CN102816394A - 一种聚氯乙烯塑料及其制备方法 - Google Patents

一种聚氯乙烯塑料及其制备方法 Download PDF

Info

Publication number
CN102816394A
CN102816394A CN2011101566357A CN201110156635A CN102816394A CN 102816394 A CN102816394 A CN 102816394A CN 2011101566357 A CN2011101566357 A CN 2011101566357A CN 201110156635 A CN201110156635 A CN 201110156635A CN 102816394 A CN102816394 A CN 102816394A
Authority
CN
China
Prior art keywords
parts
polyvinyl chloride
environment
calcium
environmental protection
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2011101566357A
Other languages
English (en)
Inventor
杨少波
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SHENZHEN XUNDAO INDUSTRIAL Co Ltd
Original Assignee
SHENZHEN XUNDAO INDUSTRIAL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SHENZHEN XUNDAO INDUSTRIAL Co Ltd filed Critical SHENZHEN XUNDAO INDUSTRIAL Co Ltd
Priority to CN2011101566357A priority Critical patent/CN102816394A/zh
Publication of CN102816394A publication Critical patent/CN102816394A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种环保型聚氯乙烯塑料，包括如下重量份的各组分：PVC树脂100份，邻苯二甲酸二辛酯35～50份，环保型热稳定剂3～4份，环氧大豆油3～4份，硬脂酸钙2～3份，氯化石腊6～8份，氧化锌0.02～0.05份，活性钙10～30份。本发明公开的环保型聚氯乙烯塑料，符合GB/T 8815-2002《电线电缆用软聚氯乙烯塑料》中“H-70”型号要求以及RoHS要求。

Description

一种聚氯乙烯塑料及其制备方法
技术领域
本发明涉及热塑性材料技术领域，特别涉及一种环保型聚氯乙烯塑料及其制备方法。
背景技术
聚氯乙烯(PVC)因其具有阻燃、耐候、防腐及耐化学品腐蚀等优点应成为人们最常用的树脂之一，广泛用于电线电缆的制备材料。随着社会的发展，电线电缆被越来越广泛应用到各个领域，因此，对电线电缆的要求也越来越高，而由于聚氯乙烯的结构的特殊性，聚氯乙烯的热稳定性、抗冲性能、加工新型及环保性较差，在实际应用体系中一般含有稳定剂、润滑剂等添加剂。传统的聚氯乙烯电线电缆材料由于其中稳定剂已有配方为普通聚氯乙烯塑料配方，涉及到的配方材料均为非环保材料，用此类配方生产出的产品，不符合中国《电子信息产品污染控制管理办法》(中国RoHS)及欧盟《关于在电子设备中限制使用某些有害物质的指令》(RoHS指令)。
发明内容
为克服上述技术缺陷，本发明公开了一种环保型聚氯乙烯塑料，符合GB/T8815-2002《电线电缆用软聚氯乙烯塑料》中“H-70”型号要求以及RoHS要求。
本发明的技术方案如下所述：一种环保型聚氯乙烯塑料，包括如下重量份的各组分：PVC树脂100份，邻苯二甲酸二辛酯35～50份，环保型热稳定剂3～4份，环氧大豆油3～4份，硬脂酸钙2～3份，氯化石腊6～8份，氧化锌0.02～0.05份，活性钙10～30份。
进一步地，上述塑料还包括颜色粉，所述颜色粉重量份为0.5～2份。
进一步地，上述塑料优选为包括如下重量份的各组分：PVC树脂100份，邻苯二甲酸二辛酯38份，环保型热稳定剂3.5份，环氧大豆油3份，硬脂酸钙2份，氯化石腊6份，氧化锌0.02份，活性钙10份。
所述环保型热稳定剂是环保型钙锌热稳定剂。
本发明还公开了上述环保型聚氯乙烯塑料的制备方法，包括如下步骤：
(1)将所有原料混合、搅拌；(2)切粒；(3)包装；(4)入库。
本发明由于在聚氯乙烯塑料中采用的是环保型配方，在保证其突出的物理性能的同时，大大降低了对人体有害物质的使用，符合中国《电子信息产品污染控制管理办法》(中国RoHS)及欧盟《关于在电子设备中限制使用某些有害物质的指令》(RoHS指令)要求。
具体实施方式
下面将通过具体实施例对本发明进行详细说明。
实施例1：
环保型聚氯乙烯塑料配方：PVC树脂100份，邻苯二甲酸二辛酯38份，环保型钙锌热稳定剂3.5份，环氧大豆油3份，硬脂酸钙2份，氯化石腊6份，氧化锌0.02份，活性钙10份。
实施例2：
环保型聚氯乙烯塑料配方：PVC树脂100份，邻苯二甲酸二辛酯35份，环保型钙锌热稳定剂4份，环氧大豆油4份，硬脂酸钙3份，氯化石腊8份，氧化锌0.05份，活性钙30份。
实施例3：
环保型聚氯乙烯塑料配方：PVC树脂100份，邻苯二甲酸二辛酯45份，环保型钙锌热稳定剂3份，环氧大豆油3.5份，硬脂酸钙2.5份，氯化石腊7份，氧化锌0.03份，活性钙20份，颜色粉1份。
实施例4：
环保型聚氯乙烯塑料配方：PVC树脂100份，邻苯二甲酸二辛酯50份，环保型钙锌热稳定剂3.2份，环氧大豆油3.5份，硬脂酸钙2.8份，氯化石腊7.5份，氧化锌0.04份，活性钙25份，颜色粉0.5份。
制备方法：分别将实施例1-4中的所有原料在混合机中混合、搅拌，将混合好的原料加入到双螺杆挤出机中挤出、切粒，然后包装、入库即得到聚氯乙烯电线电缆材料，为颗粒状，制备压片试验，其主要特性如延伸率、抗张强度、绝缘电阻等均符合国家标准GB/T 8815-2005要求。
综上所述，尽管本发明通过具体实施例对本发明进行了详细描述，但本领域一般技术人员应该明白的是，上述实施例仅仅是对本发明的优选实施例的描述，而非对本发明保护范围的限制，本领域一般技术人员在本发明所揭露的技术范围内，可轻易想到的变化，均在本发明的保护范围。

Claims (5)

1.一种聚氯乙烯塑料，其特征在于包括如下重量份的各组分：
PVC树脂：100份
邻苯二甲酸二辛酯：35～50份
环保型热稳定剂：3～4份
环氧大豆油：3～4份
硬脂酸钙：2～3份
氯化石腊：6～8份
氧化锌：0.02～0.05份
活性钙：10～30份。
2.如权利要求1所述的环保型聚氯乙烯塑料，其特征在于：还包括颜色粉，所述颜色粉重量份为0.5～2份。
3.如权利要求1所述的环保型聚氯乙烯塑料，其特征在于包括如下重量份的各组分：
PVC树脂：100份
邻苯二甲酸二辛酯：38份
环保型热稳定剂：3.5份
环氧大豆油：3份
硬脂酸钙：2份
氯化石腊：6份
氧化锌：0.02份
活性钙：10份。
4.如权利要求1-3任意一项所述的环保型聚氯乙烯塑料，其特征在于：所述环保型热稳定剂是环保型钙锌热稳定剂。
5.如权利要求1所述的环保型聚氯乙烯塑料的制备方法，其特征在于包括如下步骤：
(1)将所有原料混合、搅拌；
(2)切粒；
(3)包装；
(4)入库。
CN2011101566357A 2011-06-10 2011-06-10 一种聚氯乙烯塑料及其制备方法 Pending CN102816394A (zh)