CN101974187A - 90℃绝缘级低烟低卤pvc阻燃护套料 - Google Patents

90℃绝缘级低烟低卤pvc阻燃护套料 Download PDF

Info

Publication number
CN101974187A
CN101974187A CN 201010542703 CN201010542703A CN101974187A CN 101974187 A CN101974187 A CN 101974187A CN 201010542703 CN201010542703 CN 201010542703 CN 201010542703 A CN201010542703 A CN 201010542703A CN 101974187 A CN101974187 A CN 101974187A
Authority
CN
China
Prior art keywords
parts
jacket material
low
agent
pvc
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 201010542703
Other languages
English (en)
Inventor
解洪俊
周春云
王秋中
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JIANGSU BAOYUAN GAOXIN ELECTRIC CO Ltd
Original Assignee
JIANGSU BAOYUAN GAOXIN ELECTRIC CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JIANGSU BAOYUAN GAOXIN ELECTRIC CO Ltd filed Critical JIANGSU BAOYUAN GAOXIN ELECTRIC CO Ltd
Priority to CN 201010542703 priority Critical patent/CN101974187A/zh
Publication of CN101974187A publication Critical patent/CN101974187A/zh
Pending legal-status Critical Current

Abstract

90℃绝缘级低烟低卤PVC阻燃护套料，由重量份为：PVC为100、DOP为20-30、超细高白碳酸钙为20-25、钙锌复合稳定剂为8-10、润滑剂为2-3、三氧化二锑为5-10、锡酸锌为5-10、抑烟剂为2-3、抗老化剂为2-3等材料经高速混合机混合，挤塑机塑化造粒制成。该护套料塑化良好，性能稳定，具有良好的耐热性能、阻燃性能及加工性能。再经电线电缆厂二次加工成电线电缆产品，具有优异的耐热性、机械强度，耐应力开裂、阻燃、耐热变形、耐压等综合性能，可用于110kV及以下电缆用护层，延长产品的使用寿命。采用环保型阻燃剂、稳定剂等，铅、镉含量低，环保无污染。

