燃柔软的聚氯乙烯电线电缆材料是由以下重量份数的原料组成：
聚氯乙烯树脂          119份；
磷酸二苯异辛酯        39份；
碳酸钙                9.9份；
三氧化锑              7.5份；
十溴二苯乙烷          13.2份；
硫代二丙酸二硬脂醇酯  1.0份；
三碱式硫酸铅          3.9份；
硬脂酸钡              1.0份；
酞氰蓝(着色剂)        3份；
将上述组份准确称量后，依次加入高速混合机中进行混合，混合均匀后，转移至双螺杆塑炼机上塑炼，待塑炼均匀后再经水冷拉条后切粒，然后进入离心干燥机进行干燥后，最后进行包装，即得到蓝色阻燃柔软的聚氯乙烯电线电缆料。
经过测试，本发明一种阻燃柔软的聚氯乙烯电缆材料具有如下的性能特征：
Figure BDA0000100447100000041

Claims (9)

1.一种阻燃柔软的聚氯乙烯电线电缆材料，其特征在于其是由以下的重量份数的原料组成：
聚氯乙烯树脂            90～120份；
增塑剂                  20～40份；
矿物填料                5～10份；
金属氧化物               5～10份；
阻燃剂                   5～15份；
抗氧剂           0.8～1.4份
稳定剂                   2～4份；
润滑剂           0.5～1份。
2.根据权利要求1所述的一种阻燃柔软的聚氯乙烯电线电缆材料，其特征在于所述的聚氯乙烯树脂是指K值为73～74的软聚氯乙烯树脂。
3.根据权利要求1所述的一种阻燃柔软的聚氯乙烯电线电缆材料，其特征在于所述的增塑剂是指邻苯二甲酸二辛酯和磷酸二苯异辛酯中的任意一种。
4.根据权利要求1所述的一种阻燃柔软的聚氯乙烯电线电缆材料，其特征在于所述的矿物填料是指碳酸钙和氢氧化铝中的任意一种。
5.根据权利要求1所述的一种阻燃柔软的聚氯乙烯电线电缆材料，其特征在于所述的金属氧化物是指三氧化二锑和三氧化钼中得任意一种。
6.根据权利要求1所述的一种阻燃柔软的聚氯乙烯电线电缆材料，其特征在于所述的阻燃剂是指氯化石蜡和十溴二苯乙烷中的任意一种。
7.根据权利要求1所述的一种阻燃柔软的聚氯乙烯电线电缆材料，其特征在于所述的抗氧剂是指2.4二叔丁基苯基-亚磷酸三酯、硫代二丙酸二月桂酯、硫代二丙酸二硬脂醇酯中的任意一种。
8.根据权利要求1所述的一种阻燃柔软的聚氯乙烯电线电缆材料，其特征在于所述的稳定剂是指三碱式硫酸铅。
9.根据权利要求1所述的一种阻燃柔软的聚氯乙烯电线电缆材料，其特征在于所述的润滑剂是指硬脂酸和硬脂酸钡中的任意一个。
CN2011103203786A 2011-10-20 2011-10-20 一种阻燃柔软的聚氯乙烯电线电缆材料 Pending CN103059451A (zh)