CN102964522A - 一种魔芋葡甘聚糖复合调湿剂的制备方法 - Google Patents

一种魔芋葡甘聚糖复合调湿剂的制备方法 Download PDF

Info

Publication number
CN102964522A
CN102964522A CN2012104699567A CN201210469956A CN102964522A CN 102964522 A CN102964522 A CN 102964522A CN 2012104699567 A CN2012104699567 A CN 2012104699567A CN 201210469956 A CN201210469956 A CN 201210469956A CN 102964522 A CN102964522 A CN 102964522A
Authority
CN
China
Prior art keywords
humidity conditioning
konjac glucomannan
sodium hydroxide
temperature
urea
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2012104699567A
Other languages
English (en)
Other versions
CN102964522B (zh
Inventor
俞宁
王秉
胡智文
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhejiang Sci Tech University ZSTU
Zhejiang University of Science and Technology ZUST
Original Assignee
Zhejiang Sci Tech University ZSTU
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhejiang Sci Tech University ZSTU filed Critical Zhejiang Sci Tech University ZSTU
Priority to CN201210469956.7A priority Critical patent/CN102964522B/zh
Publication of CN102964522A publication Critical patent/CN102964522A/zh
Application granted granted Critical
Publication of CN102964522B publication Critical patent/CN102964522B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种魔芋葡甘聚糖复合调湿剂的制备方法，其步骤如下：a、取1氢氧化钠加入到去离子水中溶解，再加丙烯酸单体于前述氢氧化钠溶液中，在温度为65-70℃下搅拌均匀；b、取过硫酸钾，活化后粒度为200目的埃洛石，魔芋葡甘聚糖，纳米载银抗菌粉，N,N’-亚甲基双丙烯酰胺，尿素依次加入到盛有步骤a所得溶液的反应器中，在温度为65-70℃下反应20-30min，得到粘稠固体产物；c、待步骤b反应得到的聚合物冷却至室温后，在145-150℃下干燥4-5小时，通过尿素分解发泡，得到多孔性的调湿材料，用粉碎机粉碎2-3min，得到100-200目的调湿材料粉末；本发明湿含量、湿容量大，相对湿度稳定性好；制备简便，成本低，效果佳；环保，无污染。

Description

一种魔芋葡甘聚糖复合调湿剂的制备方法
技术领域
本发明涉及一种调湿材料的制备方法，特别是一种魔芋葡甘聚糖复合调湿剂的制备方法。
背景技术
随着生活水平的提高，人们对室内环境质量的要求也越来越高，而室内空气的相对湿度作为衡量室内环境质量的一个重要参数，也得到了越来越多的关注。
调湿材料作为一种被动调湿手段，无需消耗任何能源，对于能源节约性社会建设、促进生态环境的可持续发展并改善室内空气质量、提高环境舒适度等具有重要的实际意义，因而越来越多的研究者开始对调湿材料进行各种研究工作。
现有技术中制备的许多调湿材料存在如下缺点：调湿材料内部孔道少，造成吸放湿性能下降；在高湿环境下易霉变，产生病菌等；调湿材料粉末吸湿后造成颗粒团聚，降低调湿性能。
有机高分子材料湿容量大，但其放湿性能相对滞后，矿物材料相对于有机高分子材料湿容量小。将有机高分子材料与多孔性矿物及天然高分子材料复合可提高调湿材料内部孔隙率，改善放湿性能，湿容量大，并且具有环保功效。魔芋为天南星科多年生草本植物的块茎,在我国分布广泛，魔芋葡甘聚糖吸水性强,在水中的溶胀度高，埃洛石是一种多孔性的无机矿物材料，表面吸附性能强。将有机高分子材料与魔芋葡甘聚糖及埃洛石复合可以制备出一种天然复合调湿剂。
发明内容
本发明是要克服上述现有技术中存在的不足，提供一种魔芋葡甘聚糖复合调湿剂的制备方法，用魔芋葡甘聚糖来增加材料的湿容量，利用特殊的纳米孔道结构来改善调湿速率，并导入抗菌材料，解决调湿材料在高湿环境下易霉变的问题；再经过发泡处理，形成多重多孔性调湿材料，使其具有湿容量大，调湿响应快，提高放湿速率，环保，稳定性佳的优点。
本发明所采用的技术方案是：一种魔芋葡甘聚糖复合调湿剂的制备方法，其特征在于步骤如下：
a、按质量份数取12-15份氢氧化钠加入到100-120份去离子水中溶解，再加30份的丙烯酸单体于前述氢氧化钠溶液中，在温度为65-70℃下搅拌均匀；
b、按质量份数取0.3-0.6份过硫酸钾，1-5份活化后粒度为200目的埃洛石，1-3份魔芋葡甘聚糖，0.01-1份纳米载银抗菌粉，0.3份N,N’-亚甲基双丙烯酰胺，3份尿素依次加入到盛有步骤a所得溶液的反应器中，在温度为65-70℃下反应20-30min，得到粘稠固体产物；
c、待步骤b反应得到的聚合物冷却至室温后，在145-150℃下干燥4-5小时，通过尿素分解发泡，得到多孔性的调湿材料，用粉碎机粉碎2-3min，得到100-200目的调湿材料粉末。
埃洛石经400℃焙烧2-2.5小时活化。
本发明的有益效果是：1、在调湿材料中复合纳米载银抗菌粉，解决了调湿材料在高湿环境下易霉变的问题，具有杀菌、抗病毒，降解细菌、有机物的作用。2、采用尿素发泡，形成多孔性调湿材料，增加调湿材料内部孔洞，增大了调湿材料的湿容量，提高了其调湿响应速度和放湿速率。3、与现有调湿剂相比，本发明湿含量、湿容量大，相对湿度稳定性好；制备简便，成本低，效果佳；环保，无污染。
具体实施方式
本发明克服单一调湿材料调湿性能缺陷，将有机高分子材料，无机矿物材料，天然高分子材料及抗菌材料复合在一起，一方面吸收各类调湿材料的优点，提高合成材料本身的湿容量和调湿性能，同时解决调湿材料在高湿环境下易霉变的问题，具有杀菌、抗病毒，降解细菌、有机物的作用；另一方面通过尿素发泡，形成多孔性调湿材料，增加调湿材料内部孔洞，使其具有湿容量大，调湿响应快，提高放湿速率，环保，稳定性佳的优点。
下面结合实施例对本发明作进一步说明：
实施例1：一种魔芋葡甘聚糖复合调湿剂的制备方法，其特征在于步骤如下：
a、按质量份数取12份氢氧化钠加入到100份去离子水中溶解，再加30份的丙烯酸单体于前述氢氧化钠溶液中，在温度为65℃下搅拌均匀；
b、按质量份数取引发剂0.3份过硫酸钾，1份活化后粒度为200目的埃洛石，1份魔芋葡甘聚糖，0.01份纳米载银抗菌粉，交联剂0.3份N,N’-亚甲基双丙烯酰胺，发泡剂3份尿素依次加入到盛有步骤a所得溶液的反应器中，在温度为65℃下反应20min，得到粘稠固体产物；
c、待步骤b反应得到的聚合物冷却至室温后，在145℃下干燥4小时，通过尿素分解发泡，得到多孔性的调湿材料，用高速粉碎机粉碎2min，得到100目的调湿材料粉末。
所述的埃洛石经400℃焙烧2小时活化。
实施例2：一种魔芋葡甘聚糖复合调湿剂的制备方法，其特征在于步骤如下：
a、按质量份数取13.5份氢氧化钠加入到110份去离子水中溶解，再加30份的丙烯酸单体于前述氢氧化钠溶液中，在温度为67.5℃下搅拌均匀；
b、按质量份数取引发剂0.45份过硫酸钾，3份活化后粒度为200目的埃洛石，2份魔芋葡甘聚糖，0.5份纳米载银抗菌粉，交联剂0.3份N,N’-亚甲基双丙烯酰胺，发泡剂3份尿素依次加入到盛有步骤a所得溶液的反应器中，在温度为67.5℃下反应25min，得到粘稠固体产物；
c、待步骤b反应得到的聚合物冷却至室温后，在147.5℃下干燥4.5小时，通过尿素分解发泡，得到多孔性的调湿材料，用高速粉碎机粉碎2.5min，得到150目的调湿材料粉末。
所述的埃洛石经400℃焙烧2.25小时活化。
实施例3：一种魔芋葡甘聚糖复合调湿剂的制备方法，其特征在于步骤如下：
a、按质量份数取15份氢氧化钠加入到120份去离子水中溶解，再加30份的丙烯酸单体于前述氢氧化钠溶液中，在温度为70℃下搅拌均匀；
b、按质量份数取引发剂0.6份过硫酸钾，5份活化后粒度为200目的埃洛石，3份魔芋葡甘聚糖，1份纳米载银抗菌粉，交联剂0.3份N,N’-亚甲基双丙烯酰胺，发泡剂3份尿素依次加入到盛有步骤a所得溶液的反应器中，在温度为70℃下反应30min，得到粘稠固体产物；
c、待步骤b反应得到的聚合物冷却至室温后，在150℃下干燥5小时，通过尿素分解发泡，得到多孔性的调湿材料，用高速粉碎机粉碎3min，得到200目的调湿材料粉末。
所述的埃洛石经400℃焙烧2.5小时活化。
上述各实施例中原料均按质量份数称取。

Claims (2)

1.一种魔芋葡甘聚糖复合调湿剂的制备方法，其特征在于步骤如下：
a、按质量份数取12-15份氢氧化钠加入到100-120份去离子水中溶解，再加30份的丙烯酸单体于前述氢氧化钠溶液中，在温度为65-70℃下搅拌均匀；
b、按质量份数取0.3-0.6份过硫酸钾，1-5份活化后粒度为200目的埃洛石，1-3份魔芋葡甘聚糖，0.01-1份纳米载银抗菌粉，0.3份N,N’-亚甲基双丙烯酰胺，3份尿素依次加入到盛有步骤a所得溶液的反应器中，在温度为65-70℃下反应20-30min，得到粘稠固体产物；
c、待步骤b反应得到的聚合物冷却至室温后，在145-150℃下干燥4-5小时，通过尿素分解发泡，得到多孔性的调湿材料，用粉碎机粉碎2-3min，得到100-200目的调湿材料粉末。
2.根据权利要求1所述的魔芋葡甘聚糖复合调湿剂的制备方法，其特征在于：所述的埃洛石经400℃焙烧2-2.5小时活化。
CN201210469956.7A 2012-11-19 2012-11-19 一种魔芋葡甘聚糖复合调湿剂的制备方法 Expired - Fee Related CN102964522B (zh)