Description

90℃绝缘级低烟低卤PVC阻燃护套料
技术领域
本发明涉及用于电线电缆的护套材料，特别是90℃绝缘级低烟低卤PVC阻燃护套料，属于电缆护套材料技术领域。
背景技术
电线电缆的结构和用途有各种各样，用户按用途和布设环境选择电线电缆的型号和规格，电线电缆的型号和规格，又与电线电缆的结构、用途和性能相关。电线电缆护套料是影响电线电缆性能的一个重要方面，聚氯乙烯是含氯聚合物，有较好的阻燃性能和线缆生产与使用的要求的各种性能，价格低廉，因而是世界上最广泛使用的塑料之一。现有电线电缆的导电线芯外的绝缘与护套多由塑料或橡胶包覆，其中塑料占包覆材料的91％，而其中的聚氯乙烯又占塑料中的80％。另有资料表明，在一些发达国家，塑料占电线电缆行业中包覆材料的85％，其中聚氯乙烯又占塑料中的60％。随着科学技术的发展，社会的进步，人们环境意识的增强和可持续发展观念的深入人心，有关塑料对环境的污染和是否应禁用普通聚氯乙烯的争论非常多。所以，研究开发一种高性能的环保型的聚氯乙烯电线电缆护套料，是电线电缆护套料研究和生产单位的一项迫切和重要的任务。
发明内容
本发明的目的就是为满足市场的需要，提供一种具有优良的电绝缘和阻燃性能的新型的90℃绝缘级低烟低卤PVC阻燃护套料。
本发明的技术方案是：90℃绝缘级低烟低卤PVC阻燃护套料，其特征是含有PVC树脂、DOP、超细高白碳酸钙、钙锌复合稳定剂、润滑剂、三氧化二锑、锡酸锌、抑烟剂、抗老化剂，其配方组成重量份为：
成份                                用量(重量份)
PVC                                 100
DOP                                 20-30
超细高白碳酸钙                      20-25
钙锌复合稳定剂                      8-10
润滑剂                              2-3
三氧化二锑                          5-10
锡酸锌                              5-10
抑烟剂                              2-3
抗老化剂                            2-3。
所述的润滑剂为硬脂酸或石蜡，或硬脂酸和石蜡的组合。
所述的抑烟剂为有机钼化合物。
所述的抗老化剂为高色素碳黑或中超耐磨碳黑，或为高色素碳黑和中超耐磨碳黑的组合。
本发明配方配比科学合理，将配方组分经塑料高混机混合，挤塑机塑化造粒，该护套料塑化良好，性能稳定，具有良好的耐热性能、阻燃性能及加工性能。再经电线电缆厂二次加工成电线电缆产品，具有优异的耐热性、机械强度，耐应力开裂、阻燃、耐热变形、耐压等综合性能，用于高层建筑、汽车、医疗及电器装备等有环保阻燃要求用线缆护套，导体允许最高工作温度90℃。耐压等级高，可用于110KV及以下电缆用护层。产品既保持了PVC护层级电缆料特性同时又具有的优异电绝缘性能及阻燃性能；采用环保型阻燃剂、稳定剂等，铅、镉含量低，符合线缆绿色环保；具有良好的机械物理性能、电气性能、高阻燃及极佳的挤出加工性能，做成电线后表面平滑、平整，各项性能达到规定技术要求，挤出半制品表面光滑、平整、色泽均匀，并且成品粒料无焦烧粒料、表面颗粒等现象。在杂质控制，生产中不得带入任何杂质。试验材料混合速度、时间及加入的先后顺序，最终选择合适的混合工艺，使各种材料具有良好的分散性。本产品特别适用于电力电缆、控制电缆、船用电缆拉电站，化工、机场、地铁、计算机中心等对燃烧性能要求较高的场合电线电缆的护套料。环保无污染，保护生产人员的身体健康，延长产品的使用寿命。
产品主要物理机械及电气性能技术指标应符合表1规定
Figure BSA00000344137100031
具体实施方式
以下结合具体实施例对本发明作进一步的详细说明，以使本发明的优点更为明显。实施例仅为帮助理解本发明，本发明的保护范围在权利要求书中体现。实施例中：润滑剂为硬脂酸或石蜡，或硬脂酸和石蜡的组合，抑烟剂为有机钼化合物，抗老化剂为高色素碳黑或中超耐磨碳黑，或为高色素碳黑和中超耐磨碳黑的组合。将每一实施例的全部组分经塑料高混机混合，挤塑机塑化造粒后制得90℃绝缘级低烟低卤PVC阻燃护套料。
实施例1：
配方组成如下：
成份                                  用量
PVC                                   100
DOP                                   20
超细高白碳酸钙                        22
钙锌复合稳定剂                        7
润滑剂                                2
三氧化二锑                            5
锡酸锌                                5
抑烟剂                                2
抗老化剂                              2.5。
实施例2
配方组成如下
成份                                  用量(重量份)
PVC                                   100
DOP                                   25
超细高白碳酸钙                        20
钙锌复合稳定剂                        8
润滑剂                                2.5
三氧化二锑                            6
锡酸锌                                6
抑烟剂                                2
抗老化剂                              2.5。
实施例3
配方组成如下
成份                                  用量(重量份)
PVC                                   100
DOP                                   30
钙锌复合稳定剂                        20
超细高白碳酸钙                        9
润滑剂                                2.5
三氧化二锑                            7
锡酸锌                                7
抑烟剂                                3
抗老化剂                              2.5。
实施例4
配方组成如下
成份                                  用量(重量份)
PVC                                   100
DOP                                   30
超细高白碳酸钙                        20
钙锌复合稳定剂                        10
润滑剂                                3
三氧化二锑                            8
锡酸锌                                8
抑烟剂                                3
抗老化剂                              2.5。

Claims (4)

1.一种90℃绝缘级低烟低卤PVC阻燃护套料，其特征是含有PVC树脂、DOP、超细高白碳酸钙、钙锌复合稳定剂、润滑剂、三氧化二锑、硼酸锌、抑烟剂、抗老化剂，其配方组成重量份为：
成份                                          用量
PVC                                           100
DOP                                           20-30
超细高白碳酸钙                                20-25
钙锌复合稳定剂                                8-10
润滑剂                                        2-3
三氧化二锑                                    5-10
硼酸锌                                        5-10
抑烟剂                                        2-3
抗老化剂                                      2-3。
2.根据权利要求1所述的90℃绝缘级低烟低卤PVC阻燃护套料，其特征是所述的润滑剂为硬脂酸或石蜡，或硬脂酸和石蜡的组合。
3.根据权利要求1所述的90℃绝缘级低烟低卤PVC阻燃护套料，其特征是所述的抑烟剂为有机钼化合物。
4.根据权利要求1所述的90℃绝缘级低烟低卤PVC阻燃护套料，其特征是所述的抗老化剂为高色素碳黑或中超耐磨碳黑，或为高色素碳黑和中超耐磨碳黑的组合。
CN 201010542703 2010-11-15 2010-11-15 90℃绝缘级低烟低卤pvc阻燃护套料 Pending CN101974187A (zh)