CN102627871A - 一种新型表面有机化改性无机纳米调湿材料的制备方法 - Google Patents
一种新型表面有机化改性无机纳米调湿材料的制备方法 Download PDFInfo
- Publication number
- CN102627871A CN102627871A CN2012101195826A CN201210119582A CN102627871A CN 102627871 A CN102627871 A CN 102627871A CN 2012101195826 A CN2012101195826 A CN 2012101195826A CN 201210119582 A CN201210119582 A CN 201210119582A CN 102627871 A CN102627871 A CN 102627871A
- Authority
- CN
- China
- Prior art keywords
- halloysite
- nanotube
- novel surface
- nanotube halloysite
- modified inorganic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种新型表面有机化改性无机纳米调湿材料的制备方法，步骤在于：A)制得纯化纳米管埃洛石；B)制得酸化纳米管埃洛石；C)取酸化后的纳米管埃洛石以重量比1：10~20加入到质量百分比浓度5~10%的有机改性剂溶液中，所述的有机改性剂为十二烷基硫酸钠或十六烷基三甲基溴化铵；在50~80℃温度下，搅拌2~3小时，干燥，制得一种新型表面有机化改性无机纳米调湿材料。本发明制备的表面接枝改性无机纳米调湿材料，具有湿度响应速度快的特点，同时由于在纳米管埃洛石表面接枝上具有一定聚合度的亲水性高分子，一方面能使其湿容量得到提高，另一方面利于纳米管埃洛石进一步与别的有机调湿材料复合，制备性能更佳的有机/无机复合调湿材料。
Description
技术领域
本发明属于改性无机材料的制备技术领域，涉及的是一种新型表面有机化改性无机纳米调湿材料的制备方法。
背景技术
空气湿度是一个与人们生活和生产有密切关系的重要环境参数。湿度对人体舒适度、室内空气质量、物品的保护都有重要意义。目前温度的控制已经比较简单有效，但对空气湿度的控制还是比较困难，尤其对文物、药品、高档珠宝等来说，环境相对湿度波动造成的损害比温度造成的损害大。因此对湿度进行有效控制显得更为重要和迫切。调湿材料是无需消耗电力等不可再生能源、具有良好自动调节空气湿度能力的生态环境材料，对节约能源、改善环境舒适性、促进生态环境的可持续发展等具有重要意义。
纳米管埃洛石是一种铝硅酸盐矿物，具有纳米中空管状结构，管径在10～30nm之间，管长在10～30um之间，其化学组成与高岭石相同，但比高岭石含有更高的水分。埃洛石在催化剂、功能材料、陶瓷材料、纳米复合材料、环境保护等方面具有广泛的应用前景，如在化学工业上可合成分子筛和作催化剂的载体，在塑料、橡胶和油漆工业中用作填料等。事实上，埃洛石纳米管表面和层间含有活泼羟基，而且其具有纳米管道结构，这为其吸湿性能提供了理论基础，但目前有关纳米管埃洛石作为调湿材料并没有得到重视，未曾见过报道。
将一维纳米管道结构的埃洛石进行一定的热活化和酸活化修饰处理后再进行有机化改性，能在埃洛石纳米管内外表面附上一定的有机改性剂分子层，便于纳米管埃洛石进一步与别的有机调湿材料复合，制备性能更优的有机/无机复合调湿材料。
发明内容
本发明旨在于提供一种新型表面有机化改性无机纳米调湿材料的制备方法。
为此，本发明采用的技术方案如下：
A)将粉状纳米管埃洛石(200-500目)以重量比1∶10～100加入到水中，离心分离10～30min，将矿浆中悬浮的埃洛石过滤，干燥，制得纯化纳米管埃洛石；
B)将纯化后的纳米管埃洛石以重量比1∶10～20加入到质量百分比浓度为3～10％的盐酸溶液中，在20～30℃温度下，搅拌2～3小时，干燥，制得酸化纳米管埃洛石；
C)取酸化后的纳米管埃洛石以重量比1∶10～20加入到质量百分比浓度5～10％的有机改性剂溶液中，所述的有机改性剂为十二烷基硫酸钠或十六烷基三甲基溴化铵；在50～80℃温度下，搅拌2～3小时，干燥，制得一种新型表面有机化改性无机纳米调湿材料。
本发明制备的表面接枝改性无机纳米调湿材料，具有湿度响应速度快的特点，同时由于在纳米管埃洛石表面接枝上具有一定聚合度的亲水性高分子，一方面能使其湿容量得到提高，另一方面利于纳米管埃洛石进一步与别的有机调湿材料复合，制备性能更佳的有机/无机复合调湿材料。
具体实施方式
A)将粉状纳米管埃洛石以200目和500目两次过筛，取粒径在200-500目的粉状纳米管埃洛石，称取1kg，加入到50kg水中，离心分离30min，将矿浆中悬浮的埃洛石过滤，干燥，制得纯化纳米管埃洛石；
B)将纯化后的纳米管埃洛石700g加入到10kg质量百分比浓度为10％的盐酸溶液中，在20～30℃温度下，搅拌2小时，干燥，制得酸化纳米管埃洛石；
C)取酸化后的纳米管埃洛石700g，加入到10L质量百分比浓度5％的十二烷基硫酸钠溶液中，搅拌2～3小时，干燥，制得一种新型表面有机化改性无机纳米调湿材料。
Claims (1)
1.一种新型表面有机化改性无机纳米调湿材料的制备方法，其特征在于采用如下步骤：
A)将粉状纳米管埃洛石(200-500目)以重量比1∶10～100加入到水中，离心分离10～30min，将矿浆中悬浮的埃洛石过滤，干燥，制得纯化纳米管埃洛石；
B)将纯化后的纳米管埃洛石以重量比1∶10～20加入到质量百分比浓度为3～10％的盐酸溶液中，在20～30℃温度下，搅拌2～3小时，干燥，制得酸化纳米管埃洛石；
C)取酸化后的纳米管埃洛石以重量比1∶10～20加入到质量百分比浓度5～10％的有机改性剂溶液中，所述的有机改性剂为十二烷基硫酸钠或十六烷基三甲基溴化铵；在50～80℃温度下，搅拌2～3小时，干燥，制得一种新型表面有机化改性无机纳米调湿材料。