CN103012657B - 大孔弱碱性丙烯酸复合taic阴离子交换树脂的制备方法 - Google Patents
大孔弱碱性丙烯酸复合taic阴离子交换树脂的制备方法 Download PDFInfo
- Publication number
- CN103012657B CN103012657B CN201210489884.2A CN201210489884A CN103012657B CN 103012657 B CN103012657 B CN 103012657B CN 201210489884 A CN201210489884 A CN 201210489884A CN 103012657 B CN103012657 B CN 103012657B
- Authority
- CN
- China
- Prior art keywords
- ball
- exchange resin
- warming
- anionite
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种大孔弱碱性丙烯酸复合TAIC阴离子交换树脂的制备方法，在传统生产工艺基础上，本发明通过合理搭配悬浮保护剂、分散剂、致孔剂、络合剂，优化工艺参数，使得本方法制备的阴离子交换树脂，孔径分布均匀，交换容量提高的效果，本发明制得的离子交换树脂比表面积能达到70m2/g以上，大于2nm的中孔比例大于50％，全交换容量达到5.5mmol/g。
Description
技术领域
本发明属于一种离子交换树脂的制备方法，具体是一种大孔弱碱性丙烯酸复合TAIC阴离子交换树脂的制备方法。
背景技术
阴、阳离子交换树脂广泛地用于水处理、物质的净化、浓缩、分离、物质离子组成的转变、物质的脱色以及催化剂等领域。虽然目前的阴、阳离子交换树脂的交换容量得到了有效的提高，但孔径分布不均，小孔比例过大，交换速度低。交换容量不足等问题，满足不了客户的要求。
发明内容
本发明的目的是提供一种大孔弱碱性丙烯酸复合TAIC阴离子交换树脂的制备方法，本发明通过水相的改进，使得分散性、悬浮性提高，进而达到增加离子交换树脂的交换容量，孔径分布均匀的效果。
本发明的技术方案如下：
大孔弱碱性丙烯酸复合TAIC阴离子交换树脂的制备方法，其特征在于包括以下步骤：
（1）、聚合制备A球，包括以下步骤：
按规定配好水相，搅拌均匀；
去离子水450-480
聚乙烯醇10-15
羟乙基纤维素20-30
氯化钠40-45
过硫酸钠1-2
用硫酸调PH为6.8-7.2
称取下列重量份的原料，混合后加入后水相中，视粒度情况调整转速；
丙烯酸甲酯220-240
二乙烯苯50-55
TAIC70-90
200#汽油158-163
二茂铁10-15
偶氮二异丁腈3-5
缓慢升温至65-69℃，注意观察球体粒度及定型情况；
定型时放热，降温，放热后保持温度在68-70℃，保温2-3小时；
用25-40分钟时间升温至80-82℃保温3-4h；
用50-70分钟时间升温92-96℃保温4-5h；
用热水洗球数遍至水清澈为止；
抽干水，烘干，分筛制得A球。
（2）、胺化反应制备B球
按下列重量份称取下列原料，在干净的反应釜中加入A球和四乙烯五胺，开动搅拌；
A球380-420
四乙烯五胺1580-1620
二乙烯三胺300-320
乙酸乙酯30-35
升温至130-135℃，保温反应15-18h，测中控交换大于8.0mmol/g合格；
中控合格后，抽母液，回收四乙烯五胺；
大量水洗至中性，抽干，得B球；
（3）、甲基化反应制备树脂
将B球加入下列重量份的混合原料中，开动搅拌；
甲酸1150-1250
水200-240
甲醛60-65
升温至48-50℃，保持20-40分钟；
抽干母液，大量水洗至中性，抽干，出料。
本发明通过合理搭配悬浮保护剂、分散剂、致孔剂、络合剂，优化工艺参数，使得本方法制备的阴离子交换树脂，孔径分布均，交换容量提高的效果，本发明制得的离子交换树脂比表面积能达到70m2/g以上，大于2nm的中孔比例大于50％，全交换容量达到11.5mmol/g。
具体实施方式
大孔弱碱性丙烯酸复合TAIC阴离子交换树脂的制备方法，包括以下步骤：
（1）、聚合制备A球，包括以下步骤：
按下列重量（公斤）配好水相，搅拌均匀；
去离子水450
聚乙烯醇10
羟乙基纤维素20
氯化钠40
过硫酸钠1
用硫酸调PH为6.8-7.2
称取下列重量（公斤）的原料，混合后加入后水相中，视粒度情况调整转速；
丙烯酸甲酯220
二乙烯苯50
TAIC70
200#汽油158
二茂铁10
偶氮二异丁腈3
缓慢升温至65-69℃，注意观察球体粒度及定型情况；
定型时放热，降温，放热后保持温度在68-70℃，保温2-3小时；
用25-40分钟时间升温至80-82℃保温3-4h；
用50-70分钟时间升温92-96℃保温4-5h；
用热水洗球数遍至水清澈为止；
抽干水，烘干，分筛制得A球。
（2）、胺化反应制备B球
按下列重量（公斤）称取下列原料，在干净的反应釜中加入A球和四乙烯五胺，开动搅拌；
A球380
四乙烯五胺1580
二乙烯三胺300
乙酸乙酯30
升温至130-135℃，保温反应15-18h，测中控交换大于8.0mmol/g合格；
中控合格后，抽母液，回收四乙烯五胺；
大量水洗至中性，抽干，得B球；
（3）、甲基化反应制备树脂
将B球加入下列重量（公斤）的混合原料中，开动搅拌；
甲酸1150
水200
甲醛60
升温至48-50℃，保持20-40分钟；
抽干母液，大量水洗至中性，抽干，出料。
本发明制得的离子交换树脂比表面积能达到70m2/g以上，大于2nm的中孔比例大于50％，全交换容量达到11.5mmol/g。
Claims (1)
1.大孔弱碱性丙烯酸复合TAIC阴离子交换树脂的制备方法，其特征在于包括以下步骤：
（1）、聚合制备A球，包括以下步骤：
按规定配好水相，搅拌均匀；
去离子水450-480
聚乙烯醇10-15
羟乙基纤维素20-30
氯化钠40-45
过硫酸钠1-2
用硫酸调pH为6.8-7.2
称取下列重量份的原料，混合后加入水相中，视粒度情况调整转速；
丙烯酸甲酯220-240
二乙烯苯50-55
TAIC70-90
200#汽油158-163
二茂铁10-15
偶氮二异丁腈3-5
缓慢升温至65-69℃，注意观察球体粒度及定型情况；
定型时放热，降温，放热后保持温度在68-70℃，保温2-3小时；
用25-40分钟时间升温至80-82℃保温3-4h；
用50-70分钟时间升温至92-96℃保温4-5h；
用热水洗球数遍至水清澈为止；
抽干水，烘干，分筛制得A球；
（2）、胺化反应制备B球
按下列重量份称取下列原料，在干净的反应釜中加入A球和四乙烯五胺，开动搅拌；
A球380-420
四乙烯五胺1580-1620
二乙烯三胺300-320
乙酸乙酯30-35
升温至130-135℃，保温反应15-18h，测中控全交换容量大于8.0mmol/g合格；
中控合格后，抽母液，回收四乙烯五胺；
大量水洗至中性，抽干，得B球；
（3）、甲基化反应制备树脂
将B球加入下列重量份的混合原料中，开动搅拌；
甲酸1150-1250
水200-240
甲醛60-65
升温至48-50℃，保持20-40分钟；
抽干母液，大量水洗至中性，抽干，出料